CN113995714B - 一种顺铂交联的蛋白水凝胶及制备方法 - Google Patents
一种顺铂交联的蛋白水凝胶及制备方法 Download PDFInfo
- Publication number
- CN113995714B CN113995714B CN202111279597.4A CN202111279597A CN113995714B CN 113995714 B CN113995714 B CN 113995714B CN 202111279597 A CN202111279597 A CN 202111279597A CN 113995714 B CN113995714 B CN 113995714B
- Authority
- CN
- China
- Prior art keywords
- cisplatin
- serum albumin
- protein hydrogel
- crosslinked protein
- hydrogel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种顺铂交联的蛋白水凝胶及制备方法。一种顺铂交联的蛋白水凝胶，主成分包括以下质量含量的组分：药物0.5％～5.0％、血清白蛋白6.0％～50.0％、溶媒介质47.0％～93.0％；其中血清白蛋白表面的羧基与药物形成配位键；所述药物为顺铂。本发明提供的水凝胶制剂结构简单、易于制备，且使用的顺铂具有双重作用：既是促进蛋白水凝胶形成的交联剂，也是发挥抑瘤疗效的抗肿瘤药物。本发明有效减少了其他成分的引入，降低了机体副作用的潜在风险；另一方面，蛋白羧基通过配位作用对顺铂的释放产生限制，能够在很大程度上减少药物的爆释行为，这有助于减少顺铂的机体组织毒性。
Description
技术领域
本发明属于药物制剂领域，具体涉及一种顺铂药物作为交联剂的蛋白水凝胶及其制备方法。
背景技术
由于实体肿瘤组织生长速度快，从而造成相对于正常生理组织更高的细胞间质压力，这使得化疗过程中肿瘤区域有效的药物浓度低；另外，肿瘤微环境十分复杂，这也是影响药物扩散的重要原因之一。而静脉注射给药的方法具有毒副作用大、病灶部位有效药物浓度低等缺点。肿瘤局部治疗具有给药浓度集中、全身副作用小等优势，且能够克服生理性给药障碍，因而近年来受到了广泛的研究和关注。
水凝胶是一种具有三维网络结构且含有大量水或生物体液的材料。根据组成成分来源的不同，可分为天然高分子水凝胶和合成高分子水凝胶两大类。天然高分子主要包括多糖类(如：壳聚糖、透明质酸等)和蛋白类(如：胶原、明胶、白蛋白等)；合成高分子则主要包括聚甲基丙烯酸及其衍生物、聚酯、聚醚和聚氨基酸材料等。在不同类型的水凝胶中，使用天然来源的蛋白质作为凝胶材料的基底，具备许多优势，如生物相容性良好、粘弹性可调、及生物体内可降解等，而在药物递送、生物传感、组织工程及人造器官等方面应用前景广阔。白蛋白是机体血清中最主要的蛋白质，具有易得、易溶解、生物相容性好等特点，在生物医学领域被广泛应用。
水凝胶作为药物载体，能够在局部作为一个药物释放库，时间上能够向病灶部位持续提供有效的药物浓度，空间上能够更加直接的将药物递送到病灶部位，该方法相对于全身治疗而言更加直接有效，特别对于毒副作用较大的药物，是一种非常有发展潜力的给药手段。但对于水溶性药物来说(如顺铂、盐酸阿霉素等)，前期的药物爆释行为是一个不容忽视的问题，这会使水凝胶载体的调控作用大大削弱，影响治疗效果，而且前期爆释的药物会造成较大的局部组织毒性。因此，减少药物爆释行为，实现药物释放的可控性，对于发挥水凝胶载体的优势是十分必要的。
顺铂药物属于常规化疗药物之一，具有抗癌谱广、疗效确切等特点，临床用于多种实体肿瘤治疗。但由于其较大的毒副作用往往给病人造成巨大的心理和生理的伤害。如果能够实现该类药物的局部缓释治疗，对于减少病人全身治疗的副作用、提高病人生活质量以及改善晚期病人肿瘤压迫等均具有较好的潜在应用价值。
发明内容
本发明的目的是针对现有技术的不足，提供了一种以顺铂药物作为交联剂的蛋白前药水凝胶制剂及制备方法。
本发明提供了一种顺铂交联的蛋白水凝胶，其主成分包括以下质量含量的组分：药物0.5％～5.0％、血清白蛋白6.0％～50.0％、溶媒介质47.0％～93.0％；其中血清白蛋白表面的羧基与药物形成配位键；
所述药物为顺铂；
所述血清白蛋白为人血清白蛋白、牛血清白蛋白、鼠血清白蛋白中的一种；
所述溶媒介质为水或不含氯离子的溶液。
作为优选，所述血清白蛋白的质量含量为15.0～40.0％，最优选为20.0～30.0％。
作为优选，所述药物的质量含量为1.5～2.0％。
本发明的另一个目的是提供了一种顺铂交联蛋白水凝胶的制备方法，具体是：
步骤(1)、将血清白蛋白、溶媒介质配置成一定浓度的血清白蛋白溶液，置于25～65℃水浴中加热一段时间，直至白蛋白完全溶解，得到澄清白蛋白溶液；
步骤(2)、在上述澄清白蛋白溶液中加入药物，一定温度下药物与血清白蛋白表面的羧基在溶媒介质中发生配位反应，生成顺铂配合物；置于4～65℃恒温摇床中以10～230r/min的转速放置一段时间后，即可得到顺铂交联的蛋白水凝胶。
作为优选，配位反应中的反应温度为10～50℃。
本发明的又一个目的是提供一种顺铂交联蛋白水凝胶在缓释载体上的应用。
本发明的再一个目的是提供一种联合药物，包括顺铂交联蛋白水凝胶，以及负载在顺铂交联蛋白水凝胶上的其他药物；
作为优选，其他药物为免疫佐剂药物、免疫检查阻断药物等中的一种。
通过流变学实验和降解实验可见，该顺铂交联蛋白凝胶具有良好的体外稳定性，但在蛋白酶及氯离子刺激条件下，能够发生降解，从而实现药物缓释的目的。细胞实验数据可见：该顺铂交联白蛋白水凝胶与单纯顺铂药物相比，其毒性在短期内明显减小，证明水凝胶对药物具有明显的缓释作用，这是由于白蛋白表面的羧基与顺铂的配位作用引起的，该性质对于降低药物的爆释行为带来的副作用和延长药物在肿瘤部位的作用时间均具有重要意义。
本发明所获得的顺铂交联白蛋白水凝胶具有氯离子触发降解特性，并具有良好的生物相容性和生物可降解性，有利于其作为药物载体在体内的进一步应用，而且降解得到的产物仅为血清白蛋白和顺铂，前者可被机体吸收或分解，对人体基本无害，而后者可作为化疗药物进入肿瘤细胞内从而发挥抗肿瘤作用；因此，该水凝胶具有广阔的应用前景。
与现有技术相比，本发明提供的水凝胶制剂结构简单、易于制备，且使用的顺铂具有双重作用：既是促进蛋白水凝胶形成的交联剂，也是发挥抑瘤疗效的抗肿瘤药物。本发明有效减少了其他成分的引入，降低了机体副作用的潜在风险；另一方面，蛋白羧基通过配位作用对顺铂的释放产生限制，能够在很大程度上减少药物的爆释行为，这有助于减少顺铂的机体组织毒性，为提高肿瘤局部治疗效率提供了有效的方案。
附图说明
图1(A)为实施例1获得顺铂交联蛋白水凝胶成胶照片；
图1(B)为药物质量含量小于0.5％时无法交联成胶的照片；
图2为实施例1获得顺铂交联蛋白水凝胶SEM微观结构图；
图3为实施例1获得顺铂交联蛋白水凝胶的流变学研究结果；
图4为实施例2获得顺铂交联蛋白水凝胶的体外降解实验结果；
图5为实施例2获得顺铂交联蛋白水凝胶的细胞毒性实验结果。
具体实施方式
为了进一步理解本发明，下面结合实施例对本发明优选实施方案进行描述，但是应当理解，这些描述只是为进一步说明本发明的特征和优点，而不是对本发明权利要求的限制。
本发明提供了一种顺铂药物作为交联剂的蛋白水凝胶，包括顺铂药物、血清白蛋白和溶媒介质。其中血清白蛋白占凝胶材料的质量比优选为6.0％～50.0％，更优选为15.0～40.0％，最优选为20.0～30.0％。所述药物顺铂的含量优选为0.5％～5.0％，更优选为1.0～3.0％，最优选为1.5～2.0％。
本发明以顺铂药物制备载药水凝胶制剂，包含上述技术方案所述的血清白蛋白和溶剂。
本发明所制备的载药凝胶制剂可以通过溶媒介质配制一定浓度的血清白蛋白溶液，加入顺铂药物，通过控制条件，获得载药顺铂配合物水凝胶。
优选的，所述溶媒介质为超纯水及任何不含氯离子的溶液，且该溶液中须具备与铂原子形成配位作用的官能团。所述血清白蛋白所占凝胶材料的质量比优选为6.0％～50.0％，更优选为15.0～40.0％，最优选为20.0～30.0％。
同时，该凝胶材料中的血清白蛋白溶液不仅可以与顺铂交联成胶进行局部治疗，亦可与其他能够与羧基形成配位键的抗肿瘤药物交联成胶；该水凝胶可单独使用或通过与其他药物(如蛋白多肽类药物、免疫佐剂和免疫检查阻断药物等)共载进行联合治疗。应当说，该氯离子响应型水凝胶材料是一个可用于局部疾病治疗的通用的药物担载平台，能够根据需要调整药物种类、降解时间、适应症等。
为了进一步说明本发明，以下结合实施例对本发明提供的顺铂交联白蛋白水凝胶及其制备方法进行详细描述。
实施例1
将300mg牛血清白蛋白粉末加入700μL超纯水中，45℃水浴加热使其完全溶解得到淡黄色澄清溶液，向溶液中加入15mg顺铂后放入摇床，设置温度42℃，转速230r/min，或使用机械搅拌使顺铂均匀分散在溶液中，经过36-48h反应后，获得顺铂作为交联剂的蛋白水凝胶。
将本发明实施例1制备的顺铂交联白蛋白水凝胶通过液氮速冻法将凝胶快速冷冻，并经冷冻干燥获得冻干凝胶样品；将样品进行扫描电镜测试，获得凝胶微观形态照片。从图2中可见，配合物水凝胶材料具有联通的大孔结构，这有利于药物在凝胶材料中传输和释放。
图1(A)为实施例1获得顺铂交联蛋白水凝胶成胶照片；
图1(B)为药物质量含量小于0.5％时无法交联成胶的照片。
图3为实施例1获得顺铂交联蛋白水凝胶的流变学研究结果。
实施例2
将200mg牛血清白蛋白粉末加入800μL超纯水中，45℃水浴加热使其完全溶解得到淡黄色澄清溶液，向溶液中加入15mg顺铂后放入摇床，设置温度10℃，转速230r/min，或使用机械搅拌使顺铂均匀分散在溶液中，经过72-84h反应后，获得顺铂作为交联剂的蛋白水凝胶。
在本发明实施例2制备顺铂交联白蛋白水凝胶的过程中，顺铂完全消失时将具有流动性的胶体从容器中倒入底面直径2.5cm的模具中，将其置入摇床中，设置温度45℃继续成胶。成胶后取出圆片状凝胶置于旋转流变仪上，测试该顺铂交联白蛋白水凝胶的模量。
向实施例2所制得的顺铂交联白蛋白水凝胶中分别加入生理条件浓度的胰蛋白酶水溶液、含有生理条件浓度胰蛋白酶的生理盐水溶液，并置于37℃下培养，在特定时间点吸干液体，称取剩余凝胶质量。降解曲线参见图4，降解实验结果表明凝胶本身具有一定的稳定性，而且在胰蛋白酶和生理盐水(氯离子)存在的模拟体内条件下可降解，证明凝胶的生物降解性，且具有一定的氯离子响应性，有利于生物医学应用。
将本发明实施例2制备的顺铂交联白蛋白水凝胶精确称量得到担载不同顺铂质量的块状凝胶，并用培养基配置相对应的不同浓度的纯顺铂溶液。以4T1细胞系为研究对象，将3万/孔细胞种于12孔板中，培养过夜。以纯顺铂药物(图5中顺铂纯药)、实施例2获得的顺铂交联白蛋白水凝胶(图5中交联顺铂水凝胶)进行细胞毒性研究。通过实验结果可见，由实施例2所获得的顺铂交联白蛋白水凝胶毒性较低，这说明顺铂与羧基的作用减缓了药物的释放，表现出缓释的行为。这对于减少药物爆释，实现药物的持续释放奠定了基础。
实施例3
将60mg牛血清白蛋白粉末加入940μL超纯水中，65℃水浴加热使其完全溶解得到淡黄色澄清溶液，向溶液中加入10mg顺铂后放入摇床，设置温度37℃，转速200r/min，或使用机械搅拌使顺铂均匀分散在溶液中，经过72-84h反应后，获得顺铂作为交联剂的蛋白水凝胶。
实施例4
将50mg牛血清白蛋白粉末加入50μL超纯水中，65℃水浴加热使其完全溶解得到淡黄色澄清溶液，向溶液中加入5mg顺铂后放入摇床，设置温度42℃，转速10r/min，或使用机械搅拌使顺铂均匀分散在溶液中，经过72-84h反应后，获得顺铂作为交联剂的蛋白水凝胶。
实施例5
将20mg人血清白蛋白粉末加入80μL超纯水中，25℃水浴加热使其完全溶解得到淡黄色澄清溶液，向溶液中加入1.5mg顺铂后放入摇床，设置温度40℃，转速230r/min，或使用机械搅拌使顺铂均匀分散在溶液中，经过36-48h反应后，获得顺铂作为交联剂的蛋白水凝胶。
实施例6
将30mg鼠血清白蛋白粉末加入70μL超纯水中，45℃水浴加热使其完全溶解得到淡黄色澄清溶液，向溶液中加入1.5mg顺铂后放入摇床，设置温度25℃，转速230r/min，或使用机械搅拌使顺铂均匀分散在溶液中，经过72-84h反应后，获得顺铂作为交联剂的蛋白水凝胶。
实施例7
将500mg牛血清白蛋白粉末加入500μL超纯水中，25℃水浴加热使其完全溶解得到淡黄色澄清溶液，向溶液中加入6mg顺铂后放入摇床，设置温度65℃，转速200r/min，或使用机械搅拌使顺铂均匀分散在溶液中，经过48-72h反应后，获得顺铂作为交联剂的蛋白水凝胶。
实施例8
将100mg牛血清白蛋白粉末加入900μL超纯水中，25℃水浴加热使其完全溶解得到淡黄色澄清溶液，向溶液中加入50mg顺铂后放入摇床，设置温度4℃，转速230r/min，或使用机械搅拌使顺铂均匀分散在溶液中，经过72-84h反应后，获得顺铂作为交联剂的蛋白水凝胶。
上述实施例并非是对于本发明的限制，本发明并非仅限于上述实施例，只要符合本发明要求，均属于本发明的保护范围。
Claims (8)
1.一种顺铂交联的蛋白水凝胶，其特征在于由以下质量含量的组分制成：药物0.5%～5.0%、血清白蛋白6.0%～50.0%、溶媒介质47.0%～93.0%；其中血清白蛋白表面的羧基与药物形成配位键；所述药物为顺铂；所述溶媒介质为水；
所述顺铂交联的蛋白水凝胶采用以下方法制备得到：
步骤（1）、将血清白蛋白、溶媒介质配置成一定浓度的血清白蛋白溶液，置于25～65℃水浴中加热一段时间，直至白蛋白完全溶解，得到澄清白蛋白溶液；
步骤（2）、在上述澄清白蛋白溶液中加入药物，一定温度下药物与血清白蛋白表面的羧基在溶媒介质中发生配位反应，生成顺铂配合物；然后置于4～65℃恒温摇床中以10～230r/min的转速放置一段时间后，即可得到顺铂交联的蛋白水凝胶。
2.如权利要求1所述的一种顺铂交联的蛋白水凝胶，其特征在于所述血清白蛋白为人血清白蛋白、牛血清白蛋白、鼠血清白蛋白中的一种。
3.如权利要求1所述的一种顺铂交联的蛋白水凝胶，其特征在于所述血清白蛋白的质量含量为15.0～40.0%。
4.如权利要求3所述的一种顺铂交联的蛋白水凝胶，其特征在于所述血清白蛋白的质量含量为20.0～30.0%。
5.如权利要求1所述的一种顺铂交联的蛋白水凝胶，其特征在于所述药物的质量含量为1.5～2.0%。
6.如权利要求1所述的一种顺铂交联的蛋白水凝胶，其特征在于步骤（2）中配位反应的反应温度为10～50℃。
7.如权利要求1-6任一所述的一种顺铂交联的蛋白水凝胶在制备缓释载体中的应用。
8.一种联合药物，其特征在于包括如权利要求1-6任一所述的一种顺铂交联的蛋白水凝胶，以及负载在顺铂交联的蛋白水凝胶上的其他药物。