CN1281389C - 乐器竹材改性方法 - Google Patents
乐器竹材改性方法 Download PDFInfo
- Publication number
- CN1281389C CN1281389C CN 200410014010 CN200410014010A CN1281389C CN 1281389 C CN1281389 C CN 1281389C CN 200410014010 CN200410014010 CN 200410014010 CN 200410014010 A CN200410014010 A CN 200410014010A CN 1281389 C CN1281389 C CN 1281389C
- Authority
- CN
- China
- Prior art keywords
- bamboo
- bamboo wood
- musical instrument
- musical instruments
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
天然竹材容易开裂的缺陷是竹制乐器生产和使用中最棘手的问题。本发明乐器竹材改性方法是:将要处理的乐器竹材放入烧沸的食用植物油中炸制,炸制过程中采用温火使油温保持在沸点以下30℃内,油炸4~6分钟然后捞出。该技术通过对竹材结构的分析,使用了一套简便易行的处理方法,解决了乐器竹材易干裂的缺陷,而且无须使用缠线等防裂手段,减少了制作工序和成本,改善了乐器音色。该项技术具有成本低,易操作,效益好等优点。
Description
技术领域
本发明涉及乐器竹材的一种改性方法,特别涉及一种能够有效防止竹材类乐器干裂改性处理方法。该方法适用于使用竹材类乐器的制作,尤其是笛子、箫、笙、巴鸟、琵琶等民族乐器制作。
背景技术
以天然竹子作为材料在民族乐器制作中应用广泛,如笛子、箫、笙、巴鸟、琵琶等。竹材质地坚硬,富于弹性,具有较好的振动系数,这些都是当前其他任何材料所无法替代的。以竹材制成的乐器往往音色浓郁,深受群众喜爱,在我国具有悠久的历史。但是,竹材却有致命的缺陷,即容易干裂。一件以竹材制成的上好乐器,往往还未卖出去就因干裂而报废,特别是笛子的膜孔处那怕是一个极其微小的裂纹也会撑破笛膜,往往使演奏半途而止。为了防止笛、箫等乐器干裂,实践中,人们常常在乐器制成后将管身一圈一圈地缠以丝线,涂以油漆来加以保护;或者乐器使用后,用细竹杆缠棉布蘸水塞入管身内保持湿润等。这些办法虽然对防止竹子干裂起到一定保护作用,但是仍未能解决根本问题,实际生活中竹材乐器的干裂现象时有发生。
竹材干裂的主要原因是竹材丧失水份达一定程度后竹材自身结构发生形变造成的。在放大镜下观察,竹子内外的竹黄3和竹青1结构比较缜密,而竹身的主体部分——竹肉2皆为纤维组织的蜂窝状的密密排列的无数导管组成,见附图1所示。新采的竹子导管内充满着浅黄色的液体,称为“竹沥”。经两、三年的风干,竹内水份(竹沥)大约丧失30%左右,制作乐器之前的烘烤取直,使水份大约丧失20%左右,制成乐器之后,仍有大约一半的水份存留在竹材之中。这一半的水份将是一个变量,它会随着气温和湿度等环境条件的不同而变化。天气潮湿,气温偏低,竹材吸收水份,导管膨胀;天气干燥,气温偏高,竹材丧失水份,导管干癟。经多次反复,一旦超过一定限度,竹材的结构便发生了较大的形变,开裂就成不可避免了。
竹材还有一个特性,就是经加热后竹纤维软化,在一定的温度,一定的时间下,竹身韧性有余而不开裂。
综上所述,解决竹材干裂的问题,必须尽可能剔除竹材中的水份。为保持竹材纤维导管不致干癟,以其他不易挥发的液体充斥其中保持竹材结构的稳定,是防止竹材开裂行之有效的办法。
有鉴于此,本发明提出一种能够有效防止竹材类乐器干裂的改性处理方法。
发明内容
为达到上述目的,本发明采用的技术方案是:一种乐器竹材改性方法,将要处理的乐器竹材放入烧沸的食用植物油中炸制,其创新在于:
(1)、所述食用植物油选择菜籽油、豆油、棉籽油、花生油、芝麻油中的一种或其混合油;
(2)、炸制过程中采用温火使油温保持在沸点以下30℃内,翻动油炸4~6分钟后捞出。
上述技术方案中的有关内容解释如下:
1、在油脂与水份两种液体替换的过程中尽量对竹材进行均匀加热,比如通过翻动竹体来实现,以保证这一过程的顺利完成而不致竹身在交换的过程发生开裂。
2、上述方案中,所述炸制过程选择在竹材乐器初坯制成后至上漆工序前进行。
3、上述方案中,为了获得更好的改性处理效果,油炸时间5分钟左右为佳。
本发明工作原理是:油炸过程中,竹材内的水份受热后变成蒸气离开了竹材,竹纤维导管成负压状态,油脂乘虚而入充分地进入竹纤维之中,整个过程很象炸油条一般,竹体不断冒出气泡。油脂不断渗入竹体。大约5分钟后,竹材内水份与油脂的交换已基本完成。这时,虽然气泡还在冒,但已减少,应即时从炸油里将竹材捞出。因为油炸时间过长或旺火油炸易使竹材过于焦化。
由于上述技术方案运用,本发明与现有技术相比具有下列优点:
1、经过处理的竹材内水份基本剔除,达95%以上,竹材中最大的活性成份水已经基本丧失,油脂充斥其中,油脂性能相对稳定不易挥发,使竹纤维导管永不干癟,保持了竹材结构的稳定,竹材经这样的处理已不再干裂。
2、由于油炸的高温处理,竹材产生了一定程度的炭化作用,竹质更加坚硬,振动系数提高,用小锤敲击竹身,声音清亮。
3、经过处理的竹制乐器不但永不开裂,还无须使用缠线等其他防裂手段,减少制作工序和成本,改善了音色,可谓一举两得。
附图说明
附图1为竹材截面示意图。
以上附图中:1、竹青(亦称:竹皮);2、竹肉;3、竹黄。
具体实施方式
下面结合实施例对本发明作进一步描述:
实施例:天然竹材容易开裂的缺陷是竹制乐器生产和使用中最棘手的问题。
本实施例以竹笛为对象,给出其制作过程中的改性处理方法如下:
1、改性处理时间选择在竹笛初坯制成后,而上漆工序前进行。
2、改性处理方法为:将要处理的竹笛放入烧沸的食用植物油中炸制,炸制过程中采用温火使油温保持在沸点以下5℃左右,翻动油炸5分钟后捞出。所述食用植物油选择菜籽油、豆油、棉籽油、花生油、芝麻油等中的一种或其混合油。
3、改性处理后,将竹笛经两三天的自然风干,然后采用浸泡式上漆法,阻断竹体内外与空气直接接触,以保持竹体结构的进一步稳定,减少气温、空气湿度和人的呼吸对竹笛音准的影响。
Claims (2)
1、一种乐器竹材改性方法,将要处理的乐器竹材放入烧沸的食用植物油中炸制,其特征在于:
(1)、所述食用植物油选择菜籽油、豆油、棉籽油、花生油、芝麻油中的一种或其混合油;
(2)、炸制过程中采用温火使油温保持在沸点以下30℃内,翻动油炸4~6分钟后捞出。
2、根据权利要求1所述的乐器竹材改性方法,其特征在于:所述炸制过程选择在竹材乐器初坯制成后至上漆工序前进行。