CN1401715A - 丙烯酸树脂底面合一漆 - Google Patents

丙烯酸树脂底面合一漆 Download PDF

Info

Publication number
CN1401715A
CN1401715A CN 02135550 CN02135550A CN1401715A CN 1401715 A CN1401715 A CN 1401715A CN 02135550 CN02135550 CN 02135550 CN 02135550 A CN02135550 A CN 02135550A CN 1401715 A CN1401715 A CN 1401715A
Authority
CN
China
Prior art keywords
acrylic resin
paint
molecular weight
weight
top lacquer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 02135550
Other languages
English (en)
Inventor
于安军
王子健
李玉宁
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China National Heavy Duty Truck Group Co Ltd
Original Assignee
China National Heavy Duty Truck Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by China National Heavy Duty Truck Group Co Ltd filed Critical China National Heavy Duty Truck Group Co Ltd
Priority to CN 02135550 priority Critical patent/CN1401715A/zh
Publication of CN1401715A publication Critical patent/CN1401715A/zh
Pending legal-status Critical Current

Abstract

本发明属于化工油漆的技术领域，特别涉及一种汽车底盘用丙烯酸树脂底面合一漆。羟基丙烯酸树脂(分子量25000－30000)6－12％，丙烯酸树脂(分子量45000－60000)43－63％，炭黑1－4％，滑石粉3－6％，硫酸钡1－4％，三聚磷酸钠3－7％，防锈助剂1.5－3.5％，溶剂20－26％。本发明具有成膜温度低，强度大，施工方便的优点。

Description

丙烯酸树脂底面合一漆
(一)技术领域
本发明属于化工油漆的技术领域，特别涉及一种汽车底盘用丙烯酸树脂底面合一漆。
(二)背景技术
目前，大型部件如汽车底盘等至少需要两步刷漆——底漆和面漆，施工繁锁，成本高，强度低。而且，目前普遍使用的丙烯酸聚氨酯漆，是双组分油漆，价格高，施工不便，双组分漆配好后，6小时内必须用完，否则易凝胶报废，漆膜需80℃烘干或常温干燥24-48小时后才能搬运。如中国专利CN1102196公开了“一种高级轿车用丙烯酸罩光清漆”，其成膜温度高，只能作为面漆使用。中国专利CN1105689公开了“耐冲拔耐高温蒸煮金属涂料”，是用丙烯酸树脂改性环氧树脂而成的涂料，虽然其强度比较高，但其成膜温度也比较高，成本高，不适合于象中小批量汽车底盘这样的大型工件的施工。中国专利CN1235995公开了“高亮度发光油漆及其制造方法”，是将发光粉与丙烯酸树脂进行混合后制成的，也是只能作为面漆使用。
(三)发明内容
本发明的目的在于提供一种成膜温度低，强度大，施工方便的新型单组分丙烯酸树脂底面合一漆。
本发明的目的是这样实现的：
本发明的丙烯酸树脂底面合一漆，是由以下物质按重量百分比组成的：
羟基丙烯酸树脂 50％(分子量25000-30000)    6-12％
  丙烯酸树脂 50％(分子量45000-60000)      43-63％
  炭黑                                    1-4％
  滑石粉                                  3-6％
  硫酸钡                                  1-4％
  三聚磷酸钠                              3-7％
  防锈助剂                                1.5-3.5％
  溶剂                                    20-26％
本发明的丙烯酸底面合一漆，其更佳的配比是由以下物质按重量百分比组成的：
  羟基丙烯酸树脂 50％(分子量25000-30000)  7-10％
  丙烯酸树脂     50％(分子量45000-60000)  50-58％
  炭黑                                    2-3％
  滑石粉                                  3-5％
  硫酸钡                                  1.5-3％
  三聚磷酸钠                              4-6％
  防锈助剂                                2-3％
  溶剂                                    20-25％
本发明的防锈助剂，其组成配比(重量)为：磷酸锌∶三聚磷酸钠∶铁黑＝5∶3∶10。
本发明的溶剂，其组成配比(重量)为：二甲苯∶丁醇∶环己酮＝7∶1∶2。
本发明利用了丙烯酸树脂粘接性能好，具有可塑性的特点。分子量为45000-60000的丙烯酸树脂具有较强的粘接性能，强度大，刚性强。而分子量为25000-30000的羟基丙烯酸树脂可塑性强，柔性强，可以增加漆的耐折性。这两种丙烯酸树脂进行混合，做成的油漆，即具有较强的粘接强度，又具有可塑性，即可以作为底漆使用，又可以作为面漆使用。
本发明的丙烯酸树脂底面合一漆，加入防锈剂，可以达到防锈的目的。同时，防锈剂的成分为磷酸锌，三聚磷酸钠，铁黑，可以起到磷化的作用，增强油漆与金属部件的结合强度。
本发明的丙烯酸树脂底面合一漆，可采用传统的空气喷涂，静电喷涂或高压无气喷涂等方法施工。在常温下2小时表干，12小时自干，无需烘烤，节省能源。
因此，本发明具有成膜温度低，强度大，施工方便的优点。
(四)具体实施方式
本发明的具体实施例，是由以下物质按重量百分比组成的：
羟基丙烯酸树脂 50％(分子量25000-30000)       8.6％
丙烯酸树脂     50％(分子量45000-60000)       53.4％
炭黑           H2                            2.45％
滑石粉         1250目                        4.0％
硫酸钡         工业                          2.1％
三聚磷酸钠     工业                          5.5％
防锈助剂                                     2.25％
二甲苯         工业                          15％
丁醇           工业                          2.4％
环己酮         工业                          4.3％
防锈助剂的配比(重量)为：磷酸锌∶三聚磷酸钠∶铁黑＝5∶3∶10。
本发明的丙烯酸树脂底面合一漆，其生产设备和工艺与普通漆相同。可采用空气喷涂、静电喷涂及高压无气喷涂方法施工，一次成膜35um以上。漆膜力学和耐蚀性能性有较大的提高，盐雾试验240以上，人工老化400小时以上。

Claims (5)

1.一种丙烯酸树脂底面合一漆，其特征在于：是由以下物质按重量百分比组成的：羟基丙烯酸树脂 50％(分子量25000-30000)         6-12％丙烯酸树脂     50％(分子量45000-60000)         43-63％炭黑                                          1-4％滑石粉                                        3-6％硫酸钡                                        1-4％三聚磷酸钠                                    3-7％防锈助剂                                      1.5-3.5％溶剂                                          20-26％
2.根据权利要求1所述的丙烯酸树脂底面合一漆，其特征在于：是由以下物质按重量百分比组成的：羟基丙烯酸树脂 50％(分子量25000-30000)         7-10％丙烯酸树脂     50％(分子量45000-60000)         50-58％炭黑                                          2-3％滑石粉                                        3-5％硫酸钡                                        1.5-3％三聚磷酸钠                                    4-6％防锈助剂                                      2-3％溶剂                                          20-25％
3.根据权利要求1所述的丙烯酸树脂底面合一漆，其特征在于：是由以下物质按重量百分比组成的：羟基丙烯酸树脂 50％(分子量25000-30000)        8.6％丙烯酸树脂    50％(分子量45000-60000)         53.4％炭黑                                         2.45％滑石粉                                       4.0％硫酸钡                                       2.1％三聚磷酸钠                                   5.5％防锈助剂                                     2.25％溶剂                                         23.7％
4.根据权利要求1、2、3所述的丙烯酸树脂底面合一漆，其特征在于：所述的防锈助剂，其组成配比(重量)为：
     磷酸锌∶三聚磷酸钠∶铁黑＝5∶3∶10
5.根据权利要求1、2、3所述的丙烯酸树脂底面合一漆，其特征在于：所述的溶剂，其组成配比(重量)为：
     二甲苯∶丁醇∶环己酮＝7∶1∶2
CN 02135550 2002-09-18 2002-09-18 丙烯酸树脂底面合一漆 Pending CN1401715A (zh)