CN1765971A - 茂金属聚烯烃增韧聚丙烯树脂组合物 - Google Patents

茂金属聚烯烃增韧聚丙烯树脂组合物 Download PDF

Info

Publication number
CN1765971A
CN1765971A CN 200410067635 CN200410067635A CN1765971A CN 1765971 A CN1765971 A CN 1765971A CN 200410067635 CN200410067635 CN 200410067635 CN 200410067635 A CN200410067635 A CN 200410067635A CN 1765971 A CN1765971 A CN 1765971A
Authority
CN
China
Prior art keywords
metallocene
resin composition
polypropylene
tenacity
increased profax
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200410067635
Other languages
English (en)
Inventor
辛敏琦
陈晓东
杨涛
唐倬
吴小龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Rizhisheng New Technology Development Co Ltd
Original Assignee
Shanghai Rizhisheng New Technology Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Rizhisheng New Technology Development Co Ltd filed Critical Shanghai Rizhisheng New Technology Development Co Ltd
Priority to CN 200410067635 priority Critical patent/CN1765971A/zh
Publication of CN1765971A publication Critical patent/CN1765971A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种茂金属聚烯烃增韧聚丙烯树脂组合物，其特征在于，它由以下重量配比的原料制成：聚丙烯60－85％、茂金属聚烯烃5－30％、相容剂5－10％、抗氧剂0.1－1％、润滑剂0.1－0.5％，其制备方法：按重量配比秤取原料；将所有原料放入高混机中混合2－5分钟；出料；将混合的原料放入螺杆机中挤出造粒，螺杆机的转速为180－600转/分，温度为160－220℃。本发明的优点是韧性好、低温冲击性能优异、熔融指数高、加工性能好、喷涂性能优异、成本低。

Description

茂金属聚烯烃增韧聚丙烯树脂组合物
技术领域
本发明涉及一种茂金属聚烯烃增韧聚丙烯树脂组合物，可用于制造汽车配件及电子电气元件，属聚丙烯改性技术领域。
背景技术
聚丙烯(PP)价廉、质轻，耐腐蚀、具有良好的加工性、力学均衡性好、应用范围广，在通用树脂中有最好的耐热性。聚丙烯在汽车工业上有广泛的应用，工程化倾向十分明显，但聚丙烯的韧性，尤其是低温冲击韧性很差，从而限制了其使用。
提高聚丙烯韧性的方法很多，研究最多的是乙丙橡胶增韧聚丙烯，也有HDPE和乙丙橡胶协同增韧聚丙烯的，80年代发展起来的动态硫化技术也可以用来增韧聚丙烯。但这种方法成本均较高，工艺复杂而且材料的流动性不强。
发明内容
本发明的目的在于提供一种的具有韧性好、低温冲击性能优异、熔融指数高、加工性能好、喷涂性能优异、成本低的茂金属聚烯烃增韧聚丙烯树脂组合物。
为实现以上目的，本发明的技术方案是提供一种茂金属聚烯烃增韧聚丙烯树脂组合物，其特征在于，它由以下重量配比的原料制成：
                  聚丙烯         60-85％
                  茂金属聚烯烃   5-30％
                  相容剂         5-10％
                  抗氧剂         0.1-1％
                  润滑剂         0.1-0.5％。
所述的聚丙烯可以是共聚聚丙烯、均聚聚丙烯，可以是单一的也可以是混合的。
所述的茂金属聚烯烃是以茂金属配位化合物(metallocene)为催化剂进行烯烃聚合反应所制得的聚合物，可以是茂金属聚乙烯及其衍生物，也可以是茂金属聚乙烯与辛烯原位聚合物。
所述的相容剂为聚丙烯接枝不饱和酸或者酸酐的接枝聚合的低聚物，其熔融指数为40-150g/10min，接枝率为0.5-1％。
所述的抗氧剂为一种受阻酚类抗氧剂与亚磷酸酯类抗氧剂的复配物，可以是1010和168复配。
所述的润滑剂为脂肪酸金属皂类，可以是硬脂酸钙、硬脂酸锌、硬脂酸钡、硬脂酸镁。
一种茂金属聚烯烃增韧聚丙烯树脂组合物的制备方法，其特征在于，其方法如下：
(1)按重量配比秤取原料；
(2)将所有原料放入高混机中混合2-5分钟；
(3)出料；
(4)将混合的原料放入螺杆机中挤出造粒，螺杆机的转速为180-600转/分，温度为160-220℃。
聚丙烯(PP)价廉、质轻，耐腐蚀、具有良好的加工性、力学均衡性好、应用范围广，在通用树脂中有最好的耐热性，广泛应用于汽车部件和电子电气元件。
茂金属聚烯烃是以茂金属配位化合物(metallocene)为催化剂进行烯烃聚合反应所制得的聚合物，茂金属聚烯烃具有诸多优点，加工性能良好、高强度、高刚性、高的熔体强度及透明性好等优异性能。
聚丙烯接枝不饱和酸或者酸酐的接枝聚合的低聚物，具有超强的流动性，作为相容剂，可以提高茂金属聚烯烃在聚丙烯树脂中的分散性，提高二者的粘结能力。
抗氧剂为一种受阻酚类抗氧剂与亚磷酸酯类抗氧剂的复配物，可以是1010和168复配，可提高组合物在加工过程的抗氧化性能和使用过程中的抗老化性能。
脂肪酸金属皂类作为润滑剂，可提高材料加工流动性，降低摩擦系数，提高滑爽性，改善表面光泽。
本发明采用聚丙烯树脂，制得一种茂金属聚烯烃增韧聚丙烯树脂组合物，解决了聚丙烯树脂的低温冲击韧性很差的缺点。
本发明的优点是韧性好、低温冲击性能优异、熔融指数高、加工性能好、喷涂性能优异、成本低。
具体实施方案
下面结合实施例，对本发明作进一步详细说明：
实施例1和2：
聚丙烯采用韩国进口的均聚聚丙烯和共聚聚丙烯树脂，茂金属聚烯烃用日本进口的MPE和美国的POE，相容剂用上海日之升公司的CMG9801，抗氧剂为CIBA公司的168和1010，润滑剂采用硬脂酸钙。
              配比1-2(表1)
  原料名称  配比1(wt％)  配比2(wt％)
  共聚聚丙烯  69  50
  均聚聚丙烯  --  24
  MPE  25  --
  POE  --  20
  CMG9801  5  5
  1010/168(1∶1)  0.5  0.5
  硬脂酸钙  0.5  0.5
将所有原料组分按比例放入高混机中混合4分钟，出料，然后用螺杆挤出机挤出造粒，加工温度在200℃，螺杆转数在250转/分。
根据实施例1、实施例2制得的样品1、样品2与用乙丙橡胶增韧的产品性能对比
                 测试性能对比(表2)
  项目   样品1   样品2   乙丙橡胶增韧
  拉伸强度Mpa   24.0   23.3   22.5
  断裂伸长率％   ＞100   ＞100   ＞100
  弯曲强度Mpa   21.2   18.6   19.0
  熔融指数g/10min   28.2   24.1   16
  常温冲击强度J/M   650   680   750
  低温冲击强度J/M   614   651   724

Claims (7)

1.一种茂金属聚烯烃增韧聚丙烯树脂组合物，其特征在于，它由以下重量配比的原料制成：
聚丙烯        60-85％
茂金属聚烯烃  5-30％
相容剂        5-10％
抗氧剂        0.1-1％
润滑剂        0.1-0.5％。
2.根据权利要求1所述的茂金属聚烯烃增韧聚丙烯树脂组合物，其特征在于，所述的聚丙烯可以是共聚聚丙烯、均聚聚丙烯，可以是单一的也可以是混合的。
3.根据权利要求1所述的茂金属聚烯烃增韧聚丙烯树脂组合物，其特征在于，所述的茂金属聚烯烃是以茂金属配位化合物(metallocene)为催化剂进行烯烃聚合反应所制得的聚合物，可以是茂金属聚乙烯及其衍生物，也可以是茂金属聚乙烯与辛烯原位聚合物。
4.根据权利要求1所述的茂金属聚烯烃增韧聚丙烯树脂组合物，其特征在于，所述的相容剂为聚丙烯接枝不饱和酸或者酸酐的接枝聚合的低聚物，其熔融指数为40-150g/10min，接枝率为0.5-1％。
5.根据权利要求1所述的茂金属聚烯烃增韧聚丙烯树脂组合物，其特征在于，所述的抗氧剂为一种受阻酚类抗氧剂与亚磷酸酯类抗氧剂的复配物，可以是1010和168复配。
6.根据权利要求1所述的茂金属聚烯烃增韧聚丙烯树脂组合物，其特征在于，所述的润滑剂为脂肪酸金属皂类，可以是硬脂酸钙、硬脂酸锌、硬脂酸钡、硬脂酸镁。
7.一种茂金属聚烯烃增韧聚丙烯树脂组合物的制备方法，其特征在于，其方法如下：
(1)按重量配比秤取原料；
(2)将所他原料放入高混机中混合2-5分钟；
(3)出料；
(4)将混合的原料放入螺杆机中挤出造粒，螺杆机的转速为180-600转/分，温度为160-220℃。
CN 200410067635 2004-10-29 2004-10-29 茂金属聚烯烃增韧聚丙烯树脂组合物 Pending CN1765971A (zh)