CN103724711A - 一种家用丁腈胶手套的制备方法 - Google Patents
一种家用丁腈胶手套的制备方法 Download PDFInfo
- Publication number
- CN103724711A CN103724711A CN201210389997.5A CN201210389997A CN103724711A CN 103724711 A CN103724711 A CN 103724711A CN 201210389997 A CN201210389997 A CN 201210389997A CN 103724711 A CN103724711 A CN 103724711A
- Authority
- CN
- China
- Prior art keywords
- butadiene
- gloves
- acrylonitrile rubber
- parts
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种家用丁腈胶手套的制备方法，所述丁腈胶手套以重量份计由下列组份组成：丁腈胶100份，硫磺1.2-1.4份，氧化锌1.4-1.6份，促进剂1.6-1.8份，粉色颜料5-7份，防老剂0.6-0.8份，薄荷油0.2-0.4份；所述制备方法为：用丁腈胶、氧化锌、促进剂、粉色颜料、防老剂配置丁腈胶乳，将浸渍了凝固剂的手套模具烘干后，再浸渍配制好的丁腈胶乳，接着经过沥滤、卷边后，进入112-116℃的烘箱，干燥60-70分钟，再进行硫化，温度为110-114℃，后沥滤，再烘干，温度为90-100℃，冷却脱模，将手套里面翻转到外面，喷洒薄荷油，低温烘干后即可。
Description
技术领域
本发明涉及安全防护技术领域，尤其涉及一种家用丁腈胶手套的制备方法。
背景技术
天然乳胶手套具有良好的隔离防护作用，能够有效地防止病菌和化学品的危害，所以在二十世纪八十年代便得到了广泛的应用，但由于部份人群对天然橡胶胶乳有过敏反应，以及天然乳胶手套本身不耐溶剂和化学品的原因，人们不得不开发出各种各样的用合成材料制作的手套，如丁腈、氯丁、PVC、聚胺酯手套等等。其中，丁腈手套由于其手感舒适、强度好、耐油等特点，故深受人们的欢迎。
美国专利US6566435公开了一种应力松驰大于50％的丁腈手套。它是在丁腈胶乳中用了小于0.5份氧化锌，并加温预硫化熟成的方法。该种手套在老化后性能不好，加温预硫化的工艺限制了它的应用。
美国专利US2004/0176512公开了一种应力松驰大于50％的丁腈手套。其配方为氧化锌0.5到1份，硫磺2到5份，在149～205℃下干燥硫化制得。该种手套由于硫磺用量过多，成品手套有味道；干燥硫化工艺的温度要求太高，实际操作中手套易变色，也限制了它的应用。
应力松驰性能并不是手套标准中要求控制的一个项目。但是它和模量一起决定了手套的穿戴手感。应力松驰反映了手套的回弹性，它的值越高，手套就更能贴合在手上；否则，手套在穿戴后不久，变形后不再回复原状，不能贴合在手上，会影响使用。低伸长率下的应力越低，也即模量越低，手套就越柔软，穿戴感觉也就越舒适。
现有的一般丁腈手套，应力松驰大约在40％左右，其300％模量约为5MPa；天然乳胶手套的应力松驰一般超过70％以上，其300％模量小于2MPa，可见，天然乳胶手套的手感比已有技术的丁腈手套更柔软。
因此，需要对丁腈胶手套进行进一步的改进，使其手感更加柔软舒适，以更加适合家庭的使用，替代天然乳胶手套。
发明内容
本发明的目的在于提出一种家用丁腈胶手套的制备方法，该方法制备的手套的应力松弛比现有丁腈胶手套高，接近天然乳胶手套，适合于家庭使用。
为达此目的，本发明采用以下技术方案：
一种家用丁腈胶手套的制备方法，所述丁腈胶手套以重量份计由下列组份组成：丁腈胶100份，硫磺1.2-1.4份，氧化锌1.4-1.6份，促进剂1.6-1.8份，粉色颜料5-7份，防老剂0.6-0.8份，薄荷油0.2-0.4份；所述制备方法为：用丁腈胶、氧化锌、促进剂、粉色颜料、防老剂配置丁腈胶乳，将浸渍了凝固剂的手套模具烘干后，再浸渍配制好的丁腈胶乳，接着经过沥滤、卷边后，进入112-116℃的烘箱，干燥60-70分钟，再进行硫化，温度为110-114℃，后沥滤，再烘干，温度为90-100℃，冷却脱模，将手套里面翻转到外面，喷洒薄荷油，低温烘干后即可。
本发明具有如下有益效果：
1）本发明手套的应力松弛大于60%，接近天然乳胶的水平，穿戴手感舒适。
2）本发明产品在手套里面喷洒适量的薄荷油，穿戴有清凉感，避免穿戴时间长导致的闷热感。
3）本发明的手套韧性好，抗一般的划磨，添加的防老剂延长其使用寿命，适合家庭使用。
具体实施方式
实施例一
一种家用丁腈胶手套的制备方法，所述丁腈胶手套以重量份计由下列组份组成：丁腈胶100份，硫磺1.2份，氧化锌1.6份，促进剂1.6份，粉色颜料7份，防老剂0.6份，薄荷油0.4份；所述制备方法为：用丁腈胶、氧化锌、促进剂、粉色颜料、防老剂配置丁腈胶乳，将浸渍了凝固剂的手套模具烘干后，再浸渍配制好的丁腈胶乳，接着经过沥滤、卷边后，进入112℃的烘箱，干燥70分钟，再进行硫化，温度为110℃，后沥滤，再烘干，温度为100℃，冷却脱模，将手套里面翻转到外面，喷洒薄荷油，低温烘干后即可。
实施例二
一种家用丁腈胶手套的制备方法，所述丁腈胶手套以重量份计由下列组份组成：丁腈胶100份，硫磺1.4份，氧化锌1.4份，促进剂1.8份，粉色颜料5份，防老剂0.8份，薄荷油0.2份；所述制备方法为：用丁腈胶、氧化锌、促进剂、粉色颜料、防老剂配置丁腈胶乳，将浸渍了凝固剂的手套模具烘干后，再浸渍配制好的丁腈胶乳，接着经过沥滤、卷边后，进入116℃的烘箱，干燥60分钟，再进行硫化，温度为114℃，后沥滤，再烘干，温度为90℃，冷却脱模，将手套里面翻转到外面，喷洒薄荷油，低温烘干后即可。
实施例三
一种家用丁腈胶手套的制备方法，所述丁腈胶手套以重量份计由下列组份组成：丁腈胶100份，硫磺1.3份，氧化锌1.5份，促进剂1.7份，粉色颜料6份，防老剂0.7份，薄荷油0.3份；所述制备方法为：用丁腈胶、氧化锌、促进剂、粉色颜料、防老剂配置丁腈胶乳，将浸渍了凝固剂的手套模具烘干后，再浸渍配制好的丁腈胶乳，接着经过沥滤、卷边后，进入114℃的烘箱，干燥65分钟，再进行硫化，温度为112℃，后沥滤，再烘干，温度为95℃，冷却脱模，将手套里面翻转到外面，喷洒薄荷油，低温烘干后即可。
Claims (1)
1.一种家用丁腈胶手套的制备方法，其特征在于，所述丁腈胶手套以重量份计由下列组份组成：丁腈胶100份，硫磺1.2-1.4份，氧化锌1.4-1.6份，促进剂1.6-1.8份，粉色颜料5-7份，防老剂0.6-0.8份，薄荷油0.2-0.4份；所述制备方法为：用丁腈胶、氧化锌、促进剂、粉色颜料、防老剂配置丁腈胶乳，将浸渍了凝固剂的手套模具烘干后，再浸渍配制好的丁腈胶乳，接着经过沥滤、卷边后，进入112-116℃的烘箱，干燥60-70分钟，再进行硫化，温度为110-114℃，后沥滤，再烘干，温度为90-100℃，冷却脱模，将手套里面翻转到外面，喷洒薄荷油，低温烘干后即可。