CN1412254A - 低频电磁波磁屏蔽复合涂料及其制备方法 - Google Patents

低频电磁波磁屏蔽复合涂料及其制备方法 Download PDF

Info

Publication number
CN1412254A
CN1412254A CN 01128966 CN01128966A CN1412254A CN 1412254 A CN1412254 A CN 1412254A CN 01128966 CN01128966 CN 01128966 CN 01128966 A CN01128966 A CN 01128966A CN 1412254 A CN1412254 A CN 1412254A
Authority
CN
China
Prior art keywords
electromagnetic wave
frequency electromagnetic
magnetic shielding
magnetic
composite paint
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 01128966
Other languages
English (en)
Other versions
CN1182206C (zh
Inventor
管登高
黄婉霞
涂铭旌
陈家创
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sichuan University
Original Assignee
Sichuan University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sichuan University filed Critical Sichuan University
Priority to CNB01128966XA priority Critical patent/CN1182206C/zh
Publication of CN1412254A publication Critical patent/CN1412254A/zh
Application granted granted Critical
Publication of CN1182206C publication Critical patent/CN1182206C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种低频电磁波磁屏蔽复合涂料及其制备方法，其特点是采用磁性粉、磁性纤维和非晶磁性粉作导磁填料，用高分子树脂作成膜物质，于常温下与偶联剂和溶剂进行调配、混炼、研磨、过滤等工序，制得低频电磁波磁屏蔽涂料，它具有抗磁场干扰、防电子信息泄漏和防电磁环境污染的性能，其磁屏蔽效能达14～15dB，可广泛用于电子信息产品的磁屏蔽，建造磁屏蔽室和电子信息保密室方面。

Description

低频电磁波磁屏蔽复合涂料及其制备方法
一、技术领域
本发明属于低频电磁波磁屏蔽材料领域，涉及一种低频电磁波磁屏蔽复合涂料及其制备方法。
二、背景技术
传统的磁屏蔽材料多采用薄钢板、薄片、薄带等单一材料。有人采用粉末冶金法制造多孔质不锈钢烧结板磁屏蔽材料，其方法是把经高频感应炉溶炼的不锈钢合金熔体用水雾化制粉，将粉体在一定的压力下冲压成不锈钢平板，并将平板真空烧结(1273k×60min)成不锈钢板(厚4mm)，其低频磁屏蔽效能可达15dB(见《粉体およぴ粉末冶金》1999年第2期、第156页)。
复合磁屏蔽材料的研制和开发也越来越引起人们的重视。日本已成功研制出金属化纤磁屏蔽布“METAX”，其方法是采用无电解电镀工艺，通过催化剂，在纤维上沉积金属膜，制成高效复合磁屏蔽材料，金属膜以铜、镍膜为主，但其磁屏蔽效能未见报道。也有人将高磁导率钴系非晶合金薄片均匀地分散在聚对苯二甲酸乙二醇酯膜或金属箔上，作成三明治状，热压成片状体而成复合磁屏蔽材料。上述方法工艺复杂，设备要求严，成本高。
三、发明内容
本发明的目的是针对现有技术的不足，而提供一种低频电磁波磁屏蔽复合涂料及其制备方法，其特点是采用磁性粉、磁性纤维和非晶磁粉作导磁填料，用高分子树脂作成膜物质，经混炼、研磨、过滤等工序，制成低频电磁波磁屏蔽复合涂料。
本发明的目的由以下技术措施实现，所用原料份数，除特殊说明外，均为质量份数。
低频电磁波磁屏蔽复合涂料的配方组分为：
    成膜树脂           15～25份
    复合导磁填料       60～85份
    偶联剂              1～15份
    溶剂                30～100份
其中，成膜树脂为硅树脂、醇酸树脂、酚醛树脂、聚氨酯、环氧树脂、丙烯酸树脂和/或聚酯树脂至少一种。
复合导磁填料为20nm～40μm粒径的铜粉、铝粉、银粉、镍粉和/或锌粉至少一种；磁性纤维为100nm～80μm直径，长径比为50～200之间的铁纤维、镍纤维、铜纤维、不锈钢纤维、镀镍碳纤维和/或镀镍石墨纤维至少一种，非晶磁粉为20～100μm粒径的Fe-Cu-Mn-Si-B、Fe-Cu-Nb-Si-B和/或Fe-Nb-Mo-Cu-Si-B至少一种。
偶联剂为有机硅、硬脂酸、铝酸酯、硅烷和/或钛酸酯至少一种。
溶剂为甲乙酮、丙酮、乙酸甲酯、乙酸乙酯、乙酸丁酯、甲醇、乙醇、甲苯和/或二甲苯至少一种。
低频电磁波磁屏蔽复合涂料的制备方法
a、复合导磁填料的表面处理
将复合导磁填料60～85份加入偶联剂溶液中，偶联剂溶液浓度为0.5～10％、1～15份，在常温下用球磨机研磨10～40分钟，待分散均匀后，于温度40～140℃烘干，备用。
b、复合涂料的制备
将固含量为40～70％成膜树脂15～25份，与上述处理过的复合导磁填料60～85份，溶剂30～100份混合，在常温下用研磨机研磨2～5次，过滤、调节粘度4#杯20～50秒，获得低频电磁波磁屏蔽复合涂料。
上述方法制备的低频电磁波磁屏蔽复合涂料，采用冷喷涂设备喷涂或刷涂设备刷涂，在常温下干燥和固化。低频电磁波磁屏蔽复合涂料的物理性能和环境性能分别见表1、表2，它具有抗磁场干扰、防电子信息泄漏和防电磁环境污染的性能，其磁屏蔽效能可达到14～15dB。
低频电磁波磁屏蔽复合涂料可广泛用于电子信息产品的磁屏蔽、建造磁屏蔽室、电子信息保密室等。
本发明具有如下特点：
1.在低频电磁波频段(＜＝30MHZ)的磁屏蔽性能可达到14～15dB。
2.与常用磁屏蔽材料(如坡莫合金、不锈钢、金属化纤磁屏蔽布等)相比，每平方米磁屏蔽涂层的价格可降低30～40％。
3.涂料的配制、施工、干燥和固化均在常温下进行，能耗小、成本低，性价比高。
4.涂料制备方法简单、易于操作，可使用常规设备，投资不大、风险小。
四、具体实施方式
实施例：
下面通过实施例对本发明进行具体描述，有必要在此指出的是本实施例只能用于对本发明进行进一步说明，不能理解为对本发明保护范围的限制，本领域的技术熟练人员，可以根据上述发明的内容作出一些非本质的改进和调整。
1.将平均粒径为μm镍粉40克，纤维直径为10μm，纤维长径比为80的镀镍石墨磁性纤维5克和粒径为40μm的Fe-Cu-Nb-Si-B非晶磁粉25克，加入配制好的硅烷乙醇溶液中，硅烷乙醇溶液浓度8％ 10克，用球磨机研磨10分钟，待分散均匀后，在温度70℃烘干。将固含量为60％环氧树脂20克与上述表面处理过的复合导磁填料70克和乙醇50克混合，在常温下用研磨机研磨2～5次，过滤、调节粘度4#杯20～50秒，获得低频电磁波磁屏蔽复合涂料。
2.将平均粒径为5μm银粉30克，纤维直径为25μm，长径比为70的铁纤维7克和粒径为60μm的Fe-Cu-Mn-Si-B非晶磁粉30克，加入配制好的硬脂酸丙酮溶液中，硬脂酸的浓度6.5％8克，用球磨机研磨20分钟，待分散均匀后，在温度80℃烘干。将固含量为70％丙烯酸树脂25克与上述表面处理过的复合导磁填料67克和丙酮45克混合，在常温下用研磨机研磨2～5次，过滤、调节粘度4#杯20～50秒，获得低频电磁波磁屏蔽复合涂料。
3.将平均粒径为3μm铝粉50克，纤维直径为30μm，长径比为120的镍纤维10克和粒径为60μm的Fe-Nb-Mo-Cu-Si-B非晶磁粉15克，加入配制好钛酸酯甲苯溶液中，钛酸酯的浓度为4％12克，用球磨机研磨20分钟，待分散均匀后，在温度100℃烘干，将固含量为65％酚醛树脂18克与上述表面处理过的复合导磁填料75克和甲苯55克混合，在常温下用研磨机研磨2～5次，过滤、调节粘度4#杯20～50秒，获得低频电磁波磁屏蔽复合涂料。
     表1低频电磁波磁屏蔽复合涂料的物理性能
    检验项目及要求     检验结果
附着力，级(划格法)(SJ2573-85)     0级
铅笔硬度H(GB6739-86)     5H
冲击强度Kg.cm(GB/T1732-93)     50Kg.cm
耐磨性，失重g/cm2(GB1768-79)     0.0011g/cm2
                    表2低频电磁波磁屏蔽复合涂料的环境性能
                     检验项目及要求     检验结果
    低温实验(-55℃)(GJB150.4-86) 附着力0-1级     1级
表面不应该有龟裂、起泡、剥落等 符合
屏蔽效能下降应小于5％   (0.01-1000MHz)＜3.5％
高温实验(70℃)(GJB150.3-86) 附着力0-1级     1级
表面不应该有龟裂、起泡、剥落等 符合
屏蔽效能下降应小于5％   (0.01-1000MHz)＜3.5％
温度冲击(GJB360.7-87)(-55℃*0.5h-70℃*0.5h)100次 附着力0-1级     1级
表面不应该有龟裂、起泡、剥落等 符合
屏蔽效能下降应小于5％   (0.01-1000MHz)＜3.7％
    湿热性(GJB150.9-86)(60℃，RH：95％，120h) 附着力0-1级     1级
表面不应该有龟裂、起泡、剥落等 符合
屏蔽效能下降应小于5％   (0.01-1000MHz)＜2.1％
    盐雾(GJB360.2-87) 附着力0-1级     1级
表面不应该有龟裂、起泡、剥落等 符合
屏蔽效能下降应小于5％   (0.01-1000MHz)＜1.7％

Claims (7)

1.低频电磁波磁屏蔽复合涂料，其特征在于该复合涂料的配方组分(按质量份计)为：
  成膜树脂            15～25份
  复合导磁填料        60～85份
  偶联剂              1～15份
  溶剂                30～100份
2.按照权利要求1所述低频电磁波磁屏蔽复合涂料，其中成膜树脂为硅树脂、醇酸树脂、酚醛树脂、聚氨酯、环氧树脂、丙烯酸树脂和/或聚酯树脂至少一种。
3.按照权利要求1所述低频电磁波磁屏蔽复合涂料，其中复合导磁填料为20nm～40μm粒径的铜粉、铝粉、银粉、镍粉和/或锌粉至少一种，磁性纤维为100nm～80μm直径，长径比为50～200之间的铁纤维、镍纤维、铜纤维、不锈钢纤维、镀镍碳纤维和/或镀镍石墨纤维至少一种，非晶磁粉为20～100μm粒径的Fe-Cu-Mn-Si-B、Fe-Cu-Nb-Si-B和/或Fe-Nb-Mo-Cu-Si-B至少一种。
4.按照权利要求1所述低频电磁波磁屏蔽复合涂料，其中偶联剂为有机硅、硬脂酸、铝酸酯、硅烷和/或钛酸酯至少一种。
5.按照权利要求1所述低频电磁波磁屏蔽复合涂料，其中溶剂为甲乙酮、丙酮、乙酸甲酯、乙酸乙酯、乙酸丁酯、甲醇、乙醇、甲苯和/或二甲苯至少一种。
6.按照权利要求1所述低频电磁波磁屏蔽复合涂料的制备方法，其特征在于：
a、复合导磁填料的表面处理
将复合导磁填料60～85份加入偶联剂溶液中，偶联剂溶液浓度为0.5～10％、1～15份，在常温下用球磨机研磨10～40分钟，待分散均匀后，在温度40～140℃烘干，备用，
b、复合涂料的制备
将固含量为40～70％成膜树脂15～25份，与上述处理过的复合导磁填料60～85份，溶剂30～100份混合，在常温下用研磨机研磨2～5次，过滤、调节粘度4#杯20～50秒，获得低频电磁波磁屏蔽复合涂料。
7.按照权利要求1所述低频电磁波磁屏蔽复合涂料的用途，其特征在于该复合涂料用于电子信息产品的磁屏蔽，建造磁屏蔽室和电子信息保密室方面。
CNB01128966XA 2001-10-17 2001-10-17 低频电磁波磁屏蔽复合涂料及其制备方法 Expired - Fee Related CN1182206C (zh)