CN101759929B - 一种高透明高流动增韧聚丙烯材料及其制备方法 - Google Patents

一种高透明高流动增韧聚丙烯材料及其制备方法 Download PDF

Info

Publication number
CN101759929B
CN101759929B CN2008102074767A CN200810207476A CN101759929B CN 101759929 B CN101759929 B CN 101759929B CN 2008102074767 A CN2008102074767 A CN 2008102074767A CN 200810207476 A CN200810207476 A CN 200810207476A CN 101759929 B CN101759929 B CN 101759929B
Authority
CN
China
Prior art keywords
transparency
percent
sebs
flowability
polypropylene material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2008102074767A
Other languages
English (en)
Other versions
CN101759929A (zh
Inventor
项军
郭建鹏
陈晓东
宋懂强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Rizhisheng New Technology Development Co Ltd
Original Assignee
Shanghai Rizhisheng New Technology Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Rizhisheng New Technology Development Co Ltd filed Critical Shanghai Rizhisheng New Technology Development Co Ltd
Priority to CN2008102074767A priority Critical patent/CN101759929B/zh
Publication of CN101759929A publication Critical patent/CN101759929A/zh
Application granted granted Critical
Publication of CN101759929B publication Critical patent/CN101759929B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种高透明高流动增韧聚丙烯材料及其制备方法，其材料由以下重量配比的原料制成：聚丙烯20-70％、m-LLPE 10-30％、乙烯辛烯共聚物5-10％、相容剂3-10％、SEBS 5-15％、白油5-30％、抗氧剂0.1-0.5％。其制备方法包括按重量配比秤取原料；先将SEBS和白油放入高混机中混合均匀，然后加入其他原料混混合2-5分钟，出料；将混合均匀的原料放入螺杆机中挤出造粒。本发明的特点是制备的增韧聚丙烯材料具有优异的力学性能，而且流动性、透明性好均强于普通的PP增韧材料。可用于制作具有高透明高韧性要求的工具，仪器、仪表外壳的功能部件。

Description

一种高透明高流动增韧聚丙烯材料及其制备方法
技术领域
本发明涉及一种高透明高流动增韧聚丙烯材料及其制备方法，该材料可制作一些具有高透明高韧性要求的工具，仪器、仪表外壳的功能部件，属于聚丙烯增韧技术领域。
背景技术
通常的聚丙烯增韧材料主要有EPDM，POE等，当这些材料和聚丙烯共混时，因为EPDM，POE会影响聚丙烯的结晶状况，加之增韧剂的流动性很差，从而导致所制备的聚丙烯增韧材料不具有透明效果，且材料的流动性差。
发明内容
本发明的目的就是为了克服上述现有技术存在的缺陷而提供一种高透明高流动增韧聚丙烯材料及其制备方法。
本发明的目的可以通过以下技术方案来实现：
一种高透明高流动增韧聚丙烯材料，其特征在于，由以下重量配比的原料制成：
聚丙烯20-70％，
m-LLPE 10-30％，
乙烯辛烯共聚物5-10％，
相容剂2-5％，
SEBS 5-15％，
白油5-30％，
抗氧剂0.1-0.5％。
所述的聚丙烯为均聚聚丙烯，其熔融指数为1-20g/10min。
所述的m-LLPE，其熔融指数为1-15g/10min。
所述的乙烯辛烯共聚物为POE，其熔融指数为2-15g/10min。
所述的相容剂为马来酸酐接枝聚丙烯，其熔融指数为80-100g/10min。
所述的SEBS为粉状，氢化度＞95％。
所述的白油为26号白油。
所述的抗氧剂为受阻酚类抗氧剂与亚磷酸酯类抗氧剂复配，优选抗氧剂1010与抗氧剂168复配。
一种高透明高流动增韧聚丙烯材料的制备方法，其特征在于，该方法包括以下工艺步骤：
(1)按重量配比秤取原料：聚丙烯20-70％，m-LLPE 10-30％，乙烯辛烯共聚物5-10％，相容剂2-5％，SEBS 5-15％，白油5-30％，抗氧剂0.1-0.5％；
(2)先将SEBS和白油放入高混机中混合3-5分钟，然后加入其他原料混合3-5分钟，出料；
(3)将混合的原料放入螺杆机中挤出造粒，螺杆机的转速为180-600转/分，温度为180-220℃。
本发明采用填充油SEBS，POE，LLDPE进行共同增韧的方法，所制备的材料具有很好的抗冲击性能，不但改善了增韧材料的流动性，而且所制备的材料还具有较好的透明性。
具体实施方式
下面结合实施例，对本发明作进一步详细说明。
实施例1～2
实施例1～2配比(重量％)见表1。
表1
  原料名称   实施例1   实施例2
  聚丙烯   57.6   47.6
  POE   15   20
  m-LLDPE   10   15
  SEBS   5   5
  白油   12   12
  1010/168(1∶1)   0.4   0.4
将所有组分先将SEBS和白油放入高混机中混合3-5分钟，然后加入其他原料混合3-5分钟，加工温度在分别为190、195、215、215、215、215、215、、210、210℃，螺杆转数在200转/分。
对实施例1和2所得的一种高透明高流动增韧聚丙烯材料样品1和样品2进行性能测试对比，力学性能以ASTM测试。
样品1和样品2性能对照见表2。
表2
  测试项目   样品1   样品2
  拉伸强度MPa   15.4   12.1
  断裂伸长率％   ＞500   ＞500
  缺口冲击强度J/M   NB   NB
  熔体流动速率g/10min   23   18
  透明效果   良好   良好

Claims (2)

1.一种高透明高流动增韧聚丙烯材料，其特征在于，由以下重量配比的原料制成：
聚丙烯20-70％，
m-LLPE 10-30％，
乙烯辛烯共聚物5-10％，
相容剂2-5％，
SEBS 5-15％，
白油5-30％，
抗氧剂0.1-0.5％；
所述的聚丙烯为均聚聚丙烯，其熔融指数为1-20g/10min；
所述的m-LLPE，其熔融指数为1-15g/10min；
所述的乙烯辛烯共聚物为POE，其熔融指数为2-15g/10min；
所述的相容剂为马来酸酐接枝聚丙烯，其熔融指数为80-100g/10min；
所述的SEBS为粉状，氢化度＞95％；
所述的白油为26号白油；
所述的抗氧剂为抗氧剂1010与抗氧剂168复配。
2.一种如权利要求1所述高透明高流动增韧聚丙烯材料的制备方法，其特征在于，该方法包括以下工艺步骤：
(1)按重量配比秤取原料：聚丙烯20-70％，m-LLPE 10-30％，乙烯辛烯共聚物5-10％，相容剂2-5％，SEBS 5-15％，白油5-30％，抗氧剂0.1-0.5％；
(2)先将SEBS和白油放入高混机中混合3-5分钟，然后加入其他原料混合3-5分钟，出料；
(3)将混合的原料放入螺杆机中挤出造粒，螺杆机的转速为180-600转/分，温度为180-220℃。
CN2008102074767A 2008-12-19 2008-12-19 一种高透明高流动增韧聚丙烯材料及其制备方法 Expired - Fee Related CN101759929B (zh)