CN1193080C - 一种万能胶及其制备方法 - Google Patents
一种万能胶及其制备方法 Download PDFInfo
- Publication number
- CN1193080C CN1193080C CNB021167710A CN02116771A CN1193080C CN 1193080 C CN1193080 C CN 1193080C CN B021167710 A CNB021167710 A CN B021167710A CN 02116771 A CN02116771 A CN 02116771A CN 1193080 C CN1193080 C CN 1193080C
- Authority
- CN
- China
- Prior art keywords
- solvent oil
- benzene
- butadiene rubber
- mixture ratio
- styrene butadiene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种溶剂型无苯毒快干万能胶及其制备方法，它由56-65%的溶剂油、18-25%的热塑性丁苯橡胶、4-6%的石油树脂、4-6%的萜稀树脂、8-15%的松香树脂在搅拌罐里，其制备方法是以先后加入的顺序进行三次不同时间的搅拌，通过溶解、结合而成。即首先将配比量的溶剂油放入搅拌罐内，使其升温到5-25℃，再加入热塑性丁苯橡胶配比量的50%，搅拌1小时，再加入热塑性丁苯橡胶配比量的50%，搅拌2小时后再以次加入配比量的石油树脂、萜稀树脂、松香树脂在搅拌罐内搅拌5-8小时即为产成品。它是无苯毒、无卤烃类的粘合剂，符合国家要求标准，不怕水泡，耐酸、碱、粘接强度很高，干得快，节省施工工时，可做印刷附膜胶，可做各种鞋类用胶，配方合理，配比科学，生产工艺简单。
Description
技术领域
本发明涉及一种溶剂油型无苯毒快干万能胶及其制备方法，属无苯毒、无卤烃类粘合剂产品。
背景技术
目前，公知的万能胶、粘合剂等胶类产品，因生产原料配方和生产工艺所限，大都含有苯毒，人所共知的苯对人体极为有害，施工人员、生产人员直接受害，使用后，由于苯的挥发，使用者更深受其害，因此近几年来国家管理有关部门，三令五申禁用含苯的胶类粘合剂产品，但因多年的习惯势力长年生产产品积压，没有新产品更替，所以至今仍没达到国家要求，很不尽人意。
发明内容
为了克服上述不足，达到国家要求标准，使用户满意，本发明的目的是提供一种溶剂油型无苯毒快干万能胶及其制备方法，它是一种新型溶剂油型，不含苯毒，无卤烃类的粘合剂，快干万能胶，它不怕水泡、耐酸、耐碱，该产品不仅粘接强度高，而且绝对无苯类溶剂，它除能做装饰胶外，还可做印刷附膜，鞋类粘合剂用。
发明内容
本发明一种溶剂油型无苯毒快干万能胶，其配方、配比是：
溶剂油 56-65％
热塑性丁苯橡胶 18-25％
石油树脂 4-6％
萜稀树脂 4-6％
松香树脂 8-15％
本发明一种溶剂油型无苯毒快干万能胶的制备方法是：
按上述配比首先将溶剂油加入搅拌罐中，在溶剂油的温度达到5-25℃时，加入50％配比量的热塑性丁苯橡胶后，搅拌1小时，再加入50％配比量的热塑性丁苯橡胶后，再搅拌2个小时之后，依次加入配比量的石油树脂、萜稀树脂、松香树脂，然后再搅拌5-8小时，产成品即可出罐，然后进行质量检查，产品合格后进行灌装，入库。
本发明和现行产品相比的有益效果是：在原材料配方上采用无苯毒的溶剂油型和热塑性丁苯橡胶及树脂，配比、配方搭配巧妙、先进合理，结构严谨，无苯毒、无卤烃类，对人体无毒害物，不污染环境，符合国家要求产品标准，不怕水泡，耐酸、碱，粘接度高，干得快，节省施工时间、用途广泛，可做印刷附膜，可做鞋类生产用胶。
附图说明
图1、本发明生产工艺流程图
具体实施方式
本发明一种溶剂油型无苯毒快干万能胶，其配方、配比是：
溶剂油 252kg
热塑性丁苯橡胶 84kg
石油树脂 21kg
萜稀树脂 21kg
松香树脂 42kg
本发明一种溶剂油型无苯毒快干万能胶的制备方法是：请参阅图1所示，
首先将252kg溶剂油放入搅拌罐内，使其逐步升温到5-25℃后，再加入50％的热塑性丁苯橡胶42kg，开动搅拌罐进行搅拌，达一小时后再加入50％热塑性丁苯橡胶42kg，开动搅拌罐，搅拌两小时后，加入石油树脂21kg，萜稀树脂21kg，松香树脂42kg，进行充分搅拌5-8小时，这样使该产品得到充分溶解和充分结合而制造出产成品，开始出罐，进行质量检测和检查，产品合格后，进行灌装、入库。
Claims (2)
1、一种万能胶，其特征是：由以下各组分重量百分比组成，溶剂油56-65％，热塑性丁苯橡胶18-25％、石油树脂4-6％、松香树脂8-15％、萜稀树脂4-6％。
2、一种权利要求1所述的万能胶的制备方法，其特征是：按下述工艺流程进行生产制备，首先将配比量的溶剂油放入搅拌罐内，使其升温到5-25℃，再加入热塑性丁苯橡胶配比量的50％，搅拌1小时，再加入热塑性丁苯橡胶配比量的50％，搅拌2小时后再以次加入配比量的石油树脂、萜稀树脂、松香树脂在搅拌罐内搅拌5-8小时即为产成品。