CN110885476A - 一锅法制备的二次掺杂型氧化石墨烯/碱溶壳聚糖-聚苯胺-聚丙烯酰胺复合导电水凝胶 - Google Patents
一锅法制备的二次掺杂型氧化石墨烯/碱溶壳聚糖-聚苯胺-聚丙烯酰胺复合导电水凝胶 Download PDFInfo
- Publication number
- CN110885476A CN110885476A CN201911059662.5A CN201911059662A CN110885476A CN 110885476 A CN110885476 A CN 110885476A CN 201911059662 A CN201911059662 A CN 201911059662A CN 110885476 A CN110885476 A CN 110885476A
- Authority
- CN
- China
- Prior art keywords
- polyaniline
- graphene oxide
- alkali
- soluble chitosan
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (6)