CN1138831C - 制备冷固化软质泡沫的方法,用于该方法的多元醇组合物和反应体系,及由此获得的泡沫 - Google Patents

制备冷固化软质泡沫的方法,用于该方法的多元醇组合物和反应体系,及由此获得的泡沫 Download PDF

Info

Publication number
CN1138831C
CN1138831C CNB008105804A CN00810580A CN1138831C CN 1138831 C CN1138831 C CN 1138831C CN B008105804 A CNB008105804 A CN B008105804A CN 00810580 A CN00810580 A CN 00810580A CN 1138831 C CN1138831 C CN 1138831C
Authority
CN
China
Prior art keywords
polyvalent alcohol
composition
poly
oxyethane
polyvalent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB008105804A
Other languages
English (en)
Chinese (zh)
Other versions
CN1361811A (zh
Inventor
A
A·帕丰德里
J·于
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huntsman International LLC
Original Assignee
Huntsman International LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Huntsman International LLC filed Critical Huntsman International LLC
Publication of CN1361811A publication Critical patent/CN1361811A/zh
Application granted granted Critical
Publication of CN1138831C publication Critical patent/CN1138831C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/65—Low-molecular-weight compounds having active hydrogen with high-molecular-weight compounds having active hydrogen
    • C08G18/66—Compounds of groups C08G18/42, C08G18/48, or C08G18/52
    • C08G18/6666—Compounds of group C08G18/48 or C08G18/52
    • C08G18/667—Compounds of group C08G18/48 or C08G18/52 with compounds of group C08G18/32 or polyamines of C08G18/38
    • C08G18/6681—Compounds of group C08G18/48 or C08G18/52 with compounds of group C08G18/32 or polyamines of C08G18/38 with compounds of group C08G18/32 or C08G18/3271 and/or polyamines of C08G18/38
    • C08G18/6688—Compounds of group C08G18/48 or C08G18/52 with compounds of group C08G18/32 or polyamines of C08G18/38 with compounds of group C08G18/32 or C08G18/3271 and/or polyamines of C08G18/38 with compounds of group C08G18/3271
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/08—Processes
    • C08G18/10—Prepolymer processes involving reaction of isocyanates or isothiocyanates with compounds having active hydrogen in a first reaction step
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/48—Polyethers
    • C08G18/4804—Two or more polyethers of different physical or chemical nature
    • C08G18/482—Mixtures of polyethers containing at least one polyether containing nitrogen
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L71/00—Compositions of polyethers obtained by reactions forming an ether link in the main chain; Compositions of derivatives of such polymers
    • C08L71/02—Polyalkylene oxides
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G2110/00—Foam properties
    • C08G2110/0008—Foam properties flexible
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G2110/00—Foam properties
    • C08G2110/0083—Foam properties prepared using water as the sole blowing agent

Landscapes

  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Polyurethanes Or Polyureas (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
CNB008105804A 1999-07-26 2000-07-03 制备冷固化软质泡沫的方法,用于该方法的多元醇组合物和反应体系,及由此获得的泡沫 Expired - Fee Related CN1138831C (zh)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP99114600 1999-07-26
EP99114600.2 1999-07-26

Publications (2)

Publication Number Publication Date
CN1361811A CN1361811A (zh) 2002-07-31
CN1138831C true CN1138831C (zh) 2004-02-18

Family

ID=8238659

Family Applications (1)

Application Number Title Priority Date Filing Date
CNB008105804A Expired - Fee Related CN1138831C (zh) 1999-07-26 2000-07-03 制备冷固化软质泡沫的方法,用于该方法的多元醇组合物和反应体系,及由此获得的泡沫

Country Status (8)

Country Link
US (1) US6506813B1 (enExample)
EP (1) EP1198519B1 (enExample)
JP (2) JP2003505570A (enExample)
CN (1) CN1138831C (enExample)
AU (1) AU6154000A (enExample)
DE (1) DE60003185T2 (enExample)
ES (1) ES2200896T3 (enExample)
WO (1) WO2001007521A1 (enExample)

Families Citing this family (31)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1234843A1 (en) * 2001-02-26 2002-08-28 Huntsman International Llc Process for preparing a flexible polyurethane foam
ITMI20010619A1 (it) * 2001-03-23 2002-09-23 Enichem Spa Procedimento per la preparazione di schiume poliuretaniche
US20050131095A1 (en) * 2002-08-02 2005-06-16 Jianming Yu Novel polyols
JP4504809B2 (ja) * 2002-08-02 2010-07-14 ハンツマン・インターナショナル・エルエルシー 軟質フォームを製造するためのプレポリマー、ポリオール組成物および方法
US20040154718A1 (en) * 2003-02-06 2004-08-12 Doesburg Van I. Polyurethane filled tire and method of making same
US7238730B2 (en) * 2003-06-26 2007-07-03 Basf Corporation Viscoelastic polyurethane foam
US7078443B2 (en) * 2003-10-22 2006-07-18 Intellectual Property Holdings, Llc Viscoelastic foam layer and composition
US20080125507A1 (en) * 2006-11-28 2008-05-29 Bayer Materialscience Llc Reduction of VOC emissions from low density cavity filling NVH polyurethane foams
RU2339663C1 (ru) * 2007-06-05 2008-11-27 Федеральное казенное предприятие (ФКП) "Пермский пороховой завод" Полиоловая композиция для получения жестких пенополиуретанов теплоизоляционного назначения
US20090012195A1 (en) 2007-07-05 2009-01-08 Neff Raymond A Resin composition for use in forming a polyurethane article with increased comfort
DE102007061883A1 (de) * 2007-12-20 2009-06-25 Bayer Materialscience Ag Viskoelastischer Polyurethanschaumstoff
US8901187B1 (en) 2008-12-19 2014-12-02 Hickory Springs Manufacturing Company High resilience flexible polyurethane foam using MDI
US8604094B2 (en) 2008-12-23 2013-12-10 Basf Se Flexible polyurethane foam and method of producing same
US8906975B1 (en) 2009-02-09 2014-12-09 Hickory Springs Manufacturing Company Conventional flexible polyurethane foam using MDI
US8784518B2 (en) * 2011-01-17 2014-07-22 3M Innovative Properties Company Method of making polyurethane foam
ES2530361T3 (es) * 2012-02-15 2015-03-02 Bayer Ip Gmbh Espumas semirrígidas basadas en poliuretano, su uso y su aplicación
FR2991686B1 (fr) * 2012-06-08 2015-05-01 Michelin & Cie Bandage pneumatique dont la paroi interne est pourvue d'une couche de mousse polyurethane specifique
KR20150070220A (ko) 2012-10-10 2015-06-24 바스프 에스이 점탄성 폴리우레탄 발포체
US9783633B2 (en) 2013-09-13 2017-10-10 Dow Global Technologies Llc PIPA polyol based viscoelastic foams
PL3044244T3 (pl) 2013-09-13 2020-11-30 Dow Global Technologies Llc Konwencjonalna elastyczna pianka na bazie PIPA-poliolu
PL3044243T3 (pl) 2013-09-13 2020-12-14 Dow Global Technologies Llc Sposób wytwarzania poliaddycyjnego poliizocyjanianopoliolu z użyciem stabilizatorów
CN106632985B (zh) * 2015-11-04 2019-04-23 万华化学（北京）有限公司 一种聚氨酯泡沫材料及其制备方法和用途
WO2017104608A1 (ja) * 2015-12-16 2017-06-22 株式会社ブリヂストン 軟質ポリウレタンフォーム、及びシート用パッド
JP6928427B2 (ja) * 2016-07-08 2021-09-01 株式会社イノアックコーポレーション ウレタンフォーム製造方法、ウレタンフォームの組成物、シートクッション、寝具、および衣料用パッド
EP3980479A1 (en) * 2019-06-05 2022-04-13 Basf Se A reactive composition for polyurethane foam and use thereof in automobile parts
JP2021181538A (ja) * 2020-05-19 2021-11-25 株式会社イノアック技術研究所 低膨潤親水性ウレタンフォーム
US11738487B2 (en) * 2021-01-22 2023-08-29 Covestro Llc Processes for making molded flexible foams and flexible foams produced thereby
US20220235168A1 (en) * 2021-01-22 2022-07-28 Covestro Llc Processes for making molded flexible foams and flexible foams produced thereby
JPWO2023084651A1 (enExample) * 2021-11-10 2023-05-19
CN114716638B (zh) * 2022-04-14 2023-12-01 佳化化学科技发展（上海）有限公司 一种聚氨酯自结皮泡沫及其制备方法和应用
JPWO2024071225A1 (enExample) * 2022-09-30 2024-04-04

Family Cites Families (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS61151224A (ja) * 1984-12-20 1986-07-09 ソシエテ　シミツク　デ　シヤルボナ−ジユ　エス．ア−． ヒドロキシル基含有ポリイソシアネ−トの安定なプレポリマ−、その製造方法、そのポリウレタン製造への利用
DE3806476A1 (de) * 1988-03-01 1989-09-14 Bayer Ag Verfahren zur herstellung von kalthaertenden polyurethan-weichformschaumstoffen mit hervorragenden daempfungseigenschaften
JPH0284421A (ja) * 1988-06-04 1990-03-26 Achilles Corp 衝撃吸収性ポリウレタンフォーム及びその製造方法
DE3942330A1 (de) * 1989-12-21 1991-06-27 Basf Ag Verfahren zur herstellung von flexiblen polyurethan-weichschaumstoffen mit viskoelastischen, koerperschalldaempfenden eigenschaften und hierzu verwendbare polyoxyalkylen-polyol-mischungen
JPH03239716A (ja) * 1990-02-19 1991-10-25 Sanyo Chem Ind Ltd 軟質ポリウレタンフォーム形成組成物および製法
DE4135588A1 (de) * 1991-10-29 1993-05-06 Basf Ag, 6700 Ludwigshafen, De Hochreaktive, tertiaere aminogruppen gebunden enthaltende polyoxyalkylenpolyole, verfahren zu ihrer herstellung und ihre verwendung zur herstellung von polyisocyanat-polyadditionsprodukten
DE4204395A1 (de) * 1992-02-14 1993-08-19 Bayer Ag Verfahren zur herstellung von kalthaertenden polyurethan-weichformschaumstoffen
JPH06211978A (ja) * 1992-10-28 1994-08-02 Takeda Chem Ind Ltd 新規ポリエーテルポリオール及びそれを用いる軟質ウレタンフォームの製造法
JP3281662B2 (ja) * 1993-02-01 2002-05-13 三井化学株式会社 部分プレポリマー及びこれを用いた軟質ポリウレタンフォーム
DE4437878A1 (de) * 1994-10-22 1996-04-25 Basf Ag Verfahren zur Herstellung von fogging-armen Polyurethan-Schaumstoffen und hierfür verwendbare spezielle Polyoxyalkylen-polyole
WO1997014730A1 (en) * 1995-10-19 1997-04-24 Imperial Chemical Industries Plc Rigid polyurethane foams
JP3610138B2 (ja) * 1995-12-22 2005-01-12 三井武田ケミカル株式会社 低密度高弾性軟質ポリウレタンフォームの製造方法
DE19742012A1 (de) * 1997-09-24 1999-03-25 Basf Ag Temperaturstabile Hartschaumstoffe auf Isocyanatbasis mit geringer Sprödigkeit und niedriger Wärmeleitfähigkeit
US5874485A (en) 1997-11-10 1999-02-23 Bayer Corporation Flexible foams and flexible molded foams based on allophanate-modified diphenylmethane diisocyanates and processes for the production of these foams
US6034197A (en) * 1998-07-27 2000-03-07 Sealed Air Corporation Polyol blend, multi-component system for producing polyurethane foam, and foam produced thereby
JP3992869B2 (ja) * 1999-04-07 2007-10-17 三井化学株式会社 エネルギー吸収軟質ポリウレタン発泡体及びその製造方法

Also Published As

Publication number Publication date
CN1361811A (zh) 2002-07-31
WO2001007521A1 (en) 2001-02-01
DE60003185T2 (de) 2003-12-18
US6506813B1 (en) 2003-01-14
JP2011094154A (ja) 2011-05-12
EP1198519A1 (en) 2002-04-24
EP1198519B1 (en) 2003-06-04
ES2200896T3 (es) 2004-03-16
DE60003185D1 (de) 2003-07-10
AU6154000A (en) 2001-02-13
JP2003505570A (ja) 2003-02-12

Similar Documents

Publication Publication Date Title
CN1138831C (zh) 制备冷固化软质泡沫的方法,用于该方法的多元醇组合物和反应体系,及由此获得的泡沫
JP6807994B2 (ja) 組成物
CN1130410C (zh) 制备软质聚氨酯泡沫塑料的方法
CN101374877B (zh) 生产开孔粘弹性软质聚氨酯泡沫的方法
CN1174014C (zh) 制备高弹性泡沫体的方法
JP5367674B2 (ja) フリーライズまたはスラブストック軟質ポリウレタンフォームの製造方法
AU651743B2 (en) Polyurethane foams
RU2270205C2 (ru) Способ изготовления эластичного пенополиуретана
CN1131256C (zh) 可挠性聚氨基甲酸酯发泡体的制法
RU2284334C2 (ru) Очень мягкий полиуретановый эластомер
CN103221445A (zh) 制造低密度高弹性软质聚氨酯泡沫的方法
CN101054432B (zh) 最小化聚氨酯泡沫体劣化的芳族二酸酯二醇及其取代的氨基甲酸酯
CN101321797A (zh) 制备粘弹性柔性聚氨酯泡沫材料的方法
JP4339250B2 (ja) ポリオール
US6569913B1 (en) Isocyanate-terminated prepolymers
CN101959921B (zh) 包含高硬嵌段含量基质的泡沫材料及其制备方法
JP3504770B2 (ja) 軟質ポリウレタン発泡体およびその製造方法
HK1027369A (en) Process for preparing flexible polyurethane foam
JPS60190410A (ja) 耐摩擦、耐摩耗性ポリウレタン組成物

Legal Events

Date Code Title Description
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C06 Publication
PB01 Publication
C14 Grant of patent or utility model
GR01 Patent grant
C17 Cessation of patent right
CF01 Termination of patent right due to non-payment of annual fee

Granted publication date: 20040218

Termination date: 20130703