CN1772950A - 塑料表面化学镀镍无钯活化配方及工艺 - Google Patents

塑料表面化学镀镍无钯活化配方及工艺 Download PDF

Info

Publication number
CN1772950A
CN1772950A CN 200510118396 CN200510118396A CN1772950A CN 1772950 A CN1772950 A CN 1772950A CN 200510118396 CN200510118396 CN 200510118396 CN 200510118396 A CN200510118396 A CN 200510118396A CN 1772950 A CN1772950 A CN 1772950A
Authority
CN
China
Prior art keywords
sodium borohydride
nickel plating
nickel
chemical nickel
methyl alcohol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200510118396
Other languages
English (en)
Other versions
CN100342058C (zh
Inventor
刘峥
杨振波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guilin University of Technology
Original Assignee
Guilin University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guilin University of Technology filed Critical Guilin University of Technology
Priority to CNB2005101183960A priority Critical patent/CN100342058C/zh
Publication of CN1772950A publication Critical patent/CN1772950A/zh
Application granted granted Critical
Publication of CN100342058C publication Critical patent/CN100342058C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种塑料表面化学镀镍无钯活化配方及工艺。镀镍前预处理化学镀镍活化液的配方主要由以下物质组成：乙酸镍，硼氢化钠、甲醇。活化方法具体为：将乙酸镍溶于甲醇中，另将硼氢化钠溶于甲醇中。活化时，先把塑料基片放入乙酸镍醇溶液中，再把硼氢化钠醇溶液倒入乙酸镍醇溶液中进行活化，将其陈化一定时间即可。本发明在常温下利用硼氢化钠还原制取活性镍，以镍取代钯活化的活化方法具有低温的优点。

Description

塑料表面化学镀镍无钯活化配方及工艺
技术领域
本发明涉及非金属化学镀领域，特别是塑料表面化学镀镍前预处理配方及工艺。
背景技术
化学镀由于具有可镀复杂形状镀件，镀层厚度均匀，硬度较高，较好的耐磨性、耐蚀性等优良特性，是非金属材料金属化的有效途径之一。化学镀镍在化学镀领域里占有重要地位，在非导体上化学镀镍，一般先要在基体上形成一层化学镀的催化剂，传统工艺是采用PdCl2-SnCl2活化——敏化法。而该工艺处理过程复杂，使用PdCl2价格昂贵，且还具有毒性，使其应用受到一定的限制。因此，不断开发低成本、环保型、节约贵金属的新型活化工艺，必然具有广阔的应用前景。室温下，利用还原法获得活性镍，以活性镍代替金属钯的化学镀镍无钯活化工艺及配方未见报道。
发明内容
本发明的目的是提供了一种在塑料上化学镀镍无钯活化配方及工艺。
塑料上化学镀镍，首先将塑料经消除内应力、除油、粗化、活化等预处理后，再进行化学镀镍。本发明就是针对活化阶段，提出了一种无钯活化配方及工艺。化学镀镍活化液的主要配方由以下物质组成：乙酸镍，硼氢化钠、甲醇。活化方法具体为：将乙酸镍溶于甲醇中，另将硼氢化钠溶于甲醇中。活化时，先把塑料基片放入乙酸镍醇溶液中，再把硼氢化钠醇溶液倒入乙酸镍醇溶液中进行活化，将其陈化一定时间即可。
塑料上化学镀镍活化预处理配方及工艺：
乙酸镍               64-68g/甲醇(L)；
硼氢化钠             64-68g/甲醇(L)；
温度(℃)：           室温
时间(min)：          25-35
活化工艺中溶剂的选择原则是：首先这种溶剂对乙酸镍及硼氢化钠的溶解必须很好，硫酸镍、氯化镍等在甲醇中溶解度很小，而硝酸镍的氧化性太强，故活化液中的镍盐以乙酸镍为最好；第二，用这种溶剂得到的溶液在ABS塑料表面的铺展性必须很好，这样才能得到均匀的活化基片和良好镀层；第三，溶剂要具有良好的挥发性。因此，甲醇作为活化液的溶剂能很好的满足以上条件。
本发明在常温下利用硼氢化钠还原制取活性镍，以镍取代钯活化的活化方法具有低温的优点。利用扫描电镜对镍镀层进行形貌表征，可以明显看出镀层结合致密，颗粒分散较均匀。利用衍射仪对镍镀层进行相结构分析，可明显看出在2θ角分别为19°、45°出现衍射峰(弥散峰)，2θ角19°为磷的衍射峰，2θ角45°为镍的衍射峰，说明镀层在镀态下为非晶态结构，具有很好的耐磨、耐腐蚀性能。使用能谱仪测定了ABS塑料镀镍镀层成分和含量，表明镀层中含有C、O、P、Ni元素，镍的含量最高。
具体实施方式
实施例
化学镀镍配方及工艺：
(1)化学除油液配方及工艺条件
磷酸钠                    50g/L
无水碳酸钠                30g/L
氢氧化钠                  25g/L
十二烷基磺酸钠            适量
时间(t)                   20min
温度(T)                   50～60℃
(2)粗化液配方及工艺条件
重铬酸钾                  30g/L
硫酸                      100mL/L
时间(t)                   10min
温度(T)                   60℃
(3)活化液配方及工艺条件
乙酸镍                    66.67g/甲醇(L)；
硼氢化钠                  66.67g/甲醇(L)；
温度(℃)：                室温
时间(min)：               30
活化方法为：将乙酸镍溶于甲醇中，另将硼氢化钠溶于甲醇中；活化时，先把塑料基片放入乙酸镍醇溶液中，再把硼氢化钠醇溶液倒入乙酸镍醇溶液中进行活化，将其陈化一定时间即可。
(4)化学镀镍液配方及工艺条件
配方主要由以下物质组成：乙酸镍；次亚磷酸钠；水合肼；糖精。
乙酸镍                  19g/L
水合肼                  0.02mL/L
次亚磷酸钠              22g/L
糖精                    40g/L
pH                      5.0
温度                    70～80℃
先分别溶解乙酸镍、次亚磷酸钠和糖精。在剧烈搅拌下将乙酸镍溶液缓慢加入水合肼溶液中，然后在搅拌下分别把次亚磷酸钠溶液、糖精溶液缓慢加入上述溶液中。还可以酌情加入稳定剂等。然后用稀乙酸调节pH值，最后稀释至所需体积。

Claims (2)

1.一种塑料表面化学镀镍无钯活化配方及工艺，其特征在于预处理阶段中无钯活化配方及工艺为：
乙酸镍      64-68g/甲醇(L)；
硼氢化钠    64-68g/甲醇(L)；
温度(℃)：  室温；
时间(min)： 25-35。
2.根据权利要求1所述的塑料表面化学镀镍无钯活化工艺，其特征在于活化方法具体为：将乙酸镍溶于甲醇中，另将硼氢化钠溶于甲醇中；活化时，先把塑料基片放入乙酸镍醇溶液中，再把硼氢化钠醇溶液倒入乙酸镍醇溶液中进行活化，将其陈化一定时间即可。
CNB2005101183960A 2005-11-01 2005-11-01 塑料表面化学镀镍无钯活化液配方及工艺 Expired - Fee Related CN100342058C (zh)