CN111450849A - 3D分级立方体状α-MnS@CuS Z型异质结构光电催化剂及其制备方法和应用 - Google Patents
3D分级立方体状α-MnS@CuS Z型异质结构光电催化剂及其制备方法和应用 Download PDFInfo
- Publication number
- CN111450849A CN111450849A CN202010461331.0A CN202010461331A CN111450849A CN 111450849 A CN111450849 A CN 111450849A CN 202010461331 A CN202010461331 A CN 202010461331A CN 111450849 A CN111450849 A CN 111450849A
- Authority
- CN
- China
- Prior art keywords
- mns
- cus
- hierarchical
- type heterostructure
- cube
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明属于催化技术领域，具体涉及一种3D分级立方体状α‑MnS@CuS Z型异质结构光电催化剂及其制备方法和应用，制备方法如下：将CuCl2·2H2O溶解于乙二醇/去离子水的混合溶剂中，再加入CH3CSNH2搅拌均匀，继续加入α‑MnS，搅拌，转移到高压釜中进行反应，自然冷却至室温收集样品，去离子水和乙醇洗涤数次，干燥得到目标产物。在可见光照射以及特定附加偏压作用下，在180min内催化合成的H2O2的产量高达到1.6mmol/L。本发明具有简便、高效、成本低、对可见光吸收度高的特点能够应用于光催化制备过氧化氢以及降解有机物等领域。
Description
技术领域
本发明涉及可见光响应的3D分级立方体状α-MnS@CuS Z型异质结复合催化剂及其制备方法和在光电催化制备H2O2方面的应用，主要针对于工业上大规模生产H2O2，属于高附加值化学品、催化剂生产技术领域。
背景技术
光催化技术是一种成本低、性能高、不会引发二次污染的成熟绿色技术，在绿色氧化降解和绿色合成方面均显示出潜在的应用前景。光电催化可以实现在电驱动下更有效地利用太阳能，提高太阳能转换成化学能的光能转换效率，以取得更好的应用价值。
过氧化氢(H2O2)作为一种仅以水和氧气为副产物的清洁化学氧化剂引发了人们的广泛关注。它不仅具有环境友好以及可再生等一系列优点，还是非常有前景的新型化学资源，被广泛应用于生物科学(消毒)，环境修复(有机分解)和化学加工(纸浆漂白)等多个行业中。传统的H2O2的工业合成方法由于工艺复杂、成本高且产生大量的废弃有毒副产物等限制了这几种方法的实际应用。近年来，光催化生产H2O2受到了人们越来越多的关注，因为该过程仅需要水、氧气和阳光作为原料，将低密度太阳能转化为可储存化学能，具有无二次污染，设备简单，投资少，产量高等优点。但光催化生产H2O2这一手段很难选择性地阻止热力学更有利的4e-生成O2的副反应发生，而电催化与光催化相结合的光电催化手段进行相关改性可以有效克服这两种缺点，且催化剂更易回收，从而是一种更清洁可持续的生产方法。目前光电催化技术已被广泛被用于各种催化领域，包括产H2、O2以及CO2的还原，但由于在光阳极上通过光电化学水氧化反应生成H2O2时会具有比较高的氧化电位以及两种副产物O2和·OH，在H2O2生产方面所需要的催化剂既要有很强的氧化能力又要具有一定的选择性。另外，光生电子和空穴的复合导致光量子产率低，也限制了光电催化技术在实际中的应用。
研究发现，过渡金属硫化物兼具优良的光、电化学性能。片状、花状、立方体状等多种结构的硫化物通常具有很大的导电率使之具有很好的电化学性能；大多数过渡金属硫化物具有相对窄的带隙而具有比较好的可见光利用效率；同时具有很好的机械强度，容易获得，循环性好等优点，使其成为减少环境污染、生产和储存能源以及各种科学活动的最佳候选之一。因此，设计并构建具有大比表面积、良好的日光收集能力、良好的导电性、合适的能带位置的半导体材料，将是一种十分有效的用于生产H2O2的策略。
发明内容
本发明的目的之一是提供一种具有可见光响应并能有效分离光生电子和空穴的3D分级立方体状α-MnS@CuS Z型异质结复合催化剂及其制备方法。
本发明的目的之二是提供一种利用3D分级立方体状α-MnS@CuS Z型异质结复合催化剂光电催化制备H2O2的方法。
针对光催化生产H2O2很难选择性地阻止热力学更有利的4e-生成O2的副反应发生，通过将负载催化剂的碳纸用作工作电极、铂丝作为对电极，甘汞电极作为参比电极，通过电化学工作站给予-0.7V的电压，氙灯给光进行光电催化制备H2O2。
本发明采用的技术方案是：一种3D分级立方体状α-MnS@CuS Z型异质结构光电催化剂，制备方法包括如下步骤：将CuCl2·2H2O溶解于乙二醇/去离子水的混合溶剂中，再加入CH3CSNH2搅拌均匀，继续加入α-MnS，搅拌，转移到高压釜中进行反应，自然冷却至室温收集样品，用去离子水和乙醇洗涤数次，在60℃的烘箱中干燥12h，得到目标产物。
优选地，上述的一种3D分级立方体状α-MnS@CuS Z型异质结构光电催化剂，按质量比，CuCl2·2H2O：α-MnS为17：16。
优选地，上述的一种3D分级立方体状α-MnS@CuS Z型异质结构光电催化剂，所述的反应是在180℃下加热3h。
优选地，上述的一种3D分级立方体状α-MnS@CuS Z型异质结构光电催化剂，所述的α-MnS的制备方法包括如下步骤：分别取Mn(CH3COO)2·4H2O、CH3CSNH2溶解于吡啶中形成均匀的溶液，转移至高压釜中进行反应，自然冷却至室温后，将制备的沉淀物离心并用乙醇和丙酮洗涤数次，在55℃下干燥10h，得到α-MnS。
优选地，上述的一种3D分级立方体状α-MnS@CuS Z型异质结构光电催化剂，按摩尔比，Mn(CH3COO)2·4H2O：CH3CSNH2＝7：45。
优选地，上述的一种3D分级立方体状α-MnS@CuS Z型异质结构光电催化剂，所述的反应是在180℃下加热18h。
上述的一种3D分级立方体状α-MnS@CuS Z型异质结构光电催化剂在光电催化制备过氧化氢中的应用。
优选地，上述的应用，方法如下：将权利要求1所述的3D分级立方体状α-MnS@CuS Z型异质结构光电催化剂，加入到去离子水中超声分散，涂覆在碳纸上作为工作电极，铂丝为对电极，甘汞电极为参比电极，置于石英反应容器中，构成三电极体系；在-0.7V vs.RHE偏压、环境温度25℃的条件下，模拟太阳光照射，在含有乙醇的去离子水中，调节pH至酸性，使其在溶液中连续均匀的鼓泡，在黑暗中进行磁力搅拌60min，以达到照射前的吸附-脱附平衡，在光电驱动下进行反应。
优选地，上述的应用，所述的调节pH是采用HClO4将悬浮液的pH值调为2.9。
优选地，上述的应用，所述的模拟太阳光照射为采用300W氙灯作为光源，所述的氙灯λ≥420nm。
本发明的有益效果是：本发明通过α-MnS和CuS两种材料复合的方式，进一步提高光响应范围及光催化性能，提高其捕捉光子的效率，抑制电子空穴对的复合，提高电子从价带跃迁至导带的利用率，提高光催化活性。采用本发明的方法，在可见光照射以及特定附加偏压作用下，在180min内催化合成的H2O2的产量高达到1.6mmol/L，为生产H2O2提供了绿色的合成路线和可持续技术。
本发明具有简便、高效、成本低、对可见光吸收度高的特点，所制备的3D分级立方体状α-MnS@CuS Z型异质结构催化材料具有带隙窄、比表面积大、良好的导电性、催化活性高的特点，且有良好的可见光吸收性能和良好的稳定性，光生电子空穴对分离效率高，界面电荷传输效率快，光电催化制备H2O2产量高，能够应用于光催化制备过氧化氢以及降解有机物等领域。
附图说明
图1是3D分级立方体状α-MnS@CuS Z型异质结复合催化剂的SEM图。
图2是α-MnS、CuS和α-MnS@CuS的XRD图。
图3是不同气体环境对光电催化H2O2产生的影响。
图4是不同pH对光电催化H2O2产生的影响。
图5是CuS、α-MnS和α-MnS@CuS光电催化产生H2O2浓度。
具体实施方式
实施例1 3D分级立方体状α-MnS@CuS Z型异质结复合催化剂的制备
(一)α-MnS立方体的制备
分别称量2.8mmol的Mn(CH3COO)2·4H2O、18.0mmol的CH3CSNH2，溶解于50mL吡啶中形成均匀的溶液，并立即转移至容积为100mL的特氟龙衬里不锈钢高压釜中，在180℃下保持18h，自然冷却至室温后，将制备的沉淀物离心并用乙醇和丙酮洗涤数次，在55℃下干燥10h，得到α-MnS。
(二)3D分级立方体状α-MnS@CuS Z型异质结复合催化剂的制备
称量85mg CuCl2·2H2O加入到60mL乙二醇/去离子水(体积比为3：1)的混合溶剂中，搅拌10min。随后，加入300mg CH3CSNH2并继续磁力搅拌10min，再加入0.08gα-MnS，搅拌30min至溶液均匀。然后将溶液转移到密封的100mL特氟龙高压釜中加热到180℃持续3h，然后自然冷却至室温。通过离心收集沉淀物，用去离子水和乙醇洗涤数次，在60℃的烘箱中干燥12h，得到α-MnS@CuS复合材料。
由图1可以看到，α-MnS@CuS复合材料为3D分级立方体结构，大量多边形CuS纳米片紧密的垂直生长在MnS立方体表面，形成三维簇结构。图2的XRD谱图证实了该复合材料为α-MnS@CuS。
实施例2
方法：称量5mg的复合材料，加入到0.5mL去离子水中，超声5min，用移液枪将溶液逐滴滴涂到碳纸上(2cm×1cm)，并在60℃下干燥2h，以形成均匀的薄膜，得到光电极作为工作电极，铂丝为对电极，甘汞电极为参比电极，置于石英反应容器中，构成三电极体系。
在-0.7V vs.RHE偏压、环境温度25℃的条件下，采用300W氙灯照射模拟太阳光照射，所述的氙灯λ≥420nm，将三电极体系插入至含有47.5mL去离子水和2.5mL乙醇的混合溶液的石英反应器中，使用1.0mol/L HClO4调节溶液的pH值至2.9，在黑暗条件下向溶液中通入气体30min至饱和。在光电驱动的催化反应过程中，每30min取出1mL的溶液，与2mL的0.1mol/L KI溶液和0.05mL的0.01mol/L钼酸铵溶液混合。通过紫外可见光谱检测吸光度A(检测波长为350nm)，根据已建立的标准曲线计算H2O2的生成量。
(一)不同的气体环境对H2O2生成的影响
在pH为2.9的含有47.5mL去离子水和2.5mL乙醇的混合溶液中，黑暗条件下分别将N2、空气和O2通入溶液中30min，采用α-MnS@CuS复合材料负载在碳纸上做光电阴极制备H2O2。结果如图3。
在O2/可见光辐射的条件下H2O2的生成量最高；当溶液中通入空气时，由于空气中的氧含量较低，因此H2O2的生成量下降；当溶液中通入N2时H2O2的生成几乎被完全抑制，只有极少量的H2O2生成，表明O2对光电催化生产H2O2是至关重要的。
(二)不同pH对H2O2生成的影响
在含有47.5mL去离子水和2.5mL乙醇的混合溶液中，采用HClO4分别调节反应溶液的pH值为1.8、2.9、5.0、6.8、8.7，在黑暗条件下O2通入溶液中30min，采用α-MnS@CuS复合材料负载在碳纸上做光电阴极制备H2O2。结果如图4。
在pH值为2.9时H2O2的生成量达到最大值，而当pH值继续增加(5、6.8、8.7)或降低时(1.8)H2O2的含量相对减少，表明光电催化生产H2O2的活性还取决于水溶液的pH，故选pH为2.9时为最佳pH值。
实施例3
分别称取α-MnS、CuS和α-MnS@CuS各5mg，加入到0.5mL去离子水中，超声5min，用移液枪将溶液逐滴滴涂到碳布上(2cm×1cm)，并在60℃下干燥2h，以形成均匀的薄膜，得到不同光电极。在-0.7V vs.RHE偏压、环境温度25℃的条件下，在pH为2.9且含有2.5mL乙醇且O2饱和的50mL去离子水溶液中，采用300W氙灯照射模拟太阳光照射，采用不同光阴极进行光电催化制备H2O2，结果如图5所示。
α-MnS@CuS Z型异质结复合催化剂光催化产H2O2的效果要优于单一组分光催化剂。反应180min后，α-MnS@CuS的H2O2产量达到了最大值，约为1.6mmol/L，是分别为纯α-MnS(0.9mmol/L)和CuS(0.7mmol/L)的1.8和2.3倍。
Claims (10)
1.一种3D分级立方体状α-MnS@CuS Z型异质结构光电催化剂，其特征在于，制备方法包括如下步骤：将CuCl2·2H2O溶解于乙二醇/去离子水的混合溶剂中，再加入CH3CSNH2搅拌均匀，继续加入α-MnS，搅拌，转移到高压釜中进行反应，自然冷却至室温收集样品，用去离子水和乙醇洗涤数次，在60℃的烘箱中干燥12h，得到目标产物。
2.根据权利要求1所述的一种3D分级立方体状α-MnS@CuS Z型异质结构光电催化剂，其特征在于，按质量比，CuCl2·2H2O：α-MnS为17：16。
3.根据权利要求1所述的一种3D分级立方体状α-MnS@CuS Z型异质结构光电催化剂，其特征在于，所述的反应是在180℃下加热3h。
4.根据权利要求1所述的一种3D分级立方体状α-MnS@CuS Z型异质结构光电催化剂，其特征在于，所述的α-MnS的制备方法包括如下步骤：分别取Mn(CH3COO)2·4H2O、CH3CSNH2溶解于吡啶中形成均匀的溶液，转移至高压釜中进行反应，自然冷却至室温后，将制备的沉淀物离心并用乙醇和丙酮洗涤数次，在55℃下干燥10h，得到α-MnS。
5.根据权利要求4所述的一种3D分级立方体状α-MnS@CuS Z型异质结构光电催化剂，其特征在于，按摩尔比，Mn(CH3COO)2·4H2O：CH3CSNH2＝7：45。
6.根据权利要求4所述的一种3D分级立方体状α-MnS@CuS Z型异质结构光电催化剂，其特征在于，所述的反应是在180℃下加热18h。
7.权利要求1所述的一种3D分级立方体状α-MnS@CuS Z型异质结构光电催化剂在光电催化制备过氧化氢中的应用。
8.根据权利要求7所述的应用，其特征在于，方法如下：将权利要求1所述的3D分级立方体状α-MnS@CuS Z型异质结构光电催化剂，加入到去离子水中超声分散，涂覆在碳纸上作为工作电极，铂丝为对电极，甘汞电极为参比电极，置于石英反应容器中，构成三电极体系；在-0.7V vs.RHE偏压、环境温度25℃的条件下，模拟太阳光照射，在含有乙醇的去离子水中，调节pH至酸性，使其在溶液中连续均匀的鼓泡，在黑暗中进行磁力搅拌60min，以达到照射前的吸附-脱附平衡，在光电驱动下进行反应。
9.根据权利要求8所述的应用，其特征在于，所述的调节pH是采用HClO4将悬浮液的pH值调为2.9。
10.根据权利要求9所述的应用，其特征在于，所述的模拟太阳光照射为采用300W氙灯作为光源，所述的氙灯λ≥420nm。