CN1690169A - 一种含分子筛烃类裂化催化剂的制备方法 - Google Patents
一种含分子筛烃类裂化催化剂的制备方法 Download PDFInfo
- Publication number
- CN1690169A CN1690169A CN 200410037680 CN200410037680A CN1690169A CN 1690169 A CN1690169 A CN 1690169A CN 200410037680 CN200410037680 CN 200410037680 CN 200410037680 A CN200410037680 A CN 200410037680A CN 1690169 A CN1690169 A CN 1690169A
- Authority
- CN
- China
- Prior art keywords
- weight
- aluminum oxide
- zeolite
- molecular sieve
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种含分子筛烃类裂化催化剂的制备方法，该方法包括将铝溶胶、水合氧化铝、粘土、酸、分子筛和水打浆混合均匀，制成一种浆液，使浆液的固含量为25－40重量％，然后干燥得到的浆液，在打浆时还加入一种硅溶胶，所述硅溶胶是平均颗粒直径为5－100纳米的颗粒，并且80％以上的颗粒直径在平均颗粒直径的0.5－1.5倍之间。该方法制备出的催化剂具有较大平均孔直径，并且，孔直径为5－100纳米的中大孔孔体积较大，具有较高的轻质油选择性和较低的焦炭选择性。
Description
技术领域
本发明是关于一种烃类裂化催化剂的制备方法，更进一步地说，是关于一种含分子筛烃类裂化催化剂的制备方法。
背景技术
近年来，催化裂化原料的重质化倾向日益严重，原料中的胶质、沥青质等大分子物质具有较大的分子直径。当催化剂中缺乏中大孔时，这些大分子物质不仅难以转化为轻质油，而且易在催化剂的表面生成焦炭和干气，造成催化剂的选择性不好，即对焦炭选择性较高，对轻质油，即柴油和汽油的选择性较低。增加裂化催化剂的孔径和中大孔孔体积是改善裂催化剂选择性的重要手段。一般认为，催化剂合适的孔大小应是大分子反应物直径的2-6倍，减压渣油的分子直径为2.5-15纳米，因此，增加孔直径为5-100纳米的中大孔孔体积有利于改善催化剂的选择性。
CN1098130A公开了一种裂化催化剂的制备方法，该方法包括将粘土和去离子水混合打浆25-35分钟，加入盐酸酸化0.5-1小时，加入拟薄水铝石搅拌打浆25-35分钟，其中，水的加入量保证浆液的固含量为20-55重量％，盐酸的加入量为拟薄水铝石中氧化铝的15-50重量％；在50-80℃老化0.5-2小时；加入铝溶胶搅拌10-20分钟；加入研磨好的分子筛，继续打浆25-35分钟，干燥成型并洗涤，干燥。该方法采用双铝基粘结剂，其中，铝溶胶用来改进催化剂的强度，拟薄水铝石用来改善催化剂的孔结构，重油裂化活性得到一定程度的提高。但是，用该方法制备的裂化催化剂的孔径和孔直径为5-100纳米的中大孔孔体积偏小，催化剂的选择性不好。
CN1247885A公开了一种裂化催化剂的制备方法，该方法包括将铝溶胶、拟薄水铝石、粘土、无机酸及分子筛浆液打浆混合均匀制成催化剂浆液，使浆液的固含量为20-45重量％，然后喷雾干燥，其中，铝溶胶在粘土和无机酸之前加入，分子筛浆液在无机酸之后加入。用该方法制备的裂化催化剂的孔径和孔直径为5-100纳米的中大孔孔体积偏小，催化剂的选择性不好。
CN1246515A公开了一种裂化催化剂的制备方法，该方法包括将铝溶胶、拟薄水铝石、粘土、无机酸及分子筛浆液打浆混合均匀制成催化剂浆液，使浆液的固含量为25-45重量％，然后喷雾干燥，其中，分子筛浆液在粘土和无机酸之前加入，无机酸在铝溶胶之后加入。该方法可以提高催化剂浆液的固含量，提高催化剂的生产效率，但是，得到的裂化催化剂的孔结构没有明显改善，选择性也不好。
CN1388213A公开了一种裂化催化剂的制备方法，该方法包括将粘土浆液用酸处理后，加入拟薄水铝石、水玻璃溶液，加或不加铝溶胶，再加入分子筛浆液后进行喷雾干燥，水洗。该方法可以缩短催化剂制备的工艺流程，但是，得到的裂化催化剂的孔结构没有明显改善，选择性同样不好。
发明内容
本发明的目的是针对上述现有裂化催化剂制备方法制备出的催化剂孔径和孔直径为5-100纳米的中大孔孔体积偏小，催化剂的选择性不好的缺点，提供一种孔径和孔直径为5-100纳米的中大孔孔体积较大，选择性较好的含分子筛烃类裂化催化剂的制备方法。
本发明提供的催化剂的制备方法包括将铝溶胶、水合氧化铝、粘土、酸、分子筛和水打浆混合均匀，制成一种浆液，使浆液的固含量为20-40重量％，然后干燥得到的浆液，其中，在打浆时还加入一种硅溶胶，所述硅溶胶是平均颗粒直径为5-100纳米的颗粒，并且80％以上的颗粒直径在平均颗粒直径的0.5-1.5倍之间。
由于本发明提供的方法使用了一种颗粒直径分布较窄的硅溶胶，制备出的催化剂具有较大平均孔直径，并且，孔直径为5-100纳米的中大孔孔体积较大，具有较高的轻质油选择性和较低的焦炭选择性。
具体实施方式
按照本发明提供的方法，所述硅溶胶是平均颗粒直径为5-100纳米的颗粒，并且80％以上的颗粒直径在平均颗粒直径的0.5-1.5倍之间的硅溶胶。优选情况下，所述硅溶胶的平均颗粒直径为10-80纳米。所述具有上述颗粒直径分布的硅溶胶可以商购得到，也可以采用离子交换法制备得到。所述采用离子交换法制备硅溶胶的方法参见Ralph K Iler，JohnWiley和Sons编著《The Chemistry of Silica：Polymerization，Colloid And SurfaceProperties，And Biochemistry》及US4304575。
所述水合氧化铝选自裂化催化剂通常使用的水合氧化铝中的一种或几种，如具有拟薄水铝石(Pseudoboemite)结构、一水铝石(Boehmite)结构、三水铝石(Gibbsite)结构和拜耳石(Bayerite)结构的水合氧化铝中的一种或几种。优选为具有拟薄水铝石结构的水合氧化铝和/或具有三水铝石结构的水合氧化铝。
所述浆液中各组分的用量为常规催化剂制备方法中各物质的用量，一般来说，按干基计，各组分的用量使催化剂浆液含有5-50重量％，优选10-35重量％的粘土；5-50重量％，优选15-45重量％的水合氧化铝提供的氧化铝；1-25重量％，优选5-20重量％的铝溶胶提供的氧化铝；1-30重量％，优选5-20重量％的硅溶胶提供的氧化硅；15-60重量％，优选20-50重量％的分子筛。
酸的用量为裂化催化剂制备方法中酸的常规用量，一般来说，酸的用量使酸与水合氧化铝提供的氧化铝的摩尔比为0.18-0.30，优选为0.20-0.25。所述酸选自裂化催化剂制备方法中所用的各种酸中的一种或几种，如盐酸、硫酸、硝酸、磷酸、甲酸和乙酸中的一种或几种，优选的酸为盐酸、硝酸和/或磷酸。
打浆时，各组分加入的先后顺序没有特别限制。优选情况下，先将粘土与水混合打浆，加入酸，再加入水合氧化铝，然后在30-80℃老化0.5-5小时，最后加入铝溶胶、硅溶胶和分子筛。
所述分子筛选自用作裂化催化剂活性组分的沸石和非沸石分子筛中的一种或几种。这些沸石和分子筛为本领域技术人员所公知。
所述沸石优选为大孔沸石和中孔沸石中的一种或几种。所述大孔沸石为具有至少0.7纳米环开口的孔状结构的沸石，如八面沸石、L沸石、Beta沸石、Ω沸石、丝光沸石、ZSM-18沸石中的一种或几种，特别是Y型沸石、含磷和/或稀土的Y型沸石、超稳Y沸石、含磷和/或稀土的超稳Y沸石，Beta沸石中的一种或几种。
所述中孔沸石为具有大于0.56纳米小于0.7纳米环开口的孔状结构的沸石，如具有MFI结构的沸石(如ZSM-5沸石)，含磷和/或稀土的具有MFI结构的沸石(如含磷和/或稀土ZSM-5沸石，CN1194181A公开的含磷的具有MFI结构的沸石)、ZSM-22沸石、ZSM-23沸石、ZSM-35沸石、ZSM-50沸石、ZSM-57沸石、MCM-22沸石、MCM-49沸石、MCM-56沸石中的一种或几种。
所述非沸石分子筛指沸石中的铝和/或硅部分或全部被其它元素如磷、钛、镓、锗中的一种或几种取代的分子筛。这些分子筛的实例包括具有不同硅铝比的硅酸盐(如金属硅酸盐metallosilicate、钛硅酸盐titanosilicate)、金属铝酸盐metalloaluminates(如锗铝酸盐Germaniumaluminates)、金属磷酸盐metallophosphates、铝磷酸盐aluminophosphates、金属铝磷酸盐metalloaluminophosphates、金属结合的硅铝磷酸盐metal integrated silicoaluminophosphates(MeAPSO和ELAPSO)、硅铝磷酸盐silicoaluminophosphates(SAPO)、镓锗酸盐(gallogermanates)中的一种或几种。特别是SAPO-17分子筛、SAPO-34分子筛和SAPO-37分子筛中的一种或几种。
优选情况下，所述分子筛选自Y型沸石、含磷和/或稀土的Y型沸石、超稳Y沸石、含磷和/或稀土的超稳Y沸石、Beta沸石、具有MFI结构的沸石、含磷和/或稀土的具有MFI结构的沸石中的一种或几种。
所述粘土选自用作裂化催化剂活性组分的粘土中的一种或几种，如高岭土、多水高岭土、蒙脱土、硅藻土、埃洛石、皂石、累托土、海泡石、凹凸棒石、水滑石、膨润土中的一种或几种。这些粘土为本领域技术人员所公知。
浆液的干燥方法和条件为本领域技术人员所公知。，例如，干燥的方法可以是晾干、烘干、鼓风干燥、喷雾干燥，优选喷雾干燥的方法。干燥的温度可以是室温至400℃，优选为100-350℃
干燥得到的固体可以根据情况洗涤或不洗涤，洗涤后干燥。洗涤的目的是使催化剂的氧化钠含量降低至0.3重量％以下。洗涤后的干燥方法和条件为本领域技术人员所公知，例如，干燥的方法可以是晾干、烘干、鼓风干燥。干燥的温度可以是室温至400℃，优选为100-350℃
按照本发明提供的方法，在打浆时的任意步骤，还可以加入稀土金属氧化物、碱土金属氧化物、氧化钛、氧化磷、氧化锆、氧化锰的一种或多种氧化物或其前身物。所述氧化物的前身物指在所述裂化催化剂制备过程中，能形成所述氧化物的物质中的一种或几种。例如，稀土金属、碱土金属、钛、磷、锆、锰的各种化合物，特别是稀土金属、碱土金属、钛、锆、锰的氢氧化物、硝酸盐、氯化物、磷酸、磷酸盐中的一种或几种。
下面的实例将对本发明做进一步的说明。
下列实例和对比例所制备催化剂的磨损指数按照《石油化工分析方法(RIPP试验方法)》(杨翠定等编，科学出版社，1990年出版)中的RIPP29-90方法测定。催化剂平均孔直径和孔直径为5-100纳米孔的孔体积采用低温氮吸附BET法测定。
实例1
本实例说明本发明提供的催化剂的制备方法。
在搅拌下，将4.2千克的去离子水、1.54千克高岭土(苏州高岭土公司产品，固含量78重量％)，300毫升浓度为20重量％的盐酸，1.6千克硅溶胶(江阴国联化工有限公司产品，平均颗粒直径为15纳米，95％的硅溶胶颗粒直径在8-22纳米之间，SiO2含量为25重量％)、1.29千克拟薄水铝石(山东铝厂出品，氧化铝含量62重量％)、0.95千克铝溶胶(齐鲁催化剂厂出品，氧化铝含量21重量％)、4.38千克工业牌号为DM-4的分子筛齐鲁催化剂厂出品，晶胞常数为24.45埃，含稀土和镁的超稳Y分子筛，混合稀土氧化物含量为3.0重量％，其中，氧化镧含量为1.1重量％，氧化铈含量为1.7重量％，其它稀土氧化物含量为0.2重量％，氧化镁含量为1.5重量％)含量为32重量％的浆液打浆混合均匀，得到浆液。在250℃的温度下将得到的浆液喷雾干燥成型，得到直径为20-120微米的固体颗粒，用去离子水洗涤至无钠离子被检测出，150℃烘干，得到催化剂C1。表1给出了所述浆液干基组成、浆液的固含量及酸与水合氧化铝提供的氧化铝的摩尔比。表2给出了催化剂C1的平均孔直径、孔直径为5-100纳米孔的孔体积和磨损指数。
实例2
本实例说明本发明提供的催化剂的制备方法。
将4.2千克的去离子水与1.54千克高岭土(同实例1)打浆均匀，加入300毫升浓度为20重量％的盐酸，搅拌均匀，加入1.29千克实例1所述拟薄水铝石，搅拌均匀后升温到65℃老化2小时，再加入0.95千克铝溶胶(同实例1)和1.6千克实例1所述硅溶胶搅拌均匀，然后加入4.38千克工业牌号为DM-4的分子筛含量为32重量％的浆液，打浆混合均匀，得到浆液。在250℃的温度下将得到的浆液喷雾干燥成型，得到直径为20-120微米的固体颗粒，用去离子水洗涤至无钠离子被检测出，150℃烘干，得到催化剂C2。表1给出了所述浆液干基组成、浆液的固含量及酸与水合氧化铝提供的氧化铝的摩尔比。表2给出了催化剂C2的平均孔直径、孔直径为5-100纳米孔的孔体积和磨损指数。
对比例1
本对比例说明参比催化剂的制备方法。
按照CN1098130A的方法制备催化剂。将6.7千克的去离子水与1.54千克高岭土(同实例1)打浆均匀，加入450毫升浓度为20重量％的盐酸，搅拌均匀，加入1.94千克实例1所述拟薄水铝石，搅拌均匀后升温到65℃老化2小时，再加入0.95千克铝溶胶(同实例1)搅拌均匀，然后加入4.38千克工业牌号为DM-4的分子筛含量为32重量％的浆液，打浆混合均匀，得到浆液。在250℃的温度下将得到的浆液喷雾干燥成型，得到直径为20-120微米的固体颗粒，用去离子水洗涤至无钠离子被检测出，150℃烘干，得到催化剂CB1。表2给出了催化剂CB1的平均孔直径、孔直径为5-100纳米孔的孔体积和磨损指数。
对比例2
本对比例说明参比催化剂的制备方法。
按照CN1388213A的方法制备催化剂。将3.51千克的去离子水与1.54千克高岭土(同实例1)打浆均匀，加入300毫升浓度为20重量％的盐酸，搅拌均匀，加入1.29千克实例1所述拟薄水铝石，搅拌均匀后升温到65℃老化2小时，再加入0.95千克铝溶胶(同实例1)和4.0千克水玻璃(氧化硅含量为10重量％)搅拌均匀，然后加入4.38千克工业牌号为DM-4的分子筛含量为32重量％的浆液，打浆混合均匀，得到浆液。在250℃的温度下将得到的浆液喷雾干燥成型，得到直径为20-120微米的固体颗粒，用去离子水洗涤至无钠离子被检测出，150℃烘干，得到催化剂CB2。表1给出了所述浆液干基组成、浆液的固含量及酸与水合氧化铝提供的氧化铝的摩尔比。表2给出了催化剂CB2的平均孔直径、孔直径为5-100纳米孔的孔体积和磨损指数。
实例3
本实例说明本发明提供的催化剂的制备方法。
将2.44千克的去离子水与0.54千克多水高岭土(固含量为74重量％，四川叙永瓷土公司出品)打浆均匀，加入358毫升浓度为20重量％的盐酸，搅拌均匀，加入1.61千克实例1所述拟薄水铝石，搅拌均匀后升温到40℃老化4.5小时，依次加入2.4千克硅溶胶(依卡化学品有限公司产品，平均颗粒直径为40纳米，90％的的硅溶胶颗粒直径在20-60纳米之间，SiO2含量为25重量％)、1.90千克铝溶胶(同实例1)、4.0千克工业牌号为DM-4的分子筛含量为32重量％的浆液、1.0千克ZSM-5沸石(硅铝比为70，氧化钠含量为0.1重量％，齐鲁催化剂厂出品)含量为32重量％的浆液，每加入一种组分后都打浆混合均匀，得到浆液。在250℃的温度下将得到的浆液喷雾干燥成型，得到直径为20-120微米的固体颗粒，用去离子水洗涤至无钠离子被检测出，150℃烘干，得到催化剂C3。表1给出了所述浆液干基组成、浆液的固含量及酸与水合氧化铝提供的氧化铝的摩尔比。表2给出了催化剂C3的平均孔直径、孔直径为5-100纳米孔的孔体积和磨损指数。
实例4
本实例说明本发明提供的催化剂的制备方法。
将2.55千克的去离子水与1.28千克高岭土(同实例1)和0.51千克蒙脱土(固含量为78重量％，湖北中祥县铁矿厂出品)打浆均匀，加入383毫升浓度为20重量％的硝酸，搅拌均匀，加入0.65千克实例1所述拟薄水铝石和0.31千克三水铝石(山东铝厂出品，氧化铝含量为64重量％)，搅拌均匀后升温到75℃老化1小时，依次加入2.5千克工业牌号为REHY的含稀土Y型分子筛(齐鲁催化剂厂出品，晶胞常数为24.62埃，含稀土的Y型分子筛，混合稀土氧化物含量为4.5重量％，其中，氧化镧含量为1.7重量％，氧化铈含量为2.6重量％，其它稀土氧化物含量为0.2重量％，氧化钠含量为1.5重量％)含量为32重量％的浆液、3.2千克实例1所述硅溶胶、1.90千克铝溶胶(同实例1)，每加入一种组分后都打浆混合均匀，得到浆液。在250℃的温度下将得到的浆液喷雾干燥成型，得到直径为20-120微米的固体颗粒，用去离子水洗涤至无钠离子被检测出，150℃烘干，得到催化剂C4。表1给出了所述浆液干基组成、浆液的固含量及酸与水合氧化铝提供的氧化铝的摩尔比。表2给出了催化剂C4的平均孔直径、孔直径为5-100纳米孔的孔体积和磨损指数。
实例5
本实例说明本发明提供的催化剂的制备方法。
将3.50千克的去离子水与0.77千克高岭土(同实例1)打浆均匀，加入224毫升浓度为20重量％的硝酸，搅拌均匀，加入0.63千克实例4所述三水铝石，搅拌均匀后升温到65℃老化2小时，再加入3.81千克铝溶胶(同实例1)和0.8千克硅溶胶(依卡化学品有限公司产品，平均颗粒直径为60纳米，90％的硅溶胶颗粒直径在30-90纳米之间，SiO2含量为25重量％)、搅拌均匀，然后加入5.25千克工业牌号为DASY的超稳Y分子筛(齐鲁催化剂厂出品，晶胞常数为24.46埃，氧化钠含量为0.99重量％)含量为32重量％的浆液、1.0千克工业牌号为ZRP-1的分子筛(齐鲁催化剂厂出品，含稀土和磷的具有MFI结构的沸石，硅铝比为20，混合稀土氧化物含量为1.5重量％，其中，氧化镧含量为0.6重量％，氧化铈含量为0.8重量％，其它稀土氧化物含量为0.1重量％，五氧化二磷含量为1.4重量％)含量为32重量％的浆液，打浆混合均匀。在250℃的温度下将得到的浆液喷雾干燥成型，得到直径为20-120微米的固体颗粒，用去离子水洗涤至无钠离子被检测出，150℃烘干，得到催化剂C5。表1给出了所述浆液干基组成、浆液的固含量及酸与水合氧化铝提供的氧化铝的摩尔比。表2给出了催化剂C5的平均孔直径、孔直径为5-100纳米孔的孔体积和磨损指数。
表1
| 实例编号 | 1 | 2 | 对比例1 | 对比例2 | 3 | 4 | 5 |
| 粘土种类 | 高岭土 | 高岭土 | 高岭土 | 高岭土 | 多水高岭土 | 高岭土/蒙脱土 | 高岭土 |
| 粘土含量，重量％ | 30 | 30 | 30 | 30 | 10 | 25/10 | 15 |
| 水合氧化铝种类 | 拟薄水铝石 | 拟薄水铝石 | 拟薄水铝石 | 拟薄水铝石 | 拟薄水铝石 | 三水铝石/拟薄水铝石 | 三水铝石 |
| 水合氧化铝提供的氧化铝含量，重量％ | 20 | 20 | 30 | 20 | 25 | 5/10 | 10 |
| 铝溶胶提供的氧化铝含量，重量％ | 5 | 5 | 5 | 5 | 10 | 10 | 20 |
| 硅溶胶提供的氧化硅含量，重量％ | 10 | 10 | 0 | 10* | 15 | 20 | 5 |
| 分子筛种类 | DM-4 | DM-4 | DM-4 | DM-4 | DM-4/ZSM-5 | REHY | DASY/ZRP-1 |
| 分子筛含量，重量％ | 35 | 35 | 35 | 35 | 32/8 | 20 | 42/8 |
| 浆液的固含量，重量％ | 28.0 | 28.0 | 25.0 | 25.0 | 28.0 | 30.0 | 25.0 |
| 酸与水合氧化铝提供的氧化铝的摩尔比 | 0.23 | 0.23 | 0.23 | 0.23 | 0.22 | 0.23 | 0.20 |
*水玻璃提供的氧化硅
表2
| 实例编号 | 1 | 2 | 对比例1 | 对比例2 | 3 | 4 | 5 |
| 催化剂编号 | C1 | C2 | CB1 | CB2 | C3 | C4 | C5 |
| 孔直径5-100纳米孔的孔体积，毫升/克 | 0.10 | 0.12 | 0.06 | 0.08 | 0.11 | 0.10 | 0.11 |
| 平均孔直径，纳米 | 7.6 | 7.8 | 5.4 | 5.9 | 7.4 | 7.2 | 7.5 |
| 磨损指数，％ | 1.4 | 1.5 | 2.5 | 3.0 | 1.8 | 1.3 | 2.0 |
从表2的结果可以看出，与只加入拟薄水铝石和加入水玻璃的制备方法制备出的参比催化剂CB1和CB2相比，采用本发明提供的加入所述硅溶胶的的制备方法制备的催化剂C1和C2的平均孔直径和孔直径为5-100纳米孔的孔体积明显增大，磨损指数较小，采用实例2所述的先将粘土与水混合打浆，加入无机酸，再加入水合氧化铝，然后老化，最后加入铝溶胶、硅溶胶和分子筛的方法制备的催化剂，平均孔直径和孔直径为5-100纳米孔的孔体积增大更加突出。
实例6-10
本实例说明本发明提供的方法制备的催化剂的催化性能。
将实例1-5制备的催化剂C1-C5在800℃，用100％水蒸气老化4小时，装入小型固定流化床装置(美国KTI公司生产的ACE Model R+微反)的反应器中，催化剂装量为10克，在反应温度为500℃，剂油重量比为7.03，的条件下，通入表3所示减压瓦斯油与常压渣油的混合油，对该混合油进行催化裂化，结果如表4所示。
对比例3-4
本对比例说明参比方法制备的催化剂的催化性能。
按实例7的方法在同样条件下对同样的原料油进行催化裂化，不同的是，所用催化剂分别为对比例1和对比例2制备的催化剂CB1和CB2。结果如表4所示。
表3
| 原料油名称 | 减压瓦斯油与常压渣油的混合油 | |
| 密度(20℃)，克·厘米-3 | 0.9044 | |
| 折光率(20℃) | 1.5217 | |
| 粘度(100℃)，毫米2·秒-1 | 9.96 | |
| 凝固点，℃ | 40 | |
| 苯胺点，℃ | 95.8 | |
| C，重量％ | 85.98 | |
| H，重量％ | 12.86 | |
| S，重量％ | 0.55 | |
| N，重量％ | 0.18 | |
| 残炭，重量％ | 3.0 | |
| 馏程，℃ | 初馏点 | 243 |
| 5重量％ | 294 | |
| 10重量％ | 316 | |
| 30重量％ | 395 | |
| 50重量％ | 429 | |
| 70重量％ | 473 | |
表4
| 实例编号 | 1 | 2 | 对比例1 | 对比例2 | 3 | 4 | 5 |
| 催化剂 | C1 | C2 | CB1 | CB2 | C3 | C4 | C5 |
| 裂化产物组成，重量％H2-C2液化气C5 +汽油柴油重油焦炭总计 | 1.7517.6353.1314.875.337.29100 | 1.7217.753.1414.955.287.21100 | 1.9118.0852.5614.574.878.01100 | 1.8517.9252.7214.745.037.74100 | 1.6817.8753.2115.044.937.27100 | 1.7817.9652.3115.235.37.42100 | 1.6718.0353.9214.214.857.32100 |
| 转化率，重量％ | 79.8 | 79.77 | 80.56 | 80.23 | 80.03 | 79.47 | 80.94 |
| 汽油+柴油 | 68 | 68.09 | 67.13 | 67.46 | 68.25 | 67.54 | 68.13 |
| 产品选择性(汽油+柴油)/转化率焦炭/转化率 | 0.8520.0914 | 0.8540.0904 | 0.8330.0994 | 0.8410.0965 | 0.8530.0908 | 0.8500.0934 | 0.8420.0904 |
从表4的结果可以看出，与采用现有方法制备的组成相同或相近的参比催化剂CB1和CB2相比，本发明提供的方法制备的催化剂C1和C2对轻质油(汽油和柴油)的选择性明显提高，焦炭选择性明显下降。C2对轻质油的选择性提高的更加突出，焦炭选择性下降的更加明显。C3-C5对轻质油(汽油和柴油)的选择性也明显提高，焦炭选择性也明显下降。
Claims (8)
1.一种含分子筛烃类裂化催化剂的制备方法，该方法包括将铝溶胶、水合氧化铝、粘土、酸、分子筛和水打浆混合均匀，制成一种浆液，使浆液的固含量为25-40重量％，然后干燥得到的浆液，其特征在于，在打浆时还加入一种硅溶胶，所述硅溶胶是平均颗粒直径为5-100纳米的颗粒，并且80％以上的颗粒直径在平均颗粒直径的0.5-1.5倍之间。
2.根据权利要求1所述的方法，其特征在于，所述硅溶胶的平均颗粒直径为10-80纳米。
3.根据权利要求1所述的方法，其特征在于，按干基计，各组分的用量使催化剂浆液含有5-50重量％的粘土，5-50重量％的水合氧化铝提供的氧化铝，1-25重量％的铝溶胶提供的氧化铝，1-30重量％的硅溶胶提供的氧化硅，15-60重量％的分子筛。
4.根据权利要求3所述的方法，其特征在于，按干基计，各组分的用量使催化剂浆液含有10-35重量％的粘土，15-45重量％的水合氧化铝提供的氧化铝，5-20重量％的铝溶胶提供的氧化铝，5-20重量％的硅溶胶提供的氧化硅，20-50重量％的分子筛。
5.根据权利要求1、3或4所述的方法，其特征在于，所述分子筛选自Y型沸石、含磷和/或稀土的Y型沸石、超稳Y沸石、含磷和/或稀土的超稳Y沸石、Beta沸石、具有MFI结构的沸石、含磷和/或稀土的具有MFI结构的沸石中的一种或几种。
6.根据权利要求1所述的方法，其特征在于，酸的用量使酸与水合氧化铝提供的氧化铝的摩尔比为0.18-0.30。
7.根据权利要求1或6所述的方法，其特征在于，所述酸选自盐酸、硝酸和/或磷酸。
8.根据权利要求1所述的方法，其特征在于，各组分加入的先后顺序为先将粘土与水混合打浆，加入酸，再加入水合氧化铝，然后在30-80℃老化0.5-5小时，最后加入铝溶胶、硅溶胶和分子筛。