CN1703529A - 耐蚀性和加工性优良的热浸镀Sn-Zn系钢板 - Google Patents
耐蚀性和加工性优良的热浸镀Sn-Zn系钢板 Download PDFInfo
- Publication number
- CN1703529A CN1703529A CN200380101275.4A CN200380101275A CN1703529A CN 1703529 A CN1703529 A CN 1703529A CN 200380101275 A CN200380101275 A CN 200380101275A CN 1703529 A CN1703529 A CN 1703529A
- Authority
- CN
- China
- Prior art keywords
- steel plate
- corrosion
- coating
- solidity
- hot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
No. | 实施例 | 镀层组成 | 镀层 | 外面耐蚀性 | 内面耐蚀性 | 综合评价 | 备注 | ||
组织 | Sn树枝状面积率(%) | Sn树枝状枝间隔(mm) | 红锈面积率(%) | 金属溶解析出量(ppm) | |||||
1 | 1 | Sn-8质量%Zn | Sn树枝状+枝间二元共晶 | 40 | 0.05 | 2 | 35 | ○ | 发明例 |
2 | Sn-8质量%Zn | Sn树枝状+枝间二元共晶 | 20 | 0.08 | 5 | 70 | ○ | 发明例 | |
3 | Sn-8质量%Zn | Sn树枝状+枝间二元共晶 | 10 | 0.15 | 8 | 160 | △ | 发明例 | |
4 | Sn-4质量%Zn | Sn树枝状+枝间二元共晶 | 60 | 0.06 | 7 | 25 | ○ | 发明例 | |
5 | Sn-2质量%Zn | Sn树枝状+枝间二元共晶 | 80 | 0.05 | 9 | 10 | △ | 发明例 | |
6 | Sn-0.5质量%Zn | Sn树枝状+枝间二元共晶 | 95 | 0.20 | 30 | 40 | × | 对比例 | |
7 | Sn-10质量%Zn | 初晶Zn+锌花二元共晶 | - | - | 15 | 600 | × | 对比例 | |
8 | Sn-15质量%Zn | 初晶Zn+锌花二元共晶 | - | - | 12 | 1300 | × | 对比例 | |
9 | 2 | Sn-8质量%Zn | Sn树枝状+枝间二元共晶 | 30 | 0.06 | 0 | 15 | ○ | 发明例 |
10 | 3 | Sn-8质量%Zn | 锌花二元共晶 | - | - | 80 | 1800 | × | 对比例 |
No. | 镀浴 | FeSn2相 | 加工性 | 耐蚀性 | 综合评价 | 备注 | ||
组成(Zn质量%) | 浴温(℃) | 面积率(%) | RMS(μm) | |||||
11 | 0 | 240 | 20 | 0.8 | ○ | × | × | 对比例 |
12 | 0 | 300 | 45 | 1.1 | ○ | × | × | 对比例 |
13 | 0 | 400 | 100 | 3.1 | × | △ | × | 对比例 |
14 | 2 | 240 | 20 | 1.2 | ○ | △ | ○~△ | 发明例 |
15 | 2 | 300 | 35 | 1.9 | ○ | ○ | ○ | 发明例 |
16 | 2 | 350 | 50 | 2.1 | △ | ○ | ○~△ | 发明例 |
17 | 2 | 400 | 100 | 2.4 | × | △ | × | 对比例 |
18 | 8 | 205 | 0.5 | 0.04 | △ | △ | △ | 发明例 |
19 | 8 | 220 | 3 | 0.07 | ○ | △ | ○~△ | 发明例 |
20 | 8 | 240 | 15 | 1.4 | ○ | ○ | ○ | 发明例 |
21 | 8 | 300 | 40 | 1.3 | ○ | ○ | ○ | 发明例 |
22 | 8 | 350 | 55 | 1.8 | △ | ○ | ○~△ | 发明例 |
23 | 8 | 400 | 100 | 1.9 | × | △ | × | 对比例 |
24 | 15 | 300 | 30 | 1.2 | △ | ○ | ○ | 对比例 |
25 | 15 | 350 | 70 | 2.0 | △ | ○ | ○~△ | 对比例 |
26 | 15 | 400 | 100 | 2.2 | × | △ | × | 对比例 |
27 | 25 | 350 | 90 | 1.7 | △ | △ | △ | 对比例 |
28 | 25 | 400 | 100 | 2.4 | × | △ | × | 对比例 |
29 | 35 | 350 | 100 | 2.6 | × | △ | × | 对比例 |
30 | 35 | 400 | 100 | 2.8 | × | △ | × | 对比例 |
Claims (5)