CN114960189A - 一种具有弹力的丝织物及其制备方法 - Google Patents
一种具有弹力的丝织物及其制备方法 Download PDFInfo
- Publication number
- CN114960189A CN114960189A CN202210667232.7A CN202210667232A CN114960189A CN 114960189 A CN114960189 A CN 114960189A CN 202210667232 A CN202210667232 A CN 202210667232A CN 114960189 A CN114960189 A CN 114960189A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid
- yarn
- silk fabric
- diethylene glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本申请涉及丝织物加工生产领域,具体公开了一种具有弹力的丝织物及其制备方法,一种具有弹力的丝织物的制备方法,包括如下步骤:S1、将真丝和氨纶捻合成纱线;S2、将柠檬酸、酒石酸、壳聚糖、次磷酸钠混合搅拌15‑20min的得到整理液,将纱线投放于整理液中二浸二轧,浸轧处理过后的纱线在75‑80℃下焙烘5‑10min,然后水洗2‑3次,接着在一缩二乙二醇甲基丙烯酸环氧树脂中浸轧,接着70‑80℃焙烘3‑5min,然后皂洗1‑2次,烘干得到成品纱线,最后纱线经编得到丝织物。本申请可使得丝织物耐水洗,提高抗皱性,多次洗涤后不易走形。
Description
技术领域
本申请涉及丝织物加工生产领域,更具体地说,它涉及一种具有弹力的丝织物及其制备方法。
背景技术
随着现代纺织业的发展,以及消费者对布料舒适性能的要求和审美要求越来越高,从而促使市场上流通越来越多风格迥异的面料。
其中,真丝被称为纺织品中的“皇后”,其具有美丽轻盈、柔软爽滑的特点,一般指蚕丝,包括桑蚕丝、柞蚕丝、蓖麻蚕丝、木薯蚕丝等,真丝面料是相对于仿真丝绸面料而言的,它是一种相当昂贵的面料,广泛用于服饰和家具中,它具有其他面料所无法比拟的亲肤性。
但真丝面料缺乏弹性,因此通过真丝面料都会掺有氨纶,从而使得丝织物具有一定的延展性和回弹性,但由此所制得的面料不耐水洗,抗皱性差,多次洗涤后容易走形。
发明内容
为了丝织物耐水洗,提高抗皱性,多次洗涤后不易走形,本申请提供一种具有弹力的丝织物及其制备方法。
本申请提供的一种具有弹力的丝织物及其制备方法,采用如下的技术方案:
一种具有弹力的丝织物的制备方法,包括如下步骤:
S1、将真丝和氨纶捻合成纱线;
S2、将柠檬酸、酒石酸、壳聚糖、次磷酸钠混合搅拌15-20min的得到整理液,将纱线投放于整理液中二浸二轧,浸轧处理过后的纱线在75-80℃下焙烘5-10min,然后水洗2-3次,接着在一缩二乙二醇甲基丙烯酸环氧树脂中浸轧,接着70-80℃焙烘3-5min,然后皂洗1-2次,烘干得到成品纱线,最后纱线经编得到丝织物。
通过采用上述技术方案,壳聚糖上含有大量的氨基、羧基,溶解于柠檬酸和酒石酸中,壳聚糖大分子上-NH3+的存在而带上正电荷,对真丝具有强烈的吸附作用,在浸轧过程中壳聚糖分子均匀分布于纤维内部的无定形区,在焙烘过程中壳聚糖附着于纤维表面和内部微隙中,并在纤维表面形成一层弹性薄膜,使得纤维具有较好的回弹性,次磷酸钠与柠檬酸和酒石酸三者协同作用下对真丝蛋白质纤维中的羧基、氨基以及羟基发生交联反应,有助于提高折痕回复角,此外,次磷酸钠与柠檬酸和酒石酸可使得真丝纤维溶胀,有助于壳聚糖和一缩二乙二醇甲基丙烯酸环氧树脂向真丝纤维内部渗透,有效增加交联的位置和数量,提高分子抗外力滑移的能力,从而使得丝织物耐水洗,提高抗皱性,多次洗涤后不易走形。
优选的,制备方法中各原料的重量份如下:
真丝:200-230份;
氨纶:10-15份;
柠檬酸:50-60份;
酒石酸:50-100份;
壳聚糖:30-60份;
次磷酸钠:2-4份;
水:500-600份;
一缩二乙二醇甲基丙烯酸环氧树脂:60-80份。
优选的,步骤S2的浸轧中还加入有聚马来酸。
通过采用上述技术方案,聚马来酸对于链段较短的分子起架桥作用,使得两个分子之间与一缩二乙二醇甲基丙烯酸环氧树脂更好地交联,聚马来酸对于链段较长的分子起分散作用,一方面使得纤维分子间自由移动的空间由大变小、另一方面能减少长链段分子交联后的应力集中,从而有利于提高丝织物的抗皱性,多次洗涤后不易走形。
优选的,所述壳聚糖为改性壳聚糖,所述改性壳聚糖的制备步骤如下:
A1、将壳聚糖溶于质量浓度为2%-4%的乙酸溶液中,搅拌10-12h,搅拌温度为26℃-28℃得到预处理液a;
A2、将水杨醛加入预处理液a中,75℃-80℃下搅拌反应5-6h,用质量浓度为6%的氢氧化钠溶液调节pH值为中性,得到预处理液b;
A3、接着向步骤A2所制得的预处理液b加入质量浓度为8%-11%的四氢硼酸钠水溶液,继续搅拌反应2-3h,调节pH值为10,加入环氧氯丙烷,60℃反应2h,沉淀,过滤,水洗,乙醇索式提取48h,最后真空干燥得到改性壳聚糖。
通过采用上述技术方案,经过改性后的壳聚糖作用于真丝纤维和氨纶上一方面使得丝织物具有耐酸和耐碱性,使得丝织物不易因汗液和洗衣液而破坏纤维的回弹性能。
优选的,所述一缩二乙二醇甲基丙烯酸环氧树脂的制备步骤如下:将一缩二乙二醇、甲基丙烯酸、对苯二酚、环已烷和对苯磺酸混合,水浴加热搅拌30-40min,接着用质量浓度为10%的氢氧化钠溶液中和过量酸和洗去对苯二酚,最后减压蒸馏出去溶剂得到一缩二乙二醇甲基丙烯酸环氧树脂。
通过采用上述技术方案,所制得的一缩二乙二醇甲基丙烯酸环氧树脂的环氧基开环后与真丝蛋白纤维多肽链上含有活跃氢的胺、醇、硫醇、苯酚、羟基等基团产生共价交联,从而提高抗皱整理的耐久性,进而使得丝织物耐水洗,多次洗涤后不易走形。
优选的,所述聚马来酸和所述一缩二乙二醇甲基丙烯酸环氧树脂的重量比为1:(1-1.5)。
通过采用上述技术方案,聚马来酸和一缩二乙二醇甲基丙烯酸环氧树脂按上述配比混合,聚马来酸对于链段较短的分子起架桥作用,使得两个分子之间与一缩二乙二醇甲基丙烯酸环氧树脂更好地交联,聚马来酸对于链段较长的分子起分散作用,一方面使得纤维分子间自由移动的空间由大变小、另一方面能减少长链段分子交联后的应力集中,从而有利于提高丝织物的抗皱性,多次洗涤后不易走形。
优选的,所述柠檬酸与所述酒石酸的质量比为1:(1-2)。
通过采用上述技术方案,柠檬酸与酒石酸按上述配比作用于真丝蛋白纤维,能有效增加丝织物的折皱回复角和提高断裂强力,从而有利于提高丝织物的抗皱性,多次洗涤后不易走形。
综上所述,本申请具有以下有益效果:
1、在焙烘过程中壳聚糖附着于纤维表面和内部微隙中,并在纤维表面形成一层弹性薄膜,使得纤维具有较好的回弹性,次磷酸钠与柠檬酸和酒石酸可使得真丝纤维溶胀,有助于壳聚糖和一缩二乙二醇甲基丙烯酸环氧树脂向真丝纤维内部渗透,有效增加交联的位置和数量,提高分子抗外力滑移的能力,从而使得丝织物耐水洗,提高抗皱性,多次洗涤后不易走形。
2、聚马来酸对于链段较短的分子起架桥作用,使得两个分子之间与一缩二乙二醇甲基丙烯酸环氧树脂更好地交联,聚马来酸对于链段较长的分子起分散作用,一方面使得纤维分子间自由移动的空间由大变小、另一方面能减少长链段分子交联后的应力集中,从而有利于提高丝织物的抗皱性,多次洗涤后不易走形。
具体实施方式
实施例
实施例1
一种具有弹力的丝织物的制备步骤如下:
一缩二乙二醇甲基丙烯酸环氧树脂的制备:
将11kg一缩二乙二醇、21kg甲基丙烯酸、10kg对苯二酚、10kg环已烷和8kg对苯磺酸混合,水浴加热搅拌30min,水浴温度35℃,接着用质量浓度为10%的氢氧化钠溶液中和过量酸和洗去对苯二酚,最后减压蒸馏出去溶剂得到一缩二乙二醇甲基丙烯酸环氧树脂;
S1、将200kg真丝和10kg氨纶捻合成纱线;
S2、将50kg柠檬酸、50kg酒石酸、30kg壳聚糖、2kg次磷酸钠和500kg水混合搅拌15min的得到整理液,将纱线投放于整理液中二浸二轧,浸轧处理过后的纱线在75℃下焙烘5min,然后水洗2次,接着在60kg一缩二乙二醇甲基丙烯酸环氧树脂中浸轧,接着70℃焙烘3min,然后皂洗1次,烘干得到成品纱线,最后纱线经编得到丝织物。
实施例2
一种具有弹力的丝织物的制备步骤如下:
一缩二乙二醇甲基丙烯酸环氧树脂的制备:
将12kg一缩二乙二醇、22kg甲基丙烯酸、14kg对苯二酚、13kg环已烷和11kg对苯磺酸混合,水浴加热搅拌35min,水浴温度35℃,接着用质量浓度为10%的氢氧化钠溶液中和过量酸和洗去对苯二酚,最后减压蒸馏出去溶剂得到一缩二乙二醇甲基丙烯酸环氧树脂;
S1、将215kg真丝和13kg氨纶捻合成纱线;
S2、将55kg柠檬酸、80kg酒石酸、40kg壳聚糖、3kg次磷酸钠和550kg水混合搅拌18min的得到整理液,将纱线投放于整理液中二浸二轧,浸轧处理过后的纱线在78℃下焙烘8min,然后水洗2次,接着在70kg一缩二乙二醇甲基丙烯酸环氧树脂中浸轧,接着75℃焙烘4min,然后皂洗2次,烘干得到成品纱线,最后纱线经编得到丝织物。
实施例3
一种具有弹力的丝织物的制备步骤如下:
一缩二乙二醇甲基丙烯酸环氧树脂的制备:
将15kg一缩二乙二醇、23kg甲基丙烯酸、18kg对苯二酚、16kg环已烷和14kg对苯磺酸混合,水浴加热搅拌40min,水浴温度35℃,接着用质量浓度为10%的氢氧化钠溶液中和过量酸和洗去对苯二酚,最后减压蒸馏出去溶剂得到一缩二乙二醇甲基丙烯酸环氧树脂;
S1、将230kg真丝和15kg氨纶捻合成纱线;
S2、将60kg柠檬酸、100kg酒石酸、60kg壳聚糖、4kg次磷酸钠和600kg水混合搅拌20min的得到整理液,将纱线投放于整理液中二浸二轧,浸轧处理过后的纱线在80℃下焙烘10min,然后水洗3次,接着在80kg一缩二乙二醇甲基丙烯酸环氧树脂中浸轧,接着80℃焙烘5min,然后皂洗2次,烘干得到成品纱线,最后纱线经编得到丝织物。
实施例4
一种具有弹力的丝织物的制备步骤如下:
一缩二乙二醇甲基丙烯酸环氧树脂的制备:
将12kg一缩二乙二醇、22kg甲基丙烯酸、14kg对苯二酚、13kg环已烷和11kg对苯磺酸混合,水浴加热搅拌35min,水浴温度35℃,接着用质量浓度为10%的氢氧化钠溶液中和过量酸和洗去对苯二酚,最后减压蒸馏出去溶剂得到一缩二乙二醇甲基丙烯酸环氧树脂;
S1、将215kg真丝和13kg氨纶捻合成纱线;
S2、将55kg柠檬酸、80kg酒石酸、40kg壳聚糖、3kg次磷酸钠和550kg水混合搅拌18min的得到整理液,将纱线投放于整理液中二浸二轧,浸轧处理过后的纱线在78℃下焙烘8min,然后水洗2次,接着在70kg一缩二乙二醇甲基丙烯酸环氧树脂和70kg聚马来酸中浸轧,接着75℃焙烘4min,然后皂洗2次,烘干得到成品纱线,最后纱线经编得到丝织物。
实施例5
一种具有弹力的丝织物的制备步骤如下:
一缩二乙二醇甲基丙烯酸环氧树脂的制备:
将12kg一缩二乙二醇、22kg甲基丙烯酸、14kg对苯二酚、13kg环已烷和11kg对苯磺酸混合,水浴加热搅拌35min,水浴温度35℃,接着用质量浓度为10%的氢氧化钠溶液中和过量酸和洗去对苯二酚,最后减压蒸馏出去溶剂得到一缩二乙二醇甲基丙烯酸环氧树脂;
S1、将215kg真丝和13kg氨纶捻合成纱线;
S2、将55kg柠檬酸、80kg酒石酸、40kg壳聚糖、3kg次磷酸钠和550kg水混合搅拌18min的得到整理液,将纱线投放于整理液中二浸二轧,浸轧处理过后的纱线在78℃下焙烘8min,然后水洗2次,接着在70kg一缩二乙二醇甲基丙烯酸环氧树脂和55kg聚马来酸中浸轧,接着75℃焙烘4min,然后皂洗2次,烘干得到成品纱线,最后纱线经编得到丝织物。
实施例6
一种具有弹力的丝织物的制备步骤如下:
一缩二乙二醇甲基丙烯酸环氧树脂的制备:
将12kg一缩二乙二醇、22kg甲基丙烯酸、14kg对苯二酚、13kg环已烷和11kg对苯磺酸混合,水浴加热搅拌35min,水浴温度35℃,接着用质量浓度为10%的氢氧化钠溶液中和过量酸和洗去对苯二酚,最后减压蒸馏出去溶剂得到一缩二乙二醇甲基丙烯酸环氧树脂;
S1、将215kg真丝和13kg氨纶捻合成纱线;
S2、将55kg柠檬酸、80kg酒石酸、40kg壳聚糖、3kg次磷酸钠和550kg水混合搅拌18min的得到整理液,将纱线投放于整理液中二浸二轧,浸轧处理过后的纱线在78℃下焙烘8min,然后水洗2次,接着在70kg一缩二乙二醇甲基丙烯酸环氧树脂和46kg聚马来酸中浸轧,接着75℃焙烘4min,然后皂洗2次,烘干得到成品纱线,最后纱线经编得到丝织物。
实施例7
一种具有弹力的丝织物的制备步骤如下:
一缩二乙二醇甲基丙烯酸环氧树脂的制备:
将12kg一缩二乙二醇、22kg甲基丙烯酸、14kg对苯二酚、13kg环已烷和11kg对苯磺酸混合,水浴加热搅拌35min,水浴温度35℃,接着用质量浓度为10%的氢氧化钠溶液中和过量酸和洗去对苯二酚,最后减压蒸馏出去溶剂得到一缩二乙二醇甲基丙烯酸环氧树脂;
S1、将215kg真丝和13kg氨纶捻合成纱线;
S2、将55kg柠檬酸、80kg酒石酸、40kg壳聚糖、3kg次磷酸钠和550kg水混合搅拌18min的得到整理液,将纱线投放于整理液中二浸二轧,浸轧处理过后的纱线在78℃下焙烘8min,然后水洗2次,接着在70kg一缩二乙二醇甲基丙烯酸环氧树脂中浸轧,接着75℃焙烘4min,然后皂洗2次,烘干得到成品纱线,最后纱线经编得到丝织物。
实施例8
一种具有弹力的丝织物的制备步骤如下:
一缩二乙二醇甲基丙烯酸环氧树脂的制备:
将12kg一缩二乙二醇、22kg甲基丙烯酸、14kg对苯二酚、13kg环已烷和11kg对苯磺酸混合,水浴加热搅拌35min,水浴温度35℃,接着用质量浓度为10%的氢氧化钠溶液中和过量酸和洗去对苯二酚,最后减压蒸馏出去溶剂得到一缩二乙二醇甲基丙烯酸环氧树脂;
S1、将215kg真丝和13kg氨纶捻合成纱线;
S2、将55kg柠檬酸、80kg酒石酸、40kg壳聚糖、3kg次磷酸钠和550kg水混合搅拌18min的得到整理液,将纱线投放于整理液中二浸二轧,浸轧处理过后的纱线在78℃下焙烘8min,然后水洗2次,接着在70kg一缩二乙二醇甲基丙烯酸环氧树脂中浸轧,接着75℃焙烘4min,然后皂洗2次,烘干得到成品纱线,最后纱线经编得到丝织物。
实施例9
一种具有弹力的丝织物的制备步骤如下:
一缩二乙二醇甲基丙烯酸环氧树脂的制备:
将12kg一缩二乙二醇、22kg甲基丙烯酸、14kg对苯二酚、13kg环已烷和11kg对苯磺酸混合,水浴加热搅拌35min,水浴温度35℃,接着用质量浓度为10%的氢氧化钠溶液中和过量酸和洗去对苯二酚,最后减压蒸馏出去溶剂得到一缩二乙二醇甲基丙烯酸环氧树脂;
S1、将215kg真丝和13kg氨纶捻合成纱线;
S2、将55kg柠檬酸、80kg酒石酸、40kg壳聚糖、3kg次磷酸钠和550kg水混合搅拌18min的得到整理液,将纱线投放于整理液中二浸二轧,浸轧处理过后的纱线在78℃下焙烘8min,然后水洗2次,接着在70kg一缩二乙二醇甲基丙烯酸环氧树脂中浸轧,接着75℃焙烘4min,然后皂洗2次,烘干得到成品纱线,最后纱线经编得到丝织物。
实施例10
一种具有弹力的丝织物的制备步骤如下:
一缩二乙二醇甲基丙烯酸环氧树脂的制备:
将12kg一缩二乙二醇、22kg甲基丙烯酸、14kg对苯二酚、13kg环已烷和11kg对苯磺酸混合,水浴加热搅拌35min,水浴温度35℃,接着用质量浓度为10%的氢氧化钠溶液中和过量酸和洗去对苯二酚,最后减压蒸馏出去溶剂得到一缩二乙二醇甲基丙烯酸环氧树脂;
改性壳聚糖的制备:
A1、将壳聚糖溶于质量浓度为2%的乙酸溶液中,搅拌10h,搅拌温度为26℃得到预处理液a;
A2、将水杨醛加入预处理液a中,75℃下搅拌反应5h,用质量浓度为6%的氢氧化钠溶液调节pH值为中性,得到预处理液b;
A3、接着向步骤A2所制得的预处理液b加入质量浓度为8%的四氢硼酸钠水溶液,继续搅拌反应2h,调节pH值为10,加入环氧氯丙烷,60℃反应2h,沉淀,过滤,水洗,乙醇索式提取48h,最后真空干燥得到改性壳聚糖;
S1、将215kg真丝和13kg氨纶捻合成纱线;
S2、将55kg柠檬酸、80kg酒石酸、40kg改性壳聚糖、3kg次磷酸钠和550kg水混合搅拌18min的得到整理液,将纱线投放于整理液中二浸二轧,浸轧处理过后的纱线在78℃下焙烘8min,然后水洗2次,接着在70kg一缩二乙二醇甲基丙烯酸环氧树脂和55kg聚马来酸中浸轧,接着75℃焙烘4min,然后皂洗2次,烘干得到成品纱线,最后纱线经编得到丝织物。
实施例11
一种具有弹力的丝织物的制备步骤如下:
一缩二乙二醇甲基丙烯酸环氧树脂的制备:
将12kg一缩二乙二醇、22kg甲基丙烯酸、14kg对苯二酚、13kg环已烷和11kg对苯磺酸混合,水浴加热搅拌35min,水浴温度35℃,接着用质量浓度为10%的氢氧化钠溶液中和过量酸和洗去对苯二酚,最后减压蒸馏出去溶剂得到一缩二乙二醇甲基丙烯酸环氧树脂;
改性壳聚糖的制备:
A1、将壳聚糖溶于质量浓度为3%的乙酸溶液中,搅拌11h,搅拌温度为27℃得到预处理液a;
A2、将水杨醛加入预处理液a中,78℃下搅拌反应5.5h,用质量浓度为6%的氢氧化钠溶液调节pH值为中性,得到预处理液b;
A3、接着向步骤A2所制得的预处理液b加入质量浓度为10%的四氢硼酸钠水溶液,继续搅拌反应2.5h,调节pH值为10,加入环氧氯丙烷,60℃反应2h,沉淀,过滤,水洗,乙醇索式提取48h,最后真空干燥得到改性壳聚糖;
S1、将215kg真丝和13kg氨纶捻合成纱线;
S2、将55kg柠檬酸、80kg酒石酸、40kg改性壳聚糖、3kg次磷酸钠和550kg水混合搅拌18min的得到整理液,将纱线投放于整理液中二浸二轧,浸轧处理过后的纱线在78℃下焙烘8min,然后水洗2次,接着在70kg一缩二乙二醇甲基丙烯酸环氧树脂和55kg聚马来酸中浸轧,接着75℃焙烘4min,然后皂洗2次,烘干得到成品纱线,最后纱线经编得到丝织物。
实施例12
一种具有弹力的丝织物的制备步骤如下:
一缩二乙二醇甲基丙烯酸环氧树脂的制备:
将12kg一缩二乙二醇、22kg甲基丙烯酸、14kg对苯二酚、13kg环已烷和11kg对苯磺酸混合,水浴加热搅拌35min,水浴温度35℃,接着用质量浓度为10%的氢氧化钠溶液中和过量酸和洗去对苯二酚,最后减压蒸馏出去溶剂得到一缩二乙二醇甲基丙烯酸环氧树脂;
改性壳聚糖的制备:
A1、将壳聚糖溶于质量浓度为4%的乙酸溶液中,搅拌12h,搅拌温度为28℃得到预处理液a;
A2、将水杨醛加入预处理液a中,80℃下搅拌反应6h,用质量浓度为6%的氢氧化钠溶液调节pH值为中性,得到预处理液b;
A3、接着向步骤A2所制得的预处理液b加入质量浓度为11%的四氢硼酸钠水溶液,继续搅拌反应3h,调节pH值为10,加入环氧氯丙烷,60℃反应2h,沉淀,过滤,水洗,乙醇索式提取48h,最后真空干燥得到改性壳聚糖;
S1、将215kg真丝和13kg氨纶捻合成纱线;
S2、将55kg柠檬酸、80kg酒石酸、40kg改性壳聚糖、3kg次磷酸钠和550kg水混合搅拌18min的得到整理液,将纱线投放于整理液中二浸二轧,浸轧处理过后的纱线在78℃下焙烘8min,然后水洗2次,接着在70kg一缩二乙二醇甲基丙烯酸环氧树脂和55kg聚马来酸中浸轧,接着75℃焙烘4min,然后皂洗2次,烘干得到成品纱线,最后纱线经编得到丝织物。
对比例
对比例1
本对比例与实施例2的区别在于,在本对比例中,用等量的柠檬酸替换酒石酸。
对比例2
本对比例与实施例2的区别在于,在本对比例中,用等量的酒石酸替换柠檬酸。
对比例3
本对比例与实施例2的区别在于,在本对比例中,用等量壳聚糖替换柠檬酸和酒石酸。
对比例4
本对比例与实施例2的区别在于,在本对比例中,用等量壳聚糖替换次磷酸钠。
对比例5
本对比例与实施例2的区别在于,在本对比例中,用等量壳聚糖替换一缩二乙二醇甲基丙烯酸环氧树脂。
性能检测试验
丝织物试样的尺寸为10cm×10cm,用PH值为8-9的洗衣粉洗涤实施例1-12和对比例1-5所制得的丝织物,洗涤次数为50次,单次洗涤时间为60min,单次洗涤洗衣粉的用量为0.1kg,洗涤用水量为20L,然后进行如下试验测定:
织物强力按GB/T 3923.1-1997《纺织品织物拉伸性能》第1部分:《断裂强力和断裂伸长率的测定条样法》,进行测定。
折皱回复角按GB/T3819-1997《纺织织物-回复角表示垂直折叠试样折痕回复性的测定方法》测定。
表1
根据表1中的实施例2和对比例1-5的测试数据可知,柠檬酸、酒石酸、壳聚糖、次磷酸钠以及一缩二乙二醇甲基丙烯酸环氧树脂均缺一不可,缺少其中一种成分,丝织物的经向断裂强力、纬向断裂强力、经向缓弹回复角、纬向缓弹回复角均有所下降。
根据表1中的实施例2和实施例4-6的测试数据可知,添加聚马来酸所制得的丝织物抗皱整理的耐久性更佳,多次洗涤后不易走形,聚马来酸和一缩二乙二醇甲基丙烯酸环氧树脂按上述配比混合,聚马来酸对于链段较短的分子起架桥作用,使得两个分子之间与一缩二乙二醇甲基丙烯酸环氧树脂更好地交联,聚马来酸对于链段较长的分子起分散作用,一方面使得纤维分子间自由移动的空间由大变小、另一方面能减少长链段分子交联后的应力集中,从而有利于提高丝织物的抗皱性,多次洗涤后不易走形。
根据表1中的实施例2和实施例7-9的测试数据可知,当柠檬酸与酒石酸的质量浓度比为1:(1-2)时,有效增加丝织物的折皱回复角和提高断裂强力,从而有利于提高丝织物的抗皱性,多次洗涤后不易走形。
根据表1中的实施例2和实施例10-12的测试数据可知,经过改性后的壳聚糖作用于真丝纤维和氨纶上,丝织物的经向断裂强力、纬向断裂强力、经向缓弹回复角、纬向缓弹回复角均有所提高,所表现出来的抗皱性能更佳,丝织物耐水洗,多次洗涤后不易走形。
本具体实施例仅仅是对本申请的解释,其并不是对本申请的限制,本领域技术人员在阅读完本说明书后可以根据需要对本实施例做出没有创造性贡献的修改,但只要在本申请的权利要求范围内都受到专利法的保护。
Claims (10)
1.一种具有弹力的丝织物的制备方法,其特征在于,包括如下步骤:
S1、将真丝和氨纶捻合成纱线;
S2、将柠檬酸、酒石酸、壳聚糖、次磷酸钠混合搅拌15-20min的得到整理液,将纱线投放于整理液中二浸二轧,浸轧处理过后的纱线在75-80℃下焙烘5-10min,然后水洗2-3次,接着在一缩二乙二醇甲基丙烯酸环氧树脂中浸轧,接着70-80℃焙烘3-5min,然后皂洗1-2次,烘干得到成品纱线,最后纱线经编得到丝织物。
2.根据权利要求1所述的一种具有弹力的丝织物的制备方法,其特征在于,制备方法中各原料的重量份如下:
真丝:200-230份;
氨纶:10-15份;
柠檬酸:50-60份;
酒石酸:50-100份;
壳聚糖:30-60份;
次磷酸钠:2-4份;
水:500-600份;
一缩二乙二醇甲基丙烯酸环氧树脂:60-80份。
3.根据权利要求1所述的一种具有弹力的丝织物的制备方法,其特征在于,步骤S2的浸轧中还加入有聚马来酸。
4.根据权利要求1所述的一种具有弹力的丝织物的制备方法,其特征在于,所述壳聚糖为改性壳聚糖,所述改性壳聚糖的制备步骤如下:
A1、将壳聚糖溶于质量浓度为2%-4%的乙酸溶液中,搅拌10-12h,搅拌温度为26℃-28℃得到预处理液a;
A2、将水杨醛加入预处理液a中,75℃-80℃下搅拌反应5-6h,用质量浓度为6%的氢氧化钠溶液调节pH值为中性,得到预处理液b;
A3、接着向步骤A2所制得的预处理液b加入质量浓度为8%-11%的四氢硼酸钠水溶液,继续搅拌反应2-3h,调节pH值为10,加入环氧氯丙烷,60℃反应2h,沉淀,过滤,水洗,乙醇索式提取48h,最后真空干燥得到改性壳聚糖。
5.根据权利要求1所述的一种具有弹力的丝织物的制备方法,其特征在于,所述一缩二乙二醇甲基丙烯酸环氧树脂的制备步骤如下:将一缩二乙二醇、甲基丙烯酸、对苯二酚、环已烷和对苯磺酸混合,水浴加热搅拌30-40min,接着用质量浓度为10%的氢氧化钠溶液中和过量酸和洗去对苯二酚,最后减压蒸馏出去溶剂得到一缩二乙二醇甲基丙烯酸环氧树脂。
6.根据权利要求4所述的一种具有弹力的丝织物的制备方法,其特征在于:所述改性壳聚糖由包括如下重量份的原料制成:壳聚糖:30-50份;乙酸:50-80份;水杨醛:30-40份;四氢硼酸钠:60-80份;环氧氯丙烷:20-40份。
7.根据权利要求1所述的一种具有弹力的丝织物的制备方法,其特征在于,所述一缩二乙二醇甲基丙烯酸环氧树脂由包括如下重量份的原料制成:一缩二乙二醇:11-15份;甲基丙烯酸:21-33份;苯二酚:10-18份;环已烷:10-16份;对苯磺酸:8-14份。
8.根据权利要求3所述的一种具有弹力的丝织物的制备方法,其特征在于,所述聚马来酸和所述一缩二乙二醇甲基丙烯酸环氧树脂的重量比为1:(1-1.5)。
9.根据权利要求2所述的一种具有弹力的丝织物,其特征在于:所述柠檬酸与所述酒石酸的质量比为1:(1-2)。
10.一种具有弹力的丝织物,其特征在于,由权利要求1-9任一项所述具有弹力的丝织物的制备方法制得。