CN113279108A - 基于莱赛尔纤维的经平绒面料及其制备方法 - Google Patents
基于莱赛尔纤维的经平绒面料及其制备方法 Download PDFInfo
- Publication number
- CN113279108A CN113279108A CN202110361877.3A CN202110361877A CN113279108A CN 113279108 A CN113279108 A CN 113279108A CN 202110361877 A CN202110361877 A CN 202110361877A CN 113279108 A CN113279108 A CN 113279108A
- Authority
- CN
- China
- Prior art keywords
- fabric
- washing
- warp
- panne
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种基于莱赛尔纤维的经平绒面料及其制备方法，利用莱赛尔纤维织造经平绒面料，采用自研高速喷气平织机织造，经平绒面料的地经、绒经排列比为2:1，所述绒经为半绒V型固结结构；然后采用干定型工艺对所述经平绒面料进行坯布定型，然后对定型后的经平绒面料进行水洗，水洗方式为松式水洗，最后对水洗后的经平绒面料进行染色、固色、水洗、皂洗、刷毛，得到整理后的经平绒面料。本发明以
希赛尔纤维为原料，面料具有特有的光泽和手感，面料绒面平整，绒毛高度差极小，且绒毛不倒伏。
Description
技术领域
本发明涉及面料技术领域，尤其涉及一种基于莱赛尔纤维的经平绒面料及其制备方法。
背景技术
目前，国内外经平绒行业目前使用的织机类型主要有两类。一类是低速简易剑杆平绒织机，其是以老式有梭织机为基础，研发的一种简易剑杆织机，因为机械制造精度低，故障率高，织机的车速低、产品质量差等一系列问题，长期以来只能生产低品质的经平绒织物。另一类是老式有梭平绒织机，其同样存在机械制造精度低，故障率高，织机的车速低、产品质量差等一系列问题，由于多采用凸轮开口机构，织物组织结构更改困难。
虽然目前各种新型纤维素纤维在纺织品中得到广泛运用，但经平绒行业的上述现状限制了各种新型纤维在经平绒织物生产中的使用。
发明内容
为解决上述技术问题，本发明的目的是提供一种基于莱赛尔纤维的经平绒面料及其制备方法，以
希赛尔纤维为原料，面料具有特有的光泽和手感，面料绒面平整，绒毛高度差极小，且绒毛不倒伏。
一方面，本发明公开了一种基于莱赛尔纤维的经平绒面料的制备方法，包括以下步骤：
(1)利用莱赛尔纤维织造经平绒面料，所述经平绒面料的地经、绒经排列比为2:1，所述绒经为半绒V型固结结构；
(2)采用干定型工艺对所述经平绒面料进行坯布定型，干定型温度为180-190℃；
(3)对定型后的经平绒面料进行水洗，水洗方式为松式水洗，所述松式水洗包括在80-90℃条件下水洗15分钟以上，然后在45-55℃条件下水洗20分钟以上，最后在25℃条件下水洗的步骤；
(4)对水洗后的经平绒面料进行染色、固色、水洗、皂洗、刷毛，得到整理后的经平绒面料；其中，染色时所用的染浴中包括活性染料和元明粉，染色温度为35℃±5℃；固色时所用的固色浴中包括纯碱和元明粉，固色温度为35℃±5℃；水洗温度为20-30℃；皂洗时，先在95℃-100℃以上时用净洗剂和纯碱的混合溶液进行洗涤，然后在50-60℃下水洗，最后在20-30℃下水洗；刷毛时，采用双向起绒工艺，刷毛温度为125℃±5℃，经平绒面料移动速度为12米/分，刷毛时在氨基硅柔软剂的作用下进行。
进一步地，在步骤(1)中，所述莱赛尔纤维为14.6tex×2的股线。
为了表现出莱赛尔纤维特有的光泽和手感，要求经平绒面料的绒面平整、绒毛高度差极小，且绒毛不倒伏。本发明的经平绒面料的在沿纬线长度方向上，相邻三组绒毛的高度差异在0.2mm以内。在织造环节，织机绒经送经机构采用高灵敏度传感器检测，通过高精度伺服电机驱动，使绒经的送经量非常精准，从而保证了绒毛高度的一致性。在织物组织设计上，采用地经、绒经比例2：1的配比，绒经为半绒V型固结结构，可充分体现出莱赛尔纤维特有的光泽和质感。
进一步地，在步骤(2)中，干定型时，所述经平绒面料的移动速度为60米/分钟。
步骤(2)的坯布定型是为了消除折皱，提高分子结构摆列的均匀度，并且预收门幅也可以避免后续工艺中因为剧烈收缩造成绒面起皱的现象。
进一步地，在步骤(3)中，在80-90℃条件下水洗时，水中添加有精炼剂，所述精炼剂在水中的浓度为8g/L。
进一步地，所述精炼剂为英杰CO-01。
进一步地，在步骤(3)中，在45-55℃条件下水洗时，洗涤两次，每次≥10分钟。
出于对于绒面保护的角度考虑，本发明未采用传统的紧式整理，而是采用纯松式的吊缸水洗方式。使得绒面几乎受不到任何的作用力，保持了绒面天然的韧性。在织造前，经纱采取不上浆工艺，所以坯布前处理不需要做退浆处理，且无需复杂的煮漂工艺。
进一步地，在步骤(4)中，染浴中，活性染料的浓度为4.5-48g/L。具体地，活性染料为润土W-NN黑时，其浓度为48g/L；活性染料为苏明天彩B元青时，其浓度为4.5g/L；活性染料为苏明天彩3RF黄时，其浓度为4.5g/L。染浴中，每缸米数450-500米，水量500L±10L。
进一步地，染浴中，元明粉的浓度为50g/L。
进一步地，活性染料选自WNN黑45染色时选择活性染料，因为活性染料相比于直接染料颜色鲜艳度跟色牢度都比较好。
进一步地，染色时以松式的吊缸作为染色载体。
进一步地，染色时间为30分钟，固色时间30分钟。
进一步地，在步骤(4)中，固色浴中，纯碱浓度为3g/L，元明粉浓度为50g/L。
进一步地，在步骤(4)中，固色完后先用常温水清洗两次，一次清洗≥10分钟。
进一步地，在步骤(4)中，皂洗时，混合溶液中，净洗剂的浓度为0.25g/L，纯碱的浓度为0.25g/L。
进一步地，净洗剂选自英杰CO-01。净洗剂具有净洗，渗透，螯合，分散，乳化作用。
进一步地，在步骤(4)中，在50-60℃下水洗时，清洗两次，每次≥10分钟。
进一步地，在步骤(4)中，刷毛之前还包括采用硅油浸轧处理的步骤。
进一步地，在步骤(4)中，刷毛后成品包装，采用中空悬挂的方式放在包装箱内。
传统的短纤平绒织物染色工艺、后整理刷毛工艺对绒布的纬纱破坏很大，导致纬向撕破强力下降，本发明采用松式整理工艺，包括染色、固色、水洗、皂洗、刷毛，使面料纬纱保持完整。
另一方面，本发明还要求保护采用上述制备方法所制备的基于莱赛尔纤维的经平绒面料。
本发明中的莱赛尔纤维为
希赛尔纤维，其是由线密度为1.3dtex×38mm的莱赛尔纤维，由中纺院绿色纤维股份有限公司纺制成14.6tex×2的股线。其中，莱赛尔纤维是以N-甲基氧化吗琳(NMMO)水溶液为溶剂，直接将纤维素浆粕溶解得到纺丝溶液，再采用干喷湿法纺丝，以一定浓度的NMMO-H2O溶液为凝固浴使纤维成型，再将纺得的初生纤维经拉伸、水洗、上油、干燥而制得的一种新型纤维素纤维。
进一步地，本发明中的莱赛尔纤维(规格：1.3dtex×38mm)的性能参数(20℃，相对湿度65％条件下)如下：
借由上述方案，本发明至少具有以下优点：
本发明的基于莱赛尔纤维的经平绒面料的制备方法可以保证莱赛尔纤维的光泽和质感，使得面料绒面平整，绒毛高度差极小，且绒毛不倒伏，所制备的经平绒面料的干摩擦牢度达到4-5级，湿摩擦2-3级，皂洗牢度可以达到4级。
上述说明仅是本发明技术方案的概述，为了能够更清楚了解本发明的技术手段，并可依照说明书的内容予以实施，以下以本发明的较佳实施例并配合详细附图说明如后。
附图说明
图1是本发明所用的
希赛尔纤维的横截面SEM图。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步详细描述。以下实施例用于说明本发明，但不用来限制本发明的范围。
本发明中，代号为英杰CO-01的试剂购买自黄山怡凯新材料有限公司。
实施例1
采用
希赛尔纤维为原料制备基于莱赛尔纤维的经平绒面料，其制备方法如下：
(1)利用
希赛尔纤维织造经平绒面料，经平绒面料的地经、绒经排列比为2:1，所述绒经为半绒V型固结结构；其中，
希赛尔纤维是由线密度为1.3dtex×38mm的莱赛尔纤维，由中纺院绿色纤维股份有限公司纺制成14.6tex×2的股线。
(2)采用干定型工艺对经平绒面料进行坯布定型，干定型温度为温度控制在185℃±5℃，车速为60米/分钟。
(3)对定型后的经平绒面料进行水洗，采用纯松式的吊缸进行松式水洗。松式水洗时，首先在85℃±5℃的温水中加入8g/L的精炼剂洗涤≥15分钟。然后在50℃±5℃的温水中洗涤两次，一次≥10分钟。最后在25℃±5℃的水中清洗一次。其中，精炼剂为英杰CO-01。
(4)对水洗后的经平绒面料进行染色。染色时所用的染浴中包括活性染料和元明粉。活性染料为润土W-NN黑时，其浓度为48g/L；活性染料为苏明天彩B元青时，其浓度为4.5g/L；活性染料为苏明天彩3RF黄时，其浓度为4.5g/L。染浴中，每缸米数450-500米，水量500L±10L。元明粉的浓度为50g/L。染色温度为35℃±5℃，时间为≥30分钟。
染色完成后进行固色，固色时所用的固色浴中包括纯碱和元明粉，纯碱浓度为3g/L，元明粉浓度为50g/L，固色温度为35℃±5℃，时间为≥30分钟。固色用常温水清洗两次，一次清洗≥10分钟。
然后进行皂洗，皂洗时，头缸温度在95℃以上，所用洗剂为净洗剂和纯碱的混合溶液，混合溶液中，净洗剂的浓度为0.25g/L，纯碱的浓度为0.25g/L。然后用50-60℃温水清洗两次，一次≥10分钟，最后过一次常温水即可出缸。
皂洗完成后，柔烘刷毛。温度125℃±5℃，车速12米/分。前车料槽加入40g/L的氨基硅柔软剂。然后加10g/L硅油浸轧后进烘箱，烘箱内开2根鬃毛刷双向起绒。
最后对上述整理后的面料进行包装，包装时，采取中空悬挂的方式放在单个纸箱内，保证在运输过程中不会因为外部力量损伤绒面。
经上述工艺整理后得到的经平绒面料，干摩擦牢度达到4-5级，湿摩擦2-3级，皂洗牢度可以达到4级。
以上所述仅是本发明的优选实施方式，并不用于限制本发明，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和变型，这些改进和变型也应视为本发明的保护范围。
Claims (10)
1.一种基于莱赛尔纤维的经平绒面料的制备方法，其特征在于，包括以下步骤：
(1)利用莱赛尔纤维织造经平绒面料，所述经平绒面料的地经、绒经排列比为2:1，所述绒经为半绒V型固结结构；
(2)采用干定型工艺对所述经平绒面料进行坯布定型，干定型温度为180-190℃；
(3)对定型后的经平绒面料进行水洗，水洗方式为松式水洗，所述松式水洗包括在80-90℃条件下水洗15分钟以上，然后在45-55℃条件下水洗20分钟以上，最后在25℃条件下水洗的步骤；
(4)对水洗后的经平绒面料进行染色、固色、水洗、皂洗、刷毛，得到整理后的经平绒面料；其中，染色时所用的染浴中包括活性染料和元明粉，染色温度为35℃±5℃；固色时所用的固色浴中包括纯碱和元明粉，固色温度为35℃±5℃；水洗温度为20-30℃；皂洗时，先在95℃-100℃时用净洗剂和纯碱的混合溶液进行洗涤，然后在50-60℃下水洗，最后在20-30℃下水洗；刷毛时，采用双向起绒工艺，刷毛温度为125℃±5℃，经平绒面料移动速度为12米/分，刷毛时在氨基硅柔软剂的作用下进行。
2.根据权利要求1所述的制备方法，其特征在于：在步骤(1)中，所述莱赛尔纤维为14.6tex×2的股线。
3.根据权利要求1所述的制备方法，其特征在于：在步骤(2)中，干定型时，所述经平绒面料的移动速度为60米/分钟。
4.根据权利要求1所述的制备方法，其特征在于：在步骤(3)中，在80-90℃条件下水洗时，水中添加有精炼剂，所述精炼剂在水中的浓度为8g/L。
5.根据权利要求4所述的制备方法，其特征在于：所述精炼剂代号为英杰CO-01。
6.根据权利要求1所述的制备方法，其特征在于：在步骤(3)中，在45-55℃条件下水洗时，洗涤两次，每次10分钟以上。
7.根据权利要求1所述的制备方法，其特征在于：在步骤(4)中，染浴中，活性染料的浓度为4.5-48g/L，元明粉的浓度为50g/L。
8.根据权利要求1所述的制备方法，其特征在于：在步骤(4)中，固色浴中，纯碱浓度为3g/L，元明粉浓度为50g/L。
9.根据权利要求1所述的制备方法，其特征在于：在步骤(4)中，皂洗时，混合溶液中，净洗剂的浓度为0.25g/L，纯碱的浓度为0.25g/L。
10.一种权利要求1-9中任一项所述的制备方法所制备的基于莱赛尔纤维的经平绒面料。