CN115073652A - 一种环氧树脂除氯用极性吸附剂及其制备方法、及利用其制备超高纯环氧树脂的方法 - Google Patents
一种环氧树脂除氯用极性吸附剂及其制备方法、及利用其制备超高纯环氧树脂的方法 Download PDFInfo
- Publication number
- CN115073652A CN115073652A CN202210858469.3A CN202210858469A CN115073652A CN 115073652 A CN115073652 A CN 115073652A CN 202210858469 A CN202210858469 A CN 202210858469A CN 115073652 A CN115073652 A CN 115073652A
- Authority
- CN
- China
- Prior art keywords
- epoxy resin
- polar adsorbent
- dechlorination
- stirring
- polar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
项目 | 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | 实施例6 |
最初总氯含量/ppm | 800 | 830 | 960 | 1050 | 1140 | 1200 |
最终总氯含量/ppm | 189 | 202 | 196 | 209 | 221 | 254 |
Claims (9)