CN112071975A - 平坦化fbar谐振器制备方法 - Google Patents
平坦化fbar谐振器制备方法 Download PDFInfo
- Publication number
- CN112071975A CN112071975A CN202011028970.4A CN202011028970A CN112071975A CN 112071975 A CN112071975 A CN 112071975A CN 202011028970 A CN202011028970 A CN 202011028970A CN 112071975 A CN112071975 A CN 112071975A
- Authority
- CN
- China
- Prior art keywords
- lower electrode
- substrate
- planarized
- forming
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种平坦化FBAR谐振器制备方法，包括：在衬底上形成下电极；在下电极和衬底上形成介质层，具有第一厚度；平坦化介质层以将第一厚度减小为第二厚度；刻蚀介质层直至暴露下电极；在下电极和衬底上形成压电层；在压电层上形成上电极。依照本发明的谐振器制造方法，依次采用沉积、平坦化、刻蚀工艺分步在下电极上形成具有平坦表面的压电层，减少了缺陷，避免了声波能量泄漏。
Description
技术领域
本发明涉及一种谐振器制造方法，特别是一种具有平坦表面的平坦化FBAR谐振器制备方法。
背景技术
在无线通讯中，射频滤波器作为过滤特定频率信号的中介，用于减少不同频段的信号干扰，在无线收发器中实现镜像消除、寄生滤波和信道选择等功能。随着4GLTE网络的部署和市场的增长，射频前端的设计朝着小型化、低功耗和集成化的方向发展，市场对滤波性能的要求也越来越高。由于薄膜体声波谐振器(FilmBulkAcousticResonator，简称“FBAR”，也称“体声波”，BulkAcousticWave，简称“BAW”，)具有尺寸小、工作频率高、功耗低、品质因数(Q值)高、直接输出频率信号、与CMOS工艺兼容等特点，目前已经成为射频通讯领域重要的器件被广泛应用。
FBAR是制作在衬底材料上的电极——压电膜——电极的三明治结构的薄膜器件。FBAR的结构有空腔型、布拉格反射型(SMR)和背面刻蚀型。其中空腔型FBAR相对SMR型Q值要高，损耗要小，机电耦合系数要高；相对于背面刻蚀型FBAR不需要去掉大面积的衬底，机械强度较高。因此，空腔型FBAR是集成于CMOS器件上的首选。
在传统的制造工艺中，如图1中所示，衬底1中的空腔1A上形成的下电极2通常受限于沉积工艺而难以具有垂直侧壁，下电极2上方进一步沉积的压电层3则由于下电极2尾端倾斜侧壁而相应地也具有倾斜坡面，在该处压电薄膜生长质量不佳，在图中虚线椭圆框处容易出现断裂、塌陷等缺陷，导致产品最终Q值下降。
另一方面，压电层3上形成的上电极堆叠结构4/5不仅形成在压电层3平坦的顶部上，同时也形成在上述坡面上，因此下电极和上电极难以完全平行，如图1中箭头所示产生的电场包括纵向和水平两个分量，容易引起声波能量在水平方向的泄漏，进一步降低了Q值。
发明内容
因此，本发明的目的在于克服以上技术障碍而提供一种具有平坦表面的平坦化FBAR谐振器制备方法。
本发明提供了一种平坦化FBAR谐振器制备方法，包括：
在衬底上形成下电极；
在下电极和衬底上形成介质层，具有第一厚度；
平坦化介质层以将第一厚度减小为第二厚度；
刻蚀介质层直至暴露下电极；
在下电极和衬底上形成压电层；
在压电层上形成上电极。
形成下电极之前进一步包括，在衬底上形成衬垫层。其中，衬垫层材质为金属氮化物，优选地为AlN、HfN、HfAlN、TiN、TaN。
其中，第一厚度为0.05-10微米，任选地第二厚度为100-2000埃。
其中，平坦化介质层之后测量第二厚度，并根据第二厚度调节刻蚀介质层的工艺参数。
其中，衬底的材料为Si、SOI、Ge、GeOI、化合物半导体；介质层的材料为氧化物、氮化物或氮氧化物，优选地介质层与压电层晶格常数相同或相近；任选地，压电层的材料为ZnO、AlN、BST(钛酸锶钡)、BT(钛酸钡)、PZT(锆钛酸铅)、PBLN(铌酸铅钡锂)、PT(钛酸铅)，进一步优选地压电材料中掺杂稀土元素；任选地，下电极或上电极的材料为选自Mo、W、Ru、Al、Cu、Ti、Ta、In、Zn、Zr、Fe、Mg的金属单质或金属合金、或者这些金属的导电氧化物、或导电氮化物，以及上述材料的任意组合。
其中，在衬底上形成下电极之后下电极具有倾斜侧壁。形成第一压电层之前进一步包括刻蚀下电极的倾斜侧壁，使得下电极具有垂直侧壁。任选地，形成下电极期间在多个沉积工艺之间插入刻蚀工艺使得下电极具有垂直侧壁。
形成下电极之前进一步包括刻蚀衬底形成空腔并在空腔中填充牺牲层，形成上电极之后进一步包括湿法腐蚀去除牺牲层在衬底中留下谐振腔。
其中，上电极尺寸大于下电极尺寸。
依照本发明的平坦化FBAR谐振器制备方法，依次采用沉积、平坦化、刻蚀工艺分步在下电极上形成具有平坦表面的压电层，减少了缺陷，避免了声波能量泄漏。
本发明所述目的，以及在此未列出的其他目的，在本申请独立权利要求的范围内得以满足。本发明的实施例限定在独立权利要求中，具体特征限定在其从属权利要求中。
附图说明
以下参照附图来详细说明本发明的技术方案，其中：
图1显示了根据现有技术的谐振器的剖视图；
图2至图7显示了根据本发明实施例的谐振器制造工艺各个阶段的剖视图；以及
图8显示了根据本发明实施例的谐振器制造工艺的流程图。
具体实施方式
以下参照附图并结合示意性的实施例来详细说明本发明技术方案的特征及其技术效果，公开了具有平坦表面的谐振器的制备方法。需要指出的是，类似的附图标记表示类似的结构，本申请中所用的术语“第一”、“第二”、“上”、“下”等等可用于修饰各种器件结构。这些修饰除非特别说明并非暗示所修饰器件结构的空间、次序或层级关系。
如图2、图8所示，在衬底10上形成下电极12。提供衬底10，材质可以是体Si或绝缘体上硅(SOI)或者体Ge、GeOI以与CMOS工艺兼容并与其他数字、模拟电路集成，也可以是用于MEMS、光电器件、功率器件的化合物半导体例如GaN、GaAs、SiC、InP、GaP等，进一步优选地，衬底10是单晶材料。刻蚀衬底10形成多个空腔，并沉积牺牲层10A填充。刻蚀工艺优选各向异性的干法刻蚀或湿法刻蚀，例如碳氟基刻蚀气体的反应离子刻蚀，或者TMAH的湿法腐蚀。沉积工艺为LPCVD、APCVD、PECVD等低温工艺(沉积温度低于500摄氏度，优选100至400摄氏度)，牺牲层10A材质为氧化硅基材料，诸如掺硼氧化硅(BSG)、掺磷氧化硅(PSG)、未掺杂氧化硅(USG)、多孔氧化硅等等，如此可以降低衬底10中残留热应力，并有利于提高后续刻蚀去除的速度以节省时间成本。
任选地，在形成下电极12之前可以进一步在牺牲层10A上形成衬垫层或种子层11，其材质与未来将要形成的压电层相同或相近，用于提高下电极边缘处的外延生长质量。沉积工艺例如磁控溅射、热蒸发、MOCVD等。在本发明一个优选实施例中，衬垫层或种子层11材质为金属氮化物，例如AlN、HfN、HfAlN、TiN、TaN等，且优选地同时可以用作防止下电极金属材料向下迁移的阻挡层以避免影响谐振腔顶部以及与下方膜层之间的界面状态。
随后，例如采用磁控溅射、热蒸发、MOCVD等，在衬底10和牺牲层10A之上形成下电极12，其材质例如Mo、W、Ru、Al、Cu、Ti、Ta、In、Zn、Zr、Fe、Mg等金属单质或金属合金，或者这些金属的导电氧化物、导电氮化物，以及上述材料的任意组合。如图2中所示，由于沉积工艺的限制，下电极12末端通常具有倾斜侧壁。优选地，形成下电极12之后采用各向异性刻蚀工艺去除下电极12末端的倾斜侧壁，使其具有垂直侧壁。此外，任选地，也可以在形成下电极期间在多个沉积工艺的子循环之间插入一个或多个刻蚀工艺子循环，使得最终得到的下电极具有垂直侧壁。
接着，如图3、图8所示，在下电极12和衬底10上形成介质层13。例如采用PECVD、UHCVD、HDPCVD、MOCVD、MBE、ALD、磁控溅射、热蒸发等工艺沉积介质层13，其材质可以是氧化物、氮化物或氮氧化物。在一个优选实施例中，介质层13为晶格常数与未来要形成的压电层晶格常数相同或相近的材料，例如AlN或SiOx、SiON等等。介质层13的初始厚度H0，由于采用共形性良好的沉积工艺，介质层13在其在下电极12末端斜坡上也同样具有共形的斜坡，因此在牺牲层10A上方具有比衬底10上方更高的高度也即具有台阶差。原始厚度H0例如为0.05至10微米，优选0.1至5微米，最佳1至3微米，通过控制厚度H0可以控制薄膜质量，降低斜坡处的缺陷向上传播的几率或比例。
随后，如图4、图8所示，对介质层13执行平坦化工艺，例如采用CMP工艺，将其厚度H0减小为H1。厚度H1例如为100至2000埃，优选300至1000埃，以便利用较快的CMP工艺去除顶部薄膜质量不佳的部分。通过调节研磨液配比、研磨时间而调节研磨速度以便通过选择CMP工艺的终止节点时间而调整厚度H1。平坦化工艺之后，第一压电层13减薄为压电膜13’。优选地，通过SEM、激光干涉等方法测量压电膜13’的剩余厚度H1，以便精确地调节后续刻蚀工艺参数。
如图5、图8所示，按照剩余膜厚H1，对剩余的介质膜13’进行刻蚀，直至暴露下电极12。优选采用各向异性的干法刻蚀工艺。
如图6、图8所示，在具有平坦表面的下电极12和晶种区13”上形成压电层13B，用作最终器件的声-电转换元件。例如采用PECVD、UHVCVD、HDPCVD、MOCVD、MBE、ALD、磁控溅射、热蒸发等工艺沉积压电层13B，其材质例如ZnO、AlN、BST(钛酸锶钡)、BT(钛酸钡)、PZT(锆钛酸铅)、PBLN(铌酸铅钡锂)、PT(钛酸铅)等压电陶瓷材料；且优选地，压电层13B中掺杂稀土元素，例如包含钪(Sc)、钇(Y)、镧(La)、铈(Ce)、镨(Pr)、钕(Nd)、钷(Pm)、钐(Sm)、铕(Eu)、钆(Gd)、铽(Tb)、镝(Dy)、钬(Ho)、铒(Er)、铥(Tm)、镱(Yb)及镥(Lu)的任一种及其组合，以提高压电系数。
最后，如图7、图8所示，在压电层13B上形成上电极14，其工艺、材料与下电极12相同或相近。优选地，上电极14尺寸(例如图中宽度)大于下电极11以完全覆盖牺牲层10A，以便减小边缘处电场畸变影响谐振器Q值的可能性。随后，通过设置在器件外围的释放孔(未示出)，施加湿法腐蚀剂去除牺牲层图形。针对氧化硅基材料，采用HF基腐蚀液例如dHF(稀释HF)、dBOE(缓释刻蚀剂，HF与NH4F的混合物)去除牺牲层图形10A，留下多个谐振腔。
依照本发明的平坦化FBAR谐振器制备方法，依次采用沉积、平坦化、刻蚀工艺分步在下电极上形成具有平坦表面的压电层，减少了缺陷，避免了声波能量泄漏。
尽管已参照一个或多个示例性实施例说明本发明，本领域技术人员可以知晓无需脱离本发明范围而对器件结构做出各种合适的改变和等价方式。此外，由所公开的教导可做出许多可能适于特定情形或材料的修改而不脱离本发明范围。因此，本发明的目的不在于限定在作为用于实现本发明的最佳实施方式而公开的特定实施例，而所公开的器件结构及其制造方法将包括落入本发明范围内的所有实施例。
Claims (10)
1.一种平坦化FBAR谐振器制备方法，包括：
在衬底上形成下电极；
在下电极和衬底上形成介质层，具有第一厚度；
平坦化介质层以将第一厚度减小为第二厚度；
刻蚀介质层直至暴露下电极；
在下电极和衬底上形成压电层；
在压电层上形成上电极。
2.根据权利要求1的平坦化FBAR谐振器制备方法，形成下电极之前进一步包括，在衬底上形成衬垫层。
3.根据权利要求2的平坦化FBAR谐振器制备方法，其中，衬垫层材质为金属氮化物，优选地为AlN、HfN、HfAlN、TiN、TaN。
4.根据权利要求1的平坦化FBAR谐振器制备方法，其中，第一厚度为0.05-10微米，任选地第二厚度为100-2000埃。
5.根据权利要求1的平坦化FBAR谐振器制备方法，其中，平坦化介质层之后测量第二厚度，并根据第二厚度调节刻蚀介质层的工艺参数。
6.根据权利要求1的平坦化FBAR谐振器制备方法，其中，衬底的材料为Si、SOI、Ge、GeOI、化合物半导体；介质层的材料为氧化物、氮化物或氮氧化物，优选地介质层与压电层晶格常数相同或相近；任选地，压电层的材料为ZnO、AlN、BST(钛酸锶钡)、BT(钛酸钡)、PZT(锆钛酸铅)、PBLN(铌酸铅钡锂)、PT(钛酸铅)，进一步优选地压电材料中掺杂稀土元素；任选地，下电极或上电极的材料为选自Mo、W、Ru、Al、Cu、Ti、Ta、In、Zn、Zr、Fe、Mg的金属单质或金属合金、或者这些金属的导电氧化物、或导电氮化物，以及上述材料的任意组合。
7.根据权利要求1的平坦化FBAR谐振器制备方法，其中，在衬底上形成下电极之后下电极具有倾斜侧壁；优选地，形成介质层之前进一步包括刻蚀下电极的倾斜侧壁，使得下电极具有垂直侧壁。
8.根据权利要求1的平坦化FBAR谐振器制备方法，形成下电极期间在多个沉积工艺之间插入刻蚀工艺使得下电极具有垂直侧壁。
9.根据权利要求1的平坦化FBAR谐振器制备方法，形成下电极之前进一步包括刻蚀衬底形成空腔并在空腔中填充牺牲层，形成上电极之后进一步包括湿法腐蚀去除牺牲层在衬底中留下谐振腔。
10.根据权利要求1的平坦化FBAR谐振器制备方法，其中，上电极尺寸大于下电极尺寸。