CN110589067A - 一种固体的防潮式包装工艺 - Google Patents

一种固体的防潮式包装工艺 Download PDF

Info

Publication number
CN110589067A
CN110589067A CN201910709437.5A CN201910709437A CN110589067A CN 110589067 A CN110589067 A CN 110589067A CN 201910709437 A CN201910709437 A CN 201910709437A CN 110589067 A CN110589067 A CN 110589067A
Authority
CN
China
Prior art keywords
parts
bag
desiccant
moisture
composite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910709437.5A
Other languages
English (en)
Inventor
高艳飞
秦谦燕
陈招燕
韦敏
赵张莹
邱妍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhongshan Everything Culture Development Co Ltd
Zhongshan Torch Polytechnic
Original Assignee
Zhongshan Everything Culture Development Co Ltd
Zhongshan Torch Polytechnic
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhongshan Everything Culture Development Co Ltd, Zhongshan Torch Polytechnic filed Critical Zhongshan Everything Culture Development Co Ltd
Priority to CN201910709437.5A priority Critical patent/CN110589067A/zh
Publication of CN110589067A publication Critical patent/CN110589067A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种固体的防潮式包装工艺，包括以下步骤：A、首先将固体采用压合方式压合成立体状结构；B、之后在立体状的固体外部包覆一层复合膜，并在复合膜外部贴合若干干燥剂袋；C、之后在干燥剂袋外部再包覆一层复合膜；D、之后将包覆两层复合膜的立体状固体装入真空包装内，并抽真空；E、之后将抽真空后的包装袋放入外袋中，并在外袋内填充干燥剂，最后将外袋采用热压封口工艺进行密封，本发明采用的包装工艺操作简单，采用两层复合膜，并在复合膜之间贴合干燥剂袋，能够起到防潮、密封性能，另外，装入真空袋中，能够进一步起到密封性能。

Description

一种固体的防潮式包装工艺
技术领域
本发明涉及固体包装技术领域，具体为一种固体的防潮式包装工艺。
背景技术
包装件在存储与流通过程中均易遭受空气中水蒸气的影响，以致内装物品品质降低，甚至完全失去使用价值。防潮包装就是采取一定的防护措施，隔绝空气中水蒸气对内装物的侵袭，避免其潮湿、变质、发霉、腐烂、锈蚀等。
目前，对固体进行防潮包装，一般直接在包装袋内装入干燥剂进行干燥，其干燥性能差，而且持续时间短，无法有效的确保产品品质，因此，有必要进行改进。
发明内容
本发明的目的在于提供一种固体的防潮式包装工艺，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种固体的防潮式包装工艺,包括以下步骤：
A、首先将固体采用压合方式压合成立体状结构；
B、之后在立体状的固体外部包覆一层复合膜，并在复合膜外部贴合若干干燥剂袋；
C、之后在干燥剂袋外部再包覆一层复合膜；
D、之后将包覆两层复合膜的立体状固体装入真空包装内，并抽真空；
E、之后将抽真空后的包装袋放入外袋中，并在外袋内填充干燥剂，最后将外袋采用热压封口工艺进行密封。
优选的，所述步骤B和步骤C的复合膜结构完全一致，包括海藻酸钠纳米纤维膜、竹纤维纳米纤维膜和聚丙烯膜，所述聚丙烯膜粘合在海藻酸钠纳米纤维膜、竹纤维纳米纤维膜之间。
优选的，所述步骤B干燥剂袋内装入的干燥剂和步骤E中的干燥剂完全一致，其组份按重量份数包括高吸水树脂10-20份、二氧化硅10-20份、竹炭5-15份、膨润土4-10份、蒙脱石5-10份、活性氧化铝粉3-9份、凹凸棒粘土4-12份、三聚硅酸钠4-10份、二氧化钛2-4份、硅藻土5-10份、纳米氧化镁3-9份。
优选的，所述步骤E中的外袋采用高密度聚乙烯制成，所述外袋厚度为1mm-2mm。
与现有技术相比，本发明的有益效果是：
(1)本发明采用的包装工艺操作简单，采用两层复合膜，并在复合膜之间贴合干燥剂袋，能够起到防潮、密封性能，另外，装入真空袋中，能够进一步起到密封性能，最后再将真空袋装入外袋中并填充干燥剂，能够起到长时间防潮密封的性能，有效的防止内部固体受潮变质。
(2)本发明采用的复合膜具有拒水透气性能，此外还具有优异的抗拉强度和耐腐蚀性能，有效的保护内部固体。
(3)本发明采用的干燥剂原料来源广泛，制作成本低，不会产生有害物质，能够有效的起到吸潮功效，而且吸潮持续时间长。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例一：
本发明提供如下技术方案：一种固体的防潮式包装工艺,包括以下步骤：
A、首先将固体采用压合方式压合成立体状结构；
B、之后在立体状的固体外部包覆一层复合膜，并在复合膜外部贴合若干干燥剂袋；
C、之后在干燥剂袋外部再包覆一层复合膜；
D、之后将包覆两层复合膜的立体状固体装入真空包装内，并抽真空；
E、之后将抽真空后的包装袋放入外袋中，并在外袋内填充干燥剂，最后将外袋采用热压封口工艺进行密封。
本实施例中，步骤B和步骤C的复合膜结构完全一致，包括海藻酸钠纳米纤维膜、竹纤维纳米纤维膜和聚丙烯膜，所述聚丙烯膜粘合在海藻酸钠纳米纤维膜、竹纤维纳米纤维膜之间。本发明采用的复合膜具有拒水透气性能，此外还具有优异的抗拉强度和耐腐蚀性能，有效的保护内部固体。
本实施例中，步骤B干燥剂袋内装入的干燥剂和步骤E中的干燥剂完全一致，其组份按重量份数包括高吸水树脂10份、二氧化硅10份、竹炭5份、膨润土4份、蒙脱石5份、活性氧化铝粉3份、凹凸棒粘土4份、三聚硅酸钠4份、二氧化钛2份、硅藻土5份、纳米氧化镁3份。本发明采用的干燥剂原料来源广泛，制作成本低，不会产生有害物质，能够有效的起到吸潮功效，而且吸潮持续时间长。
本实施例中，步骤E中的外袋采用高密度聚乙烯制成，所述外袋厚度为1mm。
实施例二：
一种固体的防潮式包装工艺,包括以下步骤：
A、首先将固体采用压合方式压合成立体状结构；
B、之后在立体状的固体外部包覆一层复合膜，并在复合膜外部贴合若干干燥剂袋；
C、之后在干燥剂袋外部再包覆一层复合膜；
D、之后将包覆两层复合膜的立体状固体装入真空包装内，并抽真空；
E、之后将抽真空后的包装袋放入外袋中，并在外袋内填充干燥剂，最后将外袋采用热压封口工艺进行密封。
本实施例中，步骤B和步骤C的复合膜结构完全一致，包括海藻酸钠纳米纤维膜、竹纤维纳米纤维膜和聚丙烯膜，所述聚丙烯膜粘合在海藻酸钠纳米纤维膜、竹纤维纳米纤维膜之间。本发明采用的复合膜具有拒水透气性能，此外还具有优异的抗拉强度和耐腐蚀性能，有效的保护内部固体。
本实施例中，步骤B干燥剂袋内装入的干燥剂和步骤E中的干燥剂完全一致，其组份按重量份数包括高吸水树脂20份、二氧化硅20份、竹炭15份、膨润土10份、蒙脱石10份、活性氧化铝粉9份、凹凸棒粘土12份、三聚硅酸钠10份、二氧化钛4份、硅藻土10份、纳米氧化镁9份。本发明采用的干燥剂原料来源广泛，制作成本低，不会产生有害物质，能够有效的起到吸潮功效，而且吸潮持续时间长。
本实施例中，步骤E中的外袋采用高密度聚乙烯制成，所述外袋厚度为2mm。
实施例三：
一种固体的防潮式包装工艺,包括以下步骤：
A、首先将固体采用压合方式压合成立体状结构；
B、之后在立体状的固体外部包覆一层复合膜，并在复合膜外部贴合若干干燥剂袋；
C、之后在干燥剂袋外部再包覆一层复合膜；
D、之后将包覆两层复合膜的立体状固体装入真空包装内，并抽真空；
E、之后将抽真空后的包装袋放入外袋中，并在外袋内填充干燥剂，最后将外袋采用热压封口工艺进行密封。
本实施例中，步骤B和步骤C的复合膜结构完全一致，包括海藻酸钠纳米纤维膜、竹纤维纳米纤维膜和聚丙烯膜，所述聚丙烯膜粘合在海藻酸钠纳米纤维膜、竹纤维纳米纤维膜之间。本发明采用的复合膜具有拒水透气性能，此外还具有优异的抗拉强度和耐腐蚀性能，有效的保护内部固体。
本实施例中，步骤B干燥剂袋内装入的干燥剂和步骤E中的干燥剂完全一致，其组份按重量份数包括高吸水树脂11份、二氧化硅12份、竹炭14份、膨润土6份、蒙脱石8份、活性氧化铝粉4份、凹凸棒粘土10份、三聚硅酸钠5份、二氧化钛3份、硅藻土9份、纳米氧化镁4份。本发明采用的干燥剂原料来源广泛，制作成本低，不会产生有害物质，能够有效的起到吸潮功效，而且吸潮持续时间长。
本实施例中，步骤E中的外袋采用高密度聚乙烯制成，所述外袋厚度为2mm。
实施例四：
一种固体的防潮式包装工艺,包括以下步骤：
A、首先将固体采用压合方式压合成立体状结构；
B、之后在立体状的固体外部包覆一层复合膜，并在复合膜外部贴合若干干燥剂袋；
C、之后在干燥剂袋外部再包覆一层复合膜；
D、之后将包覆两层复合膜的立体状固体装入真空包装内，并抽真空；
E、之后将抽真空后的包装袋放入外袋中，并在外袋内填充干燥剂，最后将外袋采用热压封口工艺进行密封。
本实施例中，步骤B和步骤C的复合膜结构完全一致，包括海藻酸钠纳米纤维膜、竹纤维纳米纤维膜和聚丙烯膜，所述聚丙烯膜粘合在海藻酸钠纳米纤维膜、竹纤维纳米纤维膜之间。本发明采用的复合膜具有拒水透气性能，此外还具有优异的抗拉强度和耐腐蚀性能，有效的保护内部固体。
本实施例中，步骤B干燥剂袋内装入的干燥剂和步骤E中的干燥剂完全一致，其组份按重量份数包括高吸水树脂15份、二氧化硅15份、竹炭10份、膨润土7份、蒙脱石8份、活性氧化铝粉6份、凹凸棒粘土8份、三聚硅酸钠7份、二氧化钛3份、硅藻土80份、纳米氧化镁6份。本发明采用的干燥剂原料来源广泛，制作成本低，不会产生有害物质，能够有效的起到吸潮功效，而且吸潮持续时间长。
本实施例中，步骤E中的外袋采用高密度聚乙烯制成，所述外袋厚度为2mm。
综上所述，本发明采用的包装工艺操作简单，采用两层复合膜，并在复合膜之间贴合干燥剂袋，能够起到防潮、密封性能，另外，装入真空袋中，能够进一步起到密封性能，最后再将真空袋装入外袋中并填充干燥剂，能够起到长时间防潮密封的性能，有效的防止内部固体受潮变质。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。

Claims (4)

1.一种固体的防潮式包装工艺,其特征在于：包括以下步骤：
A、首先将固体采用压合方式压合成立体状结构；
B、之后在立体状的固体外部包覆一层复合膜，并在复合膜外部贴合若干干燥剂袋；
C、之后在干燥剂袋外部再包覆一层复合膜；
D、之后将包覆两层复合膜的立体状固体装入真空包装内，并抽真空；
E、之后将抽真空后的包装袋放入外袋中，并在外袋内填充干燥剂，最后将外袋采用热压封口工艺进行密封。
2.根据权利要求1所述的一种固体的防潮式包装工艺,其特征在于：所述步骤B和步骤C的复合膜结构完全一致，包括海藻酸钠纳米纤维膜、竹纤维纳米纤维膜和聚丙烯膜，所述聚丙烯膜粘合在海藻酸钠纳米纤维膜、竹纤维纳米纤维膜之间。
3.根据权利要求1所述的一种固体的防潮式包装工艺,其特征在于：所述步骤B干燥剂袋内装入的干燥剂和步骤E中的干燥剂完全一致，其组份按重量份数包括高吸水树脂10-20份、二氧化硅10-20份、竹炭5-15份、膨润土4-10份、蒙脱石5-10份、活性氧化铝粉3-9份、凹凸棒粘土4-12份、三聚硅酸钠4-10份、二氧化钛2-4份、硅藻土5-10份、纳米氧化镁3-9份。
4.根据权利要求1所述的一种固体的防潮式包装工艺,其特征在于：所述步骤E中的外袋采用高密度聚乙烯制成，所述外袋厚度为1mm-2mm。
CN201910709437.5A 2019-08-02 2019-08-02 一种固体的防潮式包装工艺 Pending CN110589067A (zh)