CN1105751C - 一次性生物全降解餐具的制造方法 - Google Patents
一次性生物全降解餐具的制造方法 Download PDFInfo
- Publication number
- CN1105751C CN1105751C CN99124934A CN99124934A CN1105751C CN 1105751 C CN1105751 C CN 1105751C CN 99124934 A CN99124934 A CN 99124934A CN 99124934 A CN99124934 A CN 99124934A CN 1105751 C CN1105751 C CN 1105751C
- Authority
- CN
- China
- Prior art keywords
- glue
- powder
- tableware
- disposable full
- disposable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种利用复合魔芋胶生产一次性餐具的方法，它是按每1份复合魔芋胶胶加入5-10份植物填空粉，混合均匀，从而制得生产一次性全降解餐具所需的材料，经热压成型、干燥、灭菌后，即可制得一次性全降解餐具。该方法简单易行，原料来源丰富，所得产品为全降解，从根本上解决了我国长期存在的饮食业的白色污染问题，因此具有重要的推广应用价值。
Description
技术领域
本发明涉及一种以天然产物魔芋及其它天然材料制备一次性全降解餐具的方法。
背景技术
一次性餐具在我国的使用十分普遍，但目前绝大部分的一次性餐具都是由合成高分子材料制成。由于该材料在自然界无法降解，从而给环境造成了很大的污染。为解决这种“白色污染”问题，人们纷纷从天然材料或自然界能降解的材料中寻找替代合成高分子材料的途径。
发明内容
本发明的目的是提供一种用天然材料制备一次性全降解餐具的方法，利用该方法制造的一次性全降解餐具对环境友好，不污染环境。
具体方案如下：
一种制备一次性全降解餐具的方法：
本发明是以魔芋为主要成份，将经醋酸酐处理过的魔芋精粉所制得的浓度为3％(重量比，下同)的乙酰化魔芋胶液与浓度为27％的聚乙烯醇胶液按1∶1的比例充分混合，并添加占胶液总体积的5％的戊二醛，混合均匀后在常温下静止交联5小时，便得到交联度为60厘米、固形物含量为15％的复合魔芋胶；按每1份胶(体积)加入5-10份(重量)、粒度为20目左右的秸杆粉、芦苇杆粉、木屑、红薯藤粉或甘蔗渣粉等，在常温条件下混合均匀，从而制得生产一次性全降解餐具所需的材料，再利用现有生产一次性餐具的装备，经热压成型、干燥、灭菌后，即可制得一次性全降解餐具。
按照本发明的技术方案，所述的乙酰化魔芋胶液的制备方法为：
将颗粒度为20-80目的一定量的魔芋精粉放置在耐酸的容器中，添加醋酸酐使所有的魔芋精粉颗粒充分润湿，在30℃下密闭反应1分钟，在搅拌下向经醋酸酐处理过的魔芋精粉中添加相应的水，在60℃下充分混合，制得浓度为3％的乙酰化魔芋胶液。
按照本发明的技术方案，所述的聚乙烯醇溶胶的制备方法为：
将聚合度为1000-2000的聚乙烯醇在90℃下加自来水混合搅拌均匀后，形成浓度为27％(重量比)的溶胶。
胶液交联度的简易测定方法是：将100毫升的待测胶液灌注于100毫升的量筒中，将直径为5毫米、长度为30厘米的玻璃棒插入其中至底，然后垂直提起玻璃棒，测定从玻璃棒上流下的胶液断裂时玻璃棒提起的高度(以厘米计)，作为胶液胶联度的衡量指标。
本发明由于采用天然材料，充分利用了复合魔芋胶的良好性能，解决了天然材料的抗水、抗油及强度等方面的问题，不仅满足了实用的要求，而且对环境友好，能在自然界全部降解。该方法简单易行，原料来源丰富，所得产品为全降解，从根本上解决了我国长期存在的饮食业的白色污染问题，因此具有重要的推广应用价值。
具体实施方式
下面结合实施例对本发明作进一步的说明。
实施例l
将颗粒度为20目的魔芋精粉150克放置在耐酸的容器中，添加醋酸酐120克，使所有的魔芋精粉颗粒充分润湿，在60℃下密闭反应30分钟：在搅拌下向经醋酸酐处理过的魔芋精粉中添加4850毫升自来水，在60℃下充分混合，制得浓度为3％(重量比)的乙酰化魔芋胶液；将聚合度为1700的聚乙烯醇1350克同3650ml自来水混合后，在90℃下搅拌均匀，使之形成浓度为27％(重量比)的溶胶；将以上制得的乙酰化魔芋胶液与聚乙烯醇胶液按1∶1的比例充分混合，并添加占胶液总体积的5％的戊二醛，混合均匀后在常温下静止交联5小时，便得到交联度为60厘米、固形物含量为15％的复合魔芋胶；按每1份胶(体积)加入10份(重量)、粒度为20目左右的秸杆粉，在常温条件下混合均匀，从而制得生产一次性全降解餐具所需的材料，再利用现有生产一次性餐具的装备，经热压成型、干燥、灭菌后，即可制得一次性全降解餐具。
实施例2
魔芋胶的制法与实施例1相同，将粒度为20目的芦苇杆粉按每1份胶(体积)加入9份(重量)芦苇杆粉的比例混合均匀，再利用现有生产一次性餐具的装备，经热压成型、干燥、灭菌后，即可制得一次性全降解餐具。
实施例3
魔芋胶的制法与实施例l相同，将粒度为20目的木屑按每1份胶(体积)加入5份(重量)木屑的比例混合均匀，再利用现有生产一次性餐具的装备，经热压成型、干燥、灭菌后，即可制得一次性全降解餐具。
实施例4
魔芋胶的制法与实施例1相同，将粒度为20目的红薯藤粉按每1份胶(体积)加入7份(重量)红薯藤粉的比例混合均匀，再利用现有生产一次性餐具的装备，经热压成型、干燥、灭菌后，即可制得一次性全降解餐具。
实施例5
魔芋胶的制法与实施例1相同，将粒度为20目的甘蔗渣粉按每1份胶(体积)加入9份(重量)甘蔗渣粉的比例混合均匀，再利用现有生产一次性餐具的装备，经热压成型、干燥、灭菌后，即可制得一次性全降解餐具。
Claims (2)
1.一种利用复合魔芋胶生产一次性全降解餐具的方法，其特征在于：将3％的乙酰化魔芋胶液和27％的聚乙烯醇溶胶按1∶1的重量比充分混合，并添加占胶液总体积的5％的戊二醛，混合均匀后在常温下静止交联5小时，得到交联度为60厘米、固形物含量为15％的复合魔芋胶：按每1份体积的复合魔芋胶加入5-10份重量的植物填充粉，混合均匀，经热压成型、干燥、灭菌后，即可制得一次性全降解餐具。
2.根据权利要求1所述的生产一次性全降解餐具的方法，其特征在于：所述的植物填充粉为秸杆粉、芦苇杆粉、木屑、红薯藤粉或甘蔗渣粉。