CN114011685A - 高耐候抗沾污彩涂板制作方法 - Google Patents

高耐候抗沾污彩涂板制作方法 Download PDF

Info

Publication number
CN114011685A
CN114011685A CN202111242128.5A CN202111242128A CN114011685A CN 114011685 A CN114011685 A CN 114011685A CN 202111242128 A CN202111242128 A CN 202111242128A CN 114011685 A CN114011685 A CN 114011685A
Authority
CN
China
Prior art keywords
resistant
stain
weather
layer
high weather
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202111242128.5A
Other languages
English (en)
Inventor
张海锋
章泰鸣
黄子芬
甘名海
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHUHAI SPEEDBIRD PVC FILM LAMINATED METAL SHEET CO Ltd
Original Assignee
ZHUHAI SPEEDBIRD PVC FILM LAMINATED METAL SHEET CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHUHAI SPEEDBIRD PVC FILM LAMINATED METAL SHEET CO Ltd filed Critical ZHUHAI SPEEDBIRD PVC FILM LAMINATED METAL SHEET CO Ltd
Priority to CN202111242128.5A priority Critical patent/CN114011685A/zh
Publication of CN114011685A publication Critical patent/CN114011685A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高耐候抗沾污彩涂板制作方法，包括：步骤一、采用钢板作为基材，在基材的正面涂布底漆，待干燥后形成底漆层；步骤二、在底漆层上涂布面漆，待干燥后形成面漆层；步骤三、在面漆层上涂布高耐候抗沾污涂料，固化后形成高耐候抗沾污涂层，高耐候抗沾污涂料由基于含氟二醇及聚硅氧烷共聚改性聚酯的高耐候抗沾污涂料组合物所制得。底漆层能够提高基材的防腐能力、抗碱性以及面漆的附着力，增加面漆的丰富度，面漆层除了起到装饰作用和表观效果，还能提高基材的抗划伤性和光泽硬度，高耐候抗沾污涂层能提供很好的表面硬度，得到的彩涂板表面易清洁、抗沾污，可以抵抗绝大部分物质沾污，而且具有高耐候性，可以减缓老化。

Description

高耐候抗沾污彩涂板制作方法
技术领域
本发明涉及家电外壳和建筑墙板领域，特别涉及彩涂板。
背景技术
家用电器和室内装饰墙板常常会用到彩涂板，通常这类彩涂板会面临清洁问题，目前很多材质容易到沾污，不便清洁，导致家庭环境和厨房环境面临着各种各样的物质污染，若不能及时清洁掉，后期可能需要重新装修，成本很高。另外，彩涂板可能由于长期处于光照、冷热、风雨、潮湿等综合环境下，加速损坏、老化，因此，对材料的耐候性提出了更高的要求，传统的彩涂板已逐渐难以满足要求。
发明内容
本发明旨在至少解决现有技术中存在的技术问题之一。为此，本发明提出一种高耐候抗沾污彩涂板制作方法。
根据本发明实施例的高耐候抗沾污彩涂板制作方法，包括：步骤一、采用钢板作为基材，在所述基材的正面涂布底漆，待干燥后形成底漆层；步骤二、在所述底漆层上涂布面漆，待干燥后形成面漆层；步骤三、在所述面漆层上涂布高耐候抗沾污涂料，固化后形成高耐候抗沾污涂层，所述高耐候抗沾污涂料由基于含氟二醇及聚硅氧烷共聚改性聚酯的高耐候抗沾污涂料组合物所制得。
至少具有如下有益效果：本制作方法通过在基材的正面依次涂覆底漆、面漆和高耐候抗沾污涂料，底漆层能够提高基材的防腐能力、抗碱性以及面漆的附着力，增加面漆的丰富度，面漆层除了起到装饰作用和表观效果，还能提高基材的抗划伤性和光泽硬度，高耐候抗沾污涂层能提供很好的表面硬度，得到的彩涂板表面易清洁、抗沾污，可以抵抗绝大部分物质沾污，而且具有高耐候性，可以减缓老化。
根据本发明的一些实施例，在步骤一中，先对所述基材的正面和背面进行化学处理，分别形成第一化学处理层和第二化学处理层，然后再在所述第一化学处理层的正面涂布底漆。
根据本发明的一些实施例，所述底漆的干燥温度为210～224℃，干燥时间为30～40s。
根据本发明的一些实施例，所述底漆层的厚度为5～9μm。
根据本发明的一些实施例，在步骤二中，还在所述第二化学处理层上涂布耐指纹涂料或者导电油漆，与面漆同时进行干燥，分别形成背漆层和所述面漆层。
根据本发明的一些实施例，所述面漆的干燥温度为216～232℃，干燥时间为30～50s。
根据本发明的一些实施例，所述面漆层的厚度为12～15μm。
根据本发明的一些实施例，在步骤三中，在所述高耐候抗沾污涂层上贴合一层保护膜。
根据本发明的一些实施例，所述高耐候抗沾污涂料的固化温度为60～80℃，固化时间为30～50s。
根据本发明的一些实施例，所述高耐候抗沾污涂层的厚度为2～4μm。
附图说明
本发明的上述和/或附加的方面和优点从结合下面附图对实施例的描述中将变得明显和容易理解，其中：
图1为通过本发明实施例得到的彩涂板的结构示意图。
附图标记：基材1、第一化学处理层2、底漆层3、面漆层4、高耐候抗沾污涂层5、保护膜6、第二化学处理层7、背漆层8。
具体实施方式
下面详细描述本发明的实施例，所述实施例的示例在附图中示出，其中自始至终相同或类似的标号表示相同或类似的元件或具有相同或类似功能的元件。下面通过参考附图描述的实施例是示例性的，仅用于解释本发明，而不能理解为对本发明的限制。
在本发明的描述中，需要理解的是，涉及到方位描述，例如正面、背面等指示的方位或位置关系为基于附图所示的方位或位置关系，仅是为了便于描述本发明和简化描述，而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作，因此不能理解为对本发明的限制。
在本发明的描述中，如果有描述到第一、第二只是用于区分技术特征为目的，而不能理解为指示或暗示相对重要性或者隐含指明所指示的技术特征的数量或者隐含指明所指示的技术特征的先后关系。
本发明的描述中，除非另有明确的限定，涂覆、形成、贴合、粘贴等词语应做广义理解，所属技术领域技术人员可以结合技术方案的具体内容合理确定上述词语在本发明中的具体含义。
参照图1，本发明公开一种高耐候抗沾污彩涂板制作方法，包括以下步骤：
步骤一、采用钢板作为基材1，在基材1的正面涂布底漆，待干燥后形成底漆层3；
步骤二、在底漆层3上涂布面漆，待干燥后形成面漆层4；
步骤三、在面漆层4上涂布高耐候抗沾污涂料，固化后形成高耐候抗沾污涂层5，高耐候抗沾污涂料由基于含氟二醇及聚硅氧烷共聚改性聚酯的高耐候抗沾污涂料组合物所制得。
本制作方法通过在基材1的正面依次涂覆底漆、面漆和高耐候抗沾污涂料，底漆层3能够提高基材的防腐能力、抗碱性以及面漆的附着力，增加面漆的丰富度，面漆层4除了起到装饰作用和表观效果，还能提高基材的抗划伤性和光泽硬度。
需要说明的是，高耐候抗沾污涂料由基于含氟二醇及聚硅氧烷共聚改性聚酯的高耐候抗沾污涂料组合物所制得，基于含氟二醇及聚硅氧烷共聚改性聚酯的高耐候抗沾污涂料组合物具体可以是申请公布号为“CN111748279A”、名称为“基于含氟二醇及聚硅氧烷共聚改性聚酯的高耐候抗沾污涂料组合物及其制备方法”的发明申请中的基于含氟二醇及聚硅氧烷共聚改性聚酯的高耐候抗沾污涂料组合物。
使得高耐候抗沾污涂层5能提供很好的表面硬度，得到的彩涂板表面易清洁、抗沾污，可以抵抗绝大部分物质沾污，而且具有高耐候性，可以减缓老化。
在本发明的一些实施例中，在步骤一中，先对基材1的正面和背面进行化学处理，分别形成第一化学处理层2和第二化学处理层7，可以提高基材1的耐蚀性，然后再在第一化学处理层7的正面涂布底漆，第一化学处理层2能够提高基材1与底漆层3之间的附着力。
其中，底漆的干燥温度为210～224℃，干燥时间为30～40s，可以使得底漆干燥，形成底漆层3。在一些实施例中，底漆层3的厚度配置为5～9μm，可以保障本彩涂板的防腐效果。
此外，在步骤二中，还在第二化学处理层7上涂布耐指纹涂料或者导电油漆，与面漆同时进行干燥，分别形成背漆层8和面漆层4。背漆层8可以根据不同的需求而选择不同的类型，背漆层8可以由耐指纹涂料形成，使得本彩涂板的背面耐指纹，不容易被擦伤、划伤；背漆层8也可以由导电油漆形成，能够满足部分家电对本彩涂板背面的导电需求，此外，还可以在第二化学处理层7上涂布环氧背漆，能够使得彩涂板和发泡剂、胶粘剂等良好附着，利于加工。
其中，面漆的干燥温度为216～232℃，干燥时间为30～50s，可以使得面漆干燥，形成面漆层4。在一些实施例中，面漆层4的厚度配置为12～15μm，足以使得本彩涂板具有优良的装饰作用和光泽硬度。
参照图1，在本发明的一些实施例中，在步骤三中，在高耐候抗沾污涂层5上贴合一层保护膜6，保护膜6可以起到保护作用，防止表面被划伤、刮花。保护膜6具体可以是PE膜，在生产加工，运输，贮存和使用过程中不容易受污染、腐蚀或划伤，保护原有的光洁亮泽的表面。
在一些实施例中，高耐候抗沾污涂料的固化温度为60～80℃，固化时间为30～50s，可以使得高耐候抗沾污涂料固化，形成高耐候抗沾污涂层5。高耐候抗沾污涂层5的厚度配置为2～4μm，在不影响本彩涂板本身的弯折和加工性能的情况下，已足够提供良好的抗沾污性能和高耐候性能。
在本发明的一些实施例中，参照图1，本发明还公开一种高耐候抗沾污彩涂板制作方法，包括以下步骤：
步骤一、采用钢板作为基材1，对基材1的正面和背面进行化学处理，分别形成第一化学处理层2和第二化学处理层7，然后再在第一化学处理层7的正面涂布底漆，底漆的干燥温度为210～224℃，干燥时间为30～40s，待干燥后形成厚度为5～9μm的底漆层3；
步骤二、在第二化学处理层7上涂布耐指纹涂料或者导电油漆，在底漆层3上涂布面漆，同时进行干燥，干燥温度为216～232℃，干燥时间为30～50s，分别形成背漆层8和厚度为12～15μm的面漆层4；
步骤三、在面漆层4上涂布高耐候抗沾污涂料，高耐候抗沾污涂料的固化温度为60～80℃，固化时间为30～50s，固化后形成厚度为2～4μm的高耐候抗沾污涂层5，在高耐候抗沾污涂层5上贴合一层保护膜6，其中，高耐候抗沾污涂料由基于含氟二醇及聚硅氧烷共聚改性聚酯的高耐候抗沾污涂料组合物所制得。
上面结合附图对本发明实施例作了详细说明，但是本发明不限于上述实施例，在所属技术领域普通技术人员所具备的知识范围内，还可以在不脱离本发明宗旨的前提下作出各种变化。

Claims (10)

1.高耐候抗沾污彩涂板制作方法，其特征在于，包括：
步骤一、采用钢板作为基材，在所述基材的正面涂布底漆，待干燥后形成底漆层；
步骤二、在所述底漆层上涂布面漆，待干燥后形成面漆层；
步骤三、在所述面漆层上涂布高耐候抗沾污涂料，固化后形成高耐候抗沾污涂层，所述高耐候抗沾污涂料由基于含氟二醇及聚硅氧烷共聚改性聚酯的高耐候抗沾污涂料组合物所制得。
2.根据权利要求1所述的高耐候抗沾污彩涂板制作方法，其特征在于，在步骤一中，先对所述基材的正面和背面进行化学处理，分别形成第一化学处理层和第二化学处理层，然后再在所述第一化学处理层的正面涂布底漆。
3.根据权利要求1或2所述的高耐候抗沾污彩涂板制作方法，其特征在于，所述底漆的干燥温度为210～224℃，干燥时间为30～40s。
4.根据权利要求3所述的高耐候抗沾污彩涂板制作方法，其特征在于，所述底漆层的厚度为5～9μm。
5.根据权利要求2所述的高耐候抗沾污彩涂板制作方法，其特征在于，在步骤二中，还在所述第二化学处理层上涂布耐指纹涂料或者导电油漆，与面漆同时进行干燥，分别形成背漆层和所述面漆层。
6.根据权利要求1或5所述的高耐候抗沾污彩涂板制作方法，其特征在于，所述面漆的干燥温度为216～232℃，干燥时间为30～50s。
7.根据权利要求6所述的高耐候抗沾污彩涂板制作方法，其特征在于，所述面漆层的厚度为12～15μm。
8.根据权利要求1所述的高耐候抗沾污彩涂板制作方法，其特征在于，在步骤三中，在所述高耐候抗沾污涂层上贴合一层保护膜。
9.根据权利要求1或8所述的高耐候抗沾污彩涂板制作方法，其特征在于，所述高耐候抗沾污涂料的固化温度为60～80℃，固化时间为30～50s。
10.根据权利要求9所述的高耐候抗沾污彩涂板制作方法，其特征在于，所述高耐候抗沾污涂层的厚度为2～4μm。
CN202111242128.5A 2021-10-25 2021-10-25 高耐候抗沾污彩涂板制作方法 Pending CN114011685A (zh)