CN115322306A - 一种超长保塌型减水剂及其制备方法 - Google Patents
一种超长保塌型减水剂及其制备方法 Download PDFInfo
- Publication number
- CN115322306A CN115322306A CN202211058332.6A CN202211058332A CN115322306A CN 115322306 A CN115322306 A CN 115322306A CN 202211058332 A CN202211058332 A CN 202211058332A CN 115322306 A CN115322306 A CN 115322306A
- Authority
- CN
- China
- Prior art keywords
- parts
- collapse
- preparation
- ultra
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于一种超长保塌型减水剂的制备方法，包括以下步骤：步骤1：将250‑400份TPEG、5‑20份丙烯酸羟乙酯、5‑20丙烯酸和去离子水投入到反应器中，开启搅拌至TPEG完成溶解；步骤2：向步骤1的混合物中加入双氧水，搅拌一段时间后加入硫酸亚铁继续搅拌，同时加入滴加料A和滴加料B；步骤3：步骤2制得的混合物老化60分钟，保塌母液固含量40%；其中，滴加料A由10‑30份丙烯酸、40‑70份去离子水以及15‑30份丙烯酸羟乙酯混合而成；滴加料B由0.5‑5份次亚磷酸钠、80‑150份去离子水以及0.1‑2份维生素C混合而成，本发明提供的减水剂可以减少单方用水量，提高混凝土和易性，使混凝土达到三小时坍落度损失不大于40MM的施工性能，增大施工性能，且符合国标GB8076‑2008、TB/T3275‑2018和CRCC产品认证实施规则特定要求，解决了混凝土坍落度损失快的技术问题。
Description
技术领域
本发明涉及减水剂加工技术领域，具体为一种超长保塌型减水剂及其制备方法。
背景技术
在我国经济不断发展的背景下，基础建筑设施的数量越来越多，规模在逐年增加，施工时遇到的混凝土问题很多，有时因为水泥，地材，砂子含泥量大，粉煤灰，矿粉等掺合料质量不佳，路途遥远，交通情况堵塞，或者到达施工现场后的各种原因，导致两个小时或者更长时间不能及时浇筑，混凝土坍落度损失很快，无法满足正常施工要求。因此具有超长时间保坍功能的高性能减水剂具有很大的市场需求。
发明内容
本发明的目的在于提供一种超长保塌型减水剂的制备方法，用以解决上述背景技术中提出的技术问题。
为实现上述目的，本发明提供如下技术方案：一种超长保塌型减水剂的制备方法，包括以下步骤：
步骤1：将250-400份TPEG、5-20份丙烯酸羟乙酯、5-20丙烯酸和去离子水投入到反应器中，开启搅拌至TPEG完成溶解；
步骤2：向步骤1的混合物中加入双氧水，搅拌一段时间后加入硫酸亚铁继续搅拌，同时加入滴加料A和滴加料B；
步骤3：步骤2制得的混合物老化60分钟，保塌母液固含量40%；
其中，滴加料A由10-30份丙烯酸、40-70份去离子水以及15-30份丙烯酸羟乙酯混合而成；
滴加料B由0.5-5份次亚磷酸钠、80-150份去离子水以及 0.1-2份维生素C混合而成。
进一步的改进在于：步骤2中，在加入双氧水过程中，控制反应温度在30℃以下。
进一步的改进在于：步骤2中，加入双氧水，搅拌4-6分钟后加入硫酸亚铁。
进一步的改进在于：步骤2中加入硫酸亚铁搅拌4-6分钟后同时加人滴加料A和滴加料B。
进一步的改进在于：步骤2中，滴加料A在120分钟内匀速滴加完毕。
进一步的改进在于：步骤2中，滴加料B在150分钟匀速滴加完毕。
与现有技术相比，本发明的有益效果是：
工艺优点：用双氧水-抗坏血酸，双氧水-硫酸亚铁构成氧化还原体系，室温下即可进行聚合反应，反应周期短，聚合效率高，体系粘度相对较低；
流动性提高：大单体TPEG大的分子量和长支链长度可以提供空间位阻效应，有效的分散水泥颗粒，进而水泥净浆的流动度得到提高。同时，所得的外加剂中含有次磷酸盐，丙烯酸等高亲水性基团，可以先提供静电排斥效应，也使得水泥基材料的流动度提高；
保塌性保持：体系中加入了功能单体，丙烯酸羟乙酯，脂类在碱性条件下的水解可以有效的延缓流动度的损失，底料同时加入了大单体TPEG、功能单体丙烯酸羟乙酯，小单体丙烯酸；
产品性能：减少单方用水量，提高混凝土和易性，3小时保坍功能（使混凝土达到三小时坍落度损失不大于40MM的施工性能），增大施工性能；
功能设计要求：符合国标GB8076-2008,TB/T3275-2018和CRCC产品认证实施规则特定要求。
具体实施方式
下面结合具体实施例对本发明的技术方案作进一步的描述，但本发明并不限于这些实施例。
实施例
本发明的工艺配比如下：
TPEG 250-400份
去离子水 (H2O) 100-250份
双氧水 1-10份
底料 丙烯酸 (AA) 5-20份
丙烯酸羟乙酯（HEA) 5-20份
硫酸亚铁 0.1-5份
丙烯酸 10-30份
滴加料A 去离子水 40-70份
丙烯酸羟乙酯 15-30份
次亚磷酸钠 0.5-5份
滴加料B 去离子水 80-150份
维生素C 0.1-2份
补水 去离子水 100-300份
本发明工艺条件如下：
将TPEG、HEA、AA、H2O依次投入到反应器中，开启搅拌至TPEG完全溶解，控制温度在30℃以下，加入引发剂双氧水，搅拌4-6分钟后加入硫酸亚铁搅拌4-6分钟后同时滴加滴加料A和滴加料B溶液（其中，滴加料A和滴加料B溶液需事先配好，搅拌均匀），滴加料A需120分钟匀速滴加完毕，滴加料B溶液150分钟匀速滴加完毕，老化60分钟，保塌母液固含量40%。
取上述工艺条件制得的成品做流动度测试，采用水泥300g+水87g+本实施例的减水剂母液0.9g，母液掺量0.3%，得出结果如下：
小试：初始 ：NO
1小时：185*190
2小时：260*260
3小时：210*210
中试：初试：NO
1小时：150*150
2小时：200*200
3小时：215*215
上述流动度测试可以看出水泥净净流动度在3小时内保持着较大的流动度，有效的达到了三小时的流动度保持能力，减少单方用水量，提高混凝土和易性，增大施工性能。
最终得出的本实施例实验结果如下：
c30混凝土坍落度220 ： 混凝土的塌落度达到160以上均符合施工标准，而应用本实施例提供的减水剂后，塌落度显著提高，表明外加剂和混凝土有良好的和易性，混凝土的施工性能得到了显著的改善。
砂浆扩展度350*350：砂浆扩展度显著提高，表明外加剂和混凝土有良好的和易性，混凝土的施工性能得到了显著的改善。
7天强度 30兆帕：达到了C30混凝土规定的强度标准。
综上，本发明提供的减水剂可以减少单方用水量，提高混凝土和易性，3小时保坍功能（使混凝土达到三小时坍落度损失不大于40MM的施工性能），增大施工性能，且符合国标GB8076-2008、TB/T3275-2018和CRCC产品认证实施规则特定要求。
尽管已用具体实施方案来说明和描述了本发明，但对于本领域的技术人员显而易见的是，在不背离本发明的精神和保护范围的情况下可作出许多其它的变化和修改。因此，有意识地在附加的权利要求书中包括属于本发明范围内的所有这些变化和修改。
Claims (7)
1.一种超长保塌型减水剂的制备方法，其特征在于，包括以下步骤：
步骤1：将250-400份TPEG、5-20份丙烯酸羟乙酯、5-20丙烯酸和去离子水投入到反应器中，开启搅拌至TPEG完成溶解；
步骤2：向步骤1的混合物中加入双氧水，搅拌一段时间后加入硫酸亚铁继续搅拌，同时加入滴加料A和滴加料B；
步骤3：步骤2制得的混合物老化60分钟，保塌母液固含量40%；
其中，滴加料A由10-30份丙烯酸、40-70份去离子水以及15-30份丙烯酸羟乙酯混合而成；
滴加料B由0.5-5份次亚磷酸钠、80-150份去离子水以及 0.1-2份维生素C混合而成。
2.根据权利要求1所述的一种超长保塌型减水剂的制备方法，其特征在于：步骤2中，在加入双氧水过程中，控制反应温度在30℃以下。
3.根据权利要求1所述的一种超长保塌型减水剂的制备方法，其特征在于：步骤2中，加入双氧水，搅拌4-6分钟后加入硫酸亚铁。
4.根据权利要求1或5所述的一种超长保塌型减水剂的制备方法，其特征在于：步骤2中加入硫酸亚铁搅拌4-6分钟后同时加人滴加料A和滴加料B。
5.根据权利要求1或4所述的一种超长保塌型减水剂的制备方法，其特征在于：步骤2中，滴加料A在120分钟内匀速滴加完毕。
6.根据权利要求1或4所述的一种超长保塌型减水剂的制备方法，其特征在于：步骤2中，滴加料B在150分钟匀速滴加完毕。
7.一种超长保塌型减水剂，其特征在于：采用权利要求1-6任一所述的制备方法制得。