CN113402794A - 一种丁腈双色手套及其生产工艺 - Google Patents
一种丁腈双色手套及其生产工艺 Download PDFInfo
- Publication number
- CN113402794A CN113402794A CN202110771459.1A CN202110771459A CN113402794A CN 113402794 A CN113402794 A CN 113402794A CN 202110771459 A CN202110771459 A CN 202110771459A CN 113402794 A CN113402794 A CN 113402794A
- Authority
- CN
- China
- Prior art keywords
- glove
- butyronitrile
- rubber latex
- double
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种丁腈双色手套及其生产工艺，涉及丁腈手套生产技术领域，包括丁腈手套主体，所述丁腈手套主体的一端设置有指套，所述指套的外表面上设置有防滑凸点，所述丁腈手套主体由丁腈橡胶胶乳混合液制成。本发明通过利用丁腈橡胶胶乳和天然橡胶胶乳的混合，增加橡胶胶乳的稳定性，再由抗氧化剂混合在丁腈橡胶胶乳混合液中，增加材料捕获并中和自由基的能力，同时配合活性炭对材料自身气味进行吸附与限制，避免了由于橡胶材料自身所具备的气味与材料吸附特性，使得丁腈双色手套易出现异味，影响使用者的使用体验的问题，提高丁腈双色手套的利用效率，保障丁腈双色手套的使用体验。
Description
技术领域
本发明涉及丁腈手套生产技术领域，具体涉及一种丁腈双色手套及其生产工艺。
背景技术
橡胶材料制成的手套具有广泛的应用，其不仅可以应用于医疗领域，还可以广泛的适用于生活中的方方面面领域，同时橡胶手套质地柔软亲肤，密封性好的优异性质，丁腈橡胶则具备耐油性极好，耐磨性较高，耐热性较好，粘接力强的优点，因而在橡胶手套的使用中尤为广泛。
针对现有技术存在以下问题：
1、现有丁腈双色手套在使用时，由于橡胶材料自身所具备的气味与材料吸附特性，使得丁腈双色手套易出现异味，影响使用者的使用体验，导致丁腈双色手套的使用效率降低，使用体验感降低的问题；
2、现有丁腈双色手套在生产时，不仅工序繁琐，而且由于橡胶材料粘附能力较强，脱模也存在很大不便，导致丁腈双色手套的生产效率降低，生产成本增加的问题。
发明内容
本发明提供一种丁腈双色手套及其生产工艺，其中一种目的是为了具备去除异味，减少吸附的能力，解决由于橡胶材料自身所具备的气味与材料吸附特性，使得丁腈双色手套易出现异味，影响使用者的使用体验的问题；其中另一种目的是为了解决丁腈双色手套在生产时，不仅工序繁琐，而且由于橡胶材料粘附能力较强，脱模也存在很大不便的问题，以达到提高丁腈双色手套的生产效率，减少生产成本的效果。
为解决上述技术问题，本发明所采用的技术方案是：
一种丁腈双色手套及其生产工艺，包括丁腈手套主体，所述丁腈手套主体的一端设置有指套，所述指套的外表面上设置有防滑凸点。
本发明技术方案的进一步改进在于：所述丁腈手套主体由丁腈橡胶胶乳混合液制成，丁腈橡胶胶乳混合液由丁腈橡胶胶乳、天然橡胶胶乳、抗氧化剂、热稳定剂、活性炭、着色剂、天然防霉剂、架桥剂及抗菌剂组成。
本发明技术方案的进一步改进在于：所述丁腈橡胶胶乳混合液按照数量的分配计算，包括以下的分配的原料份数：丁腈橡胶胶乳50-70份、天然橡胶胶乳30-40份、抗氧化剂0.5-1份、热稳定剂2-3份、活性炭1-3份、着色剂5-10份、天然防霉剂1-2份、架桥剂2-5份、抗菌剂1-3份。
本发明技术方案的进一步改进在于：所述抗氧化剂为黄烷酮醇、环己六醇六磷酸酷或茶多酚中的一种或两种，所述抗氧化剂的形状为胶体状。
采用上述技术方案，该方案中的黄烷酮醇、环己六醇六磷酸酷和茶多酚共同配合，与丁腈橡胶混合，用于使产品具备阻止氧气不良影响的能力。
本发明技术方案的进一步改进在于：所述热稳定剂为混合金属稳定剂，所述热稳定剂为粉末状，所述天然防霉剂的成分为百分之七十的芥子萃取物和百分之三十的艾蒿提取物。
采用上述技术方案，该方案中的芥子萃取物和艾蒿提取物共同配合，为材料增加抗霉菌的能力，提高产品的后续使用效果。
本发明技术方案的进一步改进在于：所述着色剂为朱砂、红土、雄黄、孔雀绿以及重质碳酸钙、硅灰石、重晶石粉、滑石粉、云母粉、高岭土等中的任意两种，且着色剂均为天然着色剂，着色剂等分量取用。
采用上述技术方案，该方案中的天然着色剂等分量取用，能够保证双色手套的色彩均匀程度，确保产品使用时的环保及安全性。
本发明还提供的另一种技术方案为：一种丁腈双色手套生产工艺，该丁腈双色手套生产工艺，包括以下步骤：
A1、配置丁腈橡胶胶乳混合液；
A2、手套一次浸润成型；
A3、手套二次浸润成型；
A4、手套烘干脱模。
本发明技术方案的进一步改进在于：所述A1还包括：丁腈橡胶胶乳混合液各原料混合温度为110℃-140℃，丁腈橡胶胶乳混合液需根据着色剂不同配置两份，且两份丁腈橡胶胶乳混合液等量配置，丁腈橡胶胶乳混合液配置完成后需进行2-3次过滤除杂的操作。
采用上述技术方案，该方案中的混合温度为110℃-140℃，有利于丁腈橡胶胶乳混合液中各原料的充分混合，同时对配置完成的丁腈橡胶胶乳混合液进行过滤除杂，用以减少丁腈橡胶胶乳混合液中的不充分混合杂质对生产的影响。
本发明技术方案的进一步改进在于：所述A2还包括：手套一次浸润成型需使用手套模具，手套模具的外表面上涂抹有防粘液，手套一次浸润成型需浸润20秒，且丁腈橡胶胶乳混合液温度持续保持在110℃-140℃之间，浸润完成后，进行1-1.5分钟的干燥。
采用上述技术方案，该方案中的手套模具涂抹防粘液，用以减少后期脱模的时间消耗，同时在110℃-140℃胶乳中浸润20秒，使得丁腈橡胶胶乳混合液充分包裹手套模具。
本发明技术方案的进一步改进在于：所述A3还包括：手套二次浸润成型需浸润10-15秒，浸润温度保持在110℃-140℃之间，浸润完成后，进行10分钟的干燥。
由于采用了上述技术方案，本发明相对现有技术来说，取得的技术进步是：
1、本发明通过采用丁腈橡胶胶乳、天然橡胶胶乳、抗氧化剂和活性炭之间的配合，利用丁腈橡胶胶乳和天然橡胶胶乳的混合，增加橡胶胶乳的稳定性，再由抗氧化剂混合在丁腈橡胶胶乳混合液中，增加材料捕获并中和自由基的能力，同时配合活性炭对材料自身气味进行吸附与限制，避免了由于橡胶材料自身所具备的气味与材料吸附特性，使得丁腈双色手套易出现异味，影响使用者的使用体验的问题，提高丁腈双色手套的利用效率，保障丁腈双色手套的使用体验。
2、本发明通过采用手套模具、过滤除杂操作和防粘液之间的配合，利用过滤除杂操作，去除丁腈橡胶胶乳混合液中的杂质，提高溶液的纯净度，再由手套模具和防粘液之间的配合，使得丁腈双色手套生产完成后脱模速度更快，并对生产工序进行了简化，避免了丁腈双色手套在生产时，不仅工序繁琐，而且由于橡胶材料粘附能力较强，脱模也存在很大不便的问题，提高了丁腈双色手套的生产效率，配合简化的工序达到了减少生产成本的效果。
3、本发明通过采用热稳定剂、天然防霉剂和天然着色剂之间的配合，利用热稳定剂进一步提升丁腈手套在使用时的抗高温性能，保障了其在高温下的稳定程度，再配合天然防霉剂抑制霉菌生长，保障丁腈手套的材料免受真菌侵蚀，同时防止涂料被霉菌破坏，出现色彩沉降的情况，提高丁腈手套的使用寿命，保障丁腈手套的整体的整洁性。
附图说明
图1为本发明的结构示意图；
图2为本发明的生产流程图。
图中：1、丁腈手套主体；2、指套；21、防滑凸点。
具体实施方式
下面结合实施例对本发明做进一步详细说明：
实施例1
如图1所示，本发明提供了一种丁腈双色手套，包括丁腈手套主体1，丁腈手套主体1的一端设置有指套2，指套2的外表面上设置有防滑凸点21，丁腈手套主体1由丁腈橡胶胶乳混合液制成，丁腈橡胶胶乳混合液由丁腈橡胶胶乳、天然橡胶胶乳、抗氧化剂、热稳定剂、活性炭、着色剂、天然防霉剂、架桥剂及抗菌剂组成，按照数量的分配计算，包括以下的分配的原料份数：丁腈橡胶胶乳50-70份、天然橡胶胶乳30-40份、抗氧化剂0.5-1份、热稳定剂2-3份、活性炭1-3份、着色剂5-10份、天然防霉剂1-2份、架桥剂2-5份、抗菌剂1-3份，抗氧化剂为黄烷酮醇、环己六醇六磷酸酷或茶多酚中的一种或两种，抗氧化剂的形状为胶体状。
在本实施例中，通过指套2和防滑凸点21的配合，能够增加手套的摩擦力，再由丁腈橡胶胶乳和天然橡胶胶乳混合配置，进一步增加丁腈橡胶胶乳的分子稳定性，同时利用抗氧化剂帮助丁腈双色手套捕获并中和自由基，祛除自由基中对人体有害的物质，并与金属离子结合形成螯合物，减少金属离子对材料的氧化催化，减少金属离子与橡胶材料接触产生的异味，进一步提高丁腈双色手套的利用效率，保障丁腈双色手套的使用体验。
实施例2
如图1所示，在实施例1的基础上，本发明提供一种技术方案：优选的，热稳定剂为混合金属稳定剂，热稳定剂为粉末状，天然防霉剂的成分为百分之七十的芥子萃取物和百分之三十的艾蒿提取物，着色剂为朱砂、红土、雄黄、孔雀绿以及重质碳酸钙、硅灰石、重晶石粉、滑石粉、云母粉、高岭土等中的任意两种，且着色剂均为天然着色剂，着色剂等分量取用。
在本实施例中，通过热稳定剂与丁腈橡胶的混合，提高丁腈手套的抗高温能力，并保障其使用时的耐热性，配合芥子萃取物和艾蒿提取物共同作用，为丁腈手套增加抑制霉菌生长的能力，使得丁腈手套免受真菌侵蚀，进一步保障丁腈手套使用时，内部着色剂的抗破坏能力，进一步提高丁腈手套的使用寿命。
实施例3
如图1-2所示，在实施例1、实施例2的基础上，本发明还提供了一种丁腈双色手套生产工艺，该丁腈双色手套生产工艺，包括以下步骤：
A1、配置丁腈橡胶胶乳混合液，具体为：丁腈橡胶胶乳混合液各原料混合温度为110℃-140℃，丁腈橡胶胶乳混合液需根据着色剂不同配置两份，且两份丁腈橡胶胶乳混合液等量配置，丁腈橡胶胶乳混合液配置完成后需进行2-3次过滤除杂的操作；
A2、手套一次浸润成型，具体为：手套一次浸润成型需使用手套模具，手套模具的外表面上涂抹有防粘液，手套一次浸润成型需浸润20秒，且丁腈橡胶胶乳混合液温度持续保持在110℃-140℃之间，浸润完成后，进行1-1.5分钟的干燥，即获取丁腈双色手套的内套；
A3、手套二次浸润成型，具体为：手套二次浸润成型需浸润10-15秒，浸润温度保持在110℃-140℃之间，浸润完成后，进行10分钟的干燥，即可完成丁腈双色手套的外套制作；
A4、手套烘干脱模，具体为：对手套进行收卷，将其从手套模具上取下。
在本实施例中，通过对丁腈橡胶胶乳混合液的除杂，将其中难溶的材料筛除，以提高溶液的纯净度，再利用两次将手套模具浸润在丁腈橡胶胶乳混合液中，生成双色丁腈手套，再由防粘液的设置，使得手套烘干完成后的收卷更加快速，进一步减少生产的工序，节省丁腈双色手套的生产时间和成本。
如图1-2所示，首先在110℃-140℃的环境内，将丁腈橡胶胶乳、天然橡胶胶乳、抗氧化剂、热稳定剂、活性炭、着色剂、天然防霉剂、架桥剂及抗菌剂依次按比例加入混合容器中，进行丁腈橡胶胶乳混合液的配置，然后对丁腈橡胶胶乳混合液进行2-3次的过滤除杂作业，去除其中杂质，丁腈橡胶胶乳混合液配置完成后，将外表面上涂抹有防粘液的手套模具，浸润在第一着色剂丁腈橡胶胶乳混合液中20秒，浸润完成后，对手套模具及丁腈双色手套内套进行1-1.5分钟的干燥，然后手套模具及丁腈双色手套内套浸润在第二着色剂丁腈橡胶胶乳混合液中10-15秒，浸润完成后，进行10分钟的干燥，即可完成丁腈双色手套的外套制作，然后将丁腈双色手套烘干，对手套进行收卷，即可完成丁腈双色手套的生产制造。
上文一般性的对本发明做了详尽的描述，但在本发明基础上，可以对之做一些修改或改进，这对于技术领域的一般技术人员是显而易见的。因此，在不脱离本发明思想精神的修改或改进，均在本发明的保护范围之内。
Claims (10)
1.一种丁腈双色手套，包括丁腈手套主体(1)，其特征在于：所述丁腈手套主体(1)的一端设置有指套(2)，所述指套(2)的外表面上设置有防滑凸点(21)。
2.根据权利要求1所述的一种丁腈双色手套，其特征在于：所述丁腈手套主体(1)由丁腈橡胶胶乳混合液制成，丁腈橡胶胶乳混合液由丁腈橡胶胶乳、天然橡胶胶乳、抗氧化剂、热稳定剂、活性炭、着色剂、天然防霉剂、架桥剂及抗菌剂组成。
3.根据权利要求2所述的一种丁腈双色手套，其特征在于：所述丁腈橡胶胶乳混合液按照数量的分配计算，包括以下的分配的原料份数：丁腈橡胶胶乳50-70份、天然橡胶胶乳30-40份、抗氧化剂0.5-1份、热稳定剂2-3份、活性炭1-3份、着色剂5-10份、天然防霉剂1-2份、架桥剂2-5份、抗菌剂1-3份。
4.根据权利要求2所述的一种丁腈双色手套，其特征在于：所述抗氧化剂为黄烷酮醇、环己六醇六磷酸酷或茶多酚中的一种或两种，所述抗氧化剂的形状为胶体状。
5.根据权利要求2所述的一种丁腈双色手套，其特征在于：所述热稳定剂为混合金属稳定剂，所述热稳定剂为粉末状，所述天然防霉剂的成分为百分之七十的芥子萃取物和百分之三十的艾蒿提取物。
6.根据权利要求2所述的一种丁腈双色手套，其特征在于：所述着色剂为朱砂、红土、雄黄、孔雀绿以及重质碳酸钙、硅灰石、重晶石粉、滑石粉、云母粉、高岭土等中的任意两种，且着色剂均为天然着色剂，着色剂等分量取用。
7.一种丁腈双色手套生产工艺，其特征在于：该丁腈双色手套生产工艺，包括以下步骤：
A1、配置丁腈橡胶胶乳混合液；
A2、手套一次浸润成型；
A3、手套二次浸润成型；
A4、手套烘干脱模。
8.根据权利要求7所述的一种丁腈双色手套生产工艺，其特征在于：所述A1还包括：丁腈橡胶胶乳混合液各原料混合温度为110℃-140℃，丁腈橡胶胶乳混合液需根据着色剂不同配置两份，且两份丁腈橡胶胶乳混合液等量配置，丁腈橡胶胶乳混合液配置完成后需进行2-3次过滤除杂的操作。
9.根据权利要求7所述的一种丁腈双色手套生产工艺，其特征在于：所述A2还包括：手套一次浸润成型需使用手套模具，手套模具的外表面上涂抹有防粘液，手套一次浸润成型需浸润20秒，且丁腈橡胶胶乳混合液温度持续保持在110℃-140℃之间，浸润完成后，进行1-1.5分钟的干燥。
10.根据权利要求7所述的一种丁腈双色手套生产工艺，其特征在于：所述A3还包括：手套二次浸润成型需浸润10-15秒，浸润温度保持在110℃-140℃之间，浸润完成后，进行10分钟的干燥。