CN112680118B - 一种用于笔记本电脑框架粘接的丙烯酸酯结构胶及其制备方法 - Google Patents
一种用于笔记本电脑框架粘接的丙烯酸酯结构胶及其制备方法 Download PDFInfo
- Publication number
- CN112680118B CN112680118B CN202011565946.4A CN202011565946A CN112680118B CN 112680118 B CN112680118 B CN 112680118B CN 202011565946 A CN202011565946 A CN 202011565946A CN 112680118 B CN112680118 B CN 112680118B
- Authority
- CN
- China
- Prior art keywords
- toluidine
- main agent
- structural adhesive
- preparation
- acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种用于笔记本电脑框架粘接的丙烯酸酯结构胶,所述丙烯酸酯结构胶由主剂和活化剂组成,主剂按重量百分比计算由如下组分组成:单官能丙烯酸酯单体40%~58%,多管能丙烯酸酯单体1%~8%,抗冲击核壳树脂15%~30%,弹性体5%~15%,甲基丙烯酸1~8%,促进剂0.5~2%,稳定剂0.1~1%,挥发抑制剂0.1~2%;活化剂按重量百分比计算由如下组分组成:增塑剂10%~35%,环氧树脂15%~38%,引发剂15%~35%,填料1%~5%。本发明还公开了其制备方法。本发明的丙烯酸酯结构胶适用于轻量化框架材料镁合金的结构粘接。固化后具有很好的拉拔力,同时也有很好的韧性,耐冲击性,高伸长率以及热压快速固化定位的优点。
Description
技术领域
本发明涉及双组份丙烯酸酯结构胶技术领域,具体涉及一种用于笔记本电脑框架粘接的丙烯酸酯结构胶及其制备方法。
背景技术
双组份丙烯酸酯胶黏剂因室温快速固化、强度高、韧性好、工艺简便等特点,广泛用于各行各业的结构粘接。
笔记本电脑框架组装要求胶粘剂操作时间满足框架粘接工艺标准的前提下还可以加热使胶粘剂快速固化定位,缩短工艺时间从而大大提高生产效率。
由于以前笔记本电脑框架的材料多为铝合金和不锈钢,市场上有很多胶黏剂可以满足。
不过近年来由于笔记本电脑轻量化的要求越来越高,导致其框架材料选择了质量更轻强度更高同时具有能够承受更大冲击载荷的镁合金,然而采用镁合金相对于铝合金以及不锈钢来说,不利于胶粘剂的粘接,也是导致框架结构强度低的主要原因。因此需要设计一种即能满足现有笔记本框架粘接工艺又能对镁合金材料具有良好的粘接强度的丙烯酸酯结构胶来满足现有笔记本电脑框架的粘接需要。
发明内容
有鉴于此,本发明提供了一种用于笔记本电脑框架粘接的丙烯酸酯结构胶,能够满足现有工艺条件又能解决现有胶黏剂对镁合金粘接强度低的问题。
为实现此目的,本发明所采用的技术方案如下:
一种用于笔记本电脑框架粘接的丙烯酸酯结构胶,由主剂、活化剂两部分组成,所述主剂包括如下重量百分比的组分:
单官能丙烯酸酯单体40%~58%;
多管能丙烯酸酯单体1%~8%;
抗冲击核壳树脂15%~30%;
弹性体5%~15%;
甲基丙烯酸5~10%;
稳定剂0.1~1%;
促进剂0.5~2%;
挥发抑制剂0.1~2%;
所述活化剂当中包括了如下重量百分比的组分:
增塑剂10%~35%;
环氧树脂15%~38%;
引发剂15%~35%;
填料1%~5%。
在本发明的一个优选实施例中,所述单官能丙烯酸酯单体为甲基丙烯酸甲酯、甲基丙烯酸异冰片酯、甲基丙烯酸十八烷基酯或甲基丙烯酸十六烷基酯中的任意一种或多种。
在本发明的一个优选实施例中,所述多官能丙烯酸酯单体为聚乙二醇二甲基丙烯酸酯、1,3丁二醇二甲基丙烯酸酯、乙氧化双酚A二甲基丙烯酸酯或三羟甲基丙烷三甲基丙烯酸酯中的任意一种或多种。
在本发明的一个优选实施例中,所述的抗冲击核壳树脂为MBS树脂。优选为钟渊化学生产的MBS树脂牌号为B564、M511、M521、M711,罗门哈斯生产的MBS树脂牌号为BTA753。
在本发明的一个优选实施例中,所述弹性体为丁腈橡胶、聚氨酯改性丙烯酸酯树脂、ABS树脂、SBS树脂、BS树脂或聚丁二烯橡胶中的任意一种或多种。
在本发明的一个优选实施例中,所述引发剂为过氧化物。优选为过氧化苯甲酰。
在本发明的一个优选实施例中,所述稳定剂为对苯二酚、对苯醌、1,4-萘醌、草酸或四钠盐中的任意一种或多种。
在本发明的一个优选实施例中,所述环氧树脂为双酚F型环氧树脂、双酚A型环氧树脂或酚醛环氧树脂中的任意一种或多种。
在本发明的一个优选实施例中,所述挥发抑制剂为石蜡。
在本发明的一个优选实施例中,所述促进剂为胺类化合物。优选为N,N-二甲基对甲苯胺,N,N-二羟乙基对甲苯胺中的一种或两者混合物。
在本发明的一个优选实施例中,所述增塑剂为邻苯二甲酸二丁酯、邻苯二甲酸二乙基己酯、邻苯二甲酸二乙酯或己二酸二异癸酯中的任意一种或多种。
在本发明的一个优选实施例中,所述填料为高密度聚乙烯、气相白炭黑或碳酸钙中的任意一种或多种。
一种用于笔记本电脑框架粘接的丙烯酸酯结构胶的制备方法,包括如下步骤:
主剂的制备:将所述单官能丙烯酸酯单体、多官能丙烯酸酯单体、甲基丙烯酸、抗冲击树脂、弹性体、挥发抑制剂、稳定剂投入反应釜中,搅拌至抗冲击树脂和弹性体完全溶解;再向反应釜中投入促进剂搅拌至混合均匀(优选搅拌时间为1-2小时),真空脱除气泡得主剂部分;
活化剂的制备:将所述增塑剂、环氧树脂、引发剂投入反应釜中,搅拌至完全溶解;
再向反应釜中投入填料搅拌至混合均匀(优选搅拌时间为1-2小时),真空脱出气泡得活化剂部分;
将所述主剂部分和所述活化剂按照体积比10:1进行混合均匀涂胶。
本发明的有益效果在于:
本发明制备的丙烯酸酯结构胶是一种用于笔记本电脑框架粘接的丙烯酸酯结构胶,能够满足现有工艺条件又能解决现有胶黏剂对镁合金粘接强度低的问题。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚,下面将结合具体实施例,对本发明作进一步的详细说明。
实施例1如表1所示:
表1
制备工艺:
主剂的制备:将甲基丙烯酸甲酯、甲基丙烯酸、稳定剂、多官能丙烯酸酯单体、B564、SBS、聚丁二烯橡胶、石蜡投入反应釜中,搅拌至B564及SBS完全溶解;再向反应釜中投入促进剂、聚氨酯丙烯酸酯树脂搅拌1-2小时至混合均匀,真空脱出气泡得主剂;
活化剂的制备:将增塑剂、环氧树脂、BPO投入反应釜中,搅拌至BPO均匀分散;再向反应釜中投入高密度聚乙烯、气相白炭黑搅拌至混合均匀,真空脱出气泡得活化剂。
将主剂和活化剂按照体积比10:1进行配比涂胶。
实施例2如表2所示:
表2
制备工艺同实施例1。
实施例3如表3所示:
表3
制备工艺同实施例1。
性能测试:
根据笔记本行业规定对实施例1-3、比较例(KD005)进行热压测试以及固化后的拉拔力测试(测试标准:GB/T 6329-1996)如表4所示:
表4
测试材料:镁合金对铝的粘接;
KD005:上海康达化工新材料集团股份有限公司生产的笔电行业专用的丙烯酸酯结构胶。
由表4可知,本发明实施例1-3当中的拉拔力均大幅提高,这是因为实施例1-3中聚丁二烯橡胶和丁腈橡胶提供了高柔韧性的主交联分子链,这让拉拔力提高的同时也增加了胶粘剂整体的柔韧性及伸长率.聚氨酯丙烯酸酯树脂的加入可以很明显的提高对镁合金的拉拔力。核壳树脂的加入使得实施例1-3具有优良的耐抗冲击性能,增加或减少其在实施例中的添加量会对胶黏剂整体的粘度以及单位时间的出胶量有影响。实施例1-3中添加的两种胺具有协同增效促进功能,因而可以使胶粘剂热压快速固化定位。
以上所述的具体实施例,对本发明的目的、技术方案和有益效果进行了进一步的详细说明,但是本领域技术人员可以在不脱离本发明的精神和范围的情况下做出各种修改和变型,这样的修改和变型均落入由所附权利要求所限定的范围之内。
Claims (1)
1.一种用于笔记本电脑框架粘接的丙烯酸酯结构胶,其特征在于,由主剂、活化剂两部分组成,所述主剂由如下含量的组分组成:
甲基丙烯酸甲酯 40;
甲基丙烯酸 10;
稳定剂 1;
多官能丙烯酸单体 4;
B564 14.5;
SBS 11;
聚丁二烯橡胶 11;
石蜡 1;
N,N-二羟乙基对甲苯胺 1;
N,N-二甲基对甲苯胺 0.5;
聚氨酯丙烯酸酯树脂 6;
或
甲基丙烯酸甲酯 40;
甲基丙烯酸 10;
稳定剂 1;
多官能丙烯酸单体 4;
B564 14.5;
SBS 11;
丁腈橡胶 11;
石蜡 1;
N,N-二羟乙基对甲苯胺 1;
N,N-二甲基对甲苯胺 0.5;
聚氨酯丙烯酸酯树脂 6;
所述活化剂由如下含量的组分组成:
增塑剂 20.1;
环氧树脂 30.3;
BPO 35.6;
高密度聚乙烯 10;
气相白炭黑 4;
所述丙烯酸酯结构胶由如下方法制备而成:
主剂的制备:将甲基丙烯酸甲酯、甲基丙烯酸、稳定剂、多官能丙烯酸酯单体、B564、SBS、聚丁二烯橡胶或丁腈橡胶、石蜡投入反应釜中,搅拌至B564及SBS完全溶解;再向反应釜中投入促进剂N,N-二羟乙基对甲苯胺和N,N-二甲基对甲苯胺、聚氨酯丙烯酸酯树脂搅拌1-2小时至混合均匀,真空脱出气泡得主剂;
活化剂的制备:将增塑剂、环氧树脂、BPO投入反应釜中,搅拌至BPO均匀分散;再向反应釜中投入高密度聚乙烯、气相白炭黑搅拌至混合均匀,真空脱出气泡得活化剂;
将主剂和活化剂按照体积比10:1进行配比涂胶。