CN114457262A - 一种抗海水腐蚀的铝合金材料 - Google Patents
一种抗海水腐蚀的铝合金材料 Download PDFInfo
- Publication number
- CN114457262A CN114457262A CN202210006140.4A CN202210006140A CN114457262A CN 114457262 A CN114457262 A CN 114457262A CN 202210006140 A CN202210006140 A CN 202210006140A CN 114457262 A CN114457262 A CN 114457262A
- Authority
- CN
- China
- Prior art keywords
- aluminum alloy
- alloy material
- percent
- less
- corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种铝合金材料，尤其是一种抗海水腐蚀的铝合金材料，由以下材料按照重量百分比组成：Si＜0.1％；Fe＜0.2％；Cu≤0.5％；Mn0.8‑1；Mg＜0.05％；杂质≤0.5％；其余为Al。本发明提供的一种抗海水腐蚀的铝合金材料采用抗腐蚀配方制成，抗海风腐蚀性能好，使用寿命长，达到现有的3003铝合金使用寿命的一倍以上。同样测试条件下，腐蚀坑的数量明显少于现有铝合金材料，并且腐蚀深度明显小于现有的3003铝合金材料。
Description
技术领域
本发明涉及一种铝合金材料，尤其是一种抗海水腐蚀的铝合金材料。
背景技术
由于风力发电部件元器件需要散热，目前主要采用3003铝合金制成的散热器进行散热，3003铝合金为AL-Mn系合金，是应用最广的一种防锈铝。随着风力发电的发展，海上风力发电越来越多。由于海上风电长期受海风、海上的腐蚀，使用寿命短，特别是铝制的散热器，容易腐蚀，更换频率高。
发明内容
为解决上述问题，本发明提供一种能够有效抗海水腐蚀，使用寿命长上的一种抗海水腐蚀的铝合金材料，具体技术方案为：
一种抗海水腐蚀的铝合金材料，由以下材料按照重量百分比组成：Si＜0.1％；Fe＜0.2％；Cu≤0.5％；Mn0.8-1；Mg＜0.05％；杂质≤0.5％；其余为Al。
与现有技术相比本发明具有以下有益效果：
本发明提供的一种抗海水腐蚀的铝合金材料采用抗腐蚀配方制成，抗海风腐蚀性能好，使用寿命长，达到现有的3003铝合金使用寿命的一倍以上。同样测试条件下，腐蚀坑的数量明显少于现有铝合金材料，并且腐蚀深度明显小于现有的3003铝合金材料。
附图说明
图1是本发明与现有3003在SWAAT测试下的腐蚀坑的对比图；
图2是本发明与现有3003在SWAAT测试下的截面金相图。
具体实施方式
现结合附图对本发明作进一步说明。
实施例一
一种抗海水腐蚀的铝合金材料，由以下材料按照重量百分比组成：Si0.09％；Fe0.19％；Cu0.5％；Mn0.8％；Mg0.04％；Zn0.019％；Ti0.018％；Pb0.09％；杂质0.5％；其余为Al。
实施例二
一种抗海水腐蚀的铝合金材料，由以下材料按照重量百分比组成：Si0.03％；Fe0.09％；Cu0.2％；Mn0.9％；Mg0.009％；Zn0.018％；Ti0.017％；Pb0.08％；；杂质0.4％；其余为Al。
实施例三
一种抗海水腐蚀的铝合金材料，由以下材料按照重量百分比组成：Si0.009％；Fe0.09％；Cu0.1％；Mn0.95％；Mg0.008％；Zn0.017％；Ti0.0185％；Pb0.07％；；杂质0.4％；其余为Al。
本发明的铝合金材料的制备方法为现有的常规制备方法制备，采用本发明的铝合金材料制成的散热器也是采用常规的挤出成型的方法制备。成型后的铝型材根据尺寸需要进行切割即可，可以直接使用，无需做表面处理。
如图1和图2所示，3003为现有的铝合金，本发明提供的铝合金为3003NF，经过SWAAT(循环酸性海水试验可靠性试验)10天，如图1所示，从表面上看3003腐蚀坑的数目较多，截面金相显示腐蚀深度达436微米，而3003NF腐蚀坑数目较少，最深的深度约200微米，明显优于现有的3003，使用寿命达到现有铝合金的一倍以上。
3003NF材料对Si、Fe、Cu等元素的含量进行严格控制，采用合适的配比，能够避免Al3Fe、Cu元素颗粒在样品表面形成缺陷，破坏氧化膜，导致点腐蚀，同时避免Al2Cu元素在晶界偏析，导致晶间腐蚀，从而提高材料的腐蚀寿命。
现有技术中，主要通过对铝合金表面进行涂覆防腐层，从而提高抗腐蚀性能。但是防腐层成本较高，并且防腐层如果产生破损，会导致防腐蚀层迅速失效，因此需要小心装配，避免防腐层产生破损。而本发明通过从铝合金本身进行抗腐蚀能力的提高，从而降低对外界防腐的依赖，实现从根源上提高抗腐蚀能力，对后续加工和装配要求低，并且降低了成本。
以上结合具体实施例描述了本发明的技术原理。这些描述只是为了解释本发明的原理，而不能以任何方式解释为对本发明保护范围的限制。基于此处的解释，本领域的技术人员不需要付出创造性的劳动即可联想到本发明的其它具体实施方式，这些方式都将落入本发明权利要求的保护范围之内。
Claims (3)
1.一种抗海水腐蚀的铝合金材料，其特征在于，由以下材料按照重量百分比组成：
Si＜0.1％；(＜0.005)
Fe＜0.2％；(＜0.09)
Cu≤0.5％；(＜0.01)
Mn0.8-1；
Mg＜0.05％；(＜0.005)
Ni＜0.01％；(＜0.008)
Zn＜0.02％；(＜0.015)
Ti＜0.02％；
Pb＜0.1％；(＜0.05)
杂质≤0.5％；
其余为Al。
2.根据权利要求1所述的一种抗海水腐蚀的铝合金材料，其特征在于，
Si＜0.05％；(＜0.005)
Fe＜0.1％；(＜0.09)
Cu≤0.2％；(＜0.01)
Mn0.8-1；
Mg＜0.01％；(＜0.005)
Ni＜0.01％；(＜0.008)
Zn＜0.02％；(＜0.015)
Ti＜0.02％；
Pb＜0.1％；(＜0.05)
杂质≤0.5％；
其余为Al。
3.根据权利要求2所述的一种抗海水腐蚀的铝合金材料，其特征在于，
Si＜0.01％；(＜0.005)
Fe＜0.1％；(＜0.09)
Cu≤0.1％；(＜0.01)
Mn0.8-1；
Mg＜0.01％；(＜0.005)
Ni＜0.01％；(＜0.008)
Zn＜0.02％；(＜0.015)
Ti＜0.02％；
Pb＜0.1％；(＜0.05)
杂质≤0.5％；
其余为Al。