CN113322673A - 具有抗菌和自清洁棉织物的制备方法 - Google Patents
具有抗菌和自清洁棉织物的制备方法 Download PDFInfo
- Publication number
- CN113322673A CN113322673A CN202110703470.4A CN202110703470A CN113322673A CN 113322673 A CN113322673 A CN 113322673A CN 202110703470 A CN202110703470 A CN 202110703470A CN 113322673 A CN113322673 A CN 113322673A
- Authority
- CN
- China
- Prior art keywords
- cotton fabric
- antibacterial
- self
- steps
- cleaning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本申请公开了一种具有抗菌和自清洁棉织物的制备方法，包括以下步骤：抗菌层的制备，首先将纳米银溶胶涂覆在竹纤维布料的上、下两面，继而再对涂覆有纳米银溶胶的竹纤维布料进行烘干操作，从而可将纳米银溶胶与竹纤维布料结合，得到抗菌层，继而再将抗菌层与棉织物进行热粘合连接；自清洁层的制备，通过仿生学改变棉织物的表面结构，使之形成微乳状突出表面的“荷叶结构”；同时在棉织物的表面附着二氧化钛、氧化锌等具有光催化能力的光催化剂，在紫外线的照射下能释放电子，与空气中的氧气发生反应，产生具有强氧化能力的氧自由基；本申请通过仿生学可改变布料表面结构，再经过光催化作用来增强自清洁能力，制造时也较为简单。
Description
技术领域
本申请涉及棉织物技术领域，具体是一种具有抗菌和自清洁棉织物的制备方法。
背景技术
棉织物是用棉纱织成的布，是各类棉纺织品的总称，它多用来制作时装、休闲装、内衣和衬衫，它的优点是轻松保暖，柔和贴身、吸湿性、透气性甚佳，它的缺点则是易缩、易皱，外观上不大挺括美观，在穿著时必须时常熨烫。
棉布的生产制造包括纺纱、织造和染整三项工艺过程，纺纱和织造是用机械方法把纺织纤维加工成纱线和织物的过程，染整则是用化学方法和一部分物理机械方法对纤维制品进行再加工过程，通过整理加工，可以提高纤维及其制品的服用性能并改善其外观。
传统的棉织物功能性较为单一，在长期使用时容易滋生细菌以及发霉，降低了棉织物的舒适性，同时目前的棉织物缺乏自清洁功能，易脏、不易清洗。因此，针对上述问题提出一种具有抗菌和自清洁棉织物的制备方法。
发明内容
一种具有抗菌和自清洁棉织物的制备方法，包括以下步骤：
S1.抗菌层的制备，首先将纳米银溶胶涂覆在竹纤维布料的上、下两面，继而再对涂覆有纳米银溶胶的竹纤维布料进行烘干操作，从而可将纳米银溶胶与竹纤维布料结合，得到抗菌层，继而再将抗菌层与棉织物进行热粘合连接；
S2.自清洁层的制备，通过仿生学改变棉织物的表面结构，使之形成微乳状突出表面的“荷叶结构”，从而赋予纺织品以优异的拒水阻油效果；同时在棉织物的表面附着二氧化钛、氧化锌等具有光催化能力的光催化剂，在紫外线的照射下能释放电子，与空气中的氧气发生反应，产生具有强氧化能力的氧自由基；
S3.获得功能棉织物，将上述得到的棉织物放置在洗涤设备内部进行普洗，其水温为40-60℃，加人适量的洗涤机，洗涤时长为15-20min，继而再将普洗后的棉织物进行烘干操作，以此来得到具有抗菌和自清洁功能的棉织物。
进一步地，上述步骤S1中所述纳米银溶胶可通过辊式涂布机均匀涂覆在竹纤维布料的表面，该辊式涂布机采用的是双滚涂布机，其涂覆次数为2-3次。
进一步地，上述步骤S1中所述纳米银溶胶可通过采用的是以NaBH4为还原剂、PVP为分散剂，还原不同浓度的硝酸银溶液，从而制得颗粒度较小且分散均匀的纳米银溶胶，且所述纳米银溶胶具有防静电、杀菌、除臭、抗菌等功效。
进一步地，上述步骤S1中所述竹纤维布料具有柔软悬垂、细腻光滑、飘逸动感、吸湿透气等优点，同时也具有导湿性、抑菌性、环保性、防过敏、防止静电等特性。
进一步地，上述步骤S1中所述抗菌层与所述棉织物采用的是668糊盒胶粘合连接，粘合温度为85-90℃，完成粘合后需立即降温。
进一步地，上述步骤S2中紫外线照射时间为24-26h，氧自由基能使沾附在棉织物上的有机污垢氧化降解，最终形成二氧化碳和水。
进一步地，上述步骤S2中采用超细纤维制成超高密度拒水透气的纺织品，或者用硅溶胶类材料及某些金属盐在纺织品表面通过自组装方式形成纳米级沉积物,使之具有微乳状的表面结构，得到具有超拒水性能或抗菌抑菌能力的纺织品，污垢不易沾附或易于水洗去除。
进一步地，通过棉织物表面改性，可使之同时兼具优异的拒水、拒油、易去污、抗静电等自清洁性能，是目前相对成熟、易于产业化的加工方法。
进一步地，上述步骤S3中所述洗涤设备采用的是XGP型号工业洗涤机，该工业洗涤机内胆径向尺寸大，增加洗涤物运转落差，配以合理的洗涤速度，机器洗净率比同类产品高25％。
进一步地，上述步骤S3中烘干设备采用的是ND4065型号隧道式烘干机，该隧道式烘干机采用热风循环方式，炉内温度均匀，升温快，输送方式一般低温采用钢网带。
通过本申请上述实施例，采用了竹纤维布料作为底层，竹纤维布料具有柔软悬垂、细腻光滑、飘逸动感、吸湿透气等优点，同时也具有导湿性、抑菌性、环保性、防过敏、防止静电等特性，在竹纤维布料表面涂覆有纳米银溶胶，其具有防静电、杀菌、除臭、抗菌等功效，且通过仿生学可改变布料表面结构，再经过光催化作用来增强自清洁能力。
附图说明
为了更清楚地说明本申请实施例或现有技术中的技术方案，下面将对实施例或现有技术描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本申请的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动性的前提下，还可以根据这些附图获得其它的附图。
图1为本申请一种实施例的方法流程图。
具体实施方式
为了使本技术领域的人员更好地理解本申请方案，下面将结合本申请实施例中的附图，对本申请实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本申请一部分的实施例，而不是全部的实施例。基于本申请中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都应当属于本申请保护的范围。
需要说明的是，本申请的说明书和权利要求书及上述附图中的术语“第一”、“第二”等是用于区别类似的对象，而不必用于描述特定的顺序或先后次序。应该理解这样使用的数据在适当情况下可以互换，以便这里描述的本申请的实施例。此外，术语“包括”和“具有”以及他们的任何变形，意图在于覆盖不排他的包含，例如，包含了一系列步骤或单元的过程、方法、系统、产品或设备不必限于清楚地列出的那些步骤或单元，而是可包括没有清楚地列出的或对于这些过程、方法、产品或设备固有的其它步骤或单元。
在本申请中，术语“上”、“下”、“左”、“右”、“前”、“后”、“顶”、“底”、“内”、“外”、“中”、“竖直”、“水平”、“横向”、“纵向”等指示的方位或位置关系为基于附图所示的方位或位置关系。这些术语主要是为了更好地描述本申请及其实施例，并非用于限定所指示的装置、元件或组成部分必须具有特定方位，或以特定方位进行构造和操作。
并且，上述部分术语除了可以用于表示方位或位置关系以外，还可能用于表示其他含义，例如术语“上”在某些情况下也可能用于表示某种依附关系或连接关系。对于本领域普通技术人员而言，可以根据具体情况理解这些术语在本申请中的具体含义。
此外，术语“安装”、“设置”、“设有”、“连接”、“相连”、“套接”应做广义理解。例如，可以是固定连接，可拆卸连接，或整体式构造；可以是机械连接，或电连接；可以是直接相连，或者是通过中间媒介间接相连，又或者是两个装置、元件或组成部分之间内部的连通。对于本领域普通技术人员而言，可以根据具体情况理解上述术语在本申请中的具体含义。
需要说明的是，在不冲突的情况下，本申请中的实施例及实施例中的特征可以相互组合。下面将参考附图并结合实施例来详细说明本申请。
实施例一：
一种具有抗菌和自清洁棉织物的制备方法，包括以下步骤：
S1.抗菌层的制备，首先将纳米银溶胶涂覆在竹纤维布料的上、下两面，继而再对涂覆有纳米银溶胶的竹纤维布料进行烘干操作，从而可将纳米银溶胶与竹纤维布料结合，得到抗菌层，继而再将抗菌层与棉织物进行热粘合连接；
S2.自清洁层的制备，通过仿生学改变棉织物的表面结构，使之形成微乳状突出表面的“荷叶结构”，从而赋予纺织品以优异的拒水阻油效果；同时在棉织物的表面附着二氧化钛、氧化锌等具有光催化能力的光催化剂，在紫外线的照射下能释放电子，与空气中的氧气发生反应，产生具有强氧化能力的氧自由基；
S3.获得功能棉织物，将上述得到的棉织物放置在洗涤设备内部进行普洗，其水温为40-60℃，加人适量的洗涤机，洗涤时长为15-20min，继而再将普洗后的棉织物进行烘干操作，以此来得到具有抗菌和自清洁功能的棉织物。
进一步地，上述步骤S1中所述纳米银溶胶可通过辊式涂布机均匀涂覆在竹纤维布料的表面，该辊式涂布机采用的是双滚涂布机，其涂覆次数为2-3次。
进一步地，上述步骤S1中所述纳米银溶胶可通过采用的是以NaBH4为还原剂、PVP为分散剂，还原不同浓度的硝酸银溶液，从而制得颗粒度较小且分散均匀的纳米银溶胶，且所述纳米银溶胶具有防静电、杀菌、除臭、抗菌等功效。
进一步地，上述步骤S1中所述竹纤维布料具有柔软悬垂、细腻光滑、飘逸动感、吸湿透气等优点，同时也具有导湿性、抑菌性、环保性、防过敏、防止静电等特性。
进一步地，上述步骤S1中所述抗菌层与所述棉织物采用的是668糊盒胶粘合连接，粘合温度为85-90℃，完成粘合后需立即降温。
进一步地，上述步骤S2中紫外线照射时间为24-26h，氧自由基能使沾附在棉织物上的有机污垢氧化降解，最终形成二氧化碳和水。
进一步地，上述步骤S2中采用超细纤维制成超高密度拒水透气的纺织品，或者用硅溶胶类材料及某些金属盐在纺织品表面通过自组装方式形成纳米级沉积物,使之具有微乳状的表面结构，得到具有超拒水性能或抗菌抑菌能力的纺织品，污垢不易沾附或易于水洗去除。
进一步地，通过棉织物表面改性，可使之同时兼具优异的拒水、拒油、易去污、抗静电等自清洁性能，是目前相对成熟、易于产业化的加工方法。
进一步地，上述步骤S3中所述洗涤设备采用的是XGP型号工业洗涤机，该工业洗涤机内胆径向尺寸大，增加洗涤物运转落差，配以合理的洗涤速度，机器洗净率比同类产品高25％。
进一步地，上述步骤S3中烘干设备采用的是ND4065型号隧道式烘干机，该隧道式烘干机采用热风循环方式，炉内温度均匀，升温快，输送方式一般低温采用钢网带。
实施例二：
一种具有抗菌和自清洁棉织物的制备方法，包括以下步骤：
S1.抗菌层的制备，首先将纳米银溶胶涂覆在竹纤维布料的上、下两面，继而再对涂覆有纳米银溶胶的竹纤维布料进行烘干操作，从而可将纳米银溶胶与竹纤维布料结合，得到抗菌层，继而再将抗菌层与棉织物进行热粘合连接；
S2.自清洁层的制备，通过仿生学改变棉织物的表面结构，使之形成微乳状突出表面的“荷叶结构”，从而赋予纺织品以优异的拒水阻油效果；同时在棉织物的表面附着二氧化钛、氧化锌等具有光催化能力的光催化剂，在紫外线的照射下能释放电子，与空气中的氧气发生反应，产生具有强氧化能力的氧自由基；
S3.获得功能棉织物，将上述得到的棉织物放置在洗涤设备内部进行普洗，其水温为40-60℃，加人适量的洗涤机，洗涤时长为15-20min，继而再将普洗后的棉织物进行烘干操作，以此来得到具有抗菌和自清洁功能的棉织物。
进一步地，上述步骤S1中所述纳米银溶胶可通过辊式涂布机均匀涂覆在竹纤维布料的表面，该辊式涂布机采用的是双滚涂布机，其涂覆次数为2-3次。
进一步地，上述步骤S1中所述纳米银溶胶可通过采用的是以NaBH4为还原剂、PVP为分散剂，还原不同浓度的硝酸银溶液，从而制得颗粒度较小且分散均匀的纳米银溶胶，且所述纳米银溶胶具有防静电、杀菌、除臭、抗菌等功效。
进一步地，上述步骤S1中所述竹纤维布料具有柔软悬垂、细腻光滑、飘逸动感、吸湿透气等优点，同时也具有导湿性、抑菌性、环保性、防过敏、防止静电等特性。
进一步地，上述步骤S1中所述抗菌层与所述棉织物采用的是668糊盒胶粘合连接，粘合温度为85-90℃，完成粘合后需立即降温。
进一步地，上述步骤S2中紫外线照射时间为24-26h，氧自由基能使沾附在棉织物上的有机污垢氧化降解，最终形成二氧化碳和水。
进一步地，上述步骤S2中采用超细纤维制成超高密度拒水透气的纺织品，或者用硅溶胶类材料及某些金属盐在纺织品表面通过自组装方式形成纳米级沉积物,使之具有微乳状的表面结构，得到具有超拒水性能或抗菌抑菌能力的纺织品，污垢不易沾附或易于水洗去除。
进一步地，通过棉织物表面改性，可使之同时兼具优异的拒水、拒油、易去污、抗静电等自清洁性能，是目前相对成熟、易于产业化的加工方法。
进一步地，上述步骤S3中所述洗涤设备采用的是XGP型号工业洗涤机，该工业洗涤机内胆径向尺寸大，增加洗涤物运转落差，配以合理的洗涤速度，机器洗净率比同类产品高25％。
进一步地，上述步骤S3中烘干设备采用的是ND4065型号隧道式烘干机，该隧道式烘干机采用热风循环方式，炉内温度均匀，升温快，输送方式一般低温采用钢网带。
本申请的有益之处在于：本申请采用了竹纤维布料作为底层，竹纤维布料具有柔软悬垂、细腻光滑、飘逸动感、吸湿透气等优点，同时也具有导湿性、抑菌性、环保性、防过敏、防止静电等特性，在竹纤维布料表面涂覆有纳米银溶胶，其具有防静电、杀菌、除臭、抗菌等功效，且通过仿生学可改变布料表面结构，再经过光催化作用来增强自清洁能力，制造时也较为简单。
以上所述仅为本申请的优选实施例而已，并不用于限制本申请，对于本领域的技术人员来说，本申请可以有各种更改和变化。凡在本申请的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本申请的保护范围之内。
Claims (10)
1.一种具有抗菌和自清洁棉织物的制备方法，其特征在于：包括以下步骤：
S1.抗菌层的制备，首先将纳米银溶胶涂覆在竹纤维布料的上、下两面，继而再对涂覆有纳米银溶胶的竹纤维布料进行烘干操作，从而可将纳米银溶胶与竹纤维布料结合，得到抗菌层，继而再将抗菌层与棉织物进行热粘合连接；
S2.自清洁层的制备，通过仿生学改变棉织物的表面结构，使之形成微乳状突出表面的“荷叶结构”，从而赋予纺织品以优异的拒水阻油效果；同时在棉织物的表面附着二氧化钛、氧化锌等具有光催化能力的光催化剂，在紫外线的照射下能释放电子，与空气中的氧气发生反应，产生具有强氧化能力的氧自由基；
S3.获得功能棉织物，将上述得到的棉织物放置在洗涤设备内部进行普洗，其水温为40-60℃，加人适量的洗涤机，洗涤时长为15-20min，继而再将普洗后的棉织物进行烘干操作，以此来得到具有抗菌和自清洁功能的棉织物。
2.根据权利要求1所述的一种具有抗菌和自清洁棉织物的制备方法，其特征在于：
上述步骤S1中所述纳米银溶胶可通过辊式涂布机均匀涂覆在竹纤维布料的表面，该辊式涂布机采用的是双滚涂布机，其涂覆次数为2-3次。
3.根据权利要求1所述的一种具有抗菌和自清洁棉织物的制备方法，其特征在于：
上述步骤S1中所述纳米银溶胶可通过采用的是以NaBH4为还原剂、PVP为分散剂，还原不同浓度的硝酸银溶液，从而制得颗粒度较小且分散均匀的纳米银溶胶，且所述纳米银溶胶具有防静电、杀菌、除臭、抗菌等功效。
4.根据权利要求1所述的一种具有抗菌和自清洁棉织物的制备方法，其特征在于：
上述步骤S1中所述竹纤维布料具有柔软悬垂、细腻光滑、飘逸动感、吸湿透气等优点，同时也具有导湿性、抑菌性、环保性、防过敏、防止静电等特性。
5.根据权利要求1所述的一种具有抗菌和自清洁棉织物的制备方法，其特征在于：
上述步骤S1中所述抗菌层与所述棉织物采用的是668糊盒胶粘合连接，粘合温度为85-90℃，完成粘合后需立即降温。
6.根据权利要求1所述的一种具有抗菌和自清洁棉织物的制备方法，其特征在于：
上述步骤S2中紫外线照射时间为24-26h，氧自由基能使沾附在棉织物上的有机污垢氧化降解，最终形成二氧化碳和水。
7.根据权利要求1所述的一种具有抗菌和自清洁棉织物的制备方法，其特征在于：
上述步骤S2中采用超细纤维制成超高密度拒水透气的纺织品，或者用硅溶胶类材料及某些金属盐在纺织品表面通过自组装方式形成纳米级沉积物,使之具有微乳状的表面结构，得到具有超拒水性能或抗菌抑菌能力的纺织品，污垢不易沾附或易于水洗去除。
8.根据权利要求7所述的一种具有抗菌和自清洁棉织物的制备方法，其特征在于：
通过棉织物表面改性，可使之同时兼具优异的拒水、拒油、易去污、抗静电等自清洁性能，是目前相对成熟、易于产业化的加工方法。
9.根据权利要求1所述的一种具有抗菌和自清洁棉织物的制备方法，其特征在于：
上述步骤S3中所述洗涤设备采用的是XGP型号工业洗涤机，该工业洗涤机内胆径向尺寸大，增加洗涤物运转落差，配以合理的洗涤速度，机器洗净率比同类产品高25％。
10.根据权利要求1所述的一种具有抗菌和自清洁棉织物的制备方法，其特征在于：
上述步骤S3中烘干设备采用的是ND4065型号隧道式烘干机，该隧道式烘干机采用热风循环方式，炉内温度均匀，升温快，输送方式一般低温采用钢网带。