CN101974260B - 一种零甲醛胶合板用腻子 - Google Patents
一种零甲醛胶合板用腻子 Download PDFInfo
- Publication number
- CN101974260B CN101974260B CN2010105156821A CN201010515682A CN101974260B CN 101974260 B CN101974260 B CN 101974260B CN 2010105156821 A CN2010105156821 A CN 2010105156821A CN 201010515682 A CN201010515682 A CN 201010515682A CN 101974260 B CN101974260 B CN 101974260B
- Authority
- CN
- China
- Prior art keywords
- putty
- formaldehyde
- plywood
- thin wood
- zero
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种零甲醛胶合板用腻子，包括白乳胶、改性聚醋酸乙烯酯、异氰酸酯和细木粉。本发明的零甲醛胶合板用腻子可以用于胶合板加工工序的单板修补阶段，用于填补单板表面脱落节及破裂。本发明的零甲醛胶合板用腻子无甲醛，环保；防水性好；成本低廉，最适合用于生产无甲醛的胶合板。
Description
技术领域
本发明涉及一种胶合板生产过程中的材料，更具体地，本发明涉及一种零甲醛胶合板用腻子。
背景技术
胶合板在上漆之前，需要经过毛料加工、打磨、上腻子等步骤；传统的胶合板用腻子含有甲醛，不环保，而且防水性能差。
发明内容
为了克服上述缺陷，本发明提供了一种零甲醛胶合板用腻子，其包括以下组分：
(a)白乳胶100重量份；
(b)改性聚醋酸乙烯酯10-50重量份；
(c)异氰酸酯0.5-2重量份；
(d)细木粉(40目以上)18重量份。
作为本发明的一个优选技术方案，各组分的含量为：
(a)白乳胶100重量份；
(b)改性聚醋酸乙烯酯20重量份；
(c)异氰酸酯1重量份；
(d)细木粉(40目以上)18重量份。
本发明所用的白乳胶是一种水溶性胶粘剂，化学名称聚醋酸乙烯胶粘剂，是由醋酸与乙烯合成醋酸乙烯，添加钛白粉(低档的就加轻钙，滑石粉，等粉料).再经乳液聚合而成的乳白色稠厚液体。白乳胶可常温固化、固化较快、粘接强度较高，粘接层具有较好的韧性和耐久性且不易老化。
本发明所用的改性聚醋酸乙烯酯只要不含甲醛，并无特别的限定。例如可以是申请号为01129873.1中公开的改性的聚醋酸乙烯酯乳液，也可以是有机硅改性聚醋酸乙烯酯等等。
本发明所用的异氰酸酯是异氰酸的各种酯的总称，以-NCO基团的数量分类，包括单异氰酸酯、二异氰酸酯和多异氰酸酯等。单异氰酸酯可以是烷基异氰酸酯例如甲基异氰酸酯、正丁基异氰酸酯等，任选取代的芳香基异氰酸酯例如苯基异氰酸酯、苄基异氰酸酯、氯代苯基异氰酸酯等；二异氰酸酯可以是甲苯二异氰酸酯(TDI)、二苯基甲烷二异氰酸酯(MDI)、环己烷二亚甲基二异氰酸酯等；多异氰酸酯可以是4，4’，4”-三苯甲烷三异氰酸酯、聚异氰酸酯等。
本发明的产品是将以上原料按比例混合均匀制得；细木粉添加的量以搅拌粘稠为宜，使混合腻子可以缓慢流动即可。本发明所用的细木粉是用木材打成的细粉末，可以采用家具厂、密度板厂、多层板厂木材加工剩余的边角废料或者由废料打车的细粉末。细木粉采用40目以上，可以是40目至200目，优选40目至120目。
本发明的零甲醛胶合板用腻子的制备方法是本领域常用的方法，例如可以将上述原料按比例混合均匀即可。
本发明的零甲醛胶合板用腻子可以用于胶合板加工工序的单板修补阶段，用于填补单板表面脱落节及破裂。本发明的零甲醛胶合板用腻子具有以下优点：无甲醛，环保；防水性好；成本低廉，最适合用于生产无甲醛的胶合板。
具体实施方式
以下将结合实施例对本发明的零甲醛胶合板用腻子作详细阐述，但所列的实施例并不用于限定本发明的保护范围。
实施例1
称取原料白乳胶100重量份；有机硅改性聚醋酸乙烯酯10重量份；异氰酸酯0.5重量份；细木粉(40目)18重量份。将上述原料混合均匀，制得零甲醛胶合板用腻子。
实施例2
称取原料白乳胶100重量份；有机硅改性聚醋酸乙烯酯50重量份；异氰酸酯2重量份；细木粉(80目)18重量份。将上述原料混合均匀，制得零甲醛胶合板用腻子。
实施例3
称取原料白乳胶100重量份；有机硅改性聚醋酸乙烯酯20重量份；异氰酸酯1重量份；细木粉(120目)18重量份。将上述原料混合均匀，制得零甲醛胶合板用腻子。
应用例1
按照本领域常用的方法来制备胶合板，所不同的是采用实施例1的零甲醛胶合板用腻子来进行修补。将修补后的胶合板用沸水煮4小时，无腻子脱落现象。
应用例2
按照本领域常用的方法来制备胶合板，所不同的是采用实施例2的零甲醛胶合板用腻子来进行修补。将修补后的胶合板用沸水煮4小时，无腻子脱落现象。
应用例3
按照本领域常用的方法来制备胶合板，所不同的是采用实施例3的零甲醛胶合板用腻子来进行修补。将修补后的胶合板用沸水煮4小时，无腻子脱落现象。
Claims (6)
1.一种零甲醛胶合板用腻子，其包括以下组分：
(a)白乳胶100重量份；
(b)有机硅改性聚醋酸乙烯酯10-50重量份；
(c)异氰酸酯0.5-2重量份；
(d)细木粉18重量份；
其中所述的细木粉为40目以上的细木粉。
2.根据权利要求1所述的零甲醛胶合板用腻子，其中各组分的含量为：
(a)白乳胶100重量份；
(b)有机硅改性聚醋酸乙烯酯20重量份；
(c)异氰酸酯1重量份；
(d)细木粉18重量份；
其中所述的细木粉为40目以上的细木粉。
3.根据权利要求1或2所述的零甲醛胶合板用腻子，其中所述的异氰酸酯为二异氰酸酯或多异氰酸酯。
4.根据权利要求3所述的零甲醛胶合板用腻子，其中所述的细木粉为40-200目的细木粉。
5.根据权利要求4所述的零甲醛胶合板用腻子，其中所述的细木粉为40-120目的细木粉。
6.权利要求1-5任一项所述的零甲醛胶合板用腻子用于胶合板加工工序的单板及成品修补的用途。