CN1524919A - 汽车及轻型发动机复合冷却液及其制备方法 - Google Patents

汽车及轻型发动机复合冷却液及其制备方法 Download PDF

Info

Publication number
CN1524919A
CN1524919A CNA031592945A CN03159294A CN1524919A CN 1524919 A CN1524919 A CN 1524919A CN A031592945 A CNA031592945 A CN A031592945A CN 03159294 A CN03159294 A CN 03159294A CN 1524919 A CN1524919 A CN 1524919A
Authority
CN
China
Prior art keywords
amount
inhibiter
ethylene glycol
phosphoric acid
borax
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA031592945A
Other languages
English (en)
Other versions
CN1260320C (zh
Inventor
沈维生
李炜
肖述权
李丽
Original Assignee
沈维生
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 沈维生 filed Critical 沈维生
Priority to CN 03159294 priority Critical patent/CN1260320C/zh
Publication of CN1524919A publication Critical patent/CN1524919A/zh
Application granted granted Critical
Publication of CN1260320C publication Critical patent/CN1260320C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种发动机复合冷却液及其制备方法，是以去离子水、乙二醇、三乙醇胺、苯骈三氮唑、磷酸、硼砂、苯甲酸钠、氢氧化钠、缓蚀剂、消泡剂和染色剂组成为原料，在一定条件下进行混合反应，经过滤包装成。本产品应用于各种进口和国产发动机冷却系统，可适合不同地区的气候条件，具有良好的防冻、清洁阻垢、持久抗腐蚀、抗氧化、抗起泡和沸点高等性能，质量稳定可靠、性能优越，使用效果良好。

Description

汽车及轻型发动机复合冷却液及其制备方法
技术领域
本发明涉及一种精细化工产品，特别是一种汽车及轻型发动机复合冷却液。
背景技术
冷却系统是车用等发动机的重要组成部分，它的作用是对高温下工作的机件予以适当的冷却，以保证发动机在适宜温度下能够正常工作。冷却液的防冻冷却效果、防垢和抗腐蚀等性能是保证冷却系统正常运行的关键。虽然现在车用发动机冷却液市场上，相关产品种类繁多，但大多存在着使用寿命短、易结垢或腐蚀、易氧化、易起泡、沸点低等缺陷，造成冷却系统传热效率降低或冷却系统受损，另外也造成冷却液变质或易挥发。这不仅增加了冷却液的更换频率，造成经济上的浪费，而且严重影响了发动机的正常工作，缩短了发动机运行寿命。
发明内容
本发明的目的在于通过提供一种配方合理的汽车及轻型发动机复合冷却液及其制备方法，使冷却液在不同温度条件下，具有良好的防冻、清洁阻垢、持久抗腐蚀、抗氧化、抗起泡和沸点高等性能，以达到冷却效果好，延长冷却液使用周期，保证冷却系统正常运行和延长发动机使用寿命的目的。
本发明解决其技术问题所采用的技术方案是：提供一种发动机复合冷却液，该复合冷却液是由去离子水、乙二醇、三乙醇胺、苯骈三氮唑、磷酸、硼砂、苯甲酸钠、氢氧化钠、缓蚀剂、消泡剂和染色剂组成，各组分的重量百分数为：
去离子水                        30.00----68.00
乙二醇                          30.00----68.00
三乙醇胺                        0.10----0.80
苯骈三氮唑                      0.05----0.12
磷酸                            0.30----1.10
硼砂                            0.07----0.14
苯甲酸钠                        0.40----1.50
氢氧化钠                        0.10----0.80
缓蚀剂                          适量
消泡剂                          适量
染色剂                          适量
其中，去离子水中由于不含容易结垢的离子，减少了复合冷却液结垢的机会；即使混入少量的结垢离子，亦可以与复合冷却液中的阻垢剂磷酸、硼砂、氢氧化钠络合形成水溶性物质而达到防止结垢的目的；复合冷却液中一组优良持久的缓蚀剂苯骈三氮唑、缓蚀剂可以在组成发动机的铜、钢、焊料、铸铁、铸铝等金属表面形成保护膜，阻止这些金属被氧化和腐蚀。这种发动机复合冷却液的制备方法是：复合冷却液由由去离子水、乙二醇、三乙醇胺、苯骈三氮唑、磷酸、硼砂、苯甲酸钠、氢氧化钠、缓蚀剂、消泡剂和染色剂组成，各组分的重量百分数为：
去离子水                             30.00----68.00
乙二醇                               30.00----68.00
三乙醇胺                             0.10----0.80
苯骈三氮唑                           0.05----0.12
磷酸                                 0.30----1.10
硼砂                                 0.07----0.14
苯甲酸钠                             0.40----1.50
氢氧化钠                             0.10----0.80
缓蚀剂                               适量
消泡剂                               适量
染色剂                               适量
具体制备方法为：首先向调合釜中加入配方量的去离子水，再用进料循环泵抽取原料储罐中配方量的乙二醇到调合釜中，同时开启搅拌和回转循环流程，接着在釜内按配方量依次加入三乙醇胺、苯骈三氮唑、磷酸、硼砂、苯甲酸钠、氢氧化钠、缓蚀剂、消泡剂和染色剂，在25℃-60℃温度下循环、搅拌混合4-10小时，产品经压滤机过滤后进行包装即为成品。
本发明所提供发动机复合冷却液，按冰点可分为-25号---50号多个型号，可适应不同地区的气候条件下，各种进口和国产发动机的冷却系统。不仅具有优良的防冻冷却、阻垢洁净等性能；而且具有持久抗氧化、抗腐蚀性能，产品沸点高、抗起泡、蒸发损失少，使用寿命长。产品经权威质量监督机构连续三年评价和用户四年的行车使用证实，产品质量稳定、可靠，性能优越，效果良好。
下面结合实施例对本发明作进一步说明。
具体实施方式
实施例1.向调合釜中加入去离子水68.00千克，再用进料循环泵抽取原料储罐中配方量的乙二醇30.00千克到调合釜中，同时开启搅拌和回转循环流程，接着在釜内按配方量依次加入三乙醇胺0.80千克、苯骈三氮唑0.05千克、磷酸0.30千克、硼砂0.07千克、苯甲酸钠0.40千克、氢氧化钠0.38千克、适量缓蚀剂、消泡剂和染色剂，在25℃-60℃温度下循环、搅拌混合4-10小时，产品经压滤机过滤后进行包装即为成品。
实施例2.向调合釜中加入去离子水30.00千克，再用进料循环泵抽取原料储罐中配方量的乙二醇68.00千克到调合釜中，同时开启搅拌和回转循环流程，接着在釜内按配方量依次加入三乙醇胺0.10千克、苯骈三氮唑0.12千克、磷酸0.70千克、硼砂0.14千克、苯甲酸钠0.84千克、氢氧化钠0.10千克、适量缓蚀剂、消泡剂和染色剂，在25℃-60℃温度下循环、搅拌混合4-10小时，产品经压滤机过滤后进行包装即为成品空气进行通风氧化；经静置、沉降、过滤等一系列后处理过程处理，包装即为产品。
实施例3.向调合釜中加入去离子水46.92千克，再用进料循环泵抽取原料储罐中配方量的乙二醇49.00千克到调合釜中，同时开启搅拌和回转循环流程，接着在釜内按配方量依次加入三乙醇胺0.50千克、苯骈三氮唑0.08千克、磷酸1.10千克、硼砂0.10千克、苯甲酸钠1.50千克、氢氧化钠0.80千克、适量缓蚀剂、消泡剂和染色剂，在25℃-60℃温度下循环、搅拌混合4-10小时，产品经压滤机过滤后进行包装即为成品空气进行通风氧化；经静置、沉降、过滤等一系列后处理过程处理，包装即为产品。

Claims (2)

1.一种发动机复合冷却液，其特征在于该复合冷却液是由去离子水、乙二醇、三乙醇胺、苯骈三氮唑、磷酸、硼砂、苯甲酸钠、氢氧化钠、缓蚀剂、消泡剂和染色剂组成，各组分的重量百分数为：
       去离子水                      30.00----68.00
       乙二醇                        30.00----68.00
       三乙醇胺                      0.10----0.80
       苯骈三氮唑                    0.05----0.12
       磷酸                          0.30----1.10
       硼砂                          0.07----0.14
       苯甲酸钠                      0.40----1.50
       氢氧化钠                      0.10----0.80
       缓蚀剂                        适量
       消泡剂                        适量
       染色剂                        适量。
2.一种发动机复合冷却液的制备方法，其特征在于这种复合冷却液由去离子水、乙二醇、三乙醇胺、苯骈三氮唑、磷酸、硼砂、苯甲酸钠、氢氧化钠、缓蚀剂、消泡剂和染色剂组成，各组分的重量百分数为：
       去离子水                      30.00----68.00
       乙二醇                        30.00----68.00
       三乙醇胺                      0.10----0.80
       苯骈三氮唑                    0.05----0.12
       磷酸                          0.30----1.10
       硼砂                          0.07----0.14
       苯甲酸钠                      0.40----1.50
       氢氧化钠                      0.10----0.80
       缓蚀剂                        适量
       消泡剂                        适量
       染色剂                        适量
具体制备方法为：首先向调合釜中加入配方量的去离子水，再用进料循环泵抽取原料储罐中配方量的乙二醇到调合釜中，同时开启搅拌和回转循环流程，接着在釜内按配方量依次加入三乙醇胺、苯骈三氮唑、磷酸、硼砂、苯甲酸钠、氢氧化钠、缓蚀剂、消泡剂和染色剂，在25℃-60℃温度下循环、搅拌混合4-10小时，产品经压滤机过滤后进行包装即为成品。
CN 03159294 2003-09-15 2003-09-15 汽车及轻型发动机复合冷却液及其制备方法 Expired - Fee Related CN1260320C (zh)