CN102070839B - 一种改性塑料 - Google Patents

一种改性塑料 Download PDF

Info

Publication number
CN102070839B
CN102070839B CN2011100035079A CN201110003507A CN102070839B CN 102070839 B CN102070839 B CN 102070839B CN 2011100035079 A CN2011100035079 A CN 2011100035079A CN 201110003507 A CN201110003507 A CN 201110003507A CN 102070839 B CN102070839 B CN 102070839B
Authority
CN
China
Prior art keywords
density polyethylene
modified plastics
vestolen
percent
modified plastic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2011100035079A
Other languages
English (en)
Other versions
CN102070839A (zh
Inventor
魏育南
吴莉翔
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Huasheng Ming rabbit environmental protection Polytron Technologies Inc
Original Assignee
Guangdong Huasheng Plastic Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong Huasheng Plastic Co Ltd filed Critical Guangdong Huasheng Plastic Co Ltd
Priority to CN2011100035079A priority Critical patent/CN102070839B/zh
Publication of CN102070839A publication Critical patent/CN102070839A/zh
Application granted granted Critical
Publication of CN102070839B publication Critical patent/CN102070839B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种改性塑料，其特征在于由下述重量百分比的原料制成：聚丙烯75-85％，高密度聚乙烯7-10％，茂金属低密度聚乙烯3-8％，聚乙烯辛烯共弹性体3-8％。本发明的改性塑料不仅具有良好的耐腐蚀性、刚性和透明度，而且具有良好的抗冲击性及柔韧度。采用这种改性塑料制成的包装容器与采用聚丙烯制成的包装容器相比，在容量、形状及容器壁厚度相同的条件下，其刚性、抗冲击性及柔韧度更好，强度更高，更加硬挺，盛装功能更强，拿在手上时不易变形、碎裂，降低对人体伤害的危险性，适合盛装液态、半液态或固态物料。另外，采用本发明的改性塑料制成的包装容器即使加热水也不产生异味。

Description

一种改性塑料
技术领域
本发明涉及塑料，具体地说，涉及一种以聚丙烯为主体材料的改性塑料。
背景技术
聚丙烯(PP)的耐腐蚀性、刚性和透明度较好，目前广泛用于制作包装容器。但是，聚丙烯抗冲击性较差，低温时变脆，较易老化，而且，广大厂家为了减少原材料投入、降低生产成本，尽可能地使制成的包装容器重量更轻、容器壁厚度更薄，因此，现有以聚丙烯为原材料制成的包装容器手感非常软，强度不够高，拿在手上时易变形、碎裂，难以盛装液态或半液态包装物，特别是盛装温度较高的液态或半液态物料时，温度较高的液态或半液态物料容易溢出而对人体造成伤害。
发明内容
本发明所要解决的技术问题是提供一种以聚丙烯为主体材料的改性塑料，这种改性塑料具有良好的抗冲击性及柔韧度。采用的技术方案如下：
一种改性塑料，其特征在于由下述重量百分比的原料制成：聚丙烯75-85％，高密度聚乙烯7-10％，茂金属低密度聚乙烯3-8％，聚乙烯辛烯共弹性体3-8％。
上述聚丙烯(简称PP)为主体材料；添加适量的高密度聚乙烯(High DensityPolyethylene，简称HDPE)和茂金属低密度聚乙烯(简称mLDPE)，可提高改性塑料的抗冲击性；添加适量的聚乙烯辛烯共弹性体(简称POE)，可增强改性塑料的柔韧度。上述各种原料均可在市场上购买到。
上述改性塑料可采用下述方法制成：将上述重量配比的聚丙烯、高密度聚乙烯、茂金属低密度聚乙烯和聚乙烯辛烯共弹性体混合，并搅拌至混合均匀；然后通过挤出机挤压而塑化成均匀的塑料熔体，得到的塑料熔体即为改性塑料。从挤出机挤出的改性塑料熔体经流延或压延成型，得到改性塑料片材；再将改性塑料片材根据不同要求，经吸塑或吹塑成型，制成相应的塑料包装容器。
本发明的改性塑料不仅具有良好的耐腐蚀性、刚性和透明度，而且具有良好的抗冲击性及柔韧度。采用这种改性塑料制成的包装容器与采用聚丙烯制成的包装容器相比，在容量、形状及容器壁厚度相同的条件下，其刚性、抗冲击性及柔韧度更好，强度更高，更加硬挺，盛装功能更强，拿在手上时不易变形、碎裂，降低对人体伤害的危险性，适合盛装液态、半液态或固态物料。另外，采用本发明的改性塑料制成的包装容器即使加热水也不产生异味。
具体实施方式
实施例1
按下述重量百分比配备原料：聚丙烯84％，高密度聚乙烯9％，茂金属低密度聚乙烯3.5％，聚乙烯辛烯共弹性体3.5％。
按下述方法制备改性塑料：将上述聚丙烯、高密度聚乙烯、茂金属低密度聚乙烯和聚乙烯辛烯共弹性体混合，并搅拌至混合均匀；然后通过挤出机挤压而塑化成均匀的塑料熔体，得到的塑料熔体即为改性塑料。
得到的改性塑料中各组分的重量百分比含量为：聚丙烯84％，高密度聚乙烯9％，茂金属低密度聚乙烯3.5％，聚乙烯辛烯共弹性体3.5％。
实施例2
按下述重量百分比配备原料：聚丙烯75％，高密度聚乙烯10％，茂金属低密度聚乙烯8％，聚乙烯辛烯共弹性体7％。
制备改性塑料的方法与实施例1相同。
得到的改性塑料中各组分的重量百分比含量为：聚丙烯75％，高密度聚乙烯10％，茂金属低密度聚乙烯8％，聚乙烯辛烯共弹性体7％。
实施例3
按下述重量百分比配备原料：聚丙烯80％，高密度聚乙烯7％，茂金属低密度聚乙烯5％，聚乙烯辛烯共弹性体8％。
制备改性塑料的方法与实施例1相同。
得到的改性塑料中各组分的重量百分比含量为：聚丙烯80％，高密度聚乙烯7％，茂金属低密度聚乙烯5％，聚乙烯辛烯共弹性体8％。
实施例4
按下述重量百分比配备原料：聚丙烯85％，高密度聚乙烯7％，茂金属低密度聚乙烯3％，聚乙烯辛烯共弹性体5％。
制备改性塑料的方法与实施例1相同。
得到的改性塑料中各组分的重量百分比含量为：聚丙烯85％，高密度聚乙烯7％，茂金属低密度聚乙烯3％，聚乙烯辛烯共弹性体5％。
实施例5
按下述重量百分比配备原料：聚丙烯83％，高密度聚乙烯8％，茂金属低密度聚乙烯6％，聚乙烯辛烯共弹性体3％。
制备改性塑料的方法与实施例1相同。
得到的改性塑料中各组分的重量百分比含量为：聚丙烯83％，高密度聚乙烯8％，茂金属低密度聚乙烯6％，聚乙烯辛烯共弹性体3％。
实施例6
按下述重量百分比配备原料：聚丙烯80％，高密度聚乙烯8％，茂金属低密度聚乙烯6％，聚乙烯辛烯共弹性体6％。
制备改性塑料的方法与实施例1相同。
得到的改性塑料中各组分的重量百分比含量为：聚丙烯80％，高密度聚乙烯8％，茂金属低密度聚乙烯6％，聚乙烯辛烯共弹性体6％。
下面简述一下改性塑料性能的一种检测方法：采用上述实施例1-6的改性塑料分别制作塑料杯，制作而成的塑料杯容量均为150毫升、重量均为3.5克，分别装满水并将杯口用薄膜密封，然后举到距离水泥地面1.5米的高度处，让塑料杯自由落体，对塑料杯进行检测。检测结果：上述各种塑料杯均无溢漏现象，塑料杯完好无损。上述检测结果表明，上述实施例1-6的改性塑料抗冲击性及柔韧度良好。

Claims (6)

1.一种改性塑料，其特征在于由下述重量百分比的原料制成：聚丙烯75-85%，高密度聚乙烯7-9%，茂金属低密度聚乙烯3-8%，聚乙烯辛烯共弹性体3-8%。
2.根据权利要求1所述的改性塑料，其特征在于由下述重量百分比的原料制成：聚丙烯84%，高密度聚乙烯9%，茂金属低密度聚乙烯3.5%，聚乙烯辛烯共弹性体3.5%。
3.根据权利要求1所述的改性塑料，其特征在于由下述重量百分比的原料制成：聚丙烯80%，高密度聚乙烯7%，茂金属低密度聚乙烯5%，聚乙烯辛烯共弹性体8%。
4.根据权利要求1所述的改性塑料，其特征在于由下述重量百分比的原料制成：聚丙烯85%，高密度聚乙烯7%，茂金属低密度聚乙烯3%，聚乙烯辛烯共弹性体5%。
5.根据权利要求1所述的改性塑料，其特征在于由下述重量百分比的原料制成：聚丙烯83%，高密度聚乙烯8%，茂金属低密度聚乙烯6%，聚乙烯辛烯共弹性体3%。
6.根据权利要求1所述的改性塑料，其特征在于由下述重量百分比的原料制成：聚丙烯80%，高密度聚乙烯8%，茂金属低密度聚乙烯6%，聚乙烯辛烯共弹性体6%。
CN2011100035079A 2011-01-10 2011-01-10 一种改性塑料 Active CN102070839B (zh)