CN1288029A - 导电碳油墨 - Google Patents

导电碳油墨 Download PDF

Info

Publication number
CN1288029A
CN1288029A CN 99119395 CN99119395A CN1288029A CN 1288029 A CN1288029 A CN 1288029A CN 99119395 CN99119395 CN 99119395 CN 99119395 A CN99119395 A CN 99119395A CN 1288029 A CN1288029 A CN 1288029A
Authority
CN
China
Prior art keywords
resin
parts
printing ink
conductive carbon
resol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 99119395
Other languages
English (en)
Other versions
CN1117826C (zh
Inventor
许耀康
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN99119395A priority Critical patent/CN1117826C/zh
Publication of CN1288029A publication Critical patent/CN1288029A/zh
Application granted granted Critical
Publication of CN1117826C publication Critical patent/CN1117826C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种导电碳油墨,主要由树脂、导电材料和溶剂组成,其组分为:1.树脂:胺基树脂10～30份,酚醛树脂10～20份;2.导电材料:石墨10～30份,碳黑10～30份;3.溶剂:醚类20～40份,酮类20～40份。本发明具有制作工艺简单,成本低廉,导电率高,耐热性好和适用范围宽广等优点。

Description

导电碳油墨
本发明涉及印刷油墨。
目前在导电印刷中常用的是银浆和碳浆两大类，银浆导电性能优良，但价格昂贵，资源紧缺，不宜于大批量工业化生产；碳浆虽然价格较便宜，原材料丰富，但导电性能差，耐磨、耐热性能也差。
本发明的目的即在于针对上述现有技术所存在的问题，包括银浆价格昂贵，以及碳浆的导电性能差，耐磨、耐热性能差等方面的问题，而提供一种导电性能较好，且高温阻值变化率小的导电碳油墨。
本发明的目的是通过以下技术方案来实现的：
一、一种导电碳油墨，其主要成分配方的重量比例如下：
1．树脂：胺基树脂10～30份，酚醛树脂10～20份；
2．导电材料：石墨10～30份，碳黑10～30份；
3．溶剂：醚类20～40份，酮类20～40份；
二、制作工艺过程如下：
1．配料：按上述配方比例配齐树脂、导电材料和溶剂；
2．搅拌：将上述配料加入容器中充分混合，搅拌均匀；
3．研磨：将上述搅拌均匀的配料在胶体磨上进行研磨3次，研磨后达到200～300目；
4．混练：将上述膏剂在三辊机上进行混练后进行测试合格，包装入库。
本发明具有以下优点和效果：
1、与现有的同类产品比较，具有导电率高，耐热性、耐磨性和耐碱性好(见下表)等优点。
150℃30分钟电阻 260℃阻值变化率(5秒×3次) 5％NaOH溶液浸泡后阻值变化率＜±10％
现有的同类产品 50Ω/口 ±20％ 浸泡时间＜30分钟
本发明的导电碳油墨 20Ω/口 ＜±10％ 浸泡时间2小时
2、本发明的导电碳油墨的制作工艺简单，成本低廉，应用范围广。
下面结合实施例作详细说明：
一、主要成分配方的重量比例如下：
本发明导电碳油墨的配方(重量)比例：
1．树脂：
1)胺基树脂10～30份
2)酚醛树脂10～20份
2．导电材料：
1)石墨    10～30份
2)碳黑    10～30份
3．溶剂：
1)醚类    20～40份
2)酮类    20～40份
二、工艺过程：
1．配料：按上述配方比例配齐树脂、导电材料和溶剂；
2．搅拌：将上述配料加入容器中充分混合，搅拌均匀；
3．研磨：将上述搅拌均匀的配料在胶体磨上进行研磨3次，研磨后达到200～300目；
4．混练：将上述研磨后的膏剂在三辊机上进行混练(三辊之间的间距调整到2～5μm)，经测试合格即可包装入库。
上面所说的配方中的胺基树脂包括570胺基树脂、582-2三聚氰胺树脂、578-1胺基树脂和576-1胺基树脂，其分子式分别如下：
1、570胺基树脂
Figure 9911939500041
2、582-2三聚氰胺树脂
3、578-1胺基树脂
Figure 9911939500052
4、576-1胺基树脂
上面所说的酚醛树脂、醚类和酮类包括：
1、284酚醛树脂
Figure 9911939500054
2、2402酚醛树脂
Figure 9911939500061
3、热固性酚醛树脂(碱性催化)
4、热塑性酚醛树脂(酸性催化)
醚类：
1、乙二醇苯醚
2、乙二醇二甲醚HOC2H4OCH3
3、乙二醇丁醚HOCH2CH2O(CH2)3CH3
4、乙烯基正丁基醚CH2=CHOCH2(CH2)CH3
5、二乙二醇丁醚C4H9OCH2CH2OCH2CH2OH
酮类：
1、异佛尔酮
Figure 9911939500063
2、异丙叉丙酮(CH3)2=CHCOCH3
3、对甲荃苯乙酮
4、二异丁基甲酮(CH3)2CHCH2COCH2CH(CH3)2

Claims (5)

1、一种导电碳油墨，主要由树脂和导电材料组成，其特征在于：
一、主要成分配方的重量比例如下：
1．树脂：胺基树脂10～30份，酚醛树脂10～20份；
2．导电材料：石墨10～30份，碳黑10～30份；
3．溶剂：醚类20～40份，酮类20～40份；
二、制作工艺过程如下：
1．配料：按上述配方比例配齐树脂、导电材料和溶剂；
2．搅拌：将上述配料加入容器中充分混合，搅拌均匀；
3．研磨：将上述搅拌均匀的配料在胶体磨上进行研磨3次，研磨后达到200～300目；
4．混练：将上述膏剂在三辊机上进行混练后进行测试合格，包装入库。
2、根据权利要求1所述的导电碳油墨，其特征在于：所说的胺基树脂是指570胺基树脂、582-2三聚氰胺树脂、578-1胺基树脂、576-1胺基树脂中的一种。
3、根据权利要求1所述的导电碳油墨，其特征在于：所说的酚醛树脂是指284酚醛树脂、2402酚醛树脂、热固性酚醛树脂、热塑性酚醛树脂中的一种。
4、根据权利要求1所述的导电碳油墨，其特征在于：所说的醚类是指乙二醇苯醚、乙二醇二甲醚、乙二醇丁醚、乙烯基正丁基醚、二乙二醇丁醚中的一种。
5、根据权利要求1所述的导电碳油墨，其特征在于：所说的酮类是指异佛尔酮、异丙叉丙酮、对甲基苯乙酮、二异丁基甲酮中的一种。
CN99119395A 1999-09-15 1999-09-15 导电炭油墨 Expired - Fee Related CN1117826C (zh)