CN110373258A - 一种高温高湿髙盐雾地区用武器装备防护组成物及其制备方法 - Google Patents
一种高温高湿髙盐雾地区用武器装备防护组成物及其制备方法 Download PDFInfo
- Publication number
- CN110373258A CN110373258A CN201910748436.1A CN201910748436A CN110373258A CN 110373258 A CN110373258 A CN 110373258A CN 201910748436 A CN201910748436 A CN 201910748436A CN 110373258 A CN110373258 A CN 110373258A
- Authority
- CN
- China
- Prior art keywords
- protection composition
- salt fog
- arms
- equips
- high temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种高温高湿髙盐雾地区用武器装备防护组成物及其制备方法。本发明的防护组成物主要由基础油、复合防锈剂、粘度指数改进剂、抗氧剂、分散剂和憎水剂构成，其原理是主要依靠油膜粘附力、防锈剂在金属表面的定向吸附防锈和憎水剂的斥水作用，形成油膜的超强防护作用和一定的润滑作用，使得利用其在高温高湿髙盐雾地区用武器装进行保养防护处理后，增强其耐腐蚀性能，提高其使用寿命。
Description
技术领域
本发明涉及武器装备防护技术领域，特别是涉及一种高温高湿高盐雾地区用武器装备防护组成物及其制备方法。
背景技术
目前，我军各部常年在高温、严寒等恶劣的作战环境下训练和演习，在部队得高强度锻炼的同时，武器装备也经受了残酷的考验。因为环境的特殊，对于轻武器表面的磨损异常严重。传统的表面修复材料和技术处理难度大、修复时间长、表面保护效果不佳、生产工艺落后等缺点，难以达到现阶段部队对武器装备维护保养的需求。
发明内容
本发明的目的是提供了一种高温高湿高盐雾地区用武器装备防护组成物。
本发明的另一目的是提供了该高温高湿高盐雾地区用武器装备防护组成物的制备方法。
本发明的高温高湿高盐雾地区用武器装备防护组成物包括以下重量分数的组分：粘度指数改进剂5-10％，防锈剂3.6-13.5％，抗氧剂0.5％，分散剂1.5％，憎水剂1％，其余为基础油。
优选的，所述粘度指数改进剂包括聚甲基丙烯酸酯、聚异丁烯或聚乙烯正丁基醚中的一种或几种。
优选的，所述防锈剂是由T701防锈剂、T705防锈剂以及T711防锈剂构成。其中T701防锈剂又称石油磺酸钡(流动性石油磺酸钡)，其为棕红色粘稠液体。T705防锈剂又称二壬基萘磺酸钡，其为棕褐色半透明固体。T711防锈剂又称N-油酰肌氨酸-十八胺盐，其为淡黄色蜡状固体。
进一步优选的，所述T701防锈剂占防护组成物总重量的3-9％，所述T705防锈剂占防护组成物总重量的0.5-3.5％，所述T711防锈剂占防护组成物总重量的0.1-1％。
优选的，所述抗氧剂为T501抗氧化剂，所述分散剂为T154分散剂。其中T501抗氧化剂即为2,6-二叔丁基对甲基苯酚，其与油中的活性自由基和过氧化物发生反应，形成稳定的化合物，从而消耗油中生成的自由基，阻止了油分子自身的氧化过程。其中T154分散剂即为聚异丁烯双丁二酰亚胺，具有优良的低温分散性和高温稳定性能，可与高温烟灰有良好的增溶作用。
优选的，所述憎水剂为纳米氟化树脂。
进一步优选的，所述纳米氟化树脂包括纳米PTFE树脂、纳米FEP树脂或纳米氟化聚氨酯树脂中的一种或几种。
优选的，所述基础油为矿物基础油或合成油。
进一步优选的，所述基础油为45号变压器油。
本发明所述的温高湿髙盐雾地区用武器装备防护组成物的制备方法，包括以下步骤：将基础油加入到搅拌釜中，开启搅拌，加热恒温在80℃±2℃；在不断搅拌过程中按比例加入分散剂，并搅拌均匀；按比例加入防锈剂；按比例加入抗氧化剂和和粘度指数改进剂，继续搅拌均匀；最后按比例加入憎水剂，搅拌均匀后，继续搅拌，并保温4小时得到本发明的高温高湿髙盐雾地区用武器装备防护组成物。
与现有技术相比，本发明具有以下有益效果：本发明主要由基础油、复合防锈剂、粘度指数改进剂、抗氧剂、分散剂和憎水剂构成，其原理是主要依靠油膜粘附力、防锈剂在金属表面的定向吸附防锈和憎水剂的斥水作用，形成油膜高强的防护作用和一定的润滑作用，使得利用其在高温高湿髙盐雾地区用武器装进行保养防护处理后，增强其耐腐蚀性能，提高其使用寿命。
具体实施方式
下面结合具体实施例对本发明作进一步说明。
实施例1
一种高温高湿髙盐雾地区用武器装备防护组成物，包括以下重量分数的组分：聚甲基丙烯酸酯5％，T701防锈剂3％，T705防锈剂0.5％，T711防锈剂0.1％，T501抗氧化剂0.5％，T154分散剂1.5％，纳米PTFE树脂憎水剂1％，其余为45号变压器油。
其制备方法包括以下步骤：将45号变压器油加入到搅拌釜中，开启搅拌，加热恒温在80℃；在不断搅拌过程中按比例加入T154分散剂，并搅拌均匀；按比例加入T701防锈剂、T705防锈剂、T711防锈剂，待上一种防锈剂完全溶解后再加入另一种防锈剂；按比例加入抗氧化剂和和聚甲基丙烯酸酯，继续搅拌均匀；最后按比例加入纳米PTFE树脂憎水剂，搅拌均匀后，保温4小时得到本发明的高温高湿髙盐雾地区用武器装备防护组成物。
实施例2
一种高温高湿髙盐雾地区用武器装备防护组成物，包括以下重量分数的组分：聚甲基丙烯酸酯10％，T701防锈剂9％，T705防锈剂3.5％，T711防锈剂1％，T501抗氧化剂0.5％，T154分散剂1.5％，纳米PTFE树脂憎水剂1％，其余为45号变压器油。
其制备方法包括以下步骤：将45号变压器油加入到搅拌釜中，开启搅拌，加热恒温在78℃；在不断搅拌过程中按比例加入T154分散剂，并搅拌均匀；按比例加入T701防锈剂、T705防锈剂、T711防锈剂，待上一种防锈剂完全溶解后再加入另一种防锈剂；按比例加入抗氧化剂和和聚甲基丙烯酸酯，继续搅拌均匀；最后按比例加入纳米PTFE树脂憎水剂，搅拌均匀后，保温4小时得到本发明的高温高湿髙盐雾地区用武器装备防护组成物。
实施例3
一种高温高湿髙盐雾地区用武器装备防护组成物，包括以下重量分数的组分：聚异丁烯10％，T701防锈剂6％，T705防锈剂3％，T711防锈剂0.5％，T501抗氧化剂0.5％，T154分散剂1.5％，纳米FEP树脂憎水剂1％，其余为45号变压器油。
其制备方法包括以下步骤：将45号变压器油加入到搅拌釜中，开启搅拌，加热恒温在80℃；在不断搅拌过程中那比例加入T154分散剂，并搅拌均匀；按比例加入T701防锈剂、T705防锈剂、T711防锈剂，待上一种防锈剂完全溶解后再加入另一种防锈剂；按比例加入抗氧化剂和和聚异丁烯，继续搅拌均匀；最后按比例加入纳米FEP树脂憎水剂，搅拌均匀后，保温4小时得到本发明的高温高湿髙盐雾地区用武器装备防护组成物。
实施例4
一种高温高湿髙盐雾地区用武器装备防护组成物，包括以下重量分数的组分：聚乙烯正丁基醚8％，T701防锈剂5％，T705防锈剂2.5％，T711防锈剂0.8％，T501抗氧化剂0.5％，T154分散剂1.5％，纳米氟化聚氨酯树脂憎水剂1％，其余为45号变压器油。
其制备方法包括以下步骤：将45号变压器油加入到搅拌釜中，开启搅拌，加热恒温在80℃；在不断搅拌过程中那比例加入T154分散剂，并搅拌均匀；按比例加入T701防锈剂、T705防锈剂、T711防锈剂，待上一种防锈剂完全溶解后再加入另一种防锈剂；按比例加入抗氧化剂和和聚乙烯正丁基醚，继续搅拌均匀；最后按比例加入纳米氟化聚氨酯树脂憎水剂，搅拌均匀后，保温4小时得到本发明的高温高湿髙盐雾地区用武器装备防护组成物。
实施例5
一种高温高湿髙盐雾地区用武器装备防护组成物，包括以下重量分数的组分：聚乙烯正丁基醚5％，T701防锈剂9％，T705防锈剂3.5％，T711防锈剂1％，T501抗氧化剂0.5％，T154分散剂1.5％，纳米PTFE树脂憎水剂1％，其余为45号变压器油。
其制备方法包括以下步骤：将45号变压器油加入到搅拌釜中，开启搅拌，加热恒温在80℃；在不断搅拌过程中那比例加入T154分散剂，并搅拌均匀；按比例加入T701防锈剂、T705防锈剂、T711防锈剂，待上一种防锈剂完全溶解后再加入另一种防锈剂；按比例加入抗氧化剂和和聚乙烯正丁基醚，继续搅拌均匀；最后按比例加入纳米PTFE树脂憎水剂，搅拌均匀后，保温4小时得到本发明的高温高湿髙盐雾地区用武器装备防护组成物。
性能测试
将本发明实施例1制备的防护组成物与市场上采购的我军装备保养用的“擦枪油”针对10#钢片进行日常防护，防护后的钢片进行性能检测，其结果如表1所示。
表1
| 市场采购样品 | 实施例1 | 检测依据 | |
| 耐湿热性能 | 120h | 960h | GB/T 2361 |
| 耐盐雾性能 | 24h | 96h | GB/T 0081 |
| 耐盐浸渍性能 | 20h | 48h | GB/T0025 |
| 水置换性能 | -- | 合格 | SH/T0036 |
| 磨斑直径 | 3.5mm | 0.45mm | SH/T0189 |
从表1中可以看出，本发明的防护组成物相较于现有的防护产品，具有较好的防护功效，尤其是在极端环境下使用的武器装备的防护，使武器装备在极端环境下具有较高的使用寿命。
本文中应用了具体个例对本发明的原理及实施方式进行了阐述，以上实施例的说明只是用于帮助理解本发明的方法及其核心思想；同时，对于本领域的一般技术人员，依据本发明的思想，在具体实施方式及应用范围上均会有改变之处。综上所述，本说明书内容不应理解为对本发明的限制。
Claims (10)
1.一种高温高湿髙盐雾地区用武器装备防护组成物，其特征在于，包括以下重量分数的组分：
粘度指数改进剂5-10％
防锈剂3.6-13.5％
抗氧剂0.5％
分散剂1.5％
憎水剂1％
其余为基础油。
2.根据权利要求1所述的高温高湿髙盐雾地区用武器装备防护组成物，其特征在于，所述粘度指数改进剂包括聚甲基丙烯酸酯、聚异丁烯或聚乙烯正丁基醚中的一种或几种。
3.根据权利要求1所述的高温高湿髙盐雾地区用武器装备防护组成物，其特征在于，所述防锈剂是由T701防锈剂、T705防锈剂以及T711防锈剂构成。
4.根据权利要求3所述的高温高湿髙盐雾地区用武器装备防护组成物，其特征在于，所述T701防锈剂占防护组成物总重量的3-9％，所述T705防锈剂占防护组成物总重量的0.5-3.5％，所述T711防锈剂占防护组成物总重量的0.1-1％。
5.根据权利要求1所述的高温高湿髙盐雾地区用武器装备防护组成物，其特征在于，所述抗氧剂为T501抗氧化剂，所述分散剂为T154分散剂。
6.根据权利要求1所述的高温高湿髙盐雾地区用武器装备防护组成物，其特征在于，所述憎水剂为纳米氟化树脂。
7.根据权利要求6所述的高温高湿髙盐雾地区用武器装备防护组成物，其特征在于，所述纳米氟化树脂包括纳米PTFE树脂、纳米FEP树脂或纳米氟化聚氨酯树脂中的一种或几种。
8.根据权利要求1所述的高温高湿髙盐雾地区用武器装备防护组成物，其特征在于，所述基础油为矿物基础油或合成油。
9.根据权利要求8所述的高温高湿髙盐雾地区用武器装备防护组成物，其特征在于，所述基础油为45号变压器油。
10.根据权利要求1-9任一项所述的温高湿髙盐雾地区用武器装备防护组成物的制备方法，其特征在于，包括以下步骤：将基础油加入到搅拌釜中，开启搅拌，加热恒温在80℃±2℃；在不断搅拌过程中按比例加入分散剂，并搅拌均匀；按比例加入防锈剂；按比例加入抗氧化剂和和粘度指数改进剂，继续搅拌均匀；最后按比例加入憎水剂，搅拌均匀后，保温4小时得到本发明的高温高湿髙盐雾地区用武器装备防护组成物。