CN1781992A - 可降解的环保材料的制备方法 - Google Patents

可降解的环保材料的制备方法 Download PDF

Info

Publication number
CN1781992A
CN1781992A CN 200410096490 CN200410096490A CN1781992A CN 1781992 A CN1781992 A CN 1781992A CN 200410096490 CN200410096490 CN 200410096490 CN 200410096490 A CN200410096490 A CN 200410096490A CN 1781992 A CN1781992 A CN 1781992A
Authority
CN
China
Prior art keywords
preparation
green body
sheet material
crude green
tackiness agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200410096490
Other languages
English (en)
Inventor
姚启文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 200410096490 priority Critical patent/CN1781992A/zh
Publication of CN1781992A publication Critical patent/CN1781992A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种可降解的环保材料的制备方法,它是将麦杆、稻草、蔗楂、玉米叶粉碎成细丝或粉末与用面粉、米粉、淀粉或麦皮、玉米皮、米皮的粉皮末熬制成的粘合剂或商购的粘合剂混合搅拌成胶状物后,经滚压挤流成片材或模压制成产品粗坯,再经高温烘干,喷漆,粘贴而成,本发明与现有技术相比,用本发明制成的产品,它无毒无污染,可降解,而且外观美,成本低,适于普及推广。

Description

可降解的环保材料的制备方法
技术领域
本发明涉及一种可降解的环保材料的制备方法,具体的说是涉及一种由麦杆、稻草、蔗楂、玉米叶等植物细丝与粘合剂混合制备而成的可降解的片材或产品的制备方法。
背景技术
目前,随着国民经济的迅猛发展和人民生活水平的日益提高,碗、盘、罐、盆等,及其它盛装容器的需求量,尤其是快餐餐具的需求量也越来越大。然而,市场上销售的各种容器,多为陶瓷器具,这种陶瓷器具的制备较为复杂,成本也高,而且容易破碎损坏,废弃后不能降解,易造成环境污染。另外,为适应人们快节奏的生活,市场上出现了很多一次性容器,这种一次性容器多由不可降解的聚乙稀塑料制备而成,它的使用给社会上造成了“白色污染”,给生态环境带来严重的破坏。再者,在现实生活中那些纯天然的植物原料,如麦杆、稻草、蔗楂、玉米叶等没有得到充分的利用,有的被烧掉了,有的是任其腐烂,造成浪费,污染环境。
发明内容
本发明的目的在于提供一种可降解的环保材料的制备方法,以充分利用植物的废弃物,制备有用的材料。
本发明的目的是这样实现的,它是将麦杆、稻草、蔗楂、玉米叶粉碎成细丝或粉末与用面粉、米粉、淀粉或麦皮、玉米皮、米皮的粉皮末熬制成的粘合剂或商购的粘合剂混合搅拌后,经滚压挤流成片材或模压制成产品粗坯,再经高温烘干,喷漆,粘贴而成,
其特征在于,制备方法如下:
一、骨材的制备
①先将麦杆、稻草、蔗楂、玉米叶天然植物原料,清洗消毒,
②将上述植物原料干燥至含水量小于10%
③将上述的植物原料粉碎成长度为1-1.5公分的细丝小段或粒度为50-150目的粉末,
二、粘合剂的制备
①用面粉、米粉、淀粉或麦皮、玉米皮、米皮中的一种或两种以上按1比1混合得混合物,
②将上述混合物内加入15-20倍的水,搅拌均匀,得搅拌物,
③将搅拌物用温火熬成浆糊状,得粘合剂,
三、片材或产品粗坯的制备
①将上述粘合剂或市场上商购到的粘合剂与骨材以1∶0.05-0.1混合,并搅拌至完全粘贴,得胶状物,
②将胶状物倒入滚压机内挤流出成张的平薄片材或倒入模压机内模制成产品粗坯,
③将片材或产品粗坯送进烘干机内彻底烘干,
④将烘干的片材或产品粗坯进行喷漆上胶或喷漆涂料,干燥,
四、成品的制备
①将片材喷漆上胶后,粘贴上面材,得本发明的片材产品,
②将产品粗坯喷涂上油漆,得本发明的成形产品。
其特征在于所述的片材或产品粗坯其厚度为1-10毫米。
所述的面材可为纸张、纸覆膜、纸金银薄膜、纸锡粘膜、金属膜或塑料膜。
本发明与现有技术相比,用本发明制成的产品,它无毒无污染,可降解,而且外观美,成本低,适于普及推广。
具体实施方式
以下结合实施例对本发明进一步说明:
实施例1  片材的制备
一、骨材的制备
①先将麦杆清洗,晒干,
②将麦杆原料干燥至含水量小于10%
③将麦杆原料粉碎成长度为1公分的细丝小段,
二.粘合剂的制备
①用面粉或麦皮按1比1混合得混合物,
②将上述10公斤混合物内加入180公斤的水,搅拌均匀,得搅拌物,
③将搅拌物用温火熬成浆糊状,得粘合剂,
三、片材的制备
①取上述50公斤粘合剂与5公斤骨材混合,并搅拌至完全粘贴,得胶状物,
②将胶状物倒入滚压机内挤流出成张的厚度为2毫米的平薄片材,
③将片材送进烘干机内彻底烘干,
④将烘干的片材进行喷漆上胶,干燥,
四、成品的制备
将片材喷漆上胶后,粘贴上彩色塑料膜,得本发明的片材产品。
实施例2  饭盒的制备
一、骨材的制备
①先将稻草原料,清洗,晒干消毒,
②将稻草原料干燥至含水量小于10%
③将稻草原料粉碎成粒度为100目的粉末,
二、粘合剂的制备
①用米粉和米皮按1比1混合得混合物,
②将上述10公斤混合物内加入150公斤的水,搅拌均匀,得搅拌物,
③将搅拌物用温火熬成浆糊状,得粘合剂,
三、饭盒粗坯的制备
①取上述50公斤粘合剂与5公斤稻草粉末骨材混合,并搅拌至完全粘贴,得胶状物,
②将胶状物倒入模压机内模制成100个饭盒粗坯,其厚度为1毫米,
③将饭盒粗坯送进烘干机内彻底烘干,
④将烘干的饭盒粗坯进行喷漆涂料,干燥,
四、成品的制备
将饭盒粗坯喷涂上油漆,得本发明的成形产品100个饭盒。

Claims (3)

1、一种可降解的环保材料的制备方法,它是将麦杆、稻草、蔗楂、玉米叶粉碎成细丝或粉末与用面粉、米粉、淀粉或麦皮、玉米皮、米皮的粉皮末熬制成的粘合剂或商购的粘合剂混合搅拌成胶状物后,经滚压挤流成片材或模压制成产品粗坯,再经高温烘干,喷漆,粘贴而成,
其特征在于,制备方法如下:
一、骨材的制备
①先将麦杆、稻草、蔗楂、玉米叶天然植物原料,清洗消毒,
②将上述植物原料干燥至含水量小于10%
③将上述的植物原料粉碎成长度为1-1.5公分的细丝小段或粒度为50-150目的粉末,
二、粘合剂的制备
①用面粉、米粉、淀粉或麦皮、玉米皮、米皮中的一种或两种以上按1比1混合得混合物,
②将上述混合物内加入15-20倍的水,搅拌均匀,得搅拌物,
③将搅拌物用温火熬成浆糊状,得粘合剂,
三、片材或产品粗坯的制备
①将上述粘合剂或市场上商购到的粘合剂与骨材以1∶0.05-0.1混合,并搅拌至完全粘贴,得胶状物,
②将胶状物倒入滚压机内挤流出成张的平薄片材或倒入模压机内模制成产品粗坯,
③将片材或产品粗坯送进烘干机内彻底烘干,
④将烘干的片材或产品粗坯进行喷漆上胶或喷漆涂料,干燥,
四、成品的制备
①将片材喷漆上胶后,粘贴上面材,得本发明的片材产品,
②将产品粗坯喷涂上油漆,得本发明的成形产品。
2、根据权利要求1所述的可降解的环保材料的制备方法,其特征在于所述的片材或产品粗坯其厚度为1-10毫米。
3、根据权利要求1所述的可降解的环保材料的制备方法,所述的面材为纸张、纸覆膜、纸金银薄膜、纸锡粘膜、金属膜或塑料膜。
CN 200410096490 2004-12-02 2004-12-02 可降解的环保材料的制备方法 Pending CN1781992A (zh)