CN116695307A - 一种耐磨抗皱且透气的真丝面料、校服及制作工艺 - Google Patents

一种耐磨抗皱且透气的真丝面料、校服及制作工艺 Download PDF

Info

Publication number
CN116695307A
CN116695307A CN202310660690.2A CN202310660690A CN116695307A CN 116695307 A CN116695307 A CN 116695307A CN 202310660690 A CN202310660690 A CN 202310660690A CN 116695307 A CN116695307 A CN 116695307A
Authority
CN
China
Prior art keywords
silk
resistant
wear
crease
yarn
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202310660690.2A
Other languages
English (en)
Inventor
徐英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Chint Enterprise Development Co ltd
Original Assignee
Suzhou Chint Enterprise Development Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Chint Enterprise Development Co ltd filed Critical Suzhou Chint Enterprise Development Co ltd
Priority to CN202310660690.2A priority Critical patent/CN116695307A/zh
Publication of CN116695307A publication Critical patent/CN116695307A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐磨抗皱且透气的真丝面料、校服及制作工艺，所述真丝面料包括：平纹交织的经纱和纬纱；经纱和纬纱，均由：真丝抗菌复合纱线和弹性抗皱纱线编织而成；真丝抗菌复合纱线，包括：真丝纤维、亚麻纤维和棉纤维；弹性抗皱纱线，包括：棉纤维、氨纶丝和莫代尔纤维；本发明能够织造出兼顾耐磨、抗皱、防汗透气、亲肤的特性，并具有一定防病毒和防细菌功能的真丝面料，基于此面料制作学生的夏季校服，能够提高校服的穿着舒适性和耐用性，减少病毒传播，提高校服的穿着寿命。

Description

一种耐磨抗皱且透气的真丝面料、校服及制作工艺
技术领域
本发明涉及纺织技术领域，特别是涉及一种耐磨抗皱且透气的真丝面料、校服及制作工艺。
背景技术
在夏季校服中，T恤、短袖为学生经常穿着的服装；但是，由于夏天气候炎热，学生在运动过后易出汗，夏季校服的换洗频率较高，同时伴随校服与外界摩擦和剐蹭等，这使夏季校服成为了较易损坏的校服服饰。
目前的夏季校服中，大多采用棉和聚酯纤维混纺的材质，以保证一定的舒适性和透气性；虽然此面料的制作成本较低，但是此面料的功能性较为单一，且随着学生的户外活动增多，对于校服的耐用性、耐磨性、耐皱性以及透气性的要求越来越高，但目前夏季校服的面料并不能良好兼顾以上特性，长时间的穿着下易发生破损和褶皱。
另外，夏季属于流感高发季节，棉和聚酯纤维的混纺面料制成的校服也并不具有防病毒的功能。
发明内容
本发明的目的在于，针对现有技术中的上述问题，提供一种耐磨抗皱且透气的真丝面料、校服及制作工艺，进而解决现有技术中校服面料无法良好的兼顾耐用性、耐磨性、耐皱性以及透气性，且不具备防病毒功能的问题。
为解决上述技术问题，本发明的具体技术方案如下：
一方面，本发明提供一种耐磨抗皱且透气的真丝面料，包括：
平纹交织的经纱和纬纱；
所述经纱和纬纱，均由：真丝抗菌复合纱线和弹性抗皱纱线编织而成；
所述真丝抗菌复合纱线，包括：真丝纤维、亚麻纤维和棉纤维；
所述弹性抗皱纱线，包括：棉纤维、氨纶丝和莫代尔纤维。
作为一种改进的方案，所述经纱中，所述真丝抗菌复合纱线所占重量百分比为：61%~66%；
所述经纱中，所述弹性抗皱纱线所占重量百分比为：34%~39%；
所述纬纱中，所述真丝抗菌复合纱线所占重量百分比为：60%~61%
所述纬纱中，所述弹性抗皱纱线所占重量百分比为：39%~40%。
作为一种改进的方案，所述真丝抗菌复合纱线中，所述真丝纤维、所述亚麻纤维和所述棉纤维的重量比为：6：2：2；
所述弹性抗皱纱线中，所述棉纤维、所述氨纶丝和所述莫代尔纤维的重量比为：3：5：3；
所述真丝纤维采用22D的桑蚕丝制备。
另一方面，本发明还提供一种耐磨抗皱且透气的真丝面料的制作工艺，用于生产本发明所述的一种耐磨抗皱且透气的真丝面料，所述制作工艺包括：
对桑蚕丝依次进行杂质预处理和抗菌预处理，得到真丝纤维；
将真丝纤维、亚麻纤维和棉纤维交织为真丝抗菌复合纱线；将棉纤维、氨纶丝和莫代尔纤维交织为弹性抗皱纱线；将所述真丝抗菌复合纱线和所述弹性抗皱纱线按比例织造经纱和纬纱；对所述经纱和纬纱进行平纹交织，得到初始面料；
对所述初始面料进行抗菌强化处理，得到成品真丝面料。
作为一种改进的方案，所述杂质预处理，包括：
对所述桑蚕丝进行浸泡清洗；采用丝胶固着剂对浸泡清洗后的桑蚕丝进行绞丝处理；采用脱胶剂对绞丝处理后的桑蚕丝进行脱胶处理；对脱胶后的桑蚕丝进行清洗；对清洗后的桑蚕丝进行烘干；对烘干后的桑蚕丝进行并丝、捻丝或定形，得到待抗菌处理真丝原料；
所述抗菌预处理，包括：
采用抗菌处理液对每根所述待抗菌处理真丝原料进行浸渍处理；
浸渍处理时，向所述抗菌处理液中加入柔软剂；
对浸渍处理后的所述待抗菌处理真丝原料进行烘干处理，得到所述真丝纤维。
作为一种改进的方案，所述抗菌强化处理，包括：
制备羧甲基壳聚糖，并采用所述羧甲基壳聚糖配制羧甲基壳聚糖溶液；
采用所述羧甲基壳聚糖溶液对所述初始面料进行浸泡处理，得到羧甲基壳聚糖改性真丝织物；
将所述羧甲基壳聚糖改性真丝织物放入所述含银离子溶液中，在室温下振荡20min，得到银离子真丝织物；
将所述银离子真丝织物放在所述还原剂溶液中，在室温下振荡15min，得到纳米银真丝织物；
将所述纳米银真丝织物取出水洗，并在70℃下烘干35min，得到所述成品真丝面料。
作为一种改进的方案，所述丝胶固着剂，包括：戊二醛，或稀土金属固着剂；
所述脱胶剂，包括：采用碱性精练剂配制的碱性溶液；
所述抗菌处理液，包括：含活性基团的有机抗菌剂水溶液，或水溶性有机抗菌剂与粘合剂的混合液；
所述含银离子溶液，包括：在避光条件下，采用蒸馏水配置的浓度为400ppm～450ppm的AgNO3溶液；
所述还原剂溶液，包括：采用蒸馏水溶解硼氢化钠所配置的浓度为800ppm～850ppm的溶液。
另一方面，本发明还提供一种耐磨抗皱且透气的校服，采用本发明所述的一种耐磨抗皱且透气的真丝面料制成，所述校服包括：运动T恤和运动下装。
作为一种改进的方案，所述运动下装，包括：运动短裤和运动短裙；
所述运动短裤的侧缝处缝制有荧光嵌绳；
所述运动短裙为百褶裙。
本发明技术方案的有益效果是：
本发明所述的耐磨抗皱且透气的真丝面料，可以基于真丝原料及特殊的处理工艺，实现兼顾耐磨、抗皱、防汗透气、亲肤的特性，并具有一定的防病毒和防细菌功能。
本发明所述的耐磨抗皱且透气的真丝面料，在保证以上优良特性下，还具有一定的天然性，能够作为多种夏季服饰的原材料。
本发明所述的制作工艺，可以实现制作出兼顾耐磨、抗皱、防汗透气、亲肤的特性，并具有一定的防病毒和防细菌功能的真丝面料，进而以适用于多种夏季服饰的制作。
本发明所述的校服，基于本发明所述的耐磨抗皱且透气的真丝面料制成，能够兼顾耐磨、抗皱、防汗透气、亲肤的特性，并具有一定的防病毒和防细菌功能，能够提高学生在夏季的校服穿着舒适性，以及安全性，减小病毒传播的同时，提高夏季校服的耐用性，降低因校服损坏而反复购买校服的频率，节省校服维护成本。
附图说明
为了更清楚地说明本发明具体实施方式或现有技术中的技术方案，下面将对具体实施方式或现有技术描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图是本发明的一些实施方式，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他的附图。
图1是本发明实施例2所述制作工艺的流程示意图；
图2是本发明实施例3所述校服中所述运动T恤的正面结构示意图；
图3是本发明实施例3所述校服中所述运动T恤的背面结构示意图；
图4是本发明实施例3所述校服中所述运动短裤的结构示意图；
图5是本发明实施例3所述校服中所述运动短裙的结构示意图；
附图中的标记说明如下：
1、荧光嵌绳；2、龟背网眼面料结构；3、领座嵌布。
具体实施方式
下面结合附图对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
在本发明的描述中，需要说明的是，本发明所描述的实施例是本发明一部分实施例，而不是全部的实施例；基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本文的说明书和权利要求书及上述附图中的术语“第一”、“第二”等是用于区别类似的对象，而不必用于描述特定的顺序或先后次序。应该理解这样使用的数据在适当情况下可以互换，以便这里描述的本文的实施例能够以除了在这里图示或描述的那些以外的顺序实施。此外，术语“包括”和“具有”以及他们的任何变形，意图在于覆盖不排他的包含，例如，包含了一系列步骤或单元的过程、方法、装置、产品或设备不必限于清楚地列出的那些步骤或单元，而是可包括没有清楚地列出的或对于这些过程、方法、产品或设备固有的其它步骤或单元。
实施例1
本实施例提供一种耐磨抗皱且透气的真丝面料，包括：平纹交织的经纱和纬纱；所述经纱和纬纱，均由：真丝抗菌复合纱线和弹性抗皱纱线编织而成；所述真丝抗菌复合纱线，包括：真丝纤维、亚麻纤维和棉纤维；所述弹性抗皱纱线，包括：棉纤维、氨纶丝和莫代尔纤维；在本实施方式中，真丝纤维和亚麻纤维具有良好的透气性和亲肤性，通过平纹经纬交织的方式，提高了面料的耐磨性，且氨纶丝和莫代尔纤维能够提高面料的弹性，最终使真丝面料兼顾耐磨性、抗皱性、弹性和透气性。
作为本发明的一种实施方式，所述经纱中，所述真丝抗菌复合纱线所占重量百分比为：61%~66%；
所述经纱中，所述弹性抗皱纱线所占重量百分比为：34%~39%；
所述纬纱中，所述真丝抗菌复合纱线所占重量百分比为：60%~61%
所述纬纱中，所述弹性抗皱纱线所占重量百分比为：39%~40%。
作为本发明的一种实施方式，所述真丝抗菌复合纱线中，所述真丝纤维、所述亚麻纤维和所述棉纤维的重量比为：6：2：2；所述弹性抗皱纱线中，所述棉纤维、所述氨纶丝和所述莫代尔纤维的重量比为：3：5：3；所述真丝纤维采用22D的桑蚕丝制备。在本实施方式中，根据以上重量比可以得知，本发明的面料以桑蚕丝为主，且真丝材料的占比达到60%及以上，基于天然的桑蚕丝原料，使面料具有较高的天然性。
实施例2
本实施例提供一种耐磨抗皱且透气的真丝面料的制作工艺，用于生产实施例1中的一种耐磨抗皱且透气的真丝面料，如图1所示，所述制作工艺包括以下步骤：
S100、对桑蚕丝依次进行杂质预处理和抗菌预处理，得到真丝纤维；
S200、将真丝纤维、亚麻纤维和棉纤维交织为真丝抗菌复合纱线；将棉纤维、氨纶丝和莫代尔纤维交织为弹性抗皱纱线；将所述真丝抗菌复合纱线和所述弹性抗皱纱线按比例织造经纱和纬纱；对所述经纱和纬纱进行平纹交织，得到初始面料；
S300、对所述初始面料进行抗菌强化处理，得到成品真丝面料。
作为本发明的一种实施方式，步骤S100中，所述杂质预处理，属于桑蚕丝原料预处理的步骤，具体包括：首先采用温水对所述桑蚕丝进行浸泡清洗，进而清除天然桑蚕丝上的油脂和杂质；在清洗后，采用丝胶固着剂处理绞丝，进行丝胶固着；其中，丝胶固着剂采用戊二醛或稀土金属固着剂；采用脱胶剂对绞丝处理后的桑蚕丝（即丝胶固着后的绞丝）进行脱胶处理；其中，脱胶剂采用碱性精练剂配制的pH值为9~11的碱性溶液，脱胶处理即将绞丝处理后的桑蚕丝经清洗后置入前述的碱性溶液中浸泡脱胶，且处理的温度为85℃，并使练减率控制在5%以内；脱胶后，对脱胶的桑蚕丝再次进行清洗，并进行烘干，烘干后即可络筒；络筒的桑蚕丝即可根据不同的应用需求进行并丝、捻丝或定形，最终得到待抗菌处理的真丝原料；
作为本发明的一种实施方式，步骤S100中，所述抗菌预处理，主要为真丝原料附加抗菌以及抗病毒的功能，具体包括如下步骤：
采用抗菌处理液对每根所述待抗菌处理真丝原料进行浸渍处理；在本实施方式中，抗菌处理液为含活性基团的有机抗菌剂水溶液，或水溶性有机抗菌剂添加适量粘合剂的混合液，这两种液体能够与真丝纤维上的氨基形成共价键合；同时，浸渍处理时，向所述抗菌处理液中加入柔软剂，进而还可以改善真丝纱线的柔软度；基于此，真丝沙县吸收抗菌处理液中的抗菌性能，以附带有一定的抗菌效果；最终，对浸渍处理后的所述待抗菌处理真丝原料进行烘干处理，得到所述真丝纤维；真丝纤维同样可以络成筒子以便于后续使用；
作为本发明的一种实施方式，步骤S200中，所述抗菌强化处理，属于对初始的真丝面料进行抗菌强化的处理，以再次提升面料的抗菌性能，具体包括：制备羧甲基壳聚糖，并采用所述羧甲基壳聚糖配制羧甲基壳聚糖溶液；采用所述羧甲基壳聚糖溶液对所述初始面料进行浸泡处理，得到羧甲基壳聚糖改性真丝织物；将所述羧甲基壳聚糖改性真丝织物放入所述含银离子溶液中，在室温下振荡20min，得到银离子真丝织物； 在本实施方式中，所述含银离子溶液为在避光条件下，采用蒸馏水配置的浓度为400ppm～450ppm的AgNO3溶液；之后将所述银离子真丝织物浸泡在所述还原剂溶液中，在室温下振荡15min，得到纳米银真丝织物；最终将所述纳米银真丝织物取出水洗，并在70℃下烘干35min，得到所述成品真丝面料；具体的，所述还原剂溶液为采用蒸馏水溶解硼氢化钠所配置的浓度为800ppm～850ppm的还原剂溶液。
经过以上的制作工艺，能够使最终制得的真丝面料具有较佳的天然性、抗皱性、耐磨性、透气性、弹性、防汗以及防细菌病毒的特性。
实施例3
本实施例提供一种耐磨抗皱且透气的校服，采用实施例1中的一种耐磨抗皱且透气的真丝面料制成，如图2~图5所示，所述校服包括：运动T恤和运动下装。
作为一种改进的方案，所述运动下装，包括：运动短裤和运动短裙；所述运动短裤的侧缝处缝制有荧光嵌绳1；所述运动短裙为百褶裙；对于运动T恤，在脖颈处还缝制了龟背网眼面料结构2，提升了透气性，增强了衣物吸湿排汗的效果；对于运动T恤的领口内侧，缝制了领座嵌布3，以提升衣物耐洗性，同时提升领口处对于肌肤的保护性。
区别于现有技术，采用本申请一种耐磨抗皱且透气的真丝面料、校服及制作工艺，可以织造出兼顾耐磨、抗皱、防汗透气、亲肤的特性，并具有一定防病毒和防细菌功能的真丝面料，基于此面料制作学生的夏季校服，能够提高校服的穿着舒适性和耐用性，减少病毒传播，提高校服的穿着寿命。
应理解，在本文的各种实施例中，上述各过程的序号的大小并不意味着执行顺序的先后，各过程的执行顺序应以其功能和内在逻辑确定，而不应对本文实施例的实施过程构成任何限定。
还应理解，在本文实施例中，术语“和/或”仅仅是一种描述关联对象的关联关系，表示可以存在三种关系。例如，A和/或B，可以表示：单独存在A，同时存在A和B，单独存在B这三种情况。另外，本文中字符“/”，一般表示前后关联对象是一种“或”的关系。
本领域普通技术人员可以意识到，结合本文中所公开的实施例描述的各示例的单元及算法步骤，能够以电子硬件、计算机软件或者二者的结合来实现，为了清楚地说明硬件和软件的可互换性，在上述说明中已经按照功能一般性地描述了各示例的组成及步骤。这些功能究竟以硬件还是软件方式来执行，取决于技术方案的特定应用和设计约束条件。专业技术人员可以对每个特定的应用来使用不同方法来实现所描述的功能，但是这种实现不应认为超出本文的范围。
所属领域的技术人员可以清楚地了解到，为了描述的方便和简洁，上述描述的系统、装置和单元的具体工作过程，可以参考前述方法实施例中的对应过程，在此不再赘述。
在本文所提供的几个实施例中，应该理解到，所揭露的系统、装置和方法，可以通过其它的方式实现。例如，以上所描述的装置实施例仅仅是示意性的，例如，所述单元的划分，仅仅为一种逻辑功能划分，实际实现时可以有另外的划分方式，例如多个单元或组件可以结合或者可以集成到另一个系统，或一些特征可以忽略，或不执行。另外，所显示或讨论的相互之间的耦合或直接耦合或通信连接可以是通过一些接口、装置或单元的间接耦合或通信连接，也可以是电的，机械的或其它的形式连接。
所述作为分离部件说明的单元可以是或者也可以不是物理上分开的，作为单元显示的部件可以是或者也可以不是物理单元，即可以位于一个地方，或者也可以分布到多个网络单元上。可以根据实际的需要选择其中的部分或者全部单元来实现本文实施例方案的目的。
另外，在本文各个实施例中的各功能单元可以集成在一个处理单元中，也可以是各个单元单独物理存在，也可以是两个或两个以上单元集成在一个单元中。上述集成的单元既可以采用硬件的形式实现，也可以采用软件功能单元的形式实现。
所述集成的单元如果以软件功能单元的形式实现并作为独立的产品销售或使用时，可以存储在一个计算机可读取存储介质中。基于这样的理解，本文的技术方案本质上或者说对现有技术做出贡献的部分，或者该技术方案的全部或部分可以以软件产品的形式体现出来，该计算机软件产品存储在一个存储介质中，包括若干指令用以使得一台计算机设备(可以是个人计算机，服务器，或者网络设备等)执行本文各个实施例所述方法的全部或部分步骤。而前述的存储介质包括：U盘、移动硬盘、只读存储器(ROM，Read-Only Memory)、随机存取存储器(RAM，Random Access Memory)、磁碟或者光盘等各种可以存储程序代码的介质。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书及附图内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (9)

1.一种耐磨抗皱且透气的真丝面料，其特征在于，包括：平纹交织的经纱和纬纱；
所述经纱和纬纱，均由：真丝抗菌复合纱线和弹性抗皱纱线编织而成；
所述真丝抗菌复合纱线，包括：真丝纤维、亚麻纤维和棉纤维；
所述弹性抗皱纱线，包括：棉纤维、氨纶丝和莫代尔纤维。
2.根据权利要求1所述的一种耐磨抗皱且透气的真丝面料，其特征在于：
所述经纱中，所述真丝抗菌复合纱线所占重量百分比为：61%~66%；
所述经纱中，所述弹性抗皱纱线所占重量百分比为：34%~39%；
所述纬纱中，所述真丝抗菌复合纱线所占重量百分比为：60%~61%
所述纬纱中，所述弹性抗皱纱线所占重量百分比为：39%~40%。
3.根据权利要求2所述的一种耐磨抗皱且透气的真丝面料，其特征在于：
所述真丝抗菌复合纱线中，所述真丝纤维、所述亚麻纤维和所述棉纤维的重量比为：6：2：2；
所述弹性抗皱纱线中，所述棉纤维、所述氨纶丝和所述莫代尔纤维的重量比为：3：5：3；
所述真丝纤维采用22D的桑蚕丝制备。
4.一种耐磨抗皱且透气的真丝面料的制作工艺，用于生产权利要求3中所述的一种耐磨抗皱且透气的真丝面料，其特征在于，所述制作工艺包括以下步骤：
对桑蚕丝依次进行杂质预处理和抗菌预处理，得到真丝纤维；
将真丝纤维、亚麻纤维和棉纤维交织为真丝抗菌复合纱线；将棉纤维、氨纶丝和莫代尔纤维交织为弹性抗皱纱线；将所述真丝抗菌复合纱线和所述弹性抗皱纱线按比例织造经纱和纬纱；对所述经纱和纬纱进行平纹交织，得到初始面料；
对所述初始面料进行抗菌强化处理，得到成品真丝面料。
5.根据权利要求4所述的一种耐磨抗皱且透气的真丝面料的制作工艺，其特征在于：
所述杂质预处理，包括：
对所述桑蚕丝进行浸泡清洗；采用丝胶固着剂对浸泡清洗后的桑蚕丝进行绞丝处理；采用脱胶剂对绞丝处理后的桑蚕丝进行脱胶处理；对脱胶后的桑蚕丝进行清洗；对清洗后的桑蚕丝进行烘干；对烘干后的桑蚕丝进行并丝、捻丝或定形，得到待抗菌处理真丝原料；
所述抗菌预处理，包括：
采用抗菌处理液对每根所述待抗菌处理真丝原料进行浸渍处理；浸渍处理时，向所述抗菌处理液中加入柔软剂；对浸渍处理后的所述待抗菌处理真丝原料进行烘干处理，得到所述真丝纤维。
6.根据权利要求5所述的一种耐磨抗皱且透气的真丝面料的制作工艺，其特征在于：
所述抗菌强化处理，包括：
制备羧甲基壳聚糖，并采用所述羧甲基壳聚糖配制羧甲基壳聚糖溶液；
采用所述羧甲基壳聚糖溶液对所述初始面料进行浸泡处理，得到羧甲基壳聚糖改性真丝织物；
将所述羧甲基壳聚糖改性真丝织物放入所述含银离子溶液中，在室温下振荡20min，得到银离子真丝织物；
将所述银离子真丝织物放在所述还原剂溶液中，在室温下振荡15min，得到纳米银真丝织物；
将所述纳米银真丝织物取出水洗，并在70℃下烘干35min，得到所述成品真丝面料。
7.根据权利要求5所述的一种耐磨抗皱且透气的真丝面料的制作工艺，其特征在于：
所述丝胶固着剂，包括：戊二醛，或稀土金属固着剂；
所述脱胶剂，包括：采用碱性精练剂配制的碱性溶液；
所述抗菌处理液，包括：含活性基团的有机抗菌剂水溶液，或水溶性有机抗菌剂与粘合剂的混合液；
所述含银离子溶液，包括：在避光条件下，采用蒸馏水配置的浓度为400ppm～450ppm的AgNO3溶液；
所述还原剂溶液，包括：采用蒸馏水溶解硼氢化钠所配置的浓度为800ppm～850ppm的溶液。
8.一种耐磨抗皱且透气的校服，采用权利要求3中所述的一种耐磨抗皱且透气的真丝面料制成，其特征在于，所述校服包括：运动T恤和运动下装。
9.根据权利要求8所述的一种耐磨抗皱且透气的校服，其特征在于：
所述运动下装，包括：运动短裤和运动短裙；
所述运动短裤的侧缝处缝制有荧光嵌绳；
所述运动短裙为百褶裙。
CN202310660690.2A 2023-06-06 2023-06-06 一种耐磨抗皱且透气的真丝面料、校服及制作工艺 Pending CN116695307A (zh)