CN101319130B - 一种瓶盖用胶粘剂 - Google Patents
一种瓶盖用胶粘剂 Download PDFInfo
- Publication number
- CN101319130B CN101319130B CN2008101322473A CN200810132247A CN101319130B CN 101319130 B CN101319130 B CN 101319130B CN 2008101322473 A CN2008101322473 A CN 2008101322473A CN 200810132247 A CN200810132247 A CN 200810132247A CN 101319130 B CN101319130 B CN 101319130B
- Authority
- CN
- China
- Prior art keywords
- glue
- adhesive
- bottle cap
- calcium carbonate
- gluewater
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种瓶盖用胶粘剂，特别是一种用于制造酒瓶盖的胶粘剂，属于工程塑料应用领域。该胶粘剂的制作配方是：按重量百分比：717胶水50％-78％、轻质碳酸钙20％-48％、固化剂2％-5％。所述的717胶水是单组分无溶剂潮气固化型聚氨酯胶粘剂；所述的轻质碳酸钙的细度为400-800目；所述的固化剂为芳香族异氰酸酯预聚物。与单纯使用717胶水粘接瓶盖相比，优点是大大降低了胶水的固化时间，缩短了瓶盖的生产周期，降低了生产成本。
Description
技术领域
本发明涉及一种瓶盖用胶粘剂，特别是一种用于制造酒瓶盖的胶粘剂，属于工程塑料应用领域。
背景技术
以前，本行业中制造酒瓶盖，一直使用717胶水。这种717胶水是一种单组分、无溶剂、潮气固化型聚氨酯胶粘剂，固化时间长，在室温下固化一般需要24-48小时左右。因此，进入下道工序的等待时间较长，严重影响生产。所以，为了提高生产效率，在不影响产品质量的前提下，解决固化时间长的问题，就成了本行业的攻关课题。
发明内容
本发明的目的是提供一种瓶盖用胶粘剂，可减少现用胶水固化时间；同时降低材料成本，提高生产效率。
本发明的一种瓶盖用胶粘剂的具体方案是：一种瓶盖用胶粘剂，其特征在于，该胶粘剂的制作配方是：按重量百分比，717胶水50％-78％、轻质碳酸钙20％-48％、固化剂2％-5％。
所述的717胶水是单组分、无溶剂潮气固化型聚氨酯胶粘剂；所述的轻质碳酸钙的细度为400-800目；所述的固化剂为芳香族异氰酸酯预聚物。
采用了此配方，与以前单纯使用717胶水粘接瓶盖相比，优点是：
1.加入固化剂，大大降低了胶水的固化时间，瓶盖的生产周期缩短。
2.加入轻质碳酸钙，不影响产品质量，降低了成本，每公斤降低18元。
附图说明
图1是本发明一种瓶盖用胶粘剂的工艺流程图.
具体实施方式
以下结合实施例，对本发明进行详细描述。图1是本发明一种瓶盖用胶粘剂的工艺流程图。
制作本发明的瓶盖用胶粘剂的配方是：按重量百分比，其中，717胶水50％-78％、轻质碳酸钙20％-48％、固化剂2％-5％。
上述的717胶水是用上海精细文化用品有限公司生产的单组分无溶剂潮气固化型聚氨酯胶粘剂。
上述的轻质碳酸钙的细度为400-800目；
上述的固化剂为芳香族异氰酸酯预聚物，用来与717胶中的NCO基团发生交联反应。
按上述比例选用的一个实施例：717胶水原料为50KG、轻质碳酸钙47KG、固化剂3KG。其制作方法是：
先将上述配料，717胶水原料、轻质碳酸钙、放入容器中搅拌；搅拌均匀后，再加入固化剂继续搅拌，得成品；盛入容器，5小时内用完。参见附图1。
本发明使用的原料为市场所买，设备是通用设备。本领域技术人员可以使用和操作。
用本发明制成的胶粘剂，用来粘接塑料酒瓶盖，与以前单纯使用717胶水粘接瓶盖相比，现在的配方优点有二：
1.固化剂的加入，大大降低了胶水的固化时间，瓶盖的生产周期可缩短8-10小时。
2.轻质碳酸钙的加入，降低了成本，每公斤胶水成本降低18元。
本实施例仅是本发明构思的技术方案之一，凡与本发明构思相同的各种技术方案，都在本发明的权利要求保护范围之内。
Claims (1)
1.一种瓶盖用胶粘剂，其特征在于，该胶粘剂的制作配方是：按重量百分比，717胶水50％-78％、轻质碳酸钙20％-48％、固化剂2％-5％，所述的717胶水是单组分无溶剂潮气固化型聚氨酯胶粘剂；所述的轻质碳酸钙的细度为400-800目；所述的固化剂为芳香族异氰酸酯预聚物。