CN110492177B - 电池电解液用添加剂、锂离子电池电解液、锂离子电池 - Google Patents
电池电解液用添加剂、锂离子电池电解液、锂离子电池 Download PDFInfo
- Publication number
- CN110492177B CN110492177B CN201910614031.9A CN201910614031A CN110492177B CN 110492177 B CN110492177 B CN 110492177B CN 201910614031 A CN201910614031 A CN 201910614031A CN 110492177 B CN110492177 B CN 110492177B
- Authority
- CN
- China
- Prior art keywords
- electrolyte
- lithium ion
- ion battery
- additive
- carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种电池电解液用添加剂,至少包括文中结构式1‑17所示化合物中的一种。式1‑17所示化合物中的一种作为电池电解液用添加剂,可以在电极(正极和负极)表面形成低阻抗的稳定保护膜,抑制电极和电解液的副反应,降低界面阻抗,兼顾高低温性能(具有良好的低温放电性能,以及良好的循环性能和高温存储性能),提升锂离子电池的整体输出性能。
Description
技术领域
本发明属于锂离子电池技术领域,尤其涉及一种电池电解液用添加剂、一种锂离子电池电解液和一种锂离子电池。
背景技术
锂离子二次电池是新一代最具竞争力的电池,被称为“绿色环保能源”,是解决当代环境污染问题和能源问题的首选技术。近年来,在高能电池领域中锂离子二次电池已取得了巨大成功,但消费者仍然期望综合性能更高的电池面世,而这取决于对新的电极材料和电解质体系的研究和开发。目前智能手机、平板电脑等电子数码产品对电池的能量密度要求越来越高,使得商用锂离子二次电池难以满足要求。提升电池的能量密度可以通过以下两种方式:一是选择高容量和高压实的正负极材料;二是提高电池的工作电压。
纯硅负极理论克容量高达4200mAh/g,是锂离子二次电池的理想高容量负极材料。但纯硅用作锂离子二次电池的负极时,由于体积效应,电池膨胀和极片粉化严重,循环性能差。此外,硅基材料的导电性不好,致使电池低温性能差。人们考虑将硅材料和碳材料复合,形成硅碳复合材料,可以很大程度上提高材料的比容量和导电性,一定程度上降低硅基材料的体积效应。硅碳复合材料同高容量的高镍正极搭配,能量密度能够达到300Wh/Kg以上,与此相匹配的电解液也应运而生,成为锂离子二次电池电解液研究的热点。
氟代碳酸乙烯酯可以在硅碳负极表面形成均匀稳定的SEI膜,由于硅碳负极材料的特殊性(电池膨胀和极片粉化严重),其电解液体系中往往需要比石墨负极体系更多的成膜添加剂,通常需要使用大量的氟代碳酸乙烯酯。而氟代碳酸乙烯酯在高温环境中或者高镍正极电池体系容易分解,无法满足电池高温使用要求等等,单独使用氟代碳酸乙烯酯,其存在多种弊端。为了解决含有氟代碳酸乙烯酯的锂离子二次电池在高温存储过程中的胀气问题,CN201110157665通过在电解液中添加有机二腈类物质(NC-(CH2)n-CN,其中n=2~4)的方法抑制胀气。US 2008/0311481Al公开含有两个腈基的醚/芳基化合物,能够改善电池在高电压和高温条件下的气胀,改善高温存储性能。但是腈类化合物应用于三元高镍正极材料体系会增加电池极化,严重劣化循环性能和低温特性。
发明内容
本发明的目的在于提供一种电池电解液用添加剂,旨在解决现有的锂离子电池,在高温条件下,电解液氧化分解,导致电池的高温存储性能和低温放电性能不能兼顾的问题。
本发明的另一目的在于提供一种含有上述电池电解液用添加剂的锂离子电池电解液,以及一种锂离子电池。
为实现上述发明目的,本发明采用的技术方案如下:
本发明第一方面提供一种电池电解液用添加剂,所述添加剂至少包括如下结构式1-17所示化合物中的一种,
本发明第二方面提供一种锂离子电池电解液,所述电解液包括非水有机溶剂、锂盐和添加剂,其中,所述添加剂至少包括如下结构式1-17所示化合物中的一种,
优选的,所述结构式1-17所示化合物中的至少一种作为第一类添加剂,且以所述电解液的总质量为100%计,所述第一类添加剂的质量百分含量为0.05%~2%。
优选的,所述添加剂还包括选自氟代碳酸乙烯酯、碳酸亚乙烯酯、1,3-丙烷磺内酯、1,4-丁烷磺内酯、1,3-丙烯磺酸内酯、硫酸乙烯酯、硫酸丙烯酯中的至少一种的第二类添加剂。
优选的,以所述电解液的总质量为100%计,所述添加剂的质量百分含量之和小于等于15%。
优选的,所述非水有机溶剂包括碳酸乙烯酯、碳酸丙烯酯、碳酸丁烯酯、碳酸二甲酯、碳酸二乙酯、碳酸甲乙酯、碳酸甲丙酯、乙酸甲酯、乙酸乙酯、乙酸丙酯、丙酸甲酯、丙酸乙酯、丙酸丙酯、丁酸甲酯、丁酸乙酯、γ-丁内酯、γ-戊内酯、δ-戊内酯、ε-己内酯中的至少一种。
优选的,以所述电解液的总质量为100%计,所述非水有机溶剂的质量百分含量之和为55%~75%。
本发明第三方面提供一种锂离子电池,所述锂离子电池包括正极、负极、隔膜和电解液,且所述电解液为本发明所述的锂离子电池电解液。
优选的,所述正极的活性物质为过渡金属氧化物;所述负极的活性物质为石墨、含Si的复合材料或者钛酸锂。
优选的,所述过渡金属氧化物为LiNixCoyMnzL(1-x-y-z)O2,其中,L为Al、Sr、Mg、Ti、Ca、Zr、Zn、Si和Fe中的一种,x、y、z的取值满足:0≤x<1,0<y≤1,0≤z<1,且0<x+y+z≤1。
本发明提供的电池电解液用添加剂,至少包括如下结构式1-17所示化合物中的一种,结构式1-17所示化合物的结构中含有-SO2OSi(CH3)3骨架结构。-SO2OSi(CH3)3骨架结构中的磺酸硅酯结构能够优先电解液中的有机溶剂在负极表面形成SEI膜,抑制有机溶剂的还原分解,且该成膜阻抗较低,因此,可改善锂离子电池的低温输出性能。同时,-SO2OSi(CH3)3骨架结构中的三甲基硅基,一方面可以改变SEI膜的组成,形成更薄的SEI膜,使锂离子可以更容易地穿过SEI膜,提高锂离子电池的功率性能;另一反面,三甲基硅基可以同电解液中含活性质子氢的HF、H2O发生水解或者聚合反应,达到去除H2O、抑制HF的目的,进而提升LiPF6的热稳定性,提高电池高温性能。
在所述电解液添加剂含有-SO2OSi(CH3)3骨架结构的基础上,在磺酸硅酯的硫原子上连接有-CH2CN、-CH2COR、-CH2COOR、-CHCHSi(CH3)3、-C2H4OSi(CH3)3、-RCOOSi(CH3)3、-C5H7O、-ArR、-RCOAr、-ArSi(CH3)3、-ArOSi(CH3)3、-ArSO3Si(CH3)3、-ArS(O)2OSi(CH3)3、-ArS[O(CH3)3]2中的一种,作为电解液添加剂,在首次充电过程中,可以在电极表面形成保护膜。硫原子上连接上述基团,而得到具有不同结构活性的添加剂化合物,改变其在电极表面的成膜活性和成膜组分。具体的,
如硫原子上连接含不饱和键的式1和式5化合物,可以更明显地提升电池的高温输出性能;如硫原子上连接含羰基的化合物的式2、式3、式4、式7、式8、式9、式11,在碳酸酯类电解液中的相溶性好,提升电池的综合输出性能;当硫原子上相连的基团进一步含有三甲硅基团,同时连接含苯环的化合物的式12、式13、式14、式15、式16、式17,苯环分子在同一平面,在苯环平面的两端含有三甲基硅基团,分子反应活性官能团增多,所需要的添加量降低,所述含硅基团可以有效去除电解液中含活性质子氢的HF、H2O,同时参与电极表面成膜。
综上,本发明提供的至少包括如上结构式1-17所示化合物中的一种添加剂,可以在电极(正极和负极)表面形成低阻抗的稳定保护膜,抑制电极和电解液的副反应,降低界面阻抗,兼顾高低温性能(具有良好的低温放电性能,以及良好的循环性能和高温存储性能),提升锂离子电池的整体输出性能。
本发明提供的锂离子电池电解液,含有本发明所述电池电解液用添加剂,可以在电极(正极和负极)表面形成低阻抗的保护膜,抑制电极和电解液的副反应,降低界面阻抗,兼顾高低温性能(具有良好的低温放电性能,以及良好的循环性能和高温存储性能),提升锂离子电池的整体输出性能。
本发明提供的锂离子电池,由于含有本发明的锂离子电池电解液,能够显著提升锂离子电池的循环性能和低温放电性能,提升锂离子电池的整体输出性能。
附图说明
图1是本发明实施例3、对比例1的线性伏安扫描(LSV)曲线图。
具体实施方式
为了使本发明要解决的技术问题、技术方案及有益效果更加清楚明白,以下结合实施例,对本发明进行进一步详细说明。应当理解,此处所描述的具体实施例仅仅用以解释本发明,并不用于限定本发明。
在本发明的描述中,需要理解的是,术语“第一”、“第二”仅用于描述目的,而不能理解为指示或暗示相对重要性或者隐含指明所指示的技术特征的数量。由此,限定有“第一”、“第二”的特征可以明示或者隐含地包括一个或者更多个该特征。在本发明的描述中,“多个”的含义是两个或两个以上,除非另有明确具体的限定。
本发明实施例说明书中所提到的相关成分的重量不仅仅可以指代各组分的具体含量,也可以表示各组分间重量的比例关系,因此,只要是按照本发明实施例说明书相关组分的含量按比例放大或缩小均在本发明实施例说明书公开的范围之内。具体地,本发明实施例说明书中所述的重量可以是μg、mg、g、kg等化工领域公知的质量单位。
本发明实施例第一方面提供一种电池电解液用添加剂,所述添加剂至少包括如下结构式1-17所示化合物中的一种,
本发明实施例提供的电池电解液用添加剂,至少包括如下结构式1-17所示化合物中的一种,结构式1-17所示化合物的结构中含有-SO2OSi(CH3)3骨架结构。-SO2OSi(CH3)3骨架结构中的磺酸硅酯结构能够优先电解液中的有机溶剂在负极表面形成SEI膜,抑制有机溶剂的还原分解,且该成膜阻抗较低,因此,可改善锂离子电池的低温输出性能。同时,-SO2OSi(CH3)3骨架结构中的三甲基硅基,一方面可以改变SEI膜的组成,形成更薄的SEI膜,使锂离子可以更容易地穿过SEI膜,提高锂离子电池的功率性能;另一反面,三甲基硅基可以同电解液中含活性质子氢的HF、H2O发生水解或者聚合反应,达到去除H2O、抑制HF的目的,进而提升LiPF6的热稳定性,提高电池高温性能。
在所述电解液添加剂含有-SO2OSi(CH3)3骨架结构的基础上,优选在磺酸硅酯的硫原子上连接有-CH2CN、-CH2COR、-CH2COOR、-CHCHSi(CH3)3、-C2H4OSi(CH3)3、-RCOOSi(CH3)3、-C5H7O、-ArR、-RCOAr、-ArSi(CH3)3、-ArOSi(CH3)3、-ArSO3Si(CH3)3、-ArS(O)2OSi(CH3)3、-ArS[O(CH3)3]2中的一种,作为电解液添加剂,在首次充电过程中,可以在电极表面形成保护膜。硫原子上连接上述基团,而得到具有不同结构活性的添加剂化合物,改变其在电极表面的成膜活性和成膜组分。具体的,
如硫原子上连接含不饱和键的式1和式5化合物,可以更明显地提升电池的高温输出性能;如硫原子上连接含羰基的化合物的式2、式3、式4、式7、式8、式9、式11,在碳酸酯类电解液中的相溶性好,提升电池的综合输出性能;当硫原子上相连的基团进一步含有三甲硅基团,同时连接含苯环的化合物的式12、式13、式14、式15、式16、式17,苯环分子在同一平面,在苯环平面的两端含有三甲基硅基团,分子反应活性官能团增多,所需要的添加量降低,所述含硅基团可以有效去除电解液中含活性质子氢的HF、H2O,同时参与电极表面成膜。
综上,本发明实施例提供的至少包括如上结构式1-17所示化合物中的一种的添加剂,可以在电极(正极和负极)表面形成低阻抗的稳定保护膜,抑制电极和电解液的副反应,降低界面阻抗,兼顾高低温性能(具有良好的低温放电性能,以及良好的循环性能和高温存储性能),提升锂离子电池的整体输出性能。
具体的,如硫原子上连接含不饱和键的式1和式5化合物,可以更明显地提升电池的高温输出性能,优选用量在1%以内;如硫原子上连接含羰基的化合物的式2、式3、式4、式7、式8、式9、式11,在碳酸酯类电解液中的相溶性好,提升电池的综合输出性能,优选用量在2%以内;当硫原子上相连的基团进一步含有三甲硅基团,同时连接含苯环的化合物的式12、式13、式14、式15、式16、式17,苯环分子在同一平面,在苯环平面的两端含有三甲基硅基团,分子反应活性官能团增多,所需要的添加量降低,所述含硅基团可以有效去除电解液中含活性质子氢的HF、H2O,同时参与电极表面成膜。本发明实施例第二方面提供一种锂离子电池电解液,所述电解液包括非水有机溶剂、锂盐和添加剂,其中,所述添加剂至少包括如下结构式1-17所示化合物中的一种,
本发明实施例提供的锂离子电池电解液,含有本发明实施例所述电池电解液用添加剂,可以在电极(正极和负极)表面形成低阻抗的保护膜,抑制电极和电解液的副反应,降低界面阻抗,兼顾高低温性能(具有良好的低温放电性能,以及良好的循环性能和高温存储性能),提升锂离子电池的整体输出性能。
下面分别对所述锂离子电池电解液各组分进行详细介绍。
非水有机溶剂
由于水对锂离子电池SEI的形成和电池性能有一定的影响,具体表现为电池容量变小、放电时间变短、内阻增加、循环容量衰减、电池膨胀等。本发明实施例采用非水有机溶剂作为电解液的溶剂成分。
优选的,所述非水有机溶剂包括碳酸乙烯酯、碳酸丙烯酯、碳酸丁烯酯、碳酸二甲酯、碳酸二乙酯、碳酸甲乙酯、碳酸甲丙酯、乙酸甲酯、乙酸乙酯、乙酸丙酯、丙酸甲酯、丙酸乙酯、丙酸丙酯、丁酸甲酯、丁酸乙酯、γ-丁内酯、γ-戊内酯、δ-戊内酯、ε-己内酯中的至少一种。
进一步优选的,以所述电解液的总质量为100%计,所述非水有机溶剂的质量百分含量之和为55%~75%。
锂盐
本发明实施例中,所述锂盐可以选用锂离子电池常用的锂盐,包括但不限于六氟磷酸锂、高氯酸锂、四氟硼酸锂、双草酸硼酸锂、双氟草酸硼酸锂、双(三氟甲基磺酰)亚胺锂和双氟磺酰亚胺锂中的一种或多种。进一步的,所述锂盐的用量占锂离子二次电池电解液中的质量百分比为10%~18%。
添加剂
本发明实施例中,所述添加剂主要用于在首次充放电时,用于提高成膜性能。
本发明实施例所述添加剂,至少包括如下结构式1-17所示化合物中的一种,结构式1-17所示化合物的结构中含有-S(O)2OSi(CH3)3骨架结构。-SO2OSi(CH3)3骨架结构中的磺酸硅酯结构能够优先电解液中的有机溶剂在负极表面形成SEI膜,抑制有机溶剂的还原分解,且该成膜阻抗较低,因此,可改善锂离子电池的低温输出性能。同时,-SO2OSi(CH3)3骨架结构中的三甲基硅基,一方面可以改变SEI膜的组成,形成更薄的SEI膜,使锂离子可以更容易地穿过SEI膜,提高锂离子电池的功率性能;另一反面,三甲基硅基可以同电解液中含活性质子氢的HF、H2O发生水解或者聚合反应,达到去除H2O、抑制HF的目的,进而提升LiPF6的热稳定性,提高电池高温性能。
在所述电解液添加剂含有-SO2OSi(CH3)3骨架结构的基础上,优选在磺酸硅酯的硫原子上连接有-CH2CN、-CH2COR、-CH2COOR、-CHCHSi(CH3)3、-C2H4OSi(CH3)3、-RCOOSi(CH3)3、-C5H7O、-ArR、-RCOAr、-ArSi(CH3)3、-ArOSi(CH3)3、-ArSO3Si(CH3)3、-ArS(O)2OSi(CH3)3、-ArS[O(CH3)3]2中的一种,作为电解液添加剂,在首次充电过程中,可以在电极表面形成保护膜。硫原子上连接上述基团,而得到具有不同结构活性的添加剂化合物,改变其在电极表面的成膜活性和成膜组分。具体的,
如硫原子上连接含不饱和键的式1和式5化合物,可以更明显地提升电池的高温输出性能;如硫原子上连接含羰基的化合物的式2、式3、式4、式7、式8、式9、式11,在碳酸酯类电解液中的相溶性好,提升电池的综合输出性能;当硫原子上相连的基团进一步含有三甲硅基团,同时连接含苯环的化合物的式12、式13、式14、式15、式16、式17,苯环分子在同一平面,在苯环平面的两端含有三甲基硅基团,分子反应活性官能团增多,所需要的添加量降低,所述含硅基团可以有效去除电解液中含活性质子氢的HF、H2O,同时参与电极表面成膜。
优选的,所述结构式1-17所示化合物中的至少一种作为第一类添加剂,且以所述电解液的总质量为100%计,所述第一类添加剂的质量百分含量为0.05%~2%。若所述第一类添加剂的质量百分含量低于0.05%,则不能在电极表面形成稳定的保护膜,达不到“抑制电极和电解液的副反应,降低界面阻抗,综合提升电池的输出性能”的改善进效果,此外,也不能改善高镍搭配硅碳体系的电池输出性能;若所述第一类添加剂的质量百分含量高于2%,则其在电极表面形成的保护膜过厚,电池极化增大,劣化电池性能。
本发明实施例中,在所述结构式1-17所示化合物中的至少一种作为添加剂的基础上,可以进一步添加其他添加剂来优化锂离子电池性能。优选的,所述添加剂还包括选自氟代碳酸乙烯酯、碳酸亚乙烯酯、1,3-丙烷磺内酯、1,4-丁烷磺内酯、1,3-丙烯磺酸内酯、硫酸乙烯酯、硫酸丙烯酯中的至少一种的第二类添加剂。
进一步优选的,以所述电解液的总质量为100%计,所述添加剂的质量百分含量之和小于等于15%。在此基础上,任一优选的添加剂(氟代碳酸乙烯酯、碳酸亚乙烯酯、1,3-丙烷磺内酯、1,4-丁烷磺内酯、1,3-丙烯磺酸内酯、硫酸乙烯酯、硫酸丙烯酯)的质量百分含量单独占所述电解液总质量的0.1%~10%。
以及,本发明实施例第三方面提供一种锂离子电池,所述锂离子电池包括正极、负极、隔膜和电解液,且所述电解液为本发明实施例所述的锂离子电池电解液。
本发明实施例提供的锂离子电池,由于含有本发明实施例的锂离子电池电解液,能够显著提升锂离子电池的循环性能和低温放电性能,提升锂离子电池的整体输出性能。
本发明实施例中,所述电解液的组成,各组成成分的选择、含量、优选类型及其选择依据如上文所述,为了节约篇幅,此处不再赘述。
所述正极包括正极活性物质,常规用于锂离子电池的正极活性物质均能用于本发明实施例。但优选的,所述正极的活性物质选用过渡金属氧化物。
具体优选的,所述过渡金属氧化物为LiNixCoyMnzL(1-x-y-z)O2,其中,L为Al、Sr、Mg、Ti、Ca、Zr、Zn、Si和Fe中的一种,x、y、z的取值满足:0≤x<1,0<y≤1,0≤z<1,且0<x+y+z≤1。
所述负极包括负极活性物质,常规用于锂离子电池的负极活性物质均能用于本发明实施例。但优选的,所述负极的活性物质为石墨、含Si的复合材料或者钛酸锂。
所述隔膜的选择,包括但不限于单层聚乙烯(PE)、单层聚丙烯(PP)、双层PP/PE、三层PP/PE/PP或陶瓷隔膜。
下面结合具体实施例进行说明。
各实施例中,英文简写的中文释义解释如下:
EC:碳酸乙烯酯
EMC:碳酸甲乙酯
DMC:碳酸二甲酯
LiPF6:六氟磷酸锂
EP:丙酸乙酯
PP:丙酸丙酯
PC:碳酸丙烯酯
LiFSI:双氟磺酰亚胺锂
LiTFSI:双三氟甲烷磺酰亚胺锂
各实施例中,用到的添加剂结构以及其对应的字母编号如下表1所示。
表1
实施例1
一种锂离子二次电池,包括正极、负极、隔膜和电解液,其中,正极活性物质为镍钴锰酸锂(NCM811)材料;负极活性物质为硅碳复合材料(Si/C),所述锂离子二次电池的制备方法包括以下步骤:
按96.8:2.0:1.2的质量比混合正极活性材料NCM811,导电碳黑和粘结剂聚偏二氟乙烯,分散在N-甲基-2-吡咯烷酮中,得到正极浆料,将正极浆料均匀涂布在铝箔的两面上,经过烘干、压延和真空干燥,并用超声波焊机焊上铝制引出线后得到正极板(正极片),极板的厚度在135~155μm之间;
按96:1:1.2:1.8的质量比混合硅碳复合材料、导电碳黑、粘结剂丁苯橡胶和羧甲基纤维素,分散在去离子水中,得到负极浆料,将负极浆料涂布在铜箔的两面上,经过烘干、压延和真空干燥,并用超声波焊机焊上镍制引出线后得到负极板(负极片),极板的厚度在135~155μm之间;
将碳酸乙烯酯(EC)、碳酸甲乙酯(EMC)、碳酸二甲酯(DMC)按质量比为2:1:7进行混合,混合后加入基于电解液总质量12.5%的六氟磷酸锂,加入基于电解液总质量1%的Q1,制备得到电解液。
采用厚度为14μm的PP基膜,单面涂覆2μm Al2O3的涂覆隔膜。
将制得的正极片、隔膜、负极片放于自动卷绕机上,卷绕得到裸电芯;将裸电芯置于圆柱钢壳中,焊接好负极极耳和盖帽极耳,将上述制备的电解液注入到干燥后的电芯中,封口、静置、预充、老化和分容,完成锂离子二次电池的制备(21700-4.8Ah)。
实施例2~实施例14
实施例2~实施例14,除了电解液中组分不同外,其余正极、负极、隔膜、锂离子二次电池的制备均同实施例1,各实施例中第一类添加剂(化合物1-17中的至少一种)的选择及其含量如表2所示。
对比例1
对比例1中,除了电解液中非水有机溶剂、添加剂的类型与含量(基于电解液总质量)不同外,其余正极、负极、隔膜、锂离子二次电池的制备均同实施例1,对比例1中非水有机溶剂、添加剂的类型与含量如表2所示。
将实施例1~实施例14、对比例1制备的锂离子二次电池进行性能测试,测试方法如下:
1)线性扫描伏安法(LSV)
以Pt作为工作电极,Li作为对电极和参比电极,组装三电极装置在电化学工作站上进行线性扫描。
2)循环性能测试:在25±2℃/45℃±2℃下,将分容后的电池用0.5C恒流恒压充至4.2V(截止电流为0.01C),然后用1C恒流放电至2.75V。充/放电N次循环后计算第N次循环容量的保持率,计算公式如下:
第N次循环容量保持率(%)=(第N次循环放电容量/第1次循环放电容量)×100%;
3)高温储存性能:将分容后的电池在常温下用0.5C恒流恒压充至4.2V(截止电流为0.01C),测量电池初始放电容量,然后在60℃储存7天后,以0.5C放电至2.75V测量电池的保持容量和恢复容量。计算公式如下:
电池容量保持率(%)=保持容量/初始容量×100%;
电池容量恢复率(%)=恢复容量/初始容量×100%。
4)低温放电:在室温以0.5C恒流恒压充电至4.2V,搁置5min,0.2C放电至2.75V,检测电池初始容量。搁置5min,0.5C恒流恒压充电至4.2V(截止电流为0.01C)。把电池放入-20℃的低温箱中搁置6h,并在此条件下以0.2C放电至2.75V,检测低温下的放电容量。
低温放电保持率(%)=低温放电容量/初始容量×100%。
测试结果见下表2所示。
表2
将电池体系为NCM811搭配硅碳复合材料的实施例1-14、对比例1进行对比分析。由表2可见,采用本发明技术方案的实施例1至实施例14具有良好的循环性能、高温储存性能和低温放电性能;而采用对比例1电解液的锂离子电池输出性能差,不能兼顾高低温和循环性能。
具体的,各实施例和对比例1比较,含有上述结构化合物的实施例1至实施例14,各实施例的低温放电性能、高温循环、常温循环和高温储存性能均明显优于对比例1。说明Q1、Q2、Q3、Q4、Q5、Q6、Q7、Q8、Q9、Q10、Q11、Q12、Q1+Q8、Q2+Q11的存在,能够有效地提升电池的综合输出性能。
采用对比例1和实施例3电解液,进行LSV评测,结果见图1所示。从图1可知,含Q3的样品氧化峰提前,推知该添加剂优先其它溶剂氧化,进一步说明Q3容易在正极氧化形成保护膜,抑制电解液与高镍材料的副反应。
以上所述仅为本发明的较佳实施例而已,并不用以限制本发明,凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等,均应包含在本发明的保护范围之内。
Claims (10)
3.如权利要求2所述的锂离子电池电解液,其特征在于,所述结构式2、3、5、6、9-17所示化合物中的至少一种作为第一类添加剂,且以所述电解液的总质量为100%计,所述第一类添加剂的质量百分含量为0.05%~2%。
4.如权利要求3所述的锂离子电池电解液,其特征在于,所述添加剂还包括选自氟代碳酸乙烯酯、碳酸亚乙烯酯、1,3-丙烷磺内酯、1,4-丁烷磺内酯、1,3-丙烯磺酸内酯、硫酸乙烯酯、硫酸丙烯酯中的至少一种的第二类添加剂。
5.如权利要求4所述的锂离子电池电解液,其特征在于,以所述电解液的总质量为100%计,所述添加剂的质量百分含量之和小于等于15%。
6.如权利要求2至5任一项所述的锂离子电池电解液,其特征在于,所述非水有机溶剂包括碳酸乙烯酯、碳酸丙烯酯、碳酸丁烯酯、碳酸二甲酯、碳酸二乙酯、碳酸甲乙酯、碳酸甲丙酯、乙酸甲酯、乙酸乙酯、乙酸丙酯、丙酸甲酯、丙酸乙酯、丙酸丙酯、丁酸甲酯、丁酸乙酯、γ-丁内酯、γ-戊内酯、δ-戊内酯、ε-己内酯中的至少一种。
7.如权利要求6所述的锂离子电池电解液,其特征在于,以所述电解液的总质量为100%计,所述非水有机溶剂的质量百分含量之和为55%~75%。
8.一种锂离子电池,其特征在于,所述锂离子电池包括正极、负极、隔膜和电解液,且所述电解液为权利要求2-7任一项所述的锂离子电池电解液。
9.如权利要求8所述的锂离子电池,其特征在于,所述正极的活性物质为过渡金属氧化物;所述负极的活性物质为石墨、含Si的复合材料或者钛酸锂。
10.如权利要求9所述的锂离子电池,其特征在于,所述过渡金属氧化物为LiNixCoyMnzL(1-x-y-z)O2,其中,L为Al、Sr、Mg、Ti、Ca、Zr、Zn、Si和Fe中的一种,x、y、z的取值满足:0≤x<1,0<y≤1,0≤z<1,且0<x+y+z≤1。