CN103559941A - 一种导电碳浆及其制备方法 - Google Patents

一种导电碳浆及其制备方法 Download PDF

Info

Publication number
CN103559941A
CN103559941A CN201310359165.3A CN201310359165A CN103559941A CN 103559941 A CN103559941 A CN 103559941A CN 201310359165 A CN201310359165 A CN 201310359165A CN 103559941 A CN103559941 A CN 103559941A
Authority
CN
China
Prior art keywords
toluene
mixed liquor
tdi
weight ratio
isocyanate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310359165.3A
Other languages
English (en)
Inventor
闫福江
闫夫军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LINYI ZHUYUE NEW TYPE MATERIALS Co Ltd
Original Assignee
LINYI ZHUYUE NEW TYPE MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LINYI ZHUYUE NEW TYPE MATERIALS Co Ltd filed Critical LINYI ZHUYUE NEW TYPE MATERIALS Co Ltd
Priority to CN201310359165.3A priority Critical patent/CN103559941A/zh
Publication of CN103559941A publication Critical patent/CN103559941A/zh
Pending legal-status Critical Current

Abstract

一种导电碳浆，所采用的原料为导电炭黑、导电石墨、聚乙二醇、甲苯二异氰酸酯、酚醛树脂、乙二醇乙醚醋酸酯、环己酮；所述导电碳浆的制备方法，是将聚乙二醇与甲苯二异氰酸酯和酚醛树脂与乙二醇乙醚醋酸酯分别制成混合液，再将上述两混合液制成粘接材料，再将导电炭黑和导电石墨的混合料加上述粘接材料、环己酮混合、搅拌、碾磨，即制成本发明导电碳浆。本发明导电碳浆原料组成合理，制备方法简单，所制备的导电碳浆耐温点高，其应用范围广。

Description

一种导电碳浆及其制备方法
技术领域：本发明属化学化工技术领域，涉及一种导电碳浆及其制备的方法。
背景技术：现有技术的导电碳浆主要是以环氧树脂型黏合剂为粘合材料。由于环氧树脂的耐温点较低，常规条件下仅为120℃，改性后也只有155℃，因此这种导电碳浆的耐温点较低，其应用范围窄，应用的领域受到很大的限定。
发明内容：本发明的目的是提供一种导电碳浆及其制备方法，用以有效地克服现有技术所存在的上述弊端。实现本发明目的技术方案如下：
一、本发明的导电碳浆，所采用的原料如下：导电炭黑、导电石墨、聚乙二醇、甲苯二异氰酸酯、酚醛树脂、乙二醇乙醚醋酸酯、环己酮；其中：导电炭黑与导电石墨的重量比为1∶0.5-0.8，聚乙二醇与甲苯二异氰酸酯重量比为1∶1.0-1.4，乙二醇乙醚醋酸酯与酚醛树脂重量比为1∶2.2-3.2，聚乙二醇和甲苯二异氰酸酯的混合液与酚醛树脂和乙二醇乙醚醋酸酯的混合液的重量比为1∶8-10，导电炭黑和导电石墨的混合料与聚乙二醇和甲苯二异氰酸酯的混合液、酚醛树脂和乙二醇乙醚醋酸酯的混合液制成粘接材料的重量比为1∶4-4.5，环己酮微量。
二、本发明导电碳浆的制备方法，工艺步骤如下：
(1)先在三口烧瓶中加入聚乙二醇，加热抽真空脱水大体1个小时，然后冷却并充入氮气隔离保护，当温度达到大体80℃时，按比例尽快加入甲苯二异氰酸酯，充分搅拌均匀，制得聚乙二醇与甲苯二异氰酸酯混合液，然后倒入容器冷却至常温待用；
(2)在三口烧瓶中加入酚醛树脂，边搅拌边按比例加入乙二醇乙醚醋酸酯，同时加热至酚醛树脂完全融化，形成混合液，然后按比例加入步骤(1)制得的聚乙二醇和甲苯二异氰酸酯的混合液，混合反应大体2个小时，制取酚醛树脂型粘接材料；
(3)将导电炭黑与导电石墨按比例混合在一起，充分搅拌成混合料，然后按比例加入步骤(2)制得的酚醛树脂型粘接材料，再加入环己酮适量，放入搅拌机充分搅拌均匀，最后投入碾磨机碾细，即制得本发明导电碳浆。
本发明导电碳浆原料组成合理，制备方法简单，所制备的导电碳浆耐温点高，其应用范围广。
具体实施方式：
实施例1：(1)先在三口烧瓶中加入聚乙二醇，加热抽真空脱水1个小时，然后冷却并充入氮气隔离保护，当温度达到80℃时，尽快加入甲苯二异氰酸酯，聚乙二醇与甲苯二异氰酸酯重量比为1∶1.0，充分搅拌均匀，制得聚乙二醇与甲苯二异氰酸酯混合液，然后倒入容器冷却至常温待用；
(2)在三口烧瓶中加入酚醛树脂，边搅拌边加入乙二醇乙醚醋酸酯，乙二醇乙醚醋酸酯与酚醛树脂重量比为1∶2.2，同时加热至酚醛树脂完全融化，形成混合液，然后加入步骤(1)制得的聚乙二醇和甲苯二异氰酸酯的混合液，聚乙二醇和甲苯二异氰酸酯的混合液与酚醛树脂和乙二醇乙醚醋酸酯的混合液的重量比为1∶8，混合反应2个小时，制取酚醛树脂型粘接材料；
(3)将导电炭黑与导电石墨按1∶0.5的重量比混合在一起，充分搅拌成混合料，然后加入步骤(2)制得的酚醛树脂型粘接材料，导电炭黑和导电石墨的混合料与步骤(2)制得的酚醛树脂型粘接材料的重量比为1∶4，再加入环己酮适量，放入搅拌机充分搅拌均匀，最后投入碾磨机碾细，即制得本发明导电碳浆。
实施例2：根据实施例1，其中：导电炭黑与导电石墨的重量比为1∶0.8，聚乙二醇与甲苯二异氰酸酯重量比为1∶1.4，乙二醇乙醚醋酸酯与酚醛树脂重量比为1∶3.2，聚乙二醇和甲苯二异氰酸酯的混合液与酚醛树脂和乙二醇乙醚醋酸酯的混合液的重量比为1∶10，导电炭黑和导电石墨的混合料与步骤(2)制得的酚醛树脂型粘接材料的重量比为1∶4.5。
实施例3：根据实施例1，其中：导电炭黑与导电石墨的重量比为1∶0.6-0.7，聚乙二醇与甲苯二异氰酸酯重量比为1∶1.2，乙二醇乙醚醋酸酯与酚醛树脂重量比为1∶2.6-2.8，聚乙二醇和甲苯二异氰酸酯的混合液与酚醛树脂和乙二醇乙醚醋酸酯的混合液的重量比为1∶9，导电炭黑和导电石墨的混合料与步骤(2)制得的酚醛树脂型粘接材料的重量比为1∶4.3。

Claims (3)

1.一种导电碳浆，其特征在于所采用的原料如下：导电炭黑、导电石墨、聚乙二醇、甲苯二异氰酸酯、酚醛树脂、乙二醇乙醚醋酸酯、环己酮；其中：导电炭黑与导电石墨的重量比为1∶0.5-0.8，聚乙二醇与甲苯二异氰酸酯重量比为1∶1.0-1.4，乙二醇乙醚醋酸酯与酚醛树脂重量比为1∶2.2-3.2，聚乙二醇和甲苯二异氰酸酯的混合液与酚醛树脂和乙二醇乙醚醋酸酯的混合液的重量比为1∶8-10，导电炭黑和导电石墨的混合料与聚乙二醇和甲苯二异氰酸酯的混合液、酚醛树脂和乙二醇乙醚醋酸酯的混合液制成酚醛树脂型粘接材料的重量比为1∶4-4.5，环己酮微量。
2.根据权利要求1所述的导电碳浆，其特征在于所说导电炭黑与导电石墨的重量比为1∶0.6-0.7，聚乙二醇与甲苯二异氰酸酯重量比为1∶1.2，乙二醇乙醚醋酸酯与酚醛树脂重量比为1∶2.6-2.8，聚乙二醇和甲苯二异氰酸酯的混合液与酚醛树脂和乙二醇乙醚醋酸酯的混合液的重量比为1∶9，导电炭黑和导电石墨的混合料与聚乙二醇和甲苯二异氰酸酯的混合液、酚醛树脂和乙二醇乙醚醋酸酯的混合液制成酚醛树脂型粘接材料的重量比为1∶4.3。
3.一种根据权利要求1所述导电碳浆的制备方法，其特征在于工艺步骤如下：
(1)先在三口烧瓶中加入聚乙二醇，加热抽真空脱水大体1个小时，然后冷却并充入氮气隔离保护，当温度达到大体80℃时，按比例尽快加入甲苯二异氰酸酯，充分搅拌均匀，制得聚乙二醇与甲苯二异氰酸酯混合液，然后倒入容器冷却至常温待用；
(2)在三口烧瓶中加入酚醛树脂，边搅拌边按比例加入乙二醇乙醚醋酸酯，同时加热至酚醛树脂完全融化，形成混合液，然后按比例加入步骤(1)制得的聚乙二醇和甲苯二异氰酸酯的混合液，混合反应大体2个小时，制取酚醛树脂型粘接材料；
(3)将导电炭黑与导电石墨按比例混合在一起，充分搅拌成混合料，然后按比例加入步骤(2)制得的酚醛树脂型粘接材料，再加入环己酮适量，放入搅拌机充分搅拌均匀，最后投入碾磨机碾细，即制得本发明导电碳浆。
CN201310359165.3A 2013-08-13 2013-08-13 一种导电碳浆及其制备方法 Pending CN103559941A (zh)