CN1626726A - 具有负离子功能的织物整理剂及其制备方法 - Google Patents
具有负离子功能的织物整理剂及其制备方法 Download PDFInfo
- Publication number
- CN1626726A CN1626726A CN 200310109260 CN200310109260A CN1626726A CN 1626726 A CN1626726 A CN 1626726A CN 200310109260 CN200310109260 CN 200310109260 CN 200310109260 A CN200310109260 A CN 200310109260A CN 1626726 A CN1626726 A CN 1626726A
- Authority
- CN
- China
- Prior art keywords
- preparation
- finishing agent
- fabric
- fabric finishing
- tourmaline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种织物整理剂及其制备方法,特别是涉及一种能发生负离子、远红外并具有吸收紫外线作用的织物整理剂及其制备方法。其特征在于以分散技术来制备电气石悬浮液,而非现有技术采用的有机乳化剂。克服了由于采用有机乳化剂而造成的电气石在乳化液中无法溶解,以及电气石微粒被乳液包裹而团聚的缺陷。其中至少包括载银电气石粉末悬浮液、陶瓷粉末、粘结剂和分散剂。由此所整理剂整理出的织物不仅比现有技术提高了释放负离子的功能,而且不会影响白度、抗菌性能好、耐洗涤、手感好。
Description
技术领域
本发明涉及一种织物整理剂及其制备方法,特别是涉及一种能发生负离子、远红外并具有吸收紫外线作用的织物整理剂及其制备方法。
背景技术
随着技术的发展和人们对服饰和生活环境要求也从“美观舒适”向“健康环保”发展。已有不少国外文献对负离子远红外纤维和织物进行了深入的论述和探讨。具备这功能的纤维和织物也已进入市场,其中日本敷岛纺织的“HOLIC”纤维、大和纺织的“10LINA”纤维、日清纺的“IONAGE”纤维比较具有代表性。这些纤维都采用共混纺丝的技术,用于涤纶、丙纶等合成纤维。也有不少中国专利申请对此进行了披露,如CN1266119“含有电气石颗粒的人造丝纤维及其制造方法”;再如CN1308149所述的“一种合成纤维及其制造方法”;又如CN1293278所述的“负氧离子远红外保健织物及其制备方法”。其中主要成分为天然硅酸盐矿物--电气石,英文名tourmaline。它是自身永久具有热释电效应的天然矿物,其晶体之间存在着极其微弱的电流,电流虽然很弱,但电压却可达100万电子伏特,从而使空气发生电离,放出的电子与空气中的氢氧化碳、水结合产生负离子(H3O2)-。同时电气石会辐射远红外。
负离子广泛存在于大自然中,在含量高的地方如森林、海边、瀑布区等,它使人感到身心愉快,而人长时间身处负离子含量低的场所特别是有空调的封闭型办公室、住宅会诱发以空调病为代表的各种疾病。在医学上,负离子进入人体提高氧气的转化能力,进入血液后细胞活性会得到加强,Na、K等电解质及废物的传输、交换的频率也会加快,使体内的离子保持平衡,从而提高人体的自愈力和免疫力,加速新陈代谢,恢复或减轻疲劳。同时还能活化脑内荷尔蒙e-内啡肽,安定自律神经,使人心神安宁、血压下降、改善睡眠、心情得到放松。因此每天吸入适量的负离子对健康大有稗益。另外,负离子(水合羟基离子(H3O2)-)能与空气中被污染的正离子中和,从而起到净化空气的作用。
红外线是介于可见光和微波之间的一种电磁波,波长在0.76~1000微米之间。其中波长在4-15微米波段的远红外线对人体最为有益。人体吸收这一波段的远红外线后能在皮下3~5厘米深处产生温热效应,使细胞组织中的水分子被活化,处于高能状态,有助于生物酶的合成,因此能增强机体免疫功能和再生能力,扩张毛细血管,改善微循环,促进新陈代谢和血液流动。然而,在纤维的常规制备方法中,由于所用功能性矿物粉末的每种晶形不同,如梭柱体、核锥体、蒙面体、六面体、八面体、十二面体,因此在制备化纤材料时,一方面原料和电气石粉在熔融拉丝时难以均匀且易脱落;而且,由于电气石粉末的固有颗粒结构,所以不可能得到具有光滑表面的纤维,并且纤维经常断头。另一方面,在纺纱后加工中易磨损设备的配件。如综片、罗拉和导丝件。另外,由于电气石的色泽为黑灰色,也使纤维带有灰色,给后整理带来困难。
为此人们采用织物后整理的方法,将电气石通过涂层连接到织物上。但这样一来会使增厚,不透气。在装饰用品上应用尚可,而作为内外衣服用就不舒服。中国专利CN1293278提出了一种“负氧离子远红外保健织物及其制备方法”,但由于该方法是采用制备乳化液,因而制备、储存较为复杂,使用不便。采用的乳化剂和纳米级远红外陶瓷粉价格较高。更重要的是所述织物所释放的负离子平均为180个,峰值为2000个。峰值和平均值相差甚大,说明电气石分散可能不均匀,而且其平均值远小于1000个。其原因之一就是由于采用有机乳化剂而造成的电气石在乳化液中无法溶解,分散不均匀并容易造成电气石微粒被乳液包裹而团聚所致。
发明内容
本发明的目的在于克服现有技术的缺陷,提出一种具有负离子功能的织物整理剂及其制备方法,由此所整理的织物不仅保持了释放负离子的功能,而且负离子释放量大,产品性能均匀,所整理出的织物白度高、耐洗涤、手感好。
本发明的目的是由以下技术方案得以实现的:以分散技术来制备电气石悬浮液,而非现有技术采用的有机乳化剂。克服了由于采用有机乳化剂而造成的电气石在乳化液中无法溶解,以及电气石微粒被乳液包裹而团聚的缺陷。
具体地说,首先按以下重量百分比配制:
载银电气石粉末悬浮液(细度小于0.3微米)15-40%(占固含量重量百分数)
陶瓷粉末 10-30%
粘结剂 20-40%
分散剂 3-5%
水 余量
加水制成1升原液,原液中含固量400-650克。
其中,所述的载银电气石粉末由上海兰格科技有限公司生产;陶瓷粉末为氧化锌,氧化钛;粘结剂为丙烯酸脂类;分散剂为十二烷基硫酸钠和常规无机盐;
制备工艺:在室温下将上述原料用少量水搅拌分散成糊状,再在搅拌条件下加水到上述浓度。
整理工艺:将上述1份整理剂加4-8份水搅拌均匀。加水的量按织物实际带液率计算。
采用浸轧法,二浸二轧(压力2-3KG/CM2)→烘干(70-100℃)→焙烘(130-180℃,30-120秒)→产品。
本发明的优点:
1)经本发明的整理剂整理后的纺织品白度高。
2)整理后的纺织品,在电气石的特性功能作用下,负离子释放量可达4000-8000个/cm3;产生的远红外法向辐射率近85%。
3)银离子和电气石协同抗菌,抗菌效果好,且由于是物理抗菌,避免了药物抗菌带来的诸如细菌耐药性等弊端。
4)耐洗涤;克服了涂层法所造成的缺陷,透气,手感好。
5)采用分散剂,以分散技术来制备电气石悬浮液,而非现有技术采用的有机乳化剂。克服了由于采用有机乳化剂而造成的电气石在乳化液中无法溶解,以及电气石微粒被乳液包裹而团聚的缺陷,从而使制备方法更加简单和实用。
6)采用本发明整理工艺无环境污染。经整理后的纺织品具有健康环保功能。它集多种健康保健功能为一体,紧贴身体受体温及各部位活动摩擦刺激,激发电气石产生热电、压电效应。长期穿着可以收到多种功能共同作用而产生的综合保健效果。
7)使用方便,可采用常用的染整工艺,无需特殊的工艺和设备。所用药剂均为市场能购得的产品,成本低廉。
实施例
实施例1,
按以下重量百分比配制:
载银电气石粉末悬浮液(细度小于0.3微米)15%(占固含量重量百分数)
陶瓷粉末(氧化锌) 10%
粘结剂(丙烯酸脂) 20%
分散剂(十二烷基硫酸钠和无机盐NaCl) 3%
水 余量
加水制成1升原液,原液中含固量400克。
其中,所述的载银电气石粉末由上海兰格科技有限公司生产。
制备工艺:在室温下将上述原料用少量水搅拌分散成糊状,再在搅拌条件下加水到上述浓度。
整理工艺:将上述1份整理剂加4-8份水搅拌均匀。加水的量按织物实际带液率计算。
用上述整理剂处理纯棉卡其布:
采用浸轧法,二浸二轧(压力3KG/CM2)→烘干(95℃)→焙烘(150℃,100秒)→产品。
结果检测:
1,用WSD-II型白度仪测定,整理前织物正面平均82.5%,整理后正面平均81.1%。整理前织物反面平均82.5%,整理后反面平均81.0%。结论,整理前后白度基本不变。
2,用IRE-I型红外辐射仪测量法向辐射率:全波长积分发射率
F1(全波长积分发射率)0.84,F2(8-25)μm积分发射率0.84,F3(8.45)μm积分发射率0.84,F4(9.50)μm积分发射率0.83,F5(10.60)μm积分发射率0.85,F6(12.00)μm积分发射率0.84,F7(13.50)μm积分发射率0.84,F8(14-25)μm积分发射率0.85,
3,用日本产IC-1000型负离子产率测试仪测试
洗涤前8100个/CM3,洗涤10次后6230个/CM3。
实施例2,按以下重量百分比配制:
载银电气石粉末悬浮液(细度小于0.3微米)30%(占固含量重量百分数)
陶瓷粉末(氧化钛) 25%
粘结剂(丙烯酸脂) 30%
分散剂(十二烷基硫酸钠) 5%
水 余量
加水制成1升原液,原液中含固量650克。
其中,所述的载银电气石粉末由上海兰格科技有限公司生产;
制备工艺:在室温下将上述原料用少量水搅拌分散成糊状,再在搅拌条件下加水到上述浓度。
用上述整理剂处理涤棉布:
采用浸轧法,二浸二轧(压力2KG/CM2)→烘干(90℃)→焙烘(180℃,90秒)→产品。
结果检测:
1,用WSD-II型白度仪测定,整理前织物正面平均82.5%,整理后正面平均81.1%。整理前织物反面平均82.5%,整理后反面平均81.0%。结论,整理前后白度基本不变。
2,用日本产IC-1000型负离子产率测试仪测试
洗涤前6100个/CM3,洗涤10次后4000个/CM3。
Claims (5)
1,一种具有负离子功能的织物整理剂,其至少包括载银电气石粉末悬浮液、陶瓷粉末、粘结剂和分散剂。
2,一种具有负离子功能的织物整理剂的制备方法,其特征在于其中的各组成成份为:
载银电气石粉末悬浮液(细度小于0.3微米)15-40%(占固含量重量百分数)
陶瓷粉末 10-30%
粘结剂 20-40%
分散剂 3-5%
水 余量
加水制成1升原液,原液中含固量400-650克。
3,如权利要求2所述的织物整理剂的制备方法,其特征在于其中的陶瓷粉末为氧化锌或氧化钛。
4,如权利要求2所述的织物整理剂的制备方法,其特征在于其中分散剂为十二烷基硫酸钠和常规无机盐,如NaCl,Na2SO4。
5,如权利要求2所述的织物整理剂的制备方法,其其制备工艺为:在室温下将上述原料用少量水搅拌分散成糊状,再在搅拌条件下加水到上述浓度。