CN103554565B - 一种天然橡胶和丁腈橡胶共混的医用手套及其制备方法 - Google Patents

一种天然橡胶和丁腈橡胶共混的医用手套及其制备方法 Download PDF

Info

Publication number
CN103554565B
CN103554565B CN201310362910.XA CN201310362910A CN103554565B CN 103554565 B CN103554565 B CN 103554565B CN 201310362910 A CN201310362910 A CN 201310362910A CN 103554565 B CN103554565 B CN 103554565B
Authority
CN
China
Prior art keywords
latex
paracril
natural rubber
preparation
gloves
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310362910.XA
Other languages
English (en)
Other versions
CN103554565A (zh
Inventor
高尚
王学斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhenjiang Huayang Latex Products Co., Ltd.
Original Assignee
ZHENJIANG SUHUI LATEX PRODUCT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHENJIANG SUHUI LATEX PRODUCT CO Ltd filed Critical ZHENJIANG SUHUI LATEX PRODUCT CO Ltd
Priority to CN201310362910.XA priority Critical patent/CN103554565B/zh
Publication of CN103554565A publication Critical patent/CN103554565A/zh
Application granted granted Critical
Publication of CN103554565B publication Critical patent/CN103554565B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种天然橡胶和丁腈橡胶共混的医用手套及其制备方法，本发明所述的一种天然橡胶和丁腈橡胶共混的医用手套具有乳胶手套良好的拉伸性能和柔软的手感。采用本发明方法制的橡胶医用手套，扯断力超过7.0N，伸长率大于650%，达到GB 10213-2006《一次性使用医用橡胶检查手套》的要求；手套手感柔软，使用方便舒适；同时有很好的耐油、耐溶剂性能。

Description

一种天然橡胶和丁腈橡胶共混的医用手套及其制备方法
技术领域
本发明涉及一种医用手套，特别涉及一种天然橡胶和丁腈橡胶共混的医用手套及其制备方法，属于橡胶手套技术领域。
背景技术
一次性使用手套已被广泛应用于现代生产生活中，根据生产制造所用材质的不同，可以分为天然橡胶手套、丁腈手套、PVC手套等等。这些手套，都可以很好的保护使用者免受外来致病微生物或有毒有腐蚀化学品的危害。其中，PVC手套虽然价格低廉，然而综合性能较差，在一定程度上限制了应用。为了获得更好的防护效果，人们更加倾向于天然橡胶手套和丁腈橡胶手套。其中，天然橡胶手套有手感柔软、拉伸性能好的优点，但是手套的耐化学品、耐溶剂性能差；丁腈手套有较好的耐油、耐溶剂性能，但是手套的弹性不如天然橡胶手套。
发明内容
本发明所要解决的技术问题是针对以上弊端提供一种综合了两种手套优点的手套，该手套要具有乳胶手套良好的拉伸性能和柔软的手感，同时又要具备丁腈橡胶手套的耐油、耐溶剂的优点。
为解决上述技术问题，本发明的技术方案是：
一种天然橡胶和丁腈橡胶共混的医用手套的制备方法，包括如下步骤：
Ａ、配制浸渍用的胶乳：取天然橡胶胶乳，丁腈橡胶胶乳，分散剂N，稳定剂聚丙烯酸钠，充分混合均匀；再加入硫磺、氧化锌、促进剂ZDEC，钛白粉和碱性填料，调节固含量为18%-35%，使得配制的胶乳pH值达到10-12；
Ｂ、模具烘干后，先浸渍凝固剂，凝固剂为重量百分比浓度为6%-16%的硝酸钙或氯化钙溶液；之后烘干模具；接着模具浸渍上述配制好的胶乳；再经过110-130摄氏度、20-40分钟的高温干燥；最后冷却，把手套从模具上脱下，就得到成品。
上述方法制备的天然橡胶和丁腈橡胶共混的医用手套，其中，所述一种浸渍用胶乳，其组成成分按干份质量分数计如下：
上述的天然橡胶和丁腈橡胶共混的医用手套，其中，所述碱性填料为氢氧化钾或氨水。
上述的天然橡胶和丁腈橡胶共混的医用手套，其中，所述碱性填料为氢氧化钾和氨水的混合物，氢氧化钾：氨水为1：1.5,按重量份数计。
本发明的有益效果为：使用该方法制的橡胶医用手套，扯断力超过7.0N，伸长率大于650%，达到GB10213-2006《一次性使用医用橡胶检查手套》的要求；手套手感柔软，使用方便舒适；同时有很好的耐油、耐溶剂性能。
具体实施方式
以下通过具体实施例对本发明的具体实施方式作进一步详细的说明。
本发明所述分散剂N为分散剂NNO，化学名称为亚甲基双萘磺酸钠，分子式为C21H14O6S2Na2，分子量为472.4418；所述促进剂ZDEC为橡胶硫化促进剂ZDEC，化学名称为二乙基二硫代氨基甲酸锌，分子式为C10H20N2S4Zn，分子量为361.9。
实例一：
一种天然橡胶和丁腈橡胶共混的医用手套的制备方法，其制备方法如下：首先配制浸渍用的橡胶胶乳。取天然橡胶胶乳70份，丁腈橡胶胶乳30份，分散剂N1.0份，稳定剂聚丙烯酸钠0.6份，充分混合均匀；加入硫磺1.0份，氧化锌1.0份，促进剂ZDEC0.7份，钛白粉1.9份，氢氧化钾0.6份，调节固含量至28%。陶瓷模具经过清洗、干燥后，首先浸渍重量百分比浓度10%的硝酸钙溶液，取出，烘干，浸渍该胶乳；随后卷边，接着浸入45摄氏度的温水2分钟，取出，经过125摄氏度30分钟的干燥，冷却，脱模，得成品。
实施例1所制得的一种丁腈橡胶手术手套的性能数据如下表，按GB10213-2006的标准进行检测。
表1  本发明制得的一种丁腈橡胶手术手套的性能数据
测试项目 单位 数值
扯断力 N 8.2
伸长率 % 750
GB  10213-2006 / 达标
实例二：
一种天然橡胶和丁腈橡胶共混的医用手套的制备方法，其制备方法如下：首先配制浸渍用的橡胶胶乳。取天然橡胶胶乳65份，丁腈橡胶胶乳35份，分散剂N 0.8份，稳定剂聚丙烯酸钠0.8份，充分混合均匀；加入硫磺0.6份，氧化锌1.2份，促进剂ZDEC 0.5份，钛白粉1.5份，氢氧化钾0.8份，调节固含量至25%。陶瓷模具经过清洗、干燥后，首先浸渍重量百分比浓度8%的氯化钙溶液，取出，烘干，浸渍该胶乳；随后卷边，接着浸入50摄氏度的温水2分钟，取出，经过120摄氏度35分钟的干燥，冷却，脱模，得成品。
实施例2所制得的一种丁腈橡胶手术手套的性能数据如下表：按GB10213-2006的标准进行检测。
表2  本发明制得的一种丁腈橡胶手术手套的性能数据
测试项目 单位 数值
扯断力 N 8.5
伸长率 % 730
GB  10213-2006 / 达标
实例三：
一种天然橡胶和丁腈橡胶共混的医用手套的制备方法，其制备方法如下：首先配制浸渍用的橡胶胶乳。取天然橡胶胶乳78份，丁腈橡胶胶乳40份，分散剂N 0.5份，稳定剂聚丙烯酸钠0.7份，充分混合均匀；加入硫磺0.8份，氧化锌1.5份，促进剂ZDEC 0.9份，钛白粉1.3份，氢氧化钾0.9份，调节固含量至25%。陶瓷模具经过清洗、干燥后，首先浸渍重量百分比浓度12%的氯化钙溶液，取出，烘干，浸渍该胶乳；随后卷边，接着浸入60摄氏度的温水3分钟，取出，经过130摄氏度25分钟的干燥，冷却，脱模，得成品。
实施例3所制得的一种丁腈橡胶手术手套的性能数据如下表，按GB10213-2006的标准进行检测。
表3  本发明制得的一种丁腈橡胶手术手套的性能数据
测试项目 单位 数值
扯断力 N 7.9
伸长率 % 690
GB  10213-2006 / 达标
实例四：
一种天然橡胶和丁腈橡胶共混的医用手套的制备方法，其制备方法如下：首先配制浸渍用的橡胶胶乳。取天然橡胶胶乳70份，丁腈橡胶胶乳30份，分散剂N 1.0份，稳定剂聚丙烯酸钠0.6份，充分混合均匀；加入硫磺1.0份，氧化锌1.0份，促进剂ZDEC 0.7份，钛白粉1.9份，氨水0.6份，调节固含量至28%。陶瓷模具经过清洗、干燥后，首先浸渍重量百分比浓度10%的硝酸钙溶液，取出，烘干，浸渍该胶乳；随后卷边，接着浸入45摄氏度的温水2分钟，取出，经过125摄氏度30分钟的干燥，冷却，脱模，得成品。
实施例4所制得的一种丁腈橡胶手术手套的性能数据如下表：
表4  本发明制得的一种丁腈橡胶手术手套的性能数据，按GB10213-2006的标准进行检测。
测试项目 单位 数值
扯断力 N 8.3
伸长率 % 770
GB  10213-2006 / 达标
实施例五：
一种天然橡胶和丁腈橡胶共混的医用手套的制备方法，其制备方法如下：首先配制浸渍用的橡胶胶乳。取天然橡胶胶乳68份，丁腈橡胶胶乳34份，分散剂N 0.6份，稳定剂聚丙烯酸钠0.9份，充分混合均匀；加入硫磺0.5份，氧化锌1.3份，促进剂ZDEC 0.3份，钛白粉1.1份，氨水0.3份，调节固含量至26%。陶瓷模具经过清洗、干燥后，首先浸渍重量百分比浓度11%的氯化钙溶液，取出，烘干，浸渍该胶乳；随后卷边，接着浸入48摄氏度的温水2分钟，取出，经过125摄氏度38分钟的干燥，冷却，脱模，得成品。
实施例5所制得的一种丁腈橡胶手术手套的性能数据如下表：
表5  本发明制得的一种丁腈橡胶手术手套的性能数据，按GB10213-2006的标准进行检测。
测试项目 单位 数值
扯断力 N 8.5
伸长率 % 780
GB  10213-2006 / 达标
实施例六：
一种天然橡胶和丁腈橡胶共混的医用手套的制备方法，其制备方法如下：首先配制浸渍用的橡胶胶乳。取天然橡胶胶乳73份，丁腈橡胶胶乳39份，分散剂N 0.7份，稳定剂聚丙烯酸钠0.4份，充分混合均匀；加入硫磺0.7份，氧化锌1.4份，促进剂ZDEC 0.4份，钛白粉0.7份，氢氧化钾和氨水的混合物0.9份，氢氧化钾：氨水为1：1.5,按重量份数计，调节固含量至26%。陶瓷模具经过清洗、干燥后，首先浸渍重量百分比浓度11%的氯化钙溶液，取出，烘干，浸渍该胶乳；随后卷边，接着浸入55摄氏度的温水2分钟，取出，经过128摄氏度28分钟的干燥，冷却，脱模，得成品。
实施例6所制得的一种丁腈橡胶手术手套的性能数据如下表：
表6  本发明制得的一种丁腈橡胶手术手套的性能数据，按GB10213-2006的标准进行检测。
测试项目 单位 数值
扯断力 N 8.9
伸长率 % 810
GB  10213-2006 / 达标
这里本发明的描述和应用是说明性的，并非想将本发明的范围限制在上述实施例中，因此，本发明不受本实施例的限制，任何采用等效替换取得的技术方案均在本发明保护的范围内。

Claims (1)

1.一种天然橡胶和丁腈橡胶共混的医用手套的制备方法，其特征在于，包括如下步骤：
A、配制浸渍用的胶乳：取天然橡胶胶乳，丁腈橡胶胶乳，分散剂N，稳定剂聚丙烯酸钠，充分混合均匀；再加入硫磺、氧化锌、促进剂ZDEC，钛白粉和碱性填料，调节固含量为18％-35％，使得配制的胶乳pH值达到10-12；
B、模具烘干后，先浸渍凝固剂，凝固剂为重量百分比浓度6％-16％的硝酸钙或氯化钙溶液；之后烘干模具；接着模具浸渍上述配制好的胶乳；再经过110-130摄氏度、20-40分钟的高温干燥；最后冷却，把手套从模具上脱下，就得到成品；
上述所述浸渍用胶乳，其组成成分按干份质量份数计如下：
所述碱性填料为氢氧化钾或氨水或氢氧化钾和氨水的混合物，氢氧化钾：氨水为1：1.5,按重量份数计。
CN201310362910.XA 2013-08-20 2013-08-20 一种天然橡胶和丁腈橡胶共混的医用手套及其制备方法 Active CN103554565B (zh)