CN116084205A - 一种纸张无氟防水剂及其制备方法 - Google Patents
一种纸张无氟防水剂及其制备方法 Download PDFInfo
- Publication number
- CN116084205A CN116084205A CN202211552628.3A CN202211552628A CN116084205A CN 116084205 A CN116084205 A CN 116084205A CN 202211552628 A CN202211552628 A CN 202211552628A CN 116084205 A CN116084205 A CN 116084205A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- fluorine
- paper
- liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种纸张无氟防水剂及其制备方法，涉及防水剂技术领域，所述纸张无氟防水剂按重量份数包括下列组分：硅树脂50‑60份，石蜡1‑3份，硅油3‑7份，乙醇4‑9份，阳离子蜡分散液10‑12份，交联剂3‑7份，甲基三乙基硅氧烷4‑8份，乳化剂1‑8份，辅助剂10‑15份。本发明中，通过异佛尔酮二异氰酸酯和蓖麻油酸二聚体的加入，可以使得纸张的防水性能更好，尤其是可以显著提高耐用性，在纸张反复沾水后，也可以保证防水性能，且通过硅树脂的加入，还可以提高耐腐蚀性能，这样提高了纸张的使用寿命，实用性较高，进步性显著。
Description
技术领域
本发明涉及防水剂技术领域，尤其涉及一种纸张无氟防水剂及其制备方法。
背景技术
防水剂是一种功能性整理剂，经防水剂整理过的纸张具有拒水性能，但是目前现有的防水剂在实际使用时，在用在纸张上时，若纸张反复沾染到水，则会导致纸张防水效果大幅度下降，影响了实际使用，需要进行改进。
发明内容
本发明的目的是为了解决现有技术中存在的缺点，而提出的一种纸张无氟防水剂及其制备方法。
为了实现上述目的，本发明采用了如下技术方案：一种纸张无氟防水剂，所述纸张无氟防水剂按重量份数包括下列组分：
硅树脂50-60份，石蜡1-3份，硅油3-7份，乙醇4-9份，阳离子蜡分散液10-12份，交联剂3-7份，甲基三乙基硅氧烷4-8份，乳化剂1-8份，辅助剂10-15份。
为了提高使用效果，本发明改进有，所述辅助剂为异佛尔酮二异氰酸酯、蓖麻油酸二聚体和溶剂聚合反应复配而成，且复配比例为3:1:3。
为了提高溶解效果，本发明改进有，所述溶剂包括丙酮、乙酸丁酯、乙酸丙酯和乙酸戊脂中的任意一种。
为了保证混合效果，本发明改进有，所述交联剂为二羟甲基脲、二羟甲基乙烯脲、二羟甲基二羟基乙烯脲和三羟甲基三聚氰胺中的任意一种。
为了提高乳化效果，本发明改进有，所述乳化剂为支链脂肪醇聚氧乙烯醚、脂肪酸多元醇酯和脂肪酸聚氧乙烯多元醇酯中的任意一种。
一种纸张无氟防水剂的制备方法，包括以下步骤：
S1，原材料准备，首先准备硅树脂、石蜡、硅油、乙醇、阳离子蜡分散液和甲基三乙基硅氧烷；
S2，准备交联剂和乳化剂，选择合适的成分做为交联剂和乳化剂；
S3，辅助剂制备，对异佛尔酮二异氰酸酯、蓖麻油酸二聚体和溶剂进行混合，然后75℃条件下进行聚合反应，然后保温3-4小时，随后降温至35℃，于12000rpm的转速下加入纯水乳化10-15min，得到辅助剂；
S4，液体A制备，将所述硅树脂、石蜡和硅油置于反应釜中反应，所述反应釜的转速为7500-8500r/min，反应时间为3-5小时，得到液体A；
S5，液体B制备，将所述乙醇、阳离子蜡分散液和甲基三乙基硅氧烷置于反应釜中以70℃、9000-9500r/min转速反应1-2小时，得到液体B；
S6，混合，将液体A、液体B和辅助剂进行混合，然后升温至35-50℃保温20min，然后加入交联剂和乳化剂，随后在100-150r/min的转速下搅拌混合，得到无氟防水剂。
为了提高聚合效果，本发明改进有，在S3步骤中，所述聚合反应的时间为2-3小时。
为了提高反应效果，本发明改进有，在S4步骤中，所述反应的温度为85-90℃。
与现有技术相比，本发明的优点和积极效果在于，
本发明中，通过异佛尔酮二异氰酸酯和蓖麻油酸二聚体的加入，可以使得纸张的防水性能更好，尤其是可以显著提高耐用性，在纸张反复沾水后，也可以保证防水性能，且通过硅树脂的加入，还可以提高耐腐蚀性能，这样提高了纸张的使用寿命，实用性较高，进步性显著。
附图说明
图1为本发明提出一种纸张无氟防水剂的制备方法的步骤示意图。
具体实施方式
为了能够更清楚地理解本发明的上述目的、特征和优点，下面结合附图和实施例对本发明做进一步说明。需要说明的是，在不冲突的情况下，本申请的实施例及实施例中的特征可以相互组合。
在下面的描述中阐述了很多具体细节以便于充分理解本发明，但是，本发明还可以采用不同于在此描述的其他方式来实施，因此，本发明并不限于下面公开说明书的具体实施例的限制。
实施例一
本发明提供一种技术方案：一种纸张无氟防水剂，纸张无氟防水剂按重量份数包括下列组分：
硅树脂55份，石蜡2份，硅油3份，乙醇4份，阳离子蜡分散液10份，交联剂3份，甲基三乙基硅氧烷4份，乳化剂1份，辅助剂10份。
本实施例中，辅助剂为异佛尔酮二异氰酸酯、蓖麻油酸二聚体和溶剂聚合反应复配而成，且复配比例为3:1:3。
本实施例中，溶剂包括丙酮、乙酸丁酯、乙酸丙酯和乙酸戊脂中的任意一种。
本实施例中，交联剂为二羟甲基脲、二羟甲基乙烯脲、二羟甲基二羟基乙烯脲和三羟甲基三聚氰胺中的任意一种。
本实施例中，乳化剂为支链脂肪醇聚氧乙烯醚、脂肪酸多元醇酯和脂肪酸聚氧乙烯多元醇酯中的任意一种。
请参阅图1，本发明提供一种技术方案：一种纸张无氟防水剂的制备方法，包括以下步骤：
S1，原材料准备，首先准备硅树脂、石蜡、硅油、乙醇、阳离子蜡分散液和甲基三乙基硅氧烷；
S2，准备交联剂和乳化剂，选择合适的成分做为交联剂和乳化剂；
S3，辅助剂制备，对异佛尔酮二异氰酸酯、蓖麻油酸二聚体和溶剂进行混合，然后75℃条件下进行聚合反应，然后保温3小时，随后降温至35℃，于12000rpm的转速下加入纯水乳化10min，得到辅助剂；
S4，液体A制备，将硅树脂、石蜡和硅油置于反应釜中反应，反应釜的转速为7500r/min，反应时间为3小时，得到液体A；
S5，液体B制备，将乙醇、阳离子蜡分散液和甲基三乙基硅氧烷置于反应釜中以70℃、9000r/min转速反应1小时，得到液体B；
S6，混合，将液体A、液体B和辅助剂进行混合，然后升温至35℃保温20min，然后加入交联剂和乳化剂，随后在100r/min的转速下搅拌混合，得到无氟防水剂。
本实施例中，在S3步骤中，聚合反应的时间为2小时。
本实施例中，在S4步骤中，反应的温度为85℃。
实施例二
本发明提供一种技术方案：一种纸张无氟防水剂，纸张无氟防水剂按重量份数包括下列组分：
硅树脂60份，石蜡3份，硅油7份，乙醇9份，阳离子蜡分散液12份，交联剂7份，甲基三乙基硅氧烷8份，乳化剂8份，辅助剂15份。
本实施例中，辅助剂为异佛尔酮二异氰酸酯、蓖麻油酸二聚体和溶剂聚合反应复配而成，且复配比例为3:1:3。
本实施例中，溶剂包括丙酮、乙酸丁酯、乙酸丙酯和乙酸戊脂中的任意一种。
本实施例中，交联剂为二羟甲基脲、二羟甲基乙烯脲、二羟甲基二羟基乙烯脲和三羟甲基三聚氰胺中的任意一种。
本实施例中，乳化剂为支链脂肪醇聚氧乙烯醚、脂肪酸多元醇酯和脂肪酸聚氧乙烯多元醇酯中的任意一种。
请参阅图1，本发明提供一种技术方案：一种纸张无氟防水剂的制备方法，包括以下步骤：
S1，原材料准备，首先准备硅树脂、石蜡、硅油、乙醇、阳离子蜡分散液和甲基三乙基硅氧烷；
S2，准备交联剂和乳化剂，选择合适的成分做为交联剂和乳化剂；
S3，辅助剂制备，对异佛尔酮二异氰酸酯、蓖麻油酸二聚体和溶剂进行混合，然后75℃条件下进行聚合反应，然后保温4小时，随后降温至35℃，于12000rpm的转速下加入纯水乳化15min，得到辅助剂；
S4，液体A制备，将硅树脂、石蜡和硅油置于反应釜中反应，反应釜的转速为8500r/min，反应时间为5小时，得到液体A；
S5，液体B制备，将乙醇、阳离子蜡分散液和甲基三乙基硅氧烷置于反应釜中以70℃、9500r/min转速反应2小时，得到液体B；
S6，混合，将液体A、液体B和辅助剂进行混合，然后升温至50℃保温20min，然后加入交联剂和乳化剂，随后在150r/min的转速下搅拌混合，得到无氟防水剂。
本实施例中，在S3步骤中，聚合反应的时间为3小时。
本实施例中，在S4步骤中，反应的温度为90℃。
实施例三
本发明提供一种技术方案：一种纸张无氟防水剂，纸张无氟防水剂按重量份数包括下列组分：
硅树脂52份，石蜡2份，硅油5份，乙醇8份，阳离子蜡分散液11份，交联剂6份，甲基三乙基硅氧烷8份，乳化剂8份，辅助剂10份。
本实施例中，辅助剂为异佛尔酮二异氰酸酯、蓖麻油酸二聚体和溶剂聚合反应复配而成，且复配比例为3:1:3。
本实施例中，溶剂包括丙酮、乙酸丁酯、乙酸丙酯和乙酸戊脂中的任意一种。
本实施例中，交联剂为二羟甲基脲、二羟甲基乙烯脲、二羟甲基二羟基乙烯脲和三羟甲基三聚氰胺中的任意一种。
本实施例中，乳化剂为支链脂肪醇聚氧乙烯醚、脂肪酸多元醇酯和脂肪酸聚氧乙烯多元醇酯中的任意一种。
请参阅图1，本发明提供一种技术方案：一种纸张无氟防水剂的制备方法，包括以下步骤：
S1，原材料准备，首先准备硅树脂、石蜡、硅油、乙醇、阳离子蜡分散液和甲基三乙基硅氧烷；
S2，准备交联剂和乳化剂，选择合适的成分做为交联剂和乳化剂；
S3，辅助剂制备，对异佛尔酮二异氰酸酯、蓖麻油酸二聚体和溶剂进行混合，然后75℃条件下进行聚合反应，然后保温4小时，随后降温至35℃，于12000rpm的转速下加入纯水乳化10min，得到辅助剂；
S4，液体A制备，将硅树脂、石蜡和硅油置于反应釜中反应，反应釜的转速为7500r/min，反应时间为3小时，得到液体A；
S5，液体B制备，将乙醇、阳离子蜡分散液和甲基三乙基硅氧烷置于反应釜中以70℃、9500r/min转速反应2小时，得到液体B；
S6，混合，将液体A、液体B和辅助剂进行混合，然后升温至50℃保温20min，然后加入交联剂和乳化剂，随后在100r/min的转速下搅拌混合，得到无氟防水剂。
本实施例中，在S3步骤中，聚合反应的时间为3小时。
本实施例中，在S4步骤中，反应的温度为85℃。
工作原理：通过异佛尔酮二异氰酸酯和蓖麻油酸二聚体的加入，可以使得纸张的防水性能更好，尤其是可以显著提高耐用性，在纸张反复沾水后，也可以保证防水性能，且通过硅树脂的加入，还可以提高耐腐蚀性能，这样提高了纸张的使用寿命，实用性较高，进步性显著。
以上，仅是本发明的较佳实施例而已，并非是对本发明作其它形式的限制，任何熟悉本专业的技术人员可能利用上述揭示的技术内容加以变更或改型为等同变化的等效实施例应用于其它领域，但是凡是未脱离本发明技术方案内容，依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与改型，仍属于本发明技术方案的保护范围。
Claims (8)
1.一种纸张无氟防水剂，其特征在于，所述纸张无氟防水剂按重量份数包括下列组分：
硅树脂50-60份，石蜡1-3份，硅油3-7份，乙醇4-9份，阳离子蜡分散液10-12份，交联剂3-7份，甲基三乙基硅氧烷4-8份，乳化剂1-8份，辅助剂10-15份。
2.根据权利要求1所述的纸张无氟防水剂，其特征在于：所述辅助剂为异佛尔酮二异氰酸酯、蓖麻油酸二聚体和溶剂聚合反应复配而成，且复配比例为3:1:3。
3.根据权利要求2所述的纸张无氟防水剂，其特征在于：所述溶剂包括丙酮、乙酸丁酯、乙酸丙酯和乙酸戊脂中的任意一种。
4.根据权利要求1所述的纸张无氟防水剂，其特征在于：所述交联剂为二羟甲基脲、二羟甲基乙烯脲、二羟甲基二羟基乙烯脲和三羟甲基三聚氰胺中的任意一种。
5.根据权利要求1所述的纸张无氟防水剂，其特征在于：所述乳化剂为支链脂肪醇聚氧乙烯醚、脂肪酸多元醇酯和脂肪酸聚氧乙烯多元醇酯中的任意一种。
6.一种纸张无氟防水剂的制备方法，其特征在于，包括以下步骤：
S1，原材料准备，首先准备硅树脂、石蜡、硅油、乙醇、阳离子蜡分散液和甲基三乙基硅氧烷；
S2，准备交联剂和乳化剂，选择合适的成分做为交联剂和乳化剂；
S3，辅助剂制备，对异佛尔酮二异氰酸酯、蓖麻油酸二聚体和溶剂进行混合，然后75℃条件下进行聚合反应，然后保温3-4小时，随后降温至35℃，于12000rpm的转速下加入纯水乳化10-15min，得到辅助剂；
S4，液体A制备，将所述硅树脂、石蜡和硅油置于反应釜中反应，所述反应釜的转速为7500-8500r/min，反应时间为3-5小时，得到液体A；
S5，液体B制备，将所述乙醇、阳离子蜡分散液和甲基三乙基硅氧烷置于反应釜中以70℃、9000-9500r/min转速反应1-2小时，得到液体B；
S6，混合，将液体A、液体B和辅助剂进行混合，然后升温至35-50℃保温20min，然后加入交联剂和乳化剂，随后在100-150r/min的转速下搅拌混合，得到无氟防水剂。
7.根据权利要求6所述的纸张无氟防水剂的制备方法，其特征在于：在S3步骤中，所述聚合反应的时间为2-3小时。
8.根据权利要求6所述的纸张无氟防水剂的制备方法，其特征在于：在S4步骤中，所述反应的温度为85-90℃。