CN111235926A - 一种提升涤纶织物抗热迁移色牢度的整理方法 - Google Patents
一种提升涤纶织物抗热迁移色牢度的整理方法 Download PDFInfo
- Publication number
- CN111235926A CN111235926A CN202010229842.XA CN202010229842A CN111235926A CN 111235926 A CN111235926 A CN 111235926A CN 202010229842 A CN202010229842 A CN 202010229842A CN 111235926 A CN111235926 A CN 111235926A
- Authority
- CN
- China
- Prior art keywords
- fastness
- polyester
- cleaning
- polyester fabric
- improving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种提升涤纶织物抗热迁移色牢度的整理方法，包括步骤S1)将涤纶织物染色或印花处理；S2)采用酸性还原清洗粉工作液对涤纶织物进行清洗，所述工作液包含酸性还原清洗粉DM‑1552D 2～4％、HAc 1～1.5％、余量为水；清洗时，按照一定的浴比，升温到80～90℃，并在该温度下恒温处理，出缸，常温水洗，烘干；S3)采用抗热迁移剂DM‑2021进行整理、定形。本发明提升高温定形后涤纶织物的耐皂洗、摩擦色牢度至4级或以上，提升高温定形后的涤纶织物的耐汗碱色牢度至5级。
Description
技术领域
本发明属于织物整理技术领域，具体涉及一种提升涤纶织物抗热迁移色牢度的整理方法。
背景技术
为提高涤纶织物染色牢度，常用的处理步骤是：(1)预处理；(2)等离子处理；(3)配制活性处理液；(4)改性处理；(5)超声处理；(6)清洗。具体参见公开号为CN108978269A的发明专利。但是，该处理方法步骤较多，过程复杂，实际大生产中不方便操作。经查询，没有查询到其他有关提升涤纶织物抗热迁移色牢度的方法。
涤纶织物多采用分散染料染色，公开号为CN108117771A的发明专利公开了一种提升分散染料升华牢度的方法，其具体的提升方法为：增加染料分子的分子量，提高分子的共平面性，降低分散染料在印花时的热迁移率，使得分散染料具有优异升华牢度。该专利是从改变染料的角度降低热迁移的，但是实际应用过程中该专利有一定的局限性，我国印染行业目前用于涤纶织物染色的分散染料品种多、色谱齐全，只使用该专利中提到的一类分散染料不能满足实际生产中涤纶织物的色彩要求。
发明内容
本发明所要解决的技术问题是，克服目前现有技术的缺陷，提供一种提升涤纶织物抗热迁移色牢度的整理方法，其能够有效提升涤纶染色、印花织物的高温定形后的抗热迁移色牢度，解决涤纶织物高温抗热迁移色牢度提升困难的行业难题。且该整理工艺简单、操作方便、手感好、色变小、不污染环境，适用于各种类型分散染料染色后织物后整理，不需要额外增加设备成本。
本发明解决其技术问题的技术方案是：一种提升涤纶织物抗热迁移色牢度的整理方法，其特征在于包括以下步骤：
S1)将涤纶织物染色或印花处理；
S2)采用酸性还原清洗粉工作液对涤纶织物进行清洗，所述工作液包含酸性还原清洗粉DM-1552D、HAc、水；其组分owf是：
酸性还原清洗粉 X％，
HAc Y％，
水 1－X％－Y％，
其中，X％为2～4％，Y％为1～1.5％。
清洗时，按照一定的浴比，升温到80～90℃，并在该温度下恒温处理，出缸，常温水洗，烘干；
S3)采用抗热迁移剂DM-2021进行整理、定形。
上述的整理方法中，在步骤S2)，抗热迁移剂DM-2021用量为20～40g/L，采用定形机上一浸一轧方法，并在120～180℃下定形。
上述的整理方法中，在步骤S1)，清洗恒温处理时间为20min。
上述的整理方法中，DM-1552D的组分包括磺酸盐和无机盐，其中磺酸盐的质量百分比小于无机盐的。
上述的整理方法中，抗热迁移剂DM-2021的组分包括多胺基衍生物和水，其中多胺基衍生物的质量百分比小于14％。
本发明的有益效果是：
本发明通过对涤纶织物的后整理，在纤维表面形成一层保护膜，增强与分散染料的相互作用，能阻止分散染料高温定形引起的迁移现象，为提高涤纶织物的应用价值提供了一种有效的整理方法。因此，本发明有益效果在于：
(1)提升涤纶织物抗热迁移色牢度
涤纶织物是世界上最重要的纺织品之一，涤纶织物采用分散染料染色后，为保持织物的尺寸稳定性需进行高温定形，而在高温定形时分散染料会从纤维内部通过纤维毛细管迁移到纤维表层，使得染料在纤维表面堆积，造成了一系列的影响，如涤纶织物高温定形后色变大，涤纶织物高温定形后再进行湿处理时，染料容易脱落，导致涤纶织物的耐皂洗、耐汗渍、摩擦色牢度下降，达不到纺织产品基本安全技术规范要求，近年来纺织印染行业一直在寻找一种简单、有效的提升涤纶织物的抗热迁移色牢度的整理方法，本发明中整理方法解决了这一技术难题，通过酸性还原清洗去浮色与浸轧抗热迁移剂组合工艺，在涤纶织物表面形成紧密的保护膜，从而有效提升涤纶织物抗热迁移色牢度，提升高温定形后涤纶织物的耐皂洗、摩擦色牢度至4级或以上，提升高温定形后的涤纶织物的耐汗碱色牢度至5级，提高了涤纶织物的应用价值。
(2)整理工艺简单、易实现产业化
本发明中整理方法配工作液简单、可行，抗热迁移整理可以在直接在定形机上一浸一轧，相对传统二浸二轧简单、易操作，容易实现产业。
(3)经济效益可观
由于涤纶织物是纺织品重要的一种，用途广泛，价格也相对便宜，提升涤纶织物的抗热迁移色牢度经济效益可观。
(4)织物舒适性好
本发明整理后涤纶织物手感好，穿着舒适性好。
(5)适用范围广
本发明整理后涤纶织物色变小，可用于深色、浅色、鲜艳色、敏感色涤纶染色织物及印花织物整理；可以用于服装面料、箱包面料、窗帘布使用到的涤纶织物整理。
具体实施方式
下面详细描述本发明的实施例，所述实施例仅用于解释本发明，而不能理解为对本发明的限制。
实施例1：100D/48F红色涤纶低弹丝织物
将分散红用量5％(owf)染色后的黑色涤纶织物加入DM-1552D用量3％(owf)+HAc1.5％(owf)酸性还原清洗液中，升温至80℃清洗20min，出缸，常温水洗后烘干；完成还原清洗后的涤纶织物在定形机一浸一轧抗热迁移剂DM-2021 30g/L，再采用160℃高温定形，测试此方案整理后红色涤纶织物干摩擦色牢度为4-5级，湿摩擦色牢度、耐皂洗色牢度为4级，耐汗碱色牢度为5级，色差值为0.32，织物手感柔软。
Owf是指染整工艺中以织物重量为基准的浓度单位，染料或印染助剂浓度相对织物百分比，染料或助剂与织物的重量的比值。HAc化学式CH3COOH，是有机一元酸。
DM-1552D是德美集团生产的酸性还原清洗剂，不含APEO、甲醛、有机卤化物、重金属、磷、氮，50℃耐热稳定，-5℃耐冻稳定，遇酸会分解，在pH>3时稳定。无离子性易溶于水，含固量97.5～99.5％(有效物含量38～42％)。
DM-2021是涤纶抗热迁移剂，不含APEO、甲醛、有机卤化物、重金属、磷，含氮12384ppm，含氨氮68ppm。阳离子，易溶解，50℃耐热稳定，-5℃耐冻稳定，与阳离子硅油，非离子硅油，阳离子软片，非离子软片同浴均稳定。
实施例2：75D/72F黑色超细旦涤纶双面针织物
将分散黑用量8％(owf)染色后的黑色超细旦涤纶针织物加入DM-1552D用量4％(owf)+HAc 1.5％(owf)酸性还原清洗液中，升温至85℃清洗20min，出缸，常温水洗后烘干；完成还原清洗后的在定形机一浸一轧抗热迁移剂DM-2021 40g/L，再采用170℃高温定形，测试此方案整理后黑色超细旦涤纶双面针织干、湿摩擦色牢度、耐汗碱色牢度为5级，耐皂洗色牢度为4-5级，色差值为0.17，织物手感柔软、细腻。
实施例3：箱包用200D深蓝色涤纶牛津布
将分散蓝用量6％(owf)染色后的深蓝色涤纶牛津布加入DM-1552D用量3％(owf)+HAc 1.2％(owf)酸性还原清洗液中，升温至90℃清洗20min，出缸，常温水洗后烘干；完成还原清洗后的在定形机一浸一轧抗热迁移剂DM-2021 35g/L，再采用175℃高温定形，测试此方案整理后深蓝色涤纶牛津布干摩擦色牢度、耐汗碱色牢度为5级，湿摩擦色牢度为4级，耐皂洗色牢度为4-5级，色差值为0.27。
实施例4：连衣裙用150D翠绿色金银丝涤纶提花布
将翠绿色金银丝涤纶提花布加入DM-1552D用量2％(owf)+HAc 1.0％(owf)酸性还原清洗液中，升温至80℃清洗20min，出缸，常温水洗后烘干；完成还原清洗后的在定形机一浸一轧抗热迁移剂DM-2021 25g/L，再采用170℃高温定形，测试此方案整理后涤纶提花布干、湿摩擦色牢度、耐汗碱、耐皂洗色牢度均为5级，色差值为0.51。
尽管已经示出和描述了本发明的实施例，本领域的普通技术人员应当理解：在不脱离本发明的原理和宗旨的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由权利要求及其等同替换所限定，在未经创造性劳动所作的改进等，均应包含在本发明的保护范围之内。
Claims (5)
1.一种提升涤纶织物抗热迁移色牢度的整理方法，其特征在于包括以下步骤：
S1)将涤纶织物染色或印花处理；
S2)采用酸性还原清洗粉工作液对涤纶织物进行清洗，所述工作液包含酸性还原清洗粉DM-1552D、HAc、水；其组分owf是：
酸性还原清洗粉 X％，
HAc Y％，
水 1－X％－Y％，
其中，X％为2～4％，Y％为1～1.5％。
清洗时，按照一定的浴比，升温到80～90℃，并在该温度下恒温处理，出缸，常温水洗，烘干；
S3)采用抗热迁移剂DM-2021进行整理、定形。
2.根据权利要求1所述提升涤纶织物抗热迁移色牢度的整理方法，其特征在于：在步骤S2)中，抗热迁移剂DM-2021用量为20～40g/L，采用定形机上一浸一轧方法，并在120～180℃下定形。
3.根据权利要求1所述提升涤纶织物抗热迁移色牢度的整理方法，其特征在于：在步骤S1)中，清洗恒温处理时间为20min。
4.根据权利要求1所述提升涤纶织物抗热迁移色牢度的整理方法，其特征在于：DM-1552D的组分包括磺酸盐和无机盐，其中磺酸盐的质量百分比小于无机盐的。
5.根据权利要求1所述提升涤纶织物抗热迁移色牢度的整理方法，其特征在于：抗热迁移剂DM-2021的组分包括多胺基衍生物和水，其中多胺基衍生物的质量百分比小于14％。