CN114560645A - 一种用于酷寒天气聚羧酸减水剂母液及其制备方法 - Google Patents
一种用于酷寒天气聚羧酸减水剂母液及其制备方法 Download PDFInfo
- Publication number
- CN114560645A CN114560645A CN202210284096.3A CN202210284096A CN114560645A CN 114560645 A CN114560645 A CN 114560645A CN 202210284096 A CN202210284096 A CN 202210284096A CN 114560645 A CN114560645 A CN 114560645A
- Authority
- CN
- China
- Prior art keywords
- parts
- mother liquor
- percent
- dropwise adding
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于酷寒天气聚羧酸减水剂母液，由以下质量百分比的原料组分制成：聚醚大单体：34‑36％；不饱和脂肪酸：2‑4.2％；缓释单体：0.5‑4％；功能性小单体：0.5‑1％；冰点调节剂：10‑30％；醇醚助剂：0.5‑1％；氧化剂：0.15‑0.3％；还原剂0.003‑0.06％；链转移剂：0.1‑0.5％；pH调节剂：0‑1.5％；余量为去离子水。优点在于：本发明向聚羧酸减水剂母液分子结构中引入醇类冰点调节剂和醇醚助剂从而达到气温在‑30℃至‑39.9℃的酷寒天气下不结冰凝固(现有技术中普通的40％固含量的聚羧酸减水剂母液在气温处于‑10℃至‑15℃就会结冰凝固)从而解决了我国严寒地区冬季聚羧酸减水剂母液容易结冰凝固、失去流动性，从而不利于储存、应用、运输的问题。
Description
技术领域
本发明涉及混凝土外加剂技术领域，具体是指一种用于酷寒天气聚羧酸减水剂母液及其制备方法。
背景技术
聚羧酸减水剂，全名聚羧酸系高性能减水剂，又叫聚羧酸超塑化剂，是一种新型高分子建筑材料，广泛应用于高速铁路、路桥、水利、商品混凝土、装配式建筑及混凝土预制构件等涉及到水泥混凝土的行业。聚羧酸减水剂添加到水泥混凝土中，在减少水泥使用量的基础上，还可以明显的增加水泥混凝土的工作性能、力学性能、耐久性能等。
聚羧酸减水剂是一种高分子化合物水溶液，聚羧酸减水剂通常包括聚羧酸减水剂母液和聚羧酸减水剂成品。行业中通常把固含量(有效物质含量)在35％以上的聚羧酸减水剂叫做聚羧酸减水剂母液，而市面上的聚羧酸减水剂母液主要以40％、50％为主，聚羧酸减水剂母液通常是半成品。而把加入一定量聚羧酸减水剂母液、缓凝剂、增稠剂、早强剂、防冻剂、引气剂等其他组分复配出来用于销售和应用的水溶液混合物叫聚羧酸减水剂成品，也有叫泵送剂的。或者说聚羧酸减水剂母液是按一定的化学工艺合成出后未经加工的产品，而聚羧酸减水剂成品是不止含一种功能组分，经过再加工、复配的产品。聚羧酸减水剂除有效物质之外的其他物质主要是溶剂水，这就导致聚羧酸减水剂不耐冻，在温度0℃以下逐渐结冰凝固，从而给储存、运输、施工造成很大的麻烦，为了完成在0℃以下气温环境下施工，这就要求聚羧酸减水剂具有防冻功能。
通常的防冻型聚羧酸减水剂是针对聚羧酸减水剂成品的角度入手研究的，如加入无机盐氯化钙、氯化钠、氯化钾、氯化铝、硫酸钠、硫代硫酸钠、硫酸钙、硫酸铝、硫酸铝钾、硝酸钙、亚硝酸钙、亚硝酸钠等，有机物三乙醇胺、三异丙醇胺。尿素、甲醇、乙二醇等。
专利CN200910061196.4一种早强防冻型聚羧酸盐高性能减水剂及制备方法，其中以重量百分比计，聚羧酸盐占6％～14％，早强防冻剂占4％～16％，引气剂占0.3％～0.8％，所用早强防冻组分为：三乙醇胺∶三异丙醇胺∶甲酸钙∶硝酸钙∶乙二醇＝0.1∶0.1∶3∶3∶2，所用引气剂由松香皂类引气剂与十二烷基苯酸钠复合而成。
专利CN201110450290.6一种防冻型混凝土减水剂，一种防冻型混凝土减水剂，其中物质按重量百分比混合而成：聚羧酸减水剂30.0％～50.0％、无机钠盐占1.0％～15.0％、无机钙盐占0.0～5.0％、低分子醇占0.0～10.0％、引气剂占0.05％～0.5％、缓凝剂占0.0～5.0％、水40.0％～65.0％。
专利CN201410223770.2一种防冻型聚羧酸系复合泵送减水剂及其用途，按照重量百分比计，聚羧酸高效减水剂8-12％、塑化成分0.5-1％、引气剂0.05-0.1％、三乙醇胺0.8-1.5％、无机早强组分8-15％、有机防冻组分8-15％，余量为水。
以上三种发明都是在聚羧酸减水剂母液的基础上加入各种不同功能组分的有机盐、无机盐、无机物混合出来的，属于再加工、复配，不属于化学合成。
专利CN201811432612.2一种温度敏感性小的聚羧酸减水剂，按重量份数计，包括甲基丙烯酸10-30份、碱性催化剂1-10份、防冻剂60-90份，自由基引发剂为AIBN0.1-0.3份、丙烯酸30-90份、聚乙二醇单甲醚150-450份；所述减水剂还包括火山灰10-30份。该发明从化学合成的角度，合成出一种新型聚羧酸减水剂母液，解决了不同施工环境温度中，减水剂仍能保持较高的减水率，以及其他性能也能维持在正常水平的问题。但是没有解决严寒地区冬季，特别是酷寒天气(气温在-30℃至-39.9℃)，甚至是极寒天气(气温低于-40℃)聚羧酸减水剂母液容易结冰凝固、失去流动性，从而不利于储存、应用、运输的问题。因此，亟待研发出一种基于化学合成方法，制备出适用于严寒地区冬季，特别是酷寒天气，甚至是极寒天气的聚羧酸减水剂母液，以解决现有聚羧酸减水剂在温度0℃以下逐渐结冰凝固的技术问题。
发明内容
本发明要解决的技术问题就是克服以上的技术缺陷，提供一种用于酷寒天气聚羧酸减水剂母液及其制备方法。
为解决上述技术问题，本发明提供的技术方案为：一种用于酷寒天气聚羧酸减水剂母液，由以下质量百分比的原料组分制成：聚醚大单体：34-36％；不饱和脂肪酸：2-4.2％；缓释单体：0.5-4％；功能性小单体：0.5-1％；冰点调节剂：10-30％；醇醚助剂：0.5-1％；氧化剂：0.15-0.3％；还原剂0.003-0.06％；链转移剂：0.1-0.5％；pH调节剂：0-1.5％；余量为去离子水。
进一步的，所述的聚醚大单体为甲基烯丙基聚氧乙烯醚、异戊烯基聚氧乙烯醚、乙二醇单乙烯基聚氧乙烯醚、4-羟丁基乙烯基聚氧乙烯醚中的一种或两种以上的组合，其相对分子质量为2400-4000。
进一步的，所述的不饱和脂肪酸为丙烯酸、甲基丙烯酸、衣康酸、马来酸、富马酸中的一种或两种以上的组合。
进一步的，所述的缓释单体为丙烯酸羟乙酯、丙烯酸羟丙酯、甲基丙烯酸羟乙酯、甲基丙烯酸羟丙酯、甲基丙烯酸缩水甘油酯中的一种或两种以上的组合。
进一步的，所述的功能性小单体为丙烯酰胺、烯丙基磺酸钠、甲基丙烯磺酸钠、2-丙烯酰胺-2-甲基丙磺酸中的一种或两种以上的组合。
进一步的，所述的冰点调节剂为乙二醇、丙二醇、二乙二醇、丙三醇、一缩二乙二醇中的一种或两种以上的组合。
进一步的，所述的醇醚助剂为丙二醇甲醚、丙二醇乙醚、丙二醇丙醚、二乙二醇甲醚、二乙二醇乙醚、二乙二醇丙醚、二乙二醇丁醚、一缩二丙二醇甲醚、一缩二丙二醇乙醚、一缩二丙二醇丙醚、一缩二丙二醇丁醚中的一种或两种以上的组合。
进一步的，所述的氧化剂为过硫酸铵、过硫酸钾、双氧水(27.5％)中的一种；
所述的还原剂为维生素C、D-异抗坏血酸、D-异抗坏血酸钠、还原剂E51、还原剂FF6、吊白块、硫酸亚铁、氯化亚铁中的一种或两种以上的组合。
进一步的，所述的链转移剂为巯基丙酸、巯基乙酸、巯基乙醇、次亚磷酸钠中的一种；所述的PH调节剂为片碱。
10.根据权利要求1所述的一种用于酷寒天气聚羧酸减水剂母液的制备方法，包括以下步骤：
1)以去离子水为溶剂，将34-36份的聚醚大单体置于反应釜中，连续搅拌至其完全溶解，反应釜中溶液温度控制在0-20℃之间；
2)然后加入5-10份冰点调节剂继续搅拌，再加入0.15-0.3份氧化剂继续搅拌，接着加入0.5-1份不饱和脂肪酸，然后先滴加0.003-0.05份还原剂、0.1-0.5份链转移剂的水溶液A液，并在5-10min后开始滴加3-3.7份不饱和脂肪酸、0.5-1份功能性小单体、0.5-1份醇醚助剂的水溶液B液(1-1.5份不饱和脂肪酸、0.5-4份缓释单体、0.5-1份醇醚助剂的水溶液B液)；其中，所述的滴加为匀速滴加，A液、B液在1-2.75h滴加完成；
3)与2)属于同一步骤，或者加入5-10份冰点调节剂继续搅拌，再加入0.15-0.3份氧化剂继续搅拌，接着加入0.5-1份不饱和脂肪酸，再加入0.003-0.05份还原剂继续搅拌，然后先滴加0.003-0.05份还原剂、0.1-0.5份链转移剂的水溶液A液，并在5-10min后开始滴加3-3.7份不饱和脂肪酸、0.5-1份功能性小单体、0.5-1份醇醚助剂的水溶液B液(1-1.5份不饱和脂肪酸、0.5-4份缓释单体、0.5-1份醇醚助剂的水溶液B液)；其中，所述的滴加为匀速滴加，A液、B液在1.5-1.65h滴加完成；
4)与2)属于同一步骤，或者加入5-10份冰点调节剂继续搅拌，再加入0.15-0.3份氧化剂继续搅拌，接着加入0.5-1份不饱和脂肪酸，再加入0.003-0.05份还原剂继续搅拌，然后先滴加0.003-0.05份还原剂、0.1-0.5份链转移剂的水溶液A液，并在5-10min后开始滴加3-3.7份不饱和脂肪酸、0-0.75份pH调节剂、0.5-1份功能性小单体、0.5-1份醇醚助剂的水溶液B液(1-1.5份不饱和脂肪酸、0.5-4份缓释单体、0.5-1份醇醚助剂的水溶液B液)；其中，所述的滴加为匀速滴加，A液、B液在1-1.16h滴加完成；
5)与2)属于同一步骤，或者加入5-10份冰点调节剂继续搅拌，再加入0.15-0.3份氧化剂继续搅拌，接着加入0.5-1份不饱和脂肪酸，再加入0.003-0.05份还原剂、0.1-0.5份链转移剂继续搅拌，然后先滴加0.003-0.05份还原剂的水溶液A液，并在5-10min后开始滴加3-3.7份不饱和脂肪酸、0-0.75份pH调节剂、0.5-1份功能性小单体、0.5-1份醇醚助剂的水溶液B液(1-1.5份不饱和脂肪酸、0.5-4份缓释单体、0.5-1份醇醚助剂的水溶液B液)；其中，所述的滴加为匀速滴加，A液、B液在1-1.16h滴加完成；
6)滴加完后，反应釜保温反应1h，然后加入0-1.5份的pH调节剂搅拌均匀，接着加入15-25份冰点调节剂，最终得到用于酷寒天气聚羧酸减水剂母液。
本发明与现有技术相比的优点在于：本发明向聚羧酸减水剂母液分子结构中引入醇类冰点调节剂和醇醚助剂从而达到气温在-30℃至-39.9℃的酷寒天气下不结冰凝固(现有技术中普通的40％固含量的聚羧酸减水剂母液在气温处于-10℃至-15℃就会结冰凝固)，甚至在气温-40℃至-42℃的极寒天气也不结冰凝固的目的，从而解决了我国严寒地区(东北三省、内蒙古、新疆北部、西藏北部、青海等地区)冬季，特别是酷寒天气(气温在-30℃至-39.9℃)、极寒天气(气温低于-40℃)聚羧酸减水剂母液容易结冰凝固、失去流动性，从而不利于储存、应用、运输的问题。
具体实施方式
下面进一步说明本发明的具体实施方式。
实施例1
一种用于酷寒天气聚羧酸减水剂母液及其制备方法，由下述各组分，经水溶液自由基聚合而成，原料总质量份为1000，各组分在制备时的参数如下：
底料：去离子水290份、甲基烯丙基聚氧乙烯醚(相对分子质量2400)340份、乙二醇50份、过硫酸铵2份、丙烯酸8份；
A液：维生素C0.5份、巯基丙酸1.5份、去离子水36份；
B液：丙烯酸32份、烯丙基磺酸钠5份、丙二醇甲醚5份、去离子水30份；
底料按照操作步骤加入后，控制反应釜底料溶液温度在18-20℃之间，然后先滴加A液，5min后滴加B液，A液滴加165min，B液滴加150min，A液滴加结束之后保温反应1h；
保温结束后加入乙二醇200份，搅拌均匀得到用于酷寒天气聚羧酸减水剂母液。
实施例2
一种用于酷寒天气聚羧酸减水剂母液及其制备方法，由下述各组分，经水溶液自由基聚合而成，原料总质量份为1000，各组分在制备时的参数如下：
底料：去离子水290份、异戊烯基聚氧乙烯醚(相对分子质量3000)340份、丙二醇50份、双氧水1.5份、丙烯酸10份；
A液：维生素C0.5份、巯基丙酸1.4份、去离子水30份；
B液：丙烯酸10份、丙烯酸羟乙酯40份、丙烯酸羟丙酯10份、丙二醇乙醚5份、去离子水13份；
底料按照操作步骤加入后，控制反应釜底料溶液温度在18-20℃之间，然后先滴加A液，5min后滴加B液，A液滴加165min，B液滴加150min，A液滴加结束之后保温反应1h；
保温结束后加入丙二醇200份，搅拌均匀得到用于酷寒天气聚羧酸减水剂母液。
实施例3
一种用于酷寒天气聚羧酸减水剂母液及其制备方法，由下述各组分，经水溶液自由基聚合而成，原料总质量份为1000，各组分在制备时的参数如下：
底料：去离子水280份、甲基烯丙基聚氧乙烯醚(相对分子质量2400)170份、异戊烯基聚氧乙烯醚(相对分子质量2400)170份、二乙二醇60份、双氧水1.5份、丙烯酸8份、硫酸亚铁0.05份与10份去离子水的水溶液；
A液：还原剂E51 0.5份、巯基乙醇1.2份、去离子水36份；
B液：丙烯酸32份、丙烯酰胺5份、丙二醇丙醚5份、去离子水30.8份；
底料按照操作步骤加入后，控制反应釜底料溶液温度在18-20℃之间，然后先滴加A液，5min后滴加B液，A液滴加100min，B液滴加90min，A液滴加结束之后保温反应1h；
保温结束后加入乙二醇190份，搅拌均匀得到用于酷寒天气聚羧酸减水剂母液。
实施例4
一种用于酷寒天气聚羧酸减水剂母液及其制备方法，由下述各组分，经水溶液自由基聚合而成，原料总质量份为1000，各组分在制备时的参数如下：
底料：去离子水280份、异戊烯基聚氧乙烯醚(相对分子质量2400)340份、丙三醇40份、双氧水1.5份、丙烯酸8份，硫酸亚铁0.05份与10份去离子水的水溶液；
A液：D-异抗坏血酸0.3份、巯基乙醇1份、去离子水30份；
B液：丙烯酸8份、丙烯酸羟乙酯40份、甲基丙烯酸羟丙酯5份、甲基丙烯酸缩水甘油酯5份、二乙二醇甲醚5份、去离子水16.15份；
底料按照操作步骤加入后，控制反应釜底料溶液温度在18-20℃之间，然后先滴加A液，5min后滴加B液，A液滴加100min，B液滴加90min，A液滴加结束之后保温反应1h；
保温结束后加入丙二醇210份，搅拌均匀得到用于酷寒天气聚羧酸减水剂母液。
实施例5
一种用于酷寒天气聚羧酸减水剂母液及其制备方法，由下述各组分，经水溶液自由基聚合而成，原料总质量份为1000，各组分在制备时的参数如下：
底料：去离子水245份、异戊烯基聚氧乙烯醚(相对分子质量2400)340份、二乙二醇100份、双氧水2份、丙烯酸10份、硫酸亚铁0.05份与10份去离子水的水溶液；
A液：D-异抗坏血酸钠0.35份、巯基丙酸1.5份、去离子水30份；
B液：丙烯酸30份、甲基丙烯酸缩水甘油酯5份、二乙二醇乙醚3份、一缩二丙二醇甲醚3份、去离子水20份；
底料按照操作步骤加入后，控制反应釜底料溶液温度在18-20℃之间，然后先滴加A液，5min后滴加B液，A液滴加100min，B液滴加90min，A液滴加结束之后保温反应1h；
保温结束后加入乙二醇200份，搅拌均匀得到用于酷寒天气聚羧酸减水剂母液。
实施例6
一种用于酷寒天气聚羧酸减水剂母液及其制备方法，由下述各组分，经水溶液自由基聚合而成，原料总质量份为1000，各组分在制备时的参数如下：
底料：去离子水275份异戊烯基聚氧乙烯醚(相对分子质量3000)340份、乙二醇55份、双氧水2份、丙烯酸8份，硫酸亚铁0.05份与10份去离子水的水溶液；
A液：D-异抗坏血酸钠0.4份、巯基乙醇1份、去离子水30份；
B液：丙烯酸8份、丙烯酸羟乙酯40份、甲基丙烯酸缩水甘油酯10份、一缩二丙二醇乙醚5份、丙二醇甲醚5份、去离子水15.55份；
底料按照操作步骤加入后，控制反应釜底料溶液温度在18-20℃之间，然后先滴加A液，5min后滴加B液，A液滴加100min，B液滴加90min，A液滴加结束之后保温反应1h；
保温结束后加入丙二醇195份，搅拌均匀得到用于酷寒天气聚羧酸减水剂母液。
实施例7
一种用于酷寒天气聚羧酸减水剂母液及其制备方法，由下述各组分，经水溶液自由基聚合而成，原料总质量份为1000，各组分在制备时的参数如下：
底料：去离子水288份、4-羟丁基乙烯基聚氧乙烯醚(相对分子质量4000)350份、乙二醇45份、双氧水2份、丙烯酸10份、硫酸亚铁0.03份与10份去离子水的水溶液；
A液：D-异抗坏血酸钠0.4份、巯基丙酸1.5份、去离子水30份；
B液：丙烯酸30份、一缩二丙二醇丙醚8份、去离子水20.07份；
底料按照操作步骤加入后，反应全程控制反应釜中溶液温度在5-25℃之间，然后先滴加A液，5min后滴加B液，A液滴加70min，B液滴加60min，A液滴加结束之后保温反应1h；
保温结束后加入乙二醇205份，搅拌均匀得到用于酷寒天气聚羧酸减水剂母液。
实施例8
一种用于酷寒天气聚羧酸减水剂母液及其制备方法，由下述各组分，经水溶液自由基聚合而成，原料总质量份为1000，各组分在制备时的参数如下：
底料：去离子水265份、乙二醇单乙烯基聚氧乙烯醚(相对分子质量3000)350份、乙二醇45份、双氧水2.5份、丙烯酸8份、硫酸亚铁0.03份与10份去离子水的水溶液、次亚磷酸钠5份；
A液：吊白块0.5份、巯基乙醇1份、去离子水30份；
B液：丙烯酸28份、片碱7.5份、去离子水37.47份；
底料按照操作步骤加入后，反应全程控制反应釜中溶液温度在5-25℃之间，然后先滴加A液，5min后滴加B液，A液滴加65min，B液滴加60min，A液滴加结束之后保温反应1h；
保温结束后加入丙二醇205份、丙二醇甲醚5份，搅拌均匀得到用于酷寒天气聚羧酸减水剂母液。
实施例9
一种用于酷寒天气聚羧酸减水剂母液及其制备方法，由下述各组分，经水溶液自由基聚合而成，原料总质量份为1000，各组分在制备时的参数如下：
底料：去离子水270份、乙二醇单乙烯基聚氧乙烯醚(相对分子质量3000)340份、丙二醇45份、双氧水2.0份、丙烯酸8份、硫酸亚铁0.03份与10份去离子水的水溶液、一缩二丙二醇丁醚5份；
A液：还原剂FF6 0.55份、巯基乙醇1份、去离子水30份；
B液：丙烯酸8份、丙烯酸羟乙酯40份、丙烯酰胺10份、去离子水20.42份；
底料按照操作步骤加入后，反应全程控制反应釜中溶液温度在5-25℃之间，然后先滴加A液，5min后滴加B液，A液滴加65min，B液滴加60min，A液滴加结束之后保温反应1h；
保温结束后加入乙二醇205份、二乙二醇甲醚5份，搅拌均匀得到用于酷寒天气聚羧酸减水剂母液。
本发明向聚羧酸减水剂母液分子结构中引入醇类冰点调节剂和醇醚助剂从而达到气温在-30℃至-39.9℃的酷寒天气下不结冰凝固的目的，而普通的40％固含量的聚羧酸减水剂母液在气温处于-10℃至-15℃就会结冰凝固。本发明在气温-40℃至-42℃的极寒天气也适应。本发明开发对象是聚羧酸减水剂母液，而已有类似功能的专利针对的是聚羧酸减水剂成品，二者概念不同。本发明向聚羧酸减水剂母液分子结构中引入的是醇、醇醚类有机物，而已有类似功能的专利是向聚羧酸减水剂成品复配过程中加入无机盐、有机盐等物质。
本发明提供实施例应用性能对比试验如下：
本性能试验使用普通C30混凝土，减水剂由6.8％聚羧酸减水剂母液1和6.8％聚羧酸减水剂母液2复合而成，聚羧酸减水剂母液具体使用情况见表1；在减水剂掺量为1％时，根据GB 8076-2008《混凝土外加剂》测其混凝土减水率；根据GB/T 50080-2016《普通混凝土拌合物性能试验方法标准》测试混凝土初始坍落度、1h坍落度、初始扩展度、1h扩展度；根据GB/T 50081-2019《混凝土物理力学性能试验方法标准》检测混凝土7d抗压强度和28d抗压强度。
混凝土实验水泥为亚泰PO.42.5；Ⅱ级粉煤灰；河砂，细度模数2.8；10-20mm级配碎石和16-31.5mm级配碎石；搅拌时间2分钟。混凝土配合比如表2，混凝土试验结果见表3，聚羧酸减水剂抗冻试验结果见表4。
表1减水剂使用情况表
表2混凝土配合比(kg/m3)
| 水泥 | 粉煤灰 | 河砂 | 碎石(10-20mm) | 碎石(16-31.5mm) | 水 | 减水剂掺量(％) |
| 320 | 60 | 773 | 747 | 320 | 164 | 1.0 |
表3不同实施例混凝土性能对比试验
表4不同实施例的抗冻性能试验
以上对本发明及其实施方式进行了描述，这种描述没有限制性，具体实施方式中所示的也只是本发明的一部分实施例，而不是全部的实施例，并非穷举。总而言之如果本领域的普通技术人员受其启示，在不脱离本发明创造宗旨的情况下，不经创造性的设计出与该技术方案相似的结构方式及实施例，均应属于本发明的保护范围。
Claims (10)
1.一种用于酷寒天气聚羧酸减水剂母液，其特征在于，由以下质量百分比的原料组分制成：聚醚大单体：34-36％；不饱和脂肪酸：2-4.2％；缓释单体：0.5-4％；功能性小单体：0.5-1％；冰点调节剂：10-30％；醇醚助剂：0.5-1％；氧化剂：0.15-0.3％；还原剂0.003-0.06％；链转移剂：0.1-0.5％；pH调节剂：0-1.5％；余量为去离子水。
2.根据权利要求1所述的一种用于酷寒天气聚羧酸减水剂母液，其特征在于，所述的聚醚大单体为甲基烯丙基聚氧乙烯醚、异戊烯基聚氧乙烯醚、乙二醇单乙烯基聚氧乙烯醚、4-羟丁基乙烯基聚氧乙烯醚中的一种或两种以上的组合，其相对分子质量为2400-4000。
3.根据权利要求1所述的一种用于酷寒天气聚羧酸减水剂母液，其特征在于，所述的不饱和脂肪酸为丙烯酸、甲基丙烯酸、衣康酸、马来酸、富马酸中的一种或两种以上的组合。
4.根据权利要求1所述的一种用于酷寒天气聚羧酸减水剂母液，其特征在于，所述的缓释单体为丙烯酸羟乙酯、丙烯酸羟丙酯、甲基丙烯酸羟乙酯、甲基丙烯酸羟丙酯、甲基丙烯酸缩水甘油酯中的一种或两种以上的组合。
5.根据权利要求1所述的一种用于酷寒天气聚羧酸减水剂母液，其特征在于，所述的功能性小单体为丙烯酰胺、烯丙基磺酸钠、甲基丙烯磺酸钠、2-丙烯酰胺-2-甲基丙磺酸中的一种或两种以上的组合。
6.根据权利要求1所述的一种用于酷寒天气聚羧酸减水剂母液，其特征在于，所述的冰点调节剂为乙二醇、丙二醇、二乙二醇、丙三醇、一缩二乙二醇中的一种或两种以上的组合。
7.根据权利要求1所述的一种用于酷寒天气聚羧酸减水剂母液，其特征在于，所述的醇醚助剂为丙二醇甲醚、丙二醇乙醚、丙二醇丙醚、二乙二醇甲醚、二乙二醇乙醚、二乙二醇丙醚、二乙二醇丁醚、一缩二丙二醇甲醚、一缩二丙二醇乙醚、一缩二丙二醇丙醚、一缩二丙二醇丁醚中的一种或两种以上的组合。
8.根据权利要求1所述的一种用于酷寒天气聚羧酸减水剂母液，其特征在于，所述的氧化剂为过硫酸铵、过硫酸钾、双氧水(27.5％)中的一种；
所述的还原剂为维生素C、D-异抗坏血酸、D-异抗坏血酸钠、还原剂E51、还原剂FF6、吊白块、硫酸亚铁、氯化亚铁中的一种或两种以上的组合。
9.根据权利要求1所述的一种用于酷寒天气聚羧酸减水剂母液，其特征在于，所述的链转移剂为巯基丙酸、巯基乙酸、巯基乙醇、次亚磷酸钠中的一种；所述的PH调节剂为片碱。
10.根据权利要求1所述的一种用于酷寒天气聚羧酸减水剂母液的制备方法，其特征在于，包括以下步骤：
1)以去离子水为溶剂，将34-36份的聚醚大单体置于反应釜中，连续搅拌至其完全溶解，反应釜中溶液温度控制在0-20℃之间；
2)然后加入5-10份冰点调节剂继续搅拌，再加入0.15-0.3份氧化剂继续搅拌，接着加入0.5-1份不饱和脂肪酸，然后先滴加0.003-0.05份还原剂、0.1-0.5份链转移剂的水溶液A液，并在5-10min后开始滴加3-3.7份不饱和脂肪酸、0.5-1份功能性小单体、0.5-1份醇醚助剂的水溶液B液(1-1.5份不饱和脂肪酸、0.5-4份缓释单体、0.5-1份醇醚助剂的水溶液B液)；其中，所述的滴加为匀速滴加，A液、B液在1-2.75h滴加完成；
3)与2)属于同一步骤，或者加入5-10份冰点调节剂继续搅拌，再加入0.15-0.3份氧化剂继续搅拌，接着加入0.5-1份不饱和脂肪酸，再加入0.003-0.05份还原剂继续搅拌，然后先滴加0.003-0.05份还原剂、0.1-0.5份链转移剂的水溶液A液，并在5-10min后开始滴加3-3.7份不饱和脂肪酸、0.5-1份功能性小单体、0.5-1份醇醚助剂的水溶液B液(1-1.5份不饱和脂肪酸、0.5-4份缓释单体、0.5-1份醇醚助剂的水溶液B液)；其中，所述的滴加为匀速滴加，A液、B液在1.5-1.65h滴加完成；
4)与2)属于同一步骤，或者加入5-10份冰点调节剂继续搅拌，再加入0.15-0.3份氧化剂继续搅拌，接着加入0.5-1份不饱和脂肪酸，再加入0.003-0.05份还原剂继续搅拌，然后先滴加0.003-0.05份还原剂、0.1-0.5份链转移剂的水溶液A液，并在5-10min后开始滴加3-3.7份不饱和脂肪酸、0-0.75份pH调节剂、0.5-1份功能性小单体、0.5-1份醇醚助剂的水溶液B液(1-1.5份不饱和脂肪酸、0.5-4份缓释单体、0.5-1份醇醚助剂的水溶液B液)；其中，所述的滴加为匀速滴加，A液、B液在1-1.16h滴加完成；
5)与2)属于同一步骤，或者加入5-10份冰点调节剂继续搅拌，再加入0.15-0.3份氧化剂继续搅拌，接着加入0.5-1份不饱和脂肪酸，再加入0.003-0.05份还原剂、0.1-0.5份链转移剂继续搅拌，然后先滴加0.003-0.05份还原剂的水溶液A液，并在5-10min后开始滴加3-3.7份不饱和脂肪酸、0-0.75份pH调节剂、0.5-1份功能性小单体、0.5-1份醇醚助剂的水溶液B液(1-1.5份不饱和脂肪酸、0.5-4份缓释单体、0.5-1份醇醚助剂的水溶液B液)；其中，所述的滴加为匀速滴加，A液、B液在1-1.16h滴加完成；
6)滴加完后，反应釜保温反应1h，然后加入0-1.5份的pH调节剂搅拌均匀，接着加入15-25份冰点调节剂，最终得到用于酷寒天气聚羧酸减水剂母液。