CN101028742A - 柔软薄型丁腈手套的制造方法 - Google Patents
柔软薄型丁腈手套的制造方法 Download PDFInfo
- Publication number
- CN101028742A CN101028742A CNA2007100213402A CN200710021340A CN101028742A CN 101028742 A CN101028742 A CN 101028742A CN A2007100213402 A CNA2007100213402 A CN A2007100213402A CN 200710021340 A CN200710021340 A CN 200710021340A CN 101028742 A CN101028742 A CN 101028742A
- Authority
- CN
- China
- Prior art keywords
- gloves
- soft thin
- butyronitrile gloves
- butyronitrile
- zinc oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明为一种柔软薄型丁腈手套的制造方法,其技术方案是首先配制丁腈胶乳,以干份计算,其配方为:丁腈胶:100份,硫磺:1.5~3份,氧化锌:0.1~1.1份,促进剂:0.5~2份,将浸渍了凝固剂的手套模具烘干后,再浸渍该丁腈胶乳,接着经过沥滤、卷边后,进入125~150℃的烘箱,干燥15~50分钟,再经过氯化、脱模等工序,即得到本发明成品。本发明的各项性能指标得到极大提高:应力松驰性能达50~60%,其300%模量小于3MPa;拉伸强度大于16MPa,断裂伸长率大于550%,制作出来的手套薄而柔软,手感非常接近天然乳胶手套。
Description
技术领域
本发明涉及一种丁腈手套的制造方法,尤其是一种柔软薄型丁腈手套的制造方法。
背景技术
天然乳胶手套具有良好的隔离防护作用,能够有效地防止病菌和化学品的危害,所以在二十世纪八十年代便得到了广泛的应用,但由于部份人群对天然橡胶胶乳有过敏反应,以及天然乳胶手套本身不耐溶剂和化学品的原因,人们不得不开发出各种各样的用合成材料制作的手套,如丁腈、氯丁、PVC、聚胺酯手套等等。其中,丁腈手套由于其手感舒适、强度好、耐油等特点,故深受人们的欢迎。
美国专利US6566435公开了一种应力松驰大于50%的丁腈手套。它是在丁腈胶乳中用了小于0.5份氧化锌,并加温预硫化熟成的方法。该种手套在老化后性能不好,加温预硫化的工艺限制了它的应用。
美国专利US2004/0176512公开了一种应力松驰大于50%的丁腈手套。其配方为氧化锌0.5到1份,硫磺2到5份,在149~205℃下干燥硫化制得。该种手套由于硫磺用量过多,成品手套有味道;干燥硫化工艺的温度要求太高,实际操作中手套易变色,也限制了它的应用。
应力松驰性能并不是手套标准中要求控制的一个项目。但是它和模量一起决定了手套的穿戴手感。应力松驰反映了手套的回弹性,它的值越高,手套就更能贴合在手上;否则,手套在穿戴后不久,变形后不再回复原状,不能贴合在手上,会影响使用。低伸长率下的应力越低,也即模量越低,手套就越柔软,穿戴感觉也就越舒适。
现有的一般丁腈手套,应力松驰大约在40%左右,其300%模量约为5MPa;天然乳胶手套的应力松驰一般超过70%以上,其300%模量小于2MPa,可见,天然乳胶手套的手感比已有技术的丁腈手套更柔软。
发明内容
本发明所要解决的技术问题是:提供一种应力松驰在50%以上,其300%模量为2~3MPa,手感极象天然乳胶手套那样的柔软薄型丁腈手套的制造方法。
为解决以上技术问题,所采用的技术方案是这样的:首先配制丁腈胶乳,以干份计算,其配方为:
丁腈胶:100份
硫磺:1.5~3份
氧化锌:0.1~1.1份
促进剂:0.5~2份
将浸渍了凝固剂的手套模具烘干后,再浸渍该丁腈胶乳,接着经过沥滤、卷边后,进入125~150℃的烘箱,干燥15~50分钟,再经过氯化、脱模等工序,即得到本发明成品。
由于采用以上技术方案,手套的各项性能指标得到了极大提高,其效果是显而易见的:
1、应力松驰性能达50~60%,其300%模量小于3MPa。
2、拉伸强度大于16MPa,断裂伸长率大于550%。
3、制作出来的手套薄而柔软,手感非常接近天然乳胶手套。
具体实施方式
下面结合实施例对本发明作进一步说明。
本发明应力松驰值的高低可以通过调整原料配方及生产工艺条件来进行调节。配方中氧化锌和硫磺的用量对最终成品的应力松驰性能起着很大的作用:氧化锌含量越多,手套强度和模量就越大,伸长率就越低,应力松驰值也越低;硫磺含量越高,手套模量就越低,应力松驰值也越高。
本发明在实施中,首先配制丁腈胶乳,取丁腈胶100份,硫磺1.8份,氧化锌0.5份,促进剂ZDC0.5份,BZ0.5份。再将配制好的丁腈胶乳在常温下24小时中不断加以搅拌。将浸渍了凝固剂的手套模具烘干后,再浸渍该丁腈胶乳,经过沥滤、卷边后,进入135℃的烘箱,干燥35分钟,再经过氯化、脱模工序,便得到本发明成品。
Claims (1)
1、一种柔软薄型丁腈手套的制造方法,其特征是:首先配制丁腈胶乳,以干份计算,其配方为:
丁腈胶:100份
硫磺:1.5~3份
氧化锌:0.1~1.1份
促进剂:0.5~2份
将浸渍了凝固剂的手套模具烘干后,再浸渍该丁腈胶乳,接着经过沥滤、卷边后,进入125~150℃的烘箱,干燥15~50分钟,再经过氯化、脱模等工序,即得到本发明成品。