CN1545104A - 室温硫化加成型硅氟橡胶在绝缘子上的应用 - Google Patents
室温硫化加成型硅氟橡胶在绝缘子上的应用 Download PDFInfo
- Publication number
- CN1545104A CN1545104A CNA2003101167992A CN200310116799A CN1545104A CN 1545104 A CN1545104 A CN 1545104A CN A2003101167992 A CNA2003101167992 A CN A2003101167992A CN 200310116799 A CN200310116799 A CN 200310116799A CN 1545104 A CN1545104 A CN 1545104A
- Authority
- CN
- China
- Prior art keywords
- room temperature
- prtv
- insulator
- type
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种加成型硅氟橡胶的新用途，特别是室温硫化加成型硅氟橡胶(PRTV)在绝缘子上的应用。具有：①优良的憎水性和快速、均衡、持久的憎水迁移性，耐污闪电压提高两倍以上；②介电强度高达30MV/m，耐电蚀损性大TMA4.5级，阻燃性达FV－0级，抗电弧、在异常情况下能有效保护电瓷设备不受损坏；③机械强度高。附着力好，耐酸、碱、盐和化学试剂腐蚀，耐油性好；④耐紫外线、臭氧，抵抗环境侵蚀，不起皮，不开裂，使用寿命达20年以上；⑤低摩擦系数，具有防粘性，自洁性好，正常维护器内免清扫；⑥室温硫化，就地成型，使用方便，满足输变电设备现场防污技术措施的需要的优点。
Description
(一)、技术领域
本发明涉及一种加成型硅氟橡胶的新用途，特别是室温硫化加成型硅氟橡胶(PRTV)在绝缘子上的应用。
(二)、背景技术
绝缘子是一种无机氧化物为化学成分的电力设备，它强度高，绝缘性好，在电力系统尤其是高压系统仍然发挥着不可替代的作用。但是随着日益严重的大气污染，以无机氧化物为材料的瓷绝缘子亲水性的缺陷就变得致命了，易发生污闪事故。
(三)、发明内容：
为了克服现有技术的缺点，本发明是室温硫化加成型硅氟橡胶(PRTV)在绝缘子上的应用，提高耐污闪能力。
本发明是室温硫化加成型硅氟橡胶(PRTV)在绝缘子上的应用。硅氟橡胶是一类含氟取代基的有机硅元素高分子聚合物，性能优异，一般经热硫化加工为橡胶制品。
室温硫化加成型硅氟橡胶(PRTV)应用在绝缘子上具有下列优点：①、优良的憎水性和快速、均衡、持久的憎水迁移性，耐污闪电压提高两倍以上；②、介电强度高达30MV/m，耐电蚀损性大TMA4.5级，阻燃性达FV-0级，抗电弧、在异常情况下能有效保护电瓷设备不受损坏；③、机械强度高。附着力好，耐酸、碱、盐和化学介质腐蚀，耐油性好；④、耐紫外线、臭氧，抵抗环境侵蚀，不起皮，不开裂，使用寿命达20年以上；⑤、低摩擦系数，具有防粘性，自洁性好，正常维护期内免清扫；⑥、室温硫化，就地成型，使用方便，满足输变电设备现场防污技术措施的需要。
(四)、具体实施方式
本发明是室温硫化加成型硅氟橡胶(PRTV)在绝缘子上的应用。
室温硫化加成型硅氟橡胶(PRTV)的制备方法是：硅氟橡胶与白碳黑填料在密炼集中进行混炼，炼胶温度为70-120℃，压力低于0.3MPa。混炼胶在开炼机上返炼均匀形成良好的流动性，将胶料投入反应釜中，加入固化剂，搅拌均匀，制成室温硫化加成型硅氟橡胶(PRTV)。所述的固化剂是一甲基硅氧烷。上述组分的含量为硅氟橡胶55-70％，白碳黑25-40％，一甲基硅氧烷3-5％。
将待处理的输变电绝缘子设备表面进行清扫，去污和去油、脂处理，将上述制备好的室温硫化加成型硅氟橡胶(PRTV)喷涂或刷涂在绝缘子设备表面上。涂层厚度为0.5-0.6毫米。涂层光滑、均匀、无气泡。
Claims (5)
1、一种室温硫化加成型硅氟橡胶(PRTV)在绝缘子上的应用，其特征在于：室温硫化加成型硅氟橡胶(PRTV)在绝缘子上的应用。
2、根据权利要求1所述的应用，其特征在于：室温硫化加成型硅氟橡胶(PRTV)的制备方法是：硅氟橡胶与白碳黑填料在密炼机中进行混炼，炼胶温度为70-120℃，压力低于0.3MPa。混炼胶在开炼机上返炼均匀形成良好的流动性，将胶料投入反应釜中，加入固化剂，搅拌均匀，制成室温硫化加成型硅氟橡胶(PRTV)。所述的固化剂是一甲基硅氧烷。
3、根据权利要求2所述的应用，其特征在于：所述组分的含量为硅氟橡胶55-70％，白碳黑25-40％，一甲基硅氧烷3-5％。
4、根据权利要求1、2或3所述的应用，其特征在于：将待处理的输变电电瓷设备表面进行清扫，去污和去油、脂处理，将所述制备好的室温硫化加成型硅氟橡胶(PRTV)喷涂或刷涂在电瓷设备表面上。
5、根据权利要求3所述的应用，其特征在于：所述的涂层厚度为0.5-0.6毫米，涂层光华、均匀、无气泡。