CN110965182A - Preparation method of n-butyl salicylate anti-ultraviolet blended fabric - Google Patents
Preparation method of n-butyl salicylate anti-ultraviolet blended fabric Download PDFInfo
- Publication number
- CN110965182A CN110965182A CN201811148878.4A CN201811148878A CN110965182A CN 110965182 A CN110965182 A CN 110965182A CN 201811148878 A CN201811148878 A CN 201811148878A CN 110965182 A CN110965182 A CN 110965182A
- Authority
- CN
- China
- Prior art keywords
- fabric
- layer
- ultraviolet
- blended
- fibers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention particularly relates to a preparation method of n-butyl salicylate anti-ultraviolet blended fabric, which comprises the following steps: manufacturing a surface layer: the surface layer is made of an ultraviolet-resistant fabric, the ultraviolet-resistant fabric is formed by interweaving warps and wefts, the warps are blended yarns of bamboo fibers and cotton fibers, and the wefts are blended yarns of polypropylene fibers and cotton fibers; manufacturing the intermediate layer: the polypropylene fiber and the cotton fiber in the first fabric layer and the third fabric layer are firstly blended, then are blended with the bamboo fiber, and are woven into cloth, the second fabric layer is manufactured by spinning the cotton fiber, and the first fabric layer, the second fabric layer and the third fabric layer are sequentially attached together in a dispensing or needle and thread sewing mode; manufacturing an inner layer; and (6) attaching the components into a whole. According to the preparation method of the n-butyl salicylate anti-ultraviolet blended fabric, the prepared fabric has a good anti-ultraviolet function, and the preparation process is simple and easy to operate.
Description
Technical Field
The invention belongs to the technical field of fabrics, and particularly relates to a preparation method of n-butyl salicylate anti-ultraviolet blended fabric.
Background
With the increasing awareness of environmental protection and health care, more and more people are paying attention to natural fibers, and cotton fibers are widely applied to the production of various textiles as the most common natural fibers. At present, yarns on the market come out endlessly, are different in material structure, and are widely applied to the living fields of weaving, rope making, thread making and the like. Xinjiang cotton fiber is well known in the textile industry due to its flexibility and is known as a cotton top grade product by people, and has the advantages of less frequent combing, uniform and smooth evenness and high dyeability. However, the elasticity and the heat retention of the cotton fiber blended yarn on the market at present are not good, so that the woven fabric has the defects of poor heat retention effect and poor elasticity.
Preventing ultraviolet rays from damaging human bodies is being paid more and more attention by consumers. Ultraviolet rays in the solar spectrum not only cause the color fading and embrittlement of textiles, but also cause the sunburn and aging of human skin, generate melanin and color spots, and further induce canceration to harm human health. The ultraviolet-resistant fabric is a protective material for preventing excessive ultraviolet radiation of human bodies.
In view of the above, a method for preparing an anti-ultraviolet blended fabric from n-butyl salicylate is urgently needed.
Disclosure of Invention
The invention aims to provide a preparation method of n-butyl salicylate anti-ultraviolet blended fabric, which is characterized by comprising the following steps:
a. manufacturing a surface layer: the surface layer is made of an ultraviolet-resistant fabric, the ultraviolet-resistant fabric is formed by interweaving warps and wefts, the warps are blended yarns of bamboo fibers and cotton fibers, and the wefts are blended yarns of polypropylene fibers and cotton fibers;
b. manufacturing the intermediate layer: the polypropylene fiber and the cotton fiber in the first fabric layer and the third fabric layer are firstly blended, then are blended with the bamboo fiber, and are woven into cloth, the second fabric layer is manufactured by spinning the cotton fiber, and the first fabric layer, the second fabric layer and the third fabric layer are sequentially attached together in a dispensing or needle and thread sewing mode;
c. manufacturing an inner layer: uniformly mixing bamboo fibers, polypropylene fibers and cotton fibers, then carrying out cotton cleaning, cotton carding, drawing, roving, fine sand, automatic spooling, yarn steaming, high-speed doubling and double twisting treatment to obtain fine imitation yarns, and weaving to obtain an inner-layer fabric;
d. laminating integrally: and sequentially laminating the surface layer, the middle layer and the inner layer, and then curing, shaping and calendaring to obtain the product.
Preferably, in the step a, the uvioresistant fabric is added with n-butyl salicylate uvioresistant finishing agent, soaked for 35-65 minutes and then baked at 60-80 ℃ for 35-55 minutes.
Preferably, after the step c, adding 7% of detergent and 20% of softener into the lining fabric for water washing treatment, and controlling the water temperature to be 45-65 ℃ and water washing for 85-105 minutes.
Preferably, in the step d, the time for the ripening processing is 15-25h, the temperature is 55-105 ℃, and the humidity is 32-66%.
Preferably, in the step d, the calendering temperature is 70-110 ℃, the pressure is 24-89Kg/cm2, and the speed is 18-48 m/min.
Due to the adoption of the technical scheme, the invention has the following advantages and beneficial effects:
according to the preparation method of the n-butyl salicylate anti-ultraviolet blended fabric, the prepared fabric has a good anti-ultraviolet function, and the preparation process is simple and easy to operate.
Detailed Description
In order to more clearly illustrate the invention, the invention is further described below in connection with preferred embodiments. It is to be understood by persons skilled in the art that the following detailed description is illustrative and not restrictive, and is not to be taken as limiting the scope of the invention.
Example 1
The invention aims to provide a preparation method of n-butyl salicylate anti-ultraviolet blended fabric, which is characterized by comprising the following steps:
a. manufacturing a surface layer: the surface layer is made of an ultraviolet-resistant fabric, the ultraviolet-resistant fabric is formed by interweaving warps and wefts, the warps are blended yarns of bamboo fibers and cotton fibers, and the wefts are blended yarns of polypropylene fibers and cotton fibers;
b. manufacturing the intermediate layer: the polypropylene fiber and the cotton fiber in the first fabric layer and the third fabric layer are firstly blended, then are blended with the bamboo fiber, and are woven into cloth, the second fabric layer is manufactured by spinning the cotton fiber, and the first fabric layer, the second fabric layer and the third fabric layer are sequentially attached together in a dispensing or needle and thread sewing mode;
c. manufacturing an inner layer: uniformly mixing bamboo fibers, polypropylene fibers and cotton fibers, then carrying out cotton cleaning, cotton carding, drawing, roving, fine sand, automatic spooling, yarn steaming, high-speed doubling and double twisting treatment to obtain fine imitation yarns, and weaving to obtain an inner-layer fabric;
d. laminating integrally: and sequentially laminating the surface layer, the middle layer and the inner layer, and then curing, shaping and calendaring to obtain the product.
In the step a, the anti-ultraviolet fabric is added with n-butyl salicylate anti-ultraviolet finishing agent to be soaked for 35 minutes, and then is baked for 35 minutes at the temperature of 60 ℃.
And c, after the step c, adding 7% of detergent and 20% of softening agent into the fabric on the inner layer for washing, controlling the water temperature at 45 ℃ and washing for 85 minutes.
In the step d, the curing processing time is 15 hours, the temperature is 55 ℃, and the humidity is 32%.
In the step d, the calendering temperature is 70 ℃, the pressure is 24Kg/cm2, and the speed is 18 m/min.
Example 2
The invention aims to provide a preparation method of n-butyl salicylate anti-ultraviolet blended fabric, which is characterized by comprising the following steps:
a. manufacturing a surface layer: the surface layer is made of an ultraviolet-resistant fabric, the ultraviolet-resistant fabric is formed by interweaving warps and wefts, the warps are blended yarns of bamboo fibers and cotton fibers, and the wefts are blended yarns of polypropylene fibers and cotton fibers;
b. manufacturing the intermediate layer: the polypropylene fiber and the cotton fiber in the first fabric layer and the third fabric layer are firstly blended, then are blended with the bamboo fiber, and are woven into cloth, the second fabric layer is manufactured by spinning the cotton fiber, and the first fabric layer, the second fabric layer and the third fabric layer are sequentially attached together in a dispensing or needle and thread sewing mode;
c. manufacturing an inner layer: uniformly mixing bamboo fibers, polypropylene fibers and cotton fibers, then carrying out cotton cleaning, cotton carding, drawing, roving, fine sand, automatic spooling, yarn steaming, high-speed doubling and double twisting treatment to obtain fine imitation yarns, and weaving to obtain an inner-layer fabric;
d. laminating integrally: and sequentially laminating the surface layer, the middle layer and the inner layer, and then curing, shaping and calendaring to obtain the product.
In the step a, the anti-ultraviolet fabric is added with n-butyl salicylate anti-ultraviolet finishing agent to be soaked for 65 minutes, and then baked at 80 ℃ for 55 minutes.
And c, after the step c, adding 7% of detergent and 20% of softening agent into the inner fabric for washing treatment, controlling the water temperature at 65 ℃ and washing for 105 minutes.
In the step d, the curing processing time is 25 hours, the temperature is 105 ℃, and the humidity is 66%.
In the step d, the calendering temperature is 110 ℃, the pressure is 89Kg/cm2, and the speed is 48 m/min.
Through detection, all indexes of the ultraviolet-resistant fabric prepared in the two embodiments are as follows
Breaking Strength N (warp direction) | Fracture ofStrength N (weft) | Ultraviolet transmittance/%) | |
Example 1 | 244N | 210N | 3.29 |
Example 2 | 241N | 214N | 3.01 |
The foregoing shows and describes the general principles, essential features, and advantages of the invention. It will be understood by those skilled in the art that the present invention is not limited to the embodiments described above, which are given by way of illustration of the principles of the present invention, and that various changes and modifications may be made without departing from the spirit and scope of the invention as defined by the appended claims. The scope of the invention is defined by the appended claims and equivalents thereof.
Claims (5)
1. The preparation method of the n-butyl salicylate anti-ultraviolet blended fabric is characterized by comprising the following steps:
a. manufacturing a surface layer: the surface layer is made of an ultraviolet-resistant fabric, the ultraviolet-resistant fabric is formed by interweaving warps and wefts, the warps are blended yarns of bamboo fibers and cotton fibers, and the wefts are blended yarns of polypropylene fibers and cotton fibers;
b. manufacturing the intermediate layer: the polypropylene fiber and the cotton fiber in the first fabric layer and the third fabric layer are firstly blended, then are blended with the bamboo fiber, and are woven into cloth, the second fabric layer is manufactured by spinning the cotton fiber, and the first fabric layer, the second fabric layer and the third fabric layer are sequentially attached together in a dispensing or needle and thread sewing mode;
c. manufacturing an inner layer: uniformly mixing bamboo fibers, polypropylene fibers and cotton fibers, then carrying out cotton cleaning, cotton carding, drawing, roving, fine sand, automatic spooling, yarn steaming, high-speed doubling and double twisting treatment to obtain fine imitation yarns, and weaving to obtain an inner-layer fabric;
d. laminating integrally: and sequentially laminating the surface layer, the middle layer and the inner layer, and then curing, shaping and calendaring to obtain the product.
2. The preparation method of the n-butyl salicylate anti-ultraviolet blended fabric according to claim 1, characterized in that: in the step a, the anti-ultraviolet fabric is added with n-butyl salicylate anti-ultraviolet finishing agent to be soaked for 35-65 minutes, and then baked for 35-55 minutes at the temperature of 60-80 ℃.
3. The preparation method of the n-butyl salicylate anti-ultraviolet blended fabric according to claim 1, characterized in that: and c, after the step c, adding 7% of detergent and 20% of softening agent into the inner fabric for washing, controlling the water temperature at 45-65 ℃ and washing for 85-105 minutes.
4. The preparation method of the n-butyl salicylate anti-ultraviolet blended fabric according to claim 1, characterized in that: in the step d, the curing processing time is 15-25h, the temperature is 55-105 ℃, and the humidity is 32-66%.
5. The preparation method of the n-butyl salicylate anti-ultraviolet blended fabric as claimed in claim 1, which is characterized in that: in the step d, the calendering temperature is 70-110 ℃, the pressure is 24-89Kg/cm2, and the speed is 18-48 m/min.