CN101513314A - 全植物材料环保餐具及其制备工艺 - Google Patents
全植物材料环保餐具及其制备工艺 Download PDFInfo
- Publication number
- CN101513314A CN101513314A CNA2009101193937A CN200910119393A CN101513314A CN 101513314 A CN101513314 A CN 101513314A CN A2009101193937 A CNA2009101193937 A CN A2009101193937A CN 200910119393 A CN200910119393 A CN 200910119393A CN 101513314 A CN101513314 A CN 101513314A
- Authority
- CN
- China
- Prior art keywords
- dishware
- environment friendly
- plant material
- whole plant
- material environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种全植物材料环保餐具及其制备工艺,为解决现有技术中的环保餐具仍存在化学物质的问题而发明。本发明全植物材料环保餐具,由下述重量百分含量的原料制备而成:食用粉80%-85%,长度为1厘米至3厘米的植物长纤维10%-15%,植物胶5%-10%。本发明全植物材料环保餐具的制备工艺包括下述步骤:(1)将植物长纤维掺入食用粉中;(2)用水和魔芋粉掺入植物长纤维的食用粉搅拌成塑性;(3)模压成型;(4)干燥。采用上述配方和制备工艺,提高了产品强度,改善了脆性,也降低了成本。加工方便,成品合格率高;干燥时耗能低。
Description
技术领域
本发明涉及一种全植物材料环保餐具生产工艺
背景技术:
塑料饭盒的制作,首先是将塑料加温,与发泡剂制成液态混合物,然后喷射至模具中,加温固化而成。生产工艺简单,塑料为高分子材料,物理性能好,使用方便。但是,由于塑料化学性能极其稳定,不易分解。大量使用,曾经造成严重的“白色污染”。因此,政府有规定,限制塑料饭盒的使用。
而现在生产的一些所谓的环保饭盒,采用的材料基本上是塑料掺淀粉。其目的是利用塑料的优点,而淀粉又可以分解,从而可以减少“白色污染”。但是,此混合物分解后,其塑料分子深入土壤中,对土壤仍然造成严重污染,形成“隐性污染”。
许多单位,对全植物材料餐盒,进行过多方案的研究,虽然均采用了植物纤维,但均将其制成植物纤维粉(70%,80%,90%)后配以其他为粘合剂或胶成制成;由植物纤维粉为主要材料的制成品,对“胶”的性能和工艺水平有很高的要求。在使用温度比较高的情况下,产品软化。还有采用丙酮、环氧树脂、工业用胶等化学胶,因此,这类产品生产工艺要求高,而使用性能差,仍然部分采用化工材料。
因此,全植物材料餐具的继续研制,仍然具有非常实际的意义
发明内容
为克服上述缺陷,本发明的目的在于提供一种制作加工简单的全植物材料环保餐具及其制备工艺。
为达到上述目的,本发明全植物材料环保餐具,其特征在于:由下述重量百分含量的原料制备而成:食用粉80%-85%,长度为1厘米至3厘米的植物长纤维10%-15%,植物胶5%-10%。其中,植物胶主要原料为魔芋粉和水的组合物(也可以选用优质动物胶)。
为达到上述目的,本发明全植物材料环保餐具的制备工艺包括下述步骤:
(1)将植物长纤维掺入食用粉中,搅拌均匀;
(2)用适量常温水与植物胶搅拌均匀后与掺入植物长纤维的食用粉搅拌成塑性;
(3)模压成型;
(4)干燥。
进一步地,还包括下述步骤:在干燥后的餐具表面喷涂一层植物胶。
采用上述配方和制备工艺,具有下述优点:
1、食用粉掺入植物长纤维,提高了产品强度,改善了脆性,也降低了成本。
2、掺用植物胶,使食用粉改性,提高产品强度,又提高了防水、防油、耐温性能;提高了使用性能。
3、植物胶是一种天然植物,经过加工研制成粉末。该产品含有高分子聚合物,分子量约200万;该产品粘结性强、吸水性高(达40-100倍)。
4、用常温水掺用植物胶,拌和掺入植物长纤维的食用粉,成为塑性状态的半成品,含水量低,加工方便,成品合格率高;干燥时耗能低。
5、餐具表面再喷涂一层植物胶,效果更好。
6、生产工艺比较简单,生产设备技术要求相对比较低,价格相对也比较低廉;生产效率高。
附图说明
图1为本发明全植物材料环保餐具的制备工艺的流程图。
具体实施方式
下面结合附图和实施例对本发明作进一步地说明。
本发明全植物材料环保餐具,由下述重量百分含量的原料制备而成:食用粉80%-85%,长度为1厘米至3厘米的植物长纤维10%-15%,植物胶5%-10%。其中,上述的食用粉可采用小麦粉、玉米粉等;上述的植物长纤维可以为秸杆等,植物胶可采用淀粉类植物胶(做为本发明的变形,也可以选用优质动物胶),最好采用魔芋粉,魔芋粉含有高分子聚合物,分子量约200万,具有粘结性强、吸水性高(达40倍-100倍)的特点,可大大节约淀粉使用量。
实施例1
原料配比:
面粉1800吨,长度为3厘米植物纤维180吨,普通淀粉100吨;
制备工艺
(1)将上述植物长纤维掺入食用粉中,搅拌均匀;
(2)用适量常温水与普通淀粉搅拌均匀后与掺入植物长纤维的食用粉搅拌成塑性;
(3)模压成型;
(4)干燥。
实施例2
原料配比:
面粉1600吨,长度为1厘米植物纤维200吨,魔芋粉20吨;
制备工艺
(1)将上述植物长纤维掺入食用粉中,搅拌均匀;
(2)用适量常温水与魔芋粉搅拌均匀后与掺入植物长纤维的食用粉搅拌成塑性;
(3)模压成型;
(4)干燥。
(5)在干燥后的餐具表面喷涂一层魔芋粉液。
实施例3
原料配比:
面粉2000吨,长度为2厘米植物纤维300吨,魔芋粉20吨;
制备工艺
(1)将上述植物长纤维掺入食用粉中,搅拌均匀;
(2)用适量常温水与魔芋粉搅拌均匀后与掺入植物长纤维的食用粉搅拌成塑性;
(3)模压成型;
(4)干燥。
(5)在干燥后的餐具表面喷涂一层魔芋粉液。
综上所述,本发明将食用粉用植物胶改性,并掺有少量植物长纤维,产品强度高,改善了脆性,防渗漏、防油、耐温性能好,使用性能好。全部由植物材料制成,无废弃物排出,完全符合环保要求。
Claims (4)
1、一种全植物材料环保餐具,其特征在于:由下述重量百分含量的原料制备而成:食用粉80%-85%,长度为1厘米至3厘米的植物长纤维10%-15%,植物胶5%-10%。
2、如权利要求1所述的全植物材料环保餐具,其特征在于:所述的植物胶为魔芋粉和水的混合物。
3、如权利要求1或2所述的全植物材料环保餐具的制备工艺,其特征在于:包括下述步骤:
(1)将植物长纤维掺入食用粉中,搅拌均匀;
(2)用适量常温水与魔芋粉搅拌均匀后与掺入植物长纤维的食用粉搅拌成塑性;
(3)模压成型;
(4)干燥。
4、如权利要求3所述的全植物材料环保餐具的制备工艺,其特征在于:包括下述步骤:在干燥后的餐具表面喷涂一层植物胶。