CN110965180A - Preparation method of disalicylic acid bisphenol A ester ultraviolet-resistant blended fabric - Google Patents
Preparation method of disalicylic acid bisphenol A ester ultraviolet-resistant blended fabric Download PDFInfo
- Publication number
- CN110965180A CN110965180A CN201811148040.5A CN201811148040A CN110965180A CN 110965180 A CN110965180 A CN 110965180A CN 201811148040 A CN201811148040 A CN 201811148040A CN 110965180 A CN110965180 A CN 110965180A
- Authority
- CN
- China
- Prior art keywords
- fabric
- layer
- blended
- ultraviolet
- cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention particularly relates to a preparation method of a disalicylic acid bisphenol A ester uvioresistant blended fabric, which comprises the following steps: manufacturing a surface layer: the surface layer is made of an ultraviolet-resistant fabric, the ultraviolet-resistant fabric is formed by interweaving warps and wefts, the warps are blended yarns of polyester fibers and cotton fibers, and the wefts are blended yarns of the polyester fibers and the cotton fibers; manufacturing the intermediate layer: the polyester fiber and the cotton fiber in the first fabric layer and the third fabric layer are firstly blended, then are blended with the polyester-cotton fiber, and are woven into cloth, the second fabric layer is manufactured by spinning the cotton fiber, and the first fabric layer, the second fabric layer and the third fabric layer are sequentially attached together in a dispensing or needle-thread sewing mode; manufacturing an inner layer; and (6) attaching the components into a whole. According to the preparation method of the disalicylic acid bisphenol A ester ultraviolet-resistant blended fabric, the prepared fabric has a good ultraviolet-resistant function, and the preparation process is simple and easy to operate.
Description
Technical Field
The invention belongs to the technical field of fabrics, and particularly relates to a preparation method of a disalicylic acid bisphenol A ester ultraviolet-resistant blended fabric.
Background
With the increasing awareness of environmental protection and health care, more and more people are paying attention to natural fibers, and cotton fibers are widely applied to the production of various textiles as the most common natural fibers. At present, yarns on the market come out endlessly, are different in material structure, and are widely applied to the living fields of weaving, rope making, thread making and the like. Xinjiang cotton fiber is well known in the textile industry due to its flexibility and is known as a cotton top grade product by people, and has the advantages of less frequent combing, uniform and smooth evenness and high dyeability. However, the elasticity and the heat retention of the cotton fiber blended yarn on the market at present are not good, so that the woven fabric has the defects of poor heat retention effect and poor elasticity.
Preventing ultraviolet rays from damaging human bodies is being paid more and more attention by consumers. Ultraviolet rays in the solar spectrum not only cause the color fading and embrittlement of textiles, but also cause the sunburn and aging of human skin, generate melanin and color spots, and further induce canceration to harm human health. The ultraviolet-resistant fabric is a protective material for preventing excessive ultraviolet radiation of human bodies.
In view of the above, it is urgently needed to develop a preparation method of a disalicylic acid bisphenol a ester ultraviolet resistant blended fabric.
Disclosure of Invention
The invention aims to provide a preparation method of a disalicylic acid bisphenol A ester uvioresistant blended fabric, which is characterized by comprising the following steps:
a. manufacturing a surface layer: the surface layer is made of an ultraviolet-resistant fabric, the ultraviolet-resistant fabric is formed by interweaving warps and wefts, the warps are blended yarns of polyester fibers and cotton fibers, and the wefts are blended yarns of the polyester fibers and the cotton fibers;
b. manufacturing the intermediate layer: the polyester fiber and the cotton fiber in the first fabric layer and the third fabric layer are firstly blended, then are blended with the polyester-cotton fiber, and are woven into cloth, the second fabric layer is manufactured by spinning the cotton fiber, and the first fabric layer, the second fabric layer and the third fabric layer are sequentially attached together in a dispensing or needle-thread sewing mode;
c. manufacturing an inner layer: firstly, uniformly mixing polyester cotton fibers, polyester fibers and cotton fibers, then carrying out cotton cleaning, cotton carding, drawing, roving, fine sand, automatic spooling, yarn steaming, high-speed doubling and double twisting treatment to obtain fine imitation yarns, and weaving to obtain lining fabric;
d. laminating integrally: and sequentially laminating the surface layer, the middle layer and the inner layer, and then curing, shaping and calendaring to obtain the product.
Preferably, in the step a, the ultraviolet-resistant fabric is added with a bis-salicylic acid bisphenol A ester ultraviolet-resistant finishing agent for soaking for 10-40 minutes, and then is baked at 30-55 ℃ for 20-30 minutes.
Preferably, after the step c, adding 2% of detergent and 15% of softener into the lining fabric for water washing treatment, and controlling the water temperature to be 20-40 ℃ and washing for 60-80 minutes.
Preferably, in the step d, the curing time is 20-60h, the temperature is 30-80 ℃, and the humidity is 30-70%.
Preferably, in the step d, the calendering temperature is 50-90 ℃, the pressure is 50-100Kg/cm2, and the speed is 10-40 m/min.
Due to the adoption of the technical scheme, the invention has the following advantages and beneficial effects:
according to the preparation method of the disalicylic acid bisphenol A ester ultraviolet-resistant blended fabric, the prepared fabric has a good ultraviolet-resistant function, and the preparation process is simple and easy to operate.
Detailed Description
In order to more clearly illustrate the invention, the invention is further described below in connection with preferred embodiments. It is to be understood by persons skilled in the art that the following detailed description is illustrative and not restrictive, and is not to be taken as limiting the scope of the invention.
Example 1
The invention aims to provide a preparation method of a disalicylic acid bisphenol A ester uvioresistant blended fabric, which is characterized by comprising the following steps:
a. manufacturing a surface layer: the surface layer is made of an ultraviolet-resistant fabric, the ultraviolet-resistant fabric is formed by interweaving warps and wefts, the warps are blended yarns of polyester fibers and cotton fibers, and the wefts are blended yarns of the polyester fibers and the cotton fibers;
b. manufacturing the intermediate layer: the polyester fiber and the cotton fiber in the first fabric layer and the third fabric layer are firstly blended, then are blended with the polyester-cotton fiber, and are woven into cloth, the second fabric layer is manufactured by spinning the cotton fiber, and the first fabric layer, the second fabric layer and the third fabric layer are sequentially attached together in a dispensing or needle-thread sewing mode;
c. manufacturing an inner layer: firstly, uniformly mixing polyester cotton fibers, polyester fibers and cotton fibers, then carrying out cotton cleaning, cotton carding, drawing, roving, fine sand, automatic spooling, yarn steaming, high-speed doubling and double twisting treatment to obtain fine imitation yarns, and weaving to obtain lining fabric;
d. laminating integrally: and sequentially laminating the surface layer, the middle layer and the inner layer, and then curing, shaping and calendaring to obtain the product.
In the step a, adding a bis-salicylic acid bisphenol A ester anti-ultraviolet finishing agent into the anti-ultraviolet fabric, soaking for 10 minutes, and then baking for 20 minutes at 30 ℃.
And c, adding 2% of detergent and 15% of softening agent into the inner fabric for washing after the step c, controlling the water temperature at 20 ℃ and washing for 60 minutes.
In the step d, the curing processing time is 20 hours, the temperature is 30 ℃, and the humidity is 30%.
In the step d, the calendering temperature is 50 ℃, the pressure is 50Kg/cm2, and the speed is 10 m/min.
Example 2
The invention aims to provide a preparation method of a disalicylic acid bisphenol A ester uvioresistant blended fabric, which is characterized by comprising the following steps:
a. manufacturing a surface layer: the surface layer is made of an ultraviolet-resistant fabric, the ultraviolet-resistant fabric is formed by interweaving warps and wefts, the warps are blended yarns of polyester fibers and cotton fibers, and the wefts are blended yarns of the polyester fibers and the cotton fibers;
b. manufacturing the intermediate layer: the polyester fiber and the cotton fiber in the first fabric layer and the third fabric layer are firstly blended, then are blended with the polyester-cotton fiber, and are woven into cloth, the second fabric layer is manufactured by spinning the cotton fiber, and the first fabric layer, the second fabric layer and the third fabric layer are sequentially attached together in a dispensing or needle-thread sewing mode;
c. manufacturing an inner layer: firstly, uniformly mixing polyester cotton fibers, polyester fibers and cotton fibers, then carrying out cotton cleaning, cotton carding, drawing, roving, fine sand, automatic spooling, yarn steaming, high-speed doubling and double twisting treatment to obtain fine imitation yarns, and weaving to obtain lining fabric;
d. laminating integrally: and sequentially laminating the surface layer, the middle layer and the inner layer, and then curing, shaping and calendaring to obtain the product.
In the step a, adding a bis-salicylic acid bisphenol A ester anti-ultraviolet finishing agent into the anti-ultraviolet fabric, soaking for 40 minutes, and then baking for 30 minutes at 55 ℃.
And c, adding 2% of detergent and 15% of softening agent into the inner fabric for washing treatment, wherein the water temperature is controlled at 40 ℃, and the washing treatment is carried out for 80 minutes.
In the step d, the curing processing time is 60 hours, the temperature is 80 ℃, and the humidity is 70%.
In the step d, the calendering temperature is 90 ℃, the pressure is 100Kg/cm2, and the speed is 40 m/min.
Through detection, all indexes of the ultraviolet-resistant fabric prepared in the two embodiments are as follows
Breaking Strength N (warp direction) | Breaking Strength N (weft) | Ultraviolet transmittance/%) | |
Example 1 | 245N | 212N | 4.2 |
Example 2 | 245N | 211N | 4.5 |
The foregoing shows and describes the general principles, essential features, and advantages of the invention. It will be understood by those skilled in the art that the present invention is not limited to the embodiments described above, which are given by way of illustration of the principles of the present invention, and that various changes and modifications may be made without departing from the spirit and scope of the invention as defined by the appended claims. The scope of the invention is defined by the appended claims and equivalents thereof.
Claims (5)
1. The preparation method of the disalicylic acid bisphenol A ester ultraviolet-resistant blended fabric is characterized by comprising the following steps of:
a. manufacturing a surface layer: the surface layer is made of an ultraviolet-resistant fabric, the ultraviolet-resistant fabric is formed by interweaving warps and wefts, the warps are blended yarns of polyester fibers and cotton fibers, and the wefts are blended yarns of the polyester fibers and the cotton fibers;
b. manufacturing the intermediate layer: the polyester fiber and the cotton fiber in the first fabric layer and the third fabric layer are firstly blended, then are blended with the polyester-cotton fiber, and are woven into cloth, the second fabric layer is manufactured by spinning the cotton fiber, and the first fabric layer, the second fabric layer and the third fabric layer are sequentially attached together in a dispensing or needle-thread sewing mode;
c. manufacturing an inner layer: firstly, uniformly mixing polyester cotton fibers, polyester fibers and cotton fibers, then carrying out cotton cleaning, cotton carding, drawing, roving, fine sand, automatic spooling, yarn steaming, high-speed doubling and double twisting treatment to obtain fine imitation yarns, and weaving to obtain lining fabric;
d. laminating integrally: and sequentially laminating the surface layer, the middle layer and the inner layer, and then curing, shaping and calendaring to obtain the product.
2. The preparation method of the disalicylic acid bisphenol A ester ultraviolet resistant blended fabric according to claim 1, characterized by comprising the following steps: in the step a, adding a bis-salicylic acid bisphenol A ester anti-ultraviolet finishing agent into the anti-ultraviolet fabric, soaking for 10-40 minutes, and then baking for 20-30 minutes at 30-55 ℃.
3. The preparation method of the disalicylic acid bisphenol A ester ultraviolet resistant blended fabric according to claim 1, characterized by comprising the following steps: and c, adding 2% of detergent and 15% of softening agent into the inner fabric for washing treatment, wherein the water temperature is controlled at 20-40 ℃, and the washing treatment is carried out for 60-80 minutes.
4. The preparation method of the disalicylic acid bisphenol A ester ultraviolet resistant blended fabric according to claim 1, characterized by comprising the following steps: in the step d, the curing processing time is 20-60h, the temperature is 30-80 ℃, and the humidity is 30-70%.
5. The preparation method of the disalicylic acid bisphenol A ester ultraviolet resistant blended fabric as claimed in claim 1, which is characterized in that: in the step d, the calendering temperature is 50-90 ℃, the pressure is 50-100Kg/cm2, and the speed is 10-40 m/min.