CN1148426C - 免除锈防腐防火漆 - Google Patents

免除锈防腐防火漆 Download PDF

Info

Publication number
CN1148426C
CN1148426C CNB011142146A CN01114214A CN1148426C CN 1148426 C CN1148426 C CN 1148426C CN B011142146 A CNB011142146 A CN B011142146A CN 01114214 A CN01114214 A CN 01114214A CN 1148426 C CN1148426 C CN 1148426C
Authority
CN
China
Prior art keywords
weight
agent
rust
pigment
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB011142146A
Other languages
English (en)
Other versions
CN1318597A (zh
Inventor
黄世德
郭灯祥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB011142146A priority Critical patent/CN1148426C/zh
Publication of CN1318597A publication Critical patent/CN1318597A/zh
Application granted granted Critical
Publication of CN1148426C publication Critical patent/CN1148426C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明公开了一种具有防锈、防腐、防火功能的涂料配方及其生产工艺，它主要由混合高卤化物、溶剂、复合防颜料、着色颜料、防火剂、助剂等组成，适用于金属及非金属表面，可免底漆。具有底面合一，施工成本低的特点。

Description

免除锈防腐防火漆
技术领域
本发明涉及一种涂料的配方及制造方法，特别是一种涂刷于金属、非金属表面，同时具有防锈防腐防火功能的涂料配方及制造方法。
背景技术
防锈、防腐漆的品种很多，它们各有优缺点，有的防铁性能好，但防腐性能强，有的防腐性能好，防锈性能差，有的装饰性能好，防火性能差，易燃烧。大部的防锈、防腐漆在涂刷时必须上底漆，增加施工成本和时间。
发明内容
本发明的目的是提供一种同时具有防锈、防腐、防火功能的防锈防腐防火漆，可以直接涂刷，不必上底漆，减少了施工成本和时间。
本发明的目的是这样实现的：一种免除锈防腐防火漆，它由以下组份组成：
混合高卤化物             15-30重量％
改性树脂                 0-20重量％
溶剂                     53.85-65重量％
复合防锈颜料             3-15重量％
着色颜料                 3-15重量％
复合防火剂               3-10重量％
助剂                     0.2-1.5重量％
其中：混合高卤化物为：以重量份计，改性高氯化聚乙烯10-18份，氯化橡胶0-5份，氯磺化聚乙烯0-3份，氯化石蜡4-10份；
改性树脂为：醇酸树脂0-15份，丙烯酸树脂0-15份；
溶剂为：二甲苯41-50份，醋酸丁酯8.15-15份；
复合防锈颜料为：磷酸锌2-8份，三聚磷酸铝2-10份，ST防锈颜料2-6份；
着色颜料为：红色为铁红、钼铬红，兰色为华兰和酞青兰，白色为钛白粉，黄色为铬黄，黑色为碳黑；
复合防火剂为：QD-SPA(Z)阻燃剂1-6份，锑白2-4份，聚磷酸铵1-5份，阻燃剂FB1-3份；
助剂为：流平剂BYK-306，0.1-0.5份，分散剂963，0.1-0.4份，防浮色发花剂0.2-0.5份，环氧氯丙烷0.2-0.3份，紫外线吸收剂0.3-0.5份。
一种制备上述免除锈防腐防火漆的方法，先将高卤化物与溶剂加入溶解釜中搅拌溶解后，放入配料罐中，加入改性树脂混合均匀，再加入防锈颜料、着色颜料、防火剂以及助剂在800-1200转/分的转速下搅拌分散，然后用砂磨机研磨至细度不大于50μm，最后用溶剂调整粘度不小于40s，采用涂-4杯，温度为25℃，过滤包装即为成品。
本发明由于采用了改性高氯化聚乙烯、氯化橡胶、氯磺化聚乙烯、氯化石蜡等高卤化的混合物，配以醇酸树脂、丙烯酸树脂等改性树脂，加上复合防锈颜料，使其具有了防锈、防腐的功能，复合防火剂的加入，又增加了防火的功能，从而使本发明达到防锈、防腐、防火的目的。
具体实施方式
下面结实施例对本发明作进一步说明。
实施例1：重量％混合高卤化物27，溶剂54.75，防锈颜料4，着色颜料10，复合防火剂4，助剂0.25。
各组份的配比为：以重量份计，混合高卤化物：改性高氯化聚乙烯15份，氯化橡胶3份，氯磺化聚乙烯1份，氯化石蜡8份；二甲苯41份，醋酸丁酯8.75份，三氯乙烯5份；铁红10份，ST防锈颜料4份；锑白2份，聚磷酸铵2份；环氧氯丙烷0.25份。
实施例2：重量％混合高卤化物24，溶剂53.85，防锈颜料5，着色颜料12，复合防火剂4，助剂1.15。
各组份的配比为：以重量份计，混合高卤化物：改性高氯化聚乙烯17份，氯化石蜡7份；醋酸丁酯9.85份，二甲苯44份；钛白粉12份，锑白2份，QD-SPA(Z)阻燃剂2份，磷酸锌5份，环氧氯丙烷0.25份，紫外线吸收剂0.3份，分散剂963为0.2份，防浮色发花剂0.4份。
实施例3：重量％混合高卤化物18，改性树脂10，溶剂54.15，防锈颜料5，着色颜料6.5，复合防火剂6，助剂1.35。
各组份的配比为：以重量份计，混合高卤化物：改性高氯化聚乙烯14份，氯化石蜡3份；醇酸树脂10份，二甲苯45份，醋酸丁酯8.15份，三聚磷酸铝5份，钛青兰1.5份，钛白粉5份，锑白2份，阻燃剂FB2份，聚磷酸铵2份；环氧氯丙烷0.25份，流平剂BYK-306为0.2份，分散剂963为0.2份，防浮色发花剂0.4份，紫外线吸收剂0.3份。
实施例4：重量％混合高卤化物21，改性树脂10，溶剂54.6，复合防锈颜料6.5，着色颜料3.5，复合防火剂4，助剂0.4。
各组份的配比为：以重量份计，混合高卤化物：改性高氯化聚乙烯15份，氯化石蜡3份；丙烯酸树脂10份，二甲苯43份，醋酸丁酯11.6份，碳黑3.5份，磷酸锌4.5份，三聚磷酸铝2份，锑白2份，QD-SPA(Z)阻燃剂2份，防浮色发花剂0.4份。
对照实施例：重量％，混合高氯化物23，溶剂59.95，防锈颜料6，着色颜料6，防火剂4，助剂1.05。
各组份配比为：以重份计，改性高氯化聚乙烯4份，过氯乙烯4份，氯化石蜡7份，四氯乙烯59.95份，磷酸锌6份，铁红6份，锑白2份，QD-SPA(Z)阻燃剂2份，氧氯丙烷0.25份，分散剂0.2份，防浮色发花剂0.3份，紫外线吸收剂0.3份。此配方无论是液体状态，还是涂刷后的漆膜见明火均不燃烧。
先将高卤化物与溶剂加入溶解釜搅拌溶解后，放入配料罐中，加入改性树脂混合均匀，再加入防锈颜料、着色颜料、防火剂以及助剂在800-1200转/分的转速下搅拌分散，然后用砂磨机研磨至细度不大于50μm，最后用溶剂调整粘度不小于40s，采用涂-4杯，温度为25℃，过滤包装即为成品。
本发明中，流平剂型号为BYK-306，为德国毕克公司产品；分散剂型号为963，为德国汉高公司产品；防浮色发花剂型号为D201，为上海树脂厂产品；阻燃剂FB为无机研究所产品；阻燃剂型号为QD-SPA(Z)，为齐达科技开发公司产品；紫外线吸收剂型号为UV-9，为武汉助剂厂产品。

Claims (2)

1、一种免除锈防腐防火漆，其特征在于：它由以下组份组成：
混合高卤化物             15-30重量％
改性树脂                 0-20重量％
溶剂                     53.85-65重量％
复合防锈颜料             3-15重量％
着色颜料                 3-15重量％
复合防火剂               3-10重量％
助剂                     0.2-1.5重量％
其中：混合高卤化物为：以重量份计，改性高氯化聚乙烯10-18份，氯化橡胶0-5份，氯磺化聚乙烯0-3份，氯化石蜡4-10份；
改性树脂为：醇酸树脂0-15份，丙烯酸树脂0-15份；
溶剂为：二甲苯41-50份，醋酸丁酯8.15-15份；
复合防锈颜料为：磷酸锌2-8份，三聚磷酸铝2-10份，ST防锈颜料2-6份；
着色颜料为：红色为铁红、钼铬红，兰色为华兰和酞青兰，白色为钛白粉，黄色为铬黄，黑色为碳黑；
复合防火剂为：QD-SPA(Z)阻燃剂1-6份，锑白2-4份，聚磷酸铵1-5份，阻燃剂FB1-3份；
助剂为：流平剂BYK-306，0.1-0.5份，分散剂963，0.1-0.4份，防浮色发花剂0.2-0.5份，环氧氯丙烷0.2-0.3份，紫外线吸收剂0.3-0.5份。
2、一种制备权利要求1所述的免除锈防腐防火漆的方法，其特征在于：先将高卤化物与溶剂加入溶解釜中搅拌溶解后，放入配料罐中，加入改性树脂混合均匀，再加入防锈颜料、着色颜料、防火剂以及助剂在800-1200转/分的转速下搅拌分散，然后用砂磨机研磨至细度不大于50μm，最后用溶剂调整粘度不小于40s，采用涂-4杯，温度为25℃，过滤包装即为成品。
CNB011142146A 2001-05-22 2001-05-22 免除锈防腐防火漆 Expired - Fee Related CN1148426C (zh)