CN1103827C - 特别适用于航空应用的、新的可焊、耐腐蚀、高镁含量的铝－镁合金 - Google Patents

特别适用于航空应用的、新的可焊、耐腐蚀、高镁含量的铝－镁合金 Download PDF

Info

Publication number
CN1103827C
CN1103827C CN99801242A CN99801242A CN1103827C CN 1103827 C CN1103827 C CN 1103827C CN 99801242 A CN99801242 A CN 99801242A CN 99801242 A CN99801242 A CN 99801242A CN 1103827 C CN1103827 C CN 1103827C
Authority
CN
China
Prior art keywords
weight
aluminum
magnesium alloy
magnesium
alloy according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN99801242A
Other languages
English (en)
Chinese (zh)
Other versions
CN1274392A (zh
Inventor
B·兰克佐斯基
V·叶拉金
R·劳
V·萨克哈罗夫
Y·费拉托夫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Airbus Operations GmbH
Original Assignee
DaimlerChrysler AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DaimlerChrysler AG filed Critical DaimlerChrysler AG
Publication of CN1274392A publication Critical patent/CN1274392A/zh
Application granted granted Critical
Publication of CN1103827C publication Critical patent/CN1103827C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/06—Alloys based on aluminium with magnesium as the next major constituent

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Preventing Corrosion Or Incrustation Of Metals (AREA)
  • Powder Metallurgy (AREA)
  • Arc Welding In General (AREA)
  • Conductive Materials (AREA)
  • Prevention Of Electric Corrosion (AREA)
  • Laminated Bodies (AREA)
CN99801242A 1998-08-21 1999-08-10 特别适用于航空应用的、新的可焊、耐腐蚀、高镁含量的铝－镁合金 Expired - Fee Related CN1103827C (zh)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE19838018A DE19838018C2 (de) 1998-08-21 1998-08-21 Geschweißtes Bauteil aus einer schweißbaren, korrosionsbeständigen hochmagnesiumhaltigen Aluminium-Magnesium-Legierung
DE19838018.6 1998-08-21

Publications (2)

Publication Number Publication Date
CN1274392A CN1274392A (zh) 2000-11-22
CN1103827C true CN1103827C (zh) 2003-03-26

Family

ID=7878286

Family Applications (1)

Application Number Title Priority Date Filing Date
CN99801242A Expired - Fee Related CN1103827C (zh) 1998-08-21 1999-08-10 特别适用于航空应用的、新的可焊、耐腐蚀、高镁含量的铝－镁合金

Country Status (9)

Country Link
US (1) US6531004B1 (enExample)
EP (1) EP1029097B1 (enExample)
JP (1) JP2002523622A (enExample)
CN (1) CN1103827C (enExample)
CA (1) CA2306912C (enExample)
DE (2) DE19838018C2 (enExample)
ES (1) ES2242427T3 (enExample)
RU (1) RU2226565C2 (enExample)
WO (1) WO2000011232A1 (enExample)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102395693A (zh) * 2009-04-16 2012-03-28 阿勒里斯铝业科布伦茨有限公司 可焊接的金属制品

Families Citing this family (45)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6139653A (en) * 1999-08-12 2000-10-31 Kaiser Aluminum & Chemical Corporation Aluminum-magnesium-scandium alloys with zinc and copper
US6676899B2 (en) * 2000-12-21 2004-01-13 Eads Deutschland Gmbh Non-hardenable aluminum alloy as a semi-finished product for structures
EP1217085B1 (de) * 2000-12-21 2003-10-01 EADS Deutschland GmbH Nichtaushärtbare Aluminiumlegierung als Halbzeug für Strukturen
DE10248594B4 (de) * 2001-12-14 2006-04-27 Eads Deutschland Gmbh Verfahren zum Herstellen eines Scandium (Sc)- legierten Aluminiumblechmaterials mit hoher Risszähigkeit
DE10332003B3 (de) * 2003-07-14 2004-12-16 Eads Deutschland Gmbh Geschweißtes Aluminium-Strukturbauteil mit Aluminium-Guss-Werkstoffelementen
DE10331990A1 (de) * 2003-07-14 2005-02-24 Eads Deutschland Gmbh Geschweißtes Aluminium-Strukturbauteil mit metallisch induzierter Rissabeichung
US7875132B2 (en) * 2005-05-31 2011-01-25 United Technologies Corporation High temperature aluminum alloys
BRPI0614527B1 (pt) * 2005-08-16 2015-08-18 Aleris Aluminum Koblenz Gmbh Produto de liga de alumínio
US20080311421A1 (en) * 2007-06-15 2008-12-18 United Technologies Corporation Friction stir welded structures derived from AL-RE-TM alloys
US20090263273A1 (en) * 2008-04-18 2009-10-22 United Technologies Corporation High strength L12 aluminum alloys
US7871477B2 (en) * 2008-04-18 2011-01-18 United Technologies Corporation High strength L12 aluminum alloys
US7811395B2 (en) * 2008-04-18 2010-10-12 United Technologies Corporation High strength L12 aluminum alloys
US7879162B2 (en) * 2008-04-18 2011-02-01 United Technologies Corporation High strength aluminum alloys with L12 precipitates
US20090260724A1 (en) * 2008-04-18 2009-10-22 United Technologies Corporation Heat treatable L12 aluminum alloys
US8017072B2 (en) * 2008-04-18 2011-09-13 United Technologies Corporation Dispersion strengthened L12 aluminum alloys
US8002912B2 (en) * 2008-04-18 2011-08-23 United Technologies Corporation High strength L12 aluminum alloys
US8409373B2 (en) * 2008-04-18 2013-04-02 United Technologies Corporation L12 aluminum alloys with bimodal and trimodal distribution
US7875131B2 (en) 2008-04-18 2011-01-25 United Technologies Corporation L12 strengthened amorphous aluminum alloys
US7875133B2 (en) * 2008-04-18 2011-01-25 United Technologies Corporation Heat treatable L12 aluminum alloys
US8778099B2 (en) * 2008-12-09 2014-07-15 United Technologies Corporation Conversion process for heat treatable L12 aluminum alloys
US20100143177A1 (en) * 2008-12-09 2010-06-10 United Technologies Corporation Method for forming high strength aluminum alloys containing L12 intermetallic dispersoids
US8778098B2 (en) * 2008-12-09 2014-07-15 United Technologies Corporation Method for producing high strength aluminum alloy powder containing L12 intermetallic dispersoids
NL1037667C2 (nl) 2009-02-12 2010-08-16 Aleris Aluminum Koblenz Gmbh Werkwijze voor het vervaardigen van een almg-legering vliegtuigconstructiedeel.
US20100226817A1 (en) * 2009-03-05 2010-09-09 United Technologies Corporation High strength l12 aluminum alloys produced by cryomilling
US20100254850A1 (en) * 2009-04-07 2010-10-07 United Technologies Corporation Ceracon forging of l12 aluminum alloys
US20100252148A1 (en) * 2009-04-07 2010-10-07 United Technologies Corporation Heat treatable l12 aluminum alloys
US9611522B2 (en) * 2009-05-06 2017-04-04 United Technologies Corporation Spray deposition of L12 aluminum alloys
US9127334B2 (en) * 2009-05-07 2015-09-08 United Technologies Corporation Direct forging and rolling of L12 aluminum alloys for armor applications
US20110044844A1 (en) * 2009-08-19 2011-02-24 United Technologies Corporation Hot compaction and extrusion of l12 aluminum alloys
US8728389B2 (en) * 2009-09-01 2014-05-20 United Technologies Corporation Fabrication of L12 aluminum alloy tanks and other vessels by roll forming, spin forming, and friction stir welding
US8409496B2 (en) * 2009-09-14 2013-04-02 United Technologies Corporation Superplastic forming high strength L12 aluminum alloys
US20110064599A1 (en) * 2009-09-15 2011-03-17 United Technologies Corporation Direct extrusion of shapes with l12 aluminum alloys
US9194027B2 (en) * 2009-10-14 2015-11-24 United Technologies Corporation Method of forming high strength aluminum alloy parts containing L12 intermetallic dispersoids by ring rolling
US20110091345A1 (en) * 2009-10-16 2011-04-21 United Technologies Corporation Method for fabrication of tubes using rolling and extrusion
US8409497B2 (en) * 2009-10-16 2013-04-02 United Technologies Corporation Hot and cold rolling high strength L12 aluminum alloys
US20110091346A1 (en) * 2009-10-16 2011-04-21 United Technologies Corporation Forging deformation of L12 aluminum alloys
EP2546373A1 (en) 2011-07-13 2013-01-16 Aleris Aluminum Koblenz GmbH Method of manufacturing an Al-Mg alloy sheet product
CN104195387B (zh) * 2014-09-05 2016-03-16 天津立中合金集团有限公司 一种轮胎模具用高纯净铝镁合金材料及其制备方法
CN104498785B (zh) * 2014-11-23 2016-07-06 北京工业大学 一种Al-Mg-Er-Zr耐热铝合金及其制备工艺
EP3181711B1 (de) 2015-12-14 2020-02-26 Apworks GmbH Scandiumhaltige aluminiumlegierung für pulvermetallurgische technologien
JP7229181B2 (ja) 2017-06-21 2023-02-27 オプシチェストボ エス オグラニチェンノイ オトヴェストヴェンノストユ “オベディネンナヤ カンパニア ルサール インゼネルノ－テクノロギケスキー チェントル” アルミニウム系合金
CN107460380B (zh) * 2017-09-04 2019-07-09 佛山科学技术学院 一种高强耐蚀铝合金及其制备方法
CN109457148B (zh) * 2018-12-25 2019-10-22 惠州市田宇中南铝合金新材料科技有限公司 一种Al-Mg-Mn-Cu合金及其制备方法
JP7273174B2 (ja) 2019-12-27 2023-05-12 オブシュチェストボ・エス・オグラニチェノイ・オトベツトベノスティウ“オベディネナヤ・コンパニヤ・ルサール・インツェネルノ－テフノロギチェスキー・ツェントル” アルミニウム系合金
EP4628610A1 (en) 2022-12-02 2025-10-08 Obshchestvo S Ogranichennoj Otvetstvennost'Yu "Institut Legkikh Materialov I Tekhnologij" Aluminium-based alloy

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5211143A (en) * 1975-07-18 1977-01-27 Nippon Keikinzoku Sougou Kenki Aluminium alloy filler matertal
US5624632A (en) * 1995-01-31 1997-04-29 Aluminum Company Of America Aluminum magnesium alloy product containing dispersoids

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
SU561349A1 (ru) * 1975-07-07 1978-08-25 Всесоюзный научно-исследовательский, проектно-конструкторский и технологический институт электросварочного оборудования Сплав дл алитировани оболочки порошковой проволоки
JPS59159961A (ja) 1983-02-28 1984-09-10 Mitsubishi Alum Co Ltd 超塑性Ａｌ合金
JPS63179040A (ja) 1987-01-20 1988-07-23 Showa Alum Corp 表面平滑性に優れたシリンダ用アルミニウム合金
JPS63248593A (ja) * 1987-03-31 1988-10-14 Showa Alum Corp アルミニウム合金溶加材
JP3286982B2 (ja) * 1990-04-25 2002-05-27 菱化マックス株式会社 金型素材
US5597529A (en) * 1994-05-25 1997-01-28 Ashurst Technology Corporation (Ireland Limited) Aluminum-scandium alloys
RU2081934C1 (ru) * 1995-07-13 1997-06-20 Акционерное общество открытого типа "Всероссийский институт легких сплавов" Деформируемый термически неупрочняемый сплав на основе алюминия
CA2280191C (en) * 1997-02-10 2007-07-31 Aluminum Company Of America Aluminum alloy product
EP0918095B1 (de) * 1997-11-20 2003-03-26 Alcan Technology & Management AG Verfahren zur Herstellung eines Strukturbauteiles aus einer Aluminium-Druckgusslegierung

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5211143A (en) * 1975-07-18 1977-01-27 Nippon Keikinzoku Sougou Kenki Aluminium alloy filler matertal
US5624632A (en) * 1995-01-31 1997-04-29 Aluminum Company Of America Aluminum magnesium alloy product containing dispersoids

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102395693A (zh) * 2009-04-16 2012-03-28 阿勒里斯铝业科布伦茨有限公司 可焊接的金属制品
CN102395693B (zh) * 2009-04-16 2014-04-09 阿勒里斯铝业科布伦茨有限公司 可焊接的金属制品

Also Published As

Publication number Publication date
CN1274392A (zh) 2000-11-22
DE59912240D1 (de) 2005-08-11
EP1029097B1 (de) 2005-07-06
CA2306912A1 (en) 2000-03-02
CA2306912C (en) 2008-12-23
WO2000011232A1 (de) 2000-03-02
DE19838018A1 (de) 2000-03-02
ES2242427T3 (es) 2005-11-01
US6531004B1 (en) 2003-03-11
RU2226565C2 (ru) 2004-04-10
DE19838018C2 (de) 2002-07-25
EP1029097A1 (de) 2000-08-23
JP2002523622A (ja) 2002-07-30

Similar Documents

Publication Publication Date Title
CN1103827C (zh) 特别适用于航空应用的、新的可焊、耐腐蚀、高镁含量的铝－镁合金
CN1103828C (zh) 特别适用于交通运输的、可焊、耐腐蚀铝－镁合金
CN1107120C (zh) 特别适用于汽车应用的、新的可焊、耐腐蚀、高镁含量的铝－镁合金
RU2000112642A (ru) Обладающий свариваемостью, коррозионностойкий алюминиево-магниевый сплав с высоким содержанием магния, прежде всего для применения в авиастроении
CA2663605C (en) Magnesium gadolinium alloys
RU2000112644A (ru) Обладающие свариваемостью, коррозионностойкие алюминиево-магниевые сплавы, прежде всего для применения в транспортном машиностроении
JP2002523622A5 (enExample)
RU2000112645A (ru) Новый обладающий свариваемостью, коррозионностойкий алюминиево-магниевый сплав с высоким содержанием магния, прежде всего для применения в автомобилестроении
CA2675863A1 (en) Creep-resistant magnesium alloy
JPH10147830A (ja) イットリウム含有マグネシウム合金
JP3916452B2 (ja) 高耐蝕性マグネシウム合金およびその製造方法
JP2009263792A (ja) 延性マグネシウム合金
JPH04176839A (ja) マグネシウム基合金
CA2087217A1 (en) Magnesium alloy
JPH09256099A (ja) 耐熱マグネシウム合金
JPS6289838A (ja) 圧延加工性に優れた高強度アルミニウム合金

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
ASS Succession or assignment of patent right

Owner name: AIRBUS GMBH (DE)

Free format text: FORMER OWNER: DAIMLER-KLINSLER AG

Effective date: 20130927

C41 Transfer of patent application or patent right or utility model
TR01 Transfer of patent right

Effective date of registration: 20130927

Address after: hamburg

Patentee after: Airbus GMBH (DE)

Address before: Stuttgart, Germany

Patentee before: Daimler-Benz AG

CF01 Termination of patent right due to non-payment of annual fee

Granted publication date: 20030326

Termination date: 20140810

EXPY Termination of patent right or utility model