CN115057409B - 一种与碱性水反应制氢的铝/碳复合物及其制备方法与应用 - Google Patents
一种与碱性水反应制氢的铝/碳复合物及其制备方法与应用 Download PDFInfo
- Publication number
- CN115057409B CN115057409B CN202210744531.6A CN202210744531A CN115057409B CN 115057409 B CN115057409 B CN 115057409B CN 202210744531 A CN202210744531 A CN 202210744531A CN 115057409 B CN115057409 B CN 115057409B
- Authority
- CN
- China
- Prior art keywords
- aluminum
- hydrogen production
- carbon
- alkaline water
- carbon material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种与碱性水反应制氢的铝/碳复合物及其制备方法与应用；所述铝/碳复合物由铝基体和碳材料组成；所述碳材料以亚微米或纳米尺度的颗粒形式弥散分布于铝基体表面及内部，并形成了连续或准连续的网络。本发明通过在保护气氛下将碳材料进行热处理；将铝粉与热处理后的碳材料在保护气氛下进行球磨，制得与碱性水反应制氢的铝/碳复合物。本发明提供的制备方法原料易得、操作简单、便于量产，可以显著改善铝水系统的制氢动力学，可在室温环境下与碱性水迅速反应制氢，最高制氢速率位于当前报道顶尖水平。
Description
技术领域
本发明属于制氢材料技术领域，具体涉及一种与碱性水反应制氢的铝/碳复合物及其制备方法与应用。
背景技术
氢是一种清洁、高效的能源载体，其规模化产业应用有望根本性解决能源短缺、环境污染等全球性问题，但安全、高效地储存和运输氢仍是氢能技术广泛应用所面临的巨大挑战。自2000年前后，利用富氢材料/系统与乏燃料再生相结合，按需制氢，已经成为用于移动或便携设备的化学储氢方法。在众多的候选材料/体系中，铝-水体系因其资源丰富、反应温度低、生成的氢气无须纯化以及铝的循环利用技术成熟等特点而备受关注。
然而铝表面连续致密钝化层的形成制约了铝-水体系作为氢源的应用潜力，针对这个问题，目前外国内外已经开发出多种改性手段，但都不能满足实际应用制氢的性能与成本需求。添加高浓度的碱性助剂，如氢氧化钠、氢氧化钾等，可以与氧化铝以及铝反应生成可溶性的偏铝酸盐化物，从而有效破坏钝化层的生成，但高的碱浓度又容易引发容器的应力腐蚀，对氢气发生器提出了苛刻的耐蚀性要求。采用镓、铟、锡、铋等低熔点金属与铝合金化可以通过削弱基体强度，改变钝化膜致密性等作用，从而实现在中性水中具备快速制氢性能(Studies on microstructure of activated aluminum and its hydrogengeneration properties in aluminum/water reaction)；但材料和改性成本的急剧升高，限制了这类铝基合金的实际应用。此外，铝与Al2O3，MgO等金属氧化物或NaCl，KCl等水溶性无机盐球磨也可以提升在其在中性水中的反应活性，但根据已发表的文献，在长时间的球磨过后，氧化物/盐对铝-水系统反应动力学的提升效果相当有限。因此，在不过度增加制备成本的前提下，探索先进的方法来解决铝-水系统的钝化问题仍然是当务之急。
鉴于这种情况，本发明提出采用碳材料作为改性剂与铝复合的方法，从而提高其在碱性水中的制氢性能。
发明内容
针对现有技术存在的不足，本发明的目的在于提供一种适用于移动设备的与碱性水反应制氢的铝/碳复合物及其制备方法与应用(水反应制氢体系的制氢方法)。该制备方法原料易得、操作简便、便于量产、改性后的铝基复合物在低碱浓度下具备优异的制氢性能，可以解决现有技术中存在的制备成本过高、制氢速率低等问题。
本发明采用铝/碳复合物与碱性水反应制氢体系和制氢方法，制氢体系由固体复合物和碱性液体两部分组成，固体复合物和碱性液体的重量比例在1:5～1:1000；其中，固体复合物为铝/碳材料复合物，铝/碳复合物采用机械球磨法制备，碳以微纳米尺度细小弥散的分散在铝基体内部和表面，复合物具有超亲水性，良好的抗氧化性。
本发明的目的通过以下技术方案实现：
一种与碱性水反应制氢的铝/碳复合物，所述铝/碳复合物由铝基体和碳材料组成；所述碳材料以亚微米或纳米尺度的颗粒形式弥散分布于铝基体表面及内部，并形成了连续或准连续的网络。所述铝/碳复合物，表现出超亲水性及良好的抗氧化性。
优选的，所述铝基体的纯度为99％以上，碳材料为碳纳米管、石墨烯、活性炭、碳纤维、石墨粉或导电炭黑中一种或多种的组合。
优选的，所述铝/碳复合物具有多孔结构，孔尺寸为100nm～10μm。
上述的与碱性水反应制氢的铝/碳复合物的制备方法，包含以下步骤：
(1)在保护气氛下将碳材料进行热处理；去除吸附的杂质气体与水分；所述碳材料热处理后，具有石墨碳和无定形碳两种相结构；
(2)将铝粉与步骤(1)热处理后的碳材料在保护气氛下进行球磨，制得与碱性水反应制氢的铝/碳复合物。
优选的，步骤(1)所述的保护气氛为氩气。
优选的，步骤(1)所述热处理的温度为200～550℃，时间为1～10小时；升温速率为10℃/min。
优选的，步骤(1)所述碳材料为碳纳米管、石墨烯、活性炭、碳纤维、石墨粉或导电炭黑中一种或多种的组合。
优选的，步骤(2)所述铝粉与热处理后的碳材料的质量比为1:1～100:1。
进一步优选的，步骤(2)所述铝粉与热处理后的碳材料的质量比为1:1～95:5。
优选的，步骤(2)所述铝粉的粒径1～1000μm。
进一步优选的，步骤(2)所述铝粉的粒径10～200μm；纯度为99.9％。
优选的，步骤(2)所述球磨所用的磨球的直径为5mm-15mm；所述磨球的球料质量比5:1～100:1。
进一步优选的，步骤(2)所述球磨所用的磨球的直径为5、10、15mm；
优选的，步骤(2)所述球磨的转速为100～2000转/分钟，球磨的时间为1分钟～50小时。
优选的，步骤(2)所述球磨的磨罐及磨球为玛瑙、氧化锆、硬质合金、聚氨酯或不锈钢；所述的保护气氛为氩气。
上述的与碱性水反应制氢的铝/碳复合物在与碱性水反应制氢中的应用。
优选的，所述碱性水中的碱为氢氧化钠(NaOH)、氢氧化钾(KOH)、氢氧化钙(Ca(OH)2)或氢氧化锂(LiOH)中一种或多种的组合，碱的浓度为0.1～10M。
进一步优选的，碱的浓度为0.5～5M。
优选的，所述铝/碳复合物和碱性水的重量比为1:5～1:1000。
优选的，制氢反应在室温环境中进行；制氢反应过程中不对体系温度进行控制。
本发明的设计原理是：
对于铝水反应制氢改性方法，关键点是在相对温和的溶液中具备快速制氢动力学，并且无需过高的改性成本。以往的研究往往只考虑前者而忽略了成本问题，而本发明所提供的铝/碳复合物同时对这两个问题进行了一定程度上的解决。首先，将铝粉和碳材料在氩气氛保护下机械球磨，在这个过程，碳材料不仅充当改性剂，而且还可以充当助磨剂防止铝粉在球磨过程中由冷焊现象导致的相互粘连；此外，碳材料与铝基体充分地接触，也创造了大量的界面，使铝/碳复合物具备蓬松的结构，提供了毛细效应中水分扩散的通道，进而增大了反应的接触面积，当接触到碱溶液时，铝表面的钝化膜被破坏，发生如下反应(1)
Al2O3+3H2O+2OH-→2[Al(OH)4]- (1)
随后渗透进铝/碳复合物的碱性水溶液接触到铝基体，发生反应(2)
2Al+6H2O+2OH-→2[Al(OH)4]-+3H2↑ (2)
本发明的优点及有益效果在于：
(1)本发明提供了适用于铝/水制氢的改性新方法，该刚发区别于传统方法的关键之处在于方法简单易行，快速且可大量生产，在显著提供了制氢动力学的同时兼具低改性成本。利用机械球磨法的物理混合能力，使碳材料均匀地分布于铝基体的表面及内部，提供大量的界面面积，创造了水分扩散的通道，有利于提高反应的接触面积；此外通过调控碳材料所占的比例与球磨时间进一步强化碳与铝基体的相互作用，进一步改善铝/碳复合物的制氢性能。
(2)本发明提供的适用于移动设备即时制氢的铝/碳复合材料采用的原材料廉价易得，制备工艺简单、全程无污染、便于量产。
(3)本发明提供了高制氢性能铝/碳材料-水复合体系，可在低碱浓度下实现快速的制氢动力学，且具有优异的抗氧化性，综合制氢性能位于目前的顶尖水平。
附图说明
图1a为实施例1制备的球磨15分钟Al：碳材料＝5的铝/碳复合物制备态的扫描电镜及对应的能谱图。
图1b为实施例1制备的铝/碳复合物在碱溶液中反应10秒后的扫描电镜及对应的能谱图。
图2a为实施例1制备的球磨15分钟Al：碳材料＝5的铝/碳复合物高脚环形暗场透射电镜及对应的能谱分析图。
图2b为实施例1制备的球磨15分钟Al：碳材料＝5的铝/碳复合物透射电镜及对应区域的电子衍射图片。
图2c为实施例1制备的球磨15分钟Al：碳材料＝5的铝/碳复合物高分辨透射电镜结果图。
图3为实施例1制备的球磨15分钟Al：碳材料＝5的铝/碳复合物的XRD图。
图4为实施例1制备的球磨15分钟Al：碳材料＝5的铝/碳复合物的拉曼光谱。
图5a为实施例1制备的铝/碳复合物与纯铝粉在碱溶液中的制氢动力学曲线。
图5b为实施例1制备的铝/碳复合物与纯铝粉在碱溶液中的随时间变化的的制氢速率曲线。
图6a为实施例2制备的不同球磨时间的Al：碳材料＝5的铝/碳复合物在碱溶液中的制氢动力学曲线。
图6b为实施例2制备的不同球磨时间的Al：碳材料＝5的铝/碳复合物在碱溶液中的随时间变化的的制氢速率曲线。
图7a为实施例2制备的球磨10分钟的Al：碳材料＝5的铝/碳复合物扫描电镜及对应能的谱分析图。
图7b为实施例2制备的球磨20分钟的Al：碳材料＝5的铝/碳复合物扫描电镜及对应能的谱分析图。
图7c为实施例2制备的球磨1小时的Al：碳材料＝5的铝/碳复合物扫描电镜及对应能的谱分析图。
图8a为实施例3制备的球磨15分钟铝/碳复合物中随碳材料比例降低在碱溶液中的制氢动力学曲线。
图8b为实施例3制备的球磨15分钟铝/碳复合物中随碳材料比例降低在碱溶液中的随时间变化的的制氢速率曲线。
图9a为实施例4制备的球磨15分钟Al：碳材料＝5的铝/碳复合物随着在空气中放置时间延长在碱溶液中的制氢动力学曲线。
图9b为实施例4制备的球磨15分钟Al：碳材料＝5的铝/碳复合物随着在空气中放置时间延长在碱溶液中的随时间变化的的制氢速率曲线。
图10a为实施例5制备的铝粉压片表面接触角随时间的变化图。
图10b为实施例5制备的Al/碳复合物压片表面接触角随时间的变化图。
具体实施方式
以下结合附图和实施例对本发明的具体实施作进一步说明，但本发明的实施和保护不限于此。需指出的是，以下若有未特别详细说明之过程，均是本领域技术人员可参照现有技术实现或理解的。所用试剂或仪器未注明生产厂商者，视为可以通过市售购买得到的常规产品。
实施例1
Al/碳复合物的合成、结构与制氢性能
Al/碳复合物制备
选取所应用的碳材料(活性碳)将其在氩气氛下加热至400℃，升温速率10℃/分钟，经3小时恒温处理后随炉冷却至室温。随后在手套箱中将粒径25μm的铝粉、热处理后的碳材料与磨球(5mm,10mm,15mm的磨球按照质量比为5:2:1混合)按照1:30的质量比装入球磨罐，铝粉与碳材料质量比为5:1，在1000转每分钟的转速下球磨15分钟，制得目标铝/碳复合物。
铝/碳复合物的物相/结构表征：
扫描电镜观察以及对应的能谱分析(图1a和图1b)发现：机械球磨后，大量不同尺寸的碳颗粒镶嵌在铝基体上，但在反应进行10秒后再次对样品进行观察，发现碳颗粒大量从铝基体上脱落，铝基体上出现了脱嵌形成的凹坑。
高脚环形暗场透射电镜观察及对应的能谱分析(图2a)进一步确认了铝碳在亚微米到纳米尺度的均匀复合，碳材料在铝基体中形成了连续或准连续的网络。选取电子衍射(图2b)确认了铝的衍射环，高分辨透射电子显微镜观察(图2c)到了碳材料中的特征非晶碳形貌。
XRD分析(图3)显示了清晰指认的铝的尖锐衍射峰，以及碳材料对应的非晶峰。
拉曼光谱(图4)出现的D峰和G峰以及ID/IG＝1.06同样证明了以非晶碳为主要组成相的碳材料的存在。
制氢方法：
在室温环境下(25℃)将1g铝/碳复合物置于两颈烧瓶中，通过恒压漏斗将1M NaOH溶液100mL注入两颈烧瓶，反应过程中不对体系温度进行控制。(以铝粉作为对比实验)
制氢性能测试：
产生的氢气通过冷凝管冷却至室温，后经过集气瓶收集，并通过排水法测量产生氢气的量，测得制氢量-时间曲线；将测得的制氢量对时间进行微分，测得制氢速率-时间曲线。
图5a和图5b给出了铝/碳复合物与未经改性铝粉在碱溶液中的制氢性能(包括制氢量-时间曲线及制氢速率-时间曲线)，测试结果表明：未经改性的铝粉要经过8分钟才能实现完全制氢，最高制氢速率仅为251mL min-1 g-1；而改性后的铝/碳复合物可以实现1分钟之内完全制氢，最高制氢速率达到4556mL min-1 g-1(以铝/碳复合物的质量计)，是未改性铝粉的18倍。
性能测试结果表明：铝粉与碳材料经过机械球磨改性后，在低碱浓度环境中的制氢动力学得到了显著的提升。
实施例2
球磨时间对铝/碳材料复合物制氢性能的影响、铝/碳材料复合物的微观结构随球磨时间的变化。
Al/碳复合物制备与实施例1相同，区别仅在于球磨时间不同。
制氢方法及制氢性能测试方法同实施例1。
图6a和图6b给出了不同球磨时间铝/碳材料复合物在碱溶液中的制氢性能对比情况。结果显示，铝/碳材料复合物的制氢动力学随着球磨时间的增长而升高，在到达15分钟时达到最高；当继续延长球磨时间时，却导致了制氢动力学的下降。
不同球磨时间铝/碳复合物的形貌表征
根据扫描电镜结合能谱分析(图7a、图7b和图7c)发现，碳颗粒随着球磨时间的延长逐渐破碎，并镶嵌在铝基体上，阻止了铝表面钝化膜的生成，同时为水分子进入铝基体内部提供了窗口和扩散通道；但由于纯铝具有良好的塑性和形变能力，碳颗粒很快在铝相互焊合粘连的的过程中被包覆在基体内部。(能谱中碳信号逐渐减弱乃至消失)
实施例3
碳材料比例对铝/碳复合物制氢性能的影响。
Al/碳复合物制备与实施例1相同，区别仅在于铝粉与碳材料质量比不同。
制氢方法及制氢性能测试方法同实施例1。
图8a和图8b给出了在碱溶液中铝/碳复合物中碳材料比例不断降低制氢性能曲线的规律(包括制氢量-时间曲线及制氢速率-时间曲线)：随着碳材料的比例逐渐降低，制氢动力学逐渐变差，说明碳材料的比例越高，对铝基体的改性效果越好。
实施例4
在空气中放置对铝/碳复合物制氢性能的影响。
Al/碳复合物制备与实施例1相同。
制氢方法及制氢性能测试方法同实施例1。
图9a和图9b给出了在碱溶液中Al:碳材料＝5的铝/碳复合物随着在空气中放置时间的延长制氢性能的变化(包括制氢量-时间曲线及制氢速率-时间曲线)。制氢动力学随着放置时间的延长而有减慢，最高制氢速率也随之下降，但放置时间到达12小时后，制氢动力学与最高制氢速率保持稳定，样品依旧表现出了良好的制氢性能，这表明样品有一定的抗氧化性能。
实施例5
Al/碳复合物的亲水性测试
Al/碳复合物制备与实施例1相同。
使用压片机将相同质量未经处理的铝粉与Al/碳复合物分别压制为直径为10mm，厚度1mm的圆形压片，进行表面接触角测试。
图10a和图10b给出了铝粉压片及Al/碳复合物压片的表面接触角随时间的变化，铝粉压片的表面接触角稳定在93°，表现出疏水的特性；而水滴在接触到Al/碳复合物压片0.05秒以内就迅速被压片所吸收而消失，表现出超亲水性。
实施例的结果表明：本发明采用将铝粉与碳材料机械球磨促进铝-水制氢的改性方法，可以解决现有技术中存在的制氢速率低、改性成本过高等问题，该制氢体系及制氢方法具有工艺简单、高效、安全且制氢成本较低等技术优点，可为移动或便携设备的燃料电池提供移动氢源。
以上实施例为本发明较佳的实施方式，但本发明的实施方式并不受上述实施例的限制，其他的任何未背离本发明的精神实质与原理下所作的改变、修饰、替代、组合、简化，均应为等效的置换方式，都包含在本发明的保护范围之内。
Claims (9)
1.一种与碱性水反应制氢的铝/碳复合物，其特征在于，所述铝/碳复合物由铝基体和碳材料组成；所述碳材料以亚微米或纳米尺度的颗粒形式弥散分布于铝基体表面及内部，并形成了连续或准连续的网络；所述碳材料为活性炭；
所述的与碱性水反应制氢的铝/碳复合物的制备方法包含以下步骤：
（1）在保护气氛下将碳材料进行热处理；
（2）将铝粉与步骤（1）热处理后的碳材料在保护气氛下进行球磨，制得与碱性水反应制氢的铝/碳复合物；所述铝粉与热处理后的碳材料的质量比为1:1~5:1；所述球磨的时间为10分钟~30分钟；所述球磨所用的磨球的直径为5 mm-15 mm；所述球磨的球料质量比5:1~100:1；所述球磨的转速为1000~2000转/分钟。
2.根据权利要求1所述的与碱性水反应制氢的铝/碳复合物，其特征在于，所述铝基体的纯度为99%以上。
3.权利要求1或2所述的与碱性水反应制氢的铝/碳复合物的制备方法，其特征在于，包含以下步骤：
（1）在保护气氛下将碳材料进行热处理；
（2）将铝粉与步骤（1）热处理后的碳材料在保护气氛下进行球磨，制得与碱性水反应制氢的铝/碳复合物；所述铝粉与热处理后的碳材料的质量比为1:1~5:1；所述球磨的时间为10分钟~30分钟；所述球磨所用的磨球的直径为5 mm-15 mm；所述球磨的球料质量比5:1~100:1；所述球磨的转速为1000~2000转/分钟。
4. 根据权利要求3所述的与碱性水反应制氢的铝/碳复合物的制备方法，其特征在于：步骤（1）所述的保护气氛为氩气；所述热处理的温度为200~550℃，时间为1~10小时。
5. 根据权利要求3所述的与碱性水反应制氢的铝/碳复合物的制备方法，其特征在于：步骤（2）所述铝粉的粒径1~1000μm。
6.根据权利要求3所述的与碱性水反应制氢的铝/碳复合物的制备方法，其特征在于：步骤（2）所述球磨的磨罐及磨球为玛瑙、氧化锆、硬质合金、聚氨酯或不锈钢；所述的保护气氛为氩气。
7.权利要求1或2所述的与碱性水反应制氢的铝/碳复合物在与碱性水反应制氢中的应用。
8. 根据权利要求7所述的应用，其特征在于：所述碱性水中的碱为氢氧化钠、氢氧化钾、氢氧化钙或氢氧化锂中一种或多种的组合，碱的浓度为0.1~10 M；
所述铝/碳复合物和碱性水的重量比为1:5~1:1000。
9.根据权利要求7所述的应用，其特征在于：制氢反应在室温环境中进行；制氢反应过程中不对体系温度进行控制。