CN1102379C - 牙齿脱敏用可分散微粒系统 - Google Patents

牙齿脱敏用可分散微粒系统 Download PDF

Info

Publication number
CN1102379C
CN1102379C CN96194361A CN96194361A CN1102379C CN 1102379 C CN1102379 C CN 1102379C CN 96194361 A CN96194361 A CN 96194361A CN 96194361 A CN96194361 A CN 96194361A CN 1102379 C CN1102379 C CN 1102379C
Authority
CN
China
Prior art keywords
salt
clay
described compositions
dentifrice
laponite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN96194361A
Other languages
English (en)
Other versions
CN1186426A (zh
Inventor
K·马尔科威茨
M·Y·格尔费
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Block Drug Co Inc
Original Assignee
Block Drug Co Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Block Drug Co Inc filed Critical Block Drug Co Inc
Publication of CN1186426A publication Critical patent/CN1186426A/zh
Application granted granted Critical
Publication of CN1102379C publication Critical patent/CN1102379C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

通过用含水辉石粘土，特别是合成锂皂石粘土的口腔用组合物处理牙齿来治疗过敏牙齿的方法。

Description

牙齿脱敏用可分散微粒系统
1.发明领域
本发明涉及处理过敏牙齿的新的脱敏剂及制备和使用这种脱敏剂的方法。
2.背景技术
当被感染牙齿中神经接触包括温度及触觉刺激的某些外界刺激时，牙齿过敏引起患者口腔疼痛。牙齿过敏的原因之一可能是因外伤、疾病或其它原因被感染的牙齿的牙质过度接触刺激原。牙质中一般带有通道，称作髓管。通过髓管在牙质外和存在神经的牙齿内之间转运物质和能量。这些髓管接触外界刺激可引起牙神经发炎，引起不适。虽然过敏的确切机理尚在研究中，最近的研究表明气流引起的疼痛与每单位面积牙质中暴露髓管的数量有关(Kontturi-Narhi，DentinHypersensitivity-Factors Related to the Occurrence of PainSymptoms(与疼痛症状有关的牙齿过敏因素).Kuopio UniversityPublications B.Dental Sciences 5)。按照牙齿过敏的流体动力学理论，对无釉质的、暴露的牙质表面的机械及热刺激引起髓管内流体的细微运动。这些流体运动引起疼痛，带动位于牙质/髓界面附近牙质内神经中的神经反应。最近研究结果证明，实验数据支持这种联系(B.Matthewsand N.Vongsavan Archs Oral Biol，39(增补)：875-955，1994)。
一般通过处理牙神经使其对刺激不敏感或通过阻断，或封闭髓管以防止或限制神经接触外界刺激，并限制牙髓管中刺激引起的流体运动来治疗牙齿过敏。
直接影响神经的治疗一般干扰神经附近的电解质平衡以使神经外表面受影响，使得此神经不象为处理神经那样经常地、强烈地反应。按此方法治疗牙齿过敏所用的制剂包括硝酸钾(见美国专利3863006，Hodosh，1975年1月28日)、氯化钾(见美国专利4751072，Kim，1988年6月14日)、碳酸氢钾(见美国专利4631185，Kim，1986年12月23日)、氯化锶(见美国专利3122483，Rosenthal，1964年2月25日)。
封闭髓管提供了另一种治疗方法。所用的、已报道的制剂包括聚合物制剂如水溶乙烯聚合物(Carbopol)(见美国专利5270031，Lim等，1993年12月14日)及某些聚苯乙烯珠(见美国专利5211939，Turesky等，1993年5月18日)。
磷灰石也可用作抗过敏剂。Scheller的美国专利4634589(1987年1月6日)和美国专利4710372(1987年12月1日)公开了含有磷灰石和任意含有局部麻醉剂的、治疗过敏牙齿的洁牙剂，磷灰石的平均粒度小于10微米。其它可溶性无机盐未被允许在患者中发挥任何干扰作用。磷灰石降低了牙质通道的直径。
蒙脱石(Montmorrolinite)粘土也已被用作脱敏剂，见美国专利4992258(Mason，1991年2月12日)。遗憾的是，蒙脱石粘土与多数已知氟化剂不相容，因此限制了它的使用。此外，在无机盐如钾盐存在时，蒙脱石粘土失去了其给口腔用组合物增稠的能力，阻断髓管的能力也降低，故其作脱敏剂的用途受到了限制。
其它类型的粘土已用于牙齿领域，尽管不基于它们的脱敏能力。随着清澈凝胶洁牙剂的出现，水辉石粘土，特别是合成锂皂石(Laponite)粘土，已用作洁牙剂的增稠剂，例如Harrison的美国专利4069310及Mayes，B.“Synthetic Hectorite--A New ToothpasteBinder(合成水辉石--一种新型牙膏粘合剂)”，International Journalof Cosmetic Science，1329-340(1990)。虽然洁牙剂中增稠剂和粘合剂的含量一般约1％(重量)，但Harrison在其专利中指出增稠剂的含量可高达5％。确实，上述Mason的专利指出合成锂皂石可以是洁牙剂中的增稠剂之一，但是其中并无蒙脱石粘土作为脱敏剂的教导。
美国专利4474750(Gaffar等，1984年10月2日)公开了牙膏、牙齿用霜剂或凝胶，其中增稠剂可以是Laponite CP或SP，其含量不超过约10％(重量)。此专利中未公开为治疗过敏牙齿的目的在洁牙剂中掺入合成锂皂石。
美国专利4081526(Asakawa等，1978年3月28日)公开了洁牙剂，其中含有0.5至13％水辉石粘土例如合成锂皂石，目的是清除牙斑。
尽管人们在脱敏剂领域已进行了很多工作，本领域依然存在强烈的、长期的要求，要求得到有效的髓管阻断剂，它与氟化物及其它常规洁牙剂组份相容。此制剂必须很好地起作用，并易于被人接受。就洁牙剂的典型货架寿命而言，它必须是稳定的，并使消费者在经济上能够承受。
本发明概述
本发明的主要目的是提供与氟化物及其它常规洁牙剂组份相容的且感官感觉也可接受的髓管阻断剂。
本发明的其它目的和优点将在下面的说明书中给出，或从此说明书看来是显而易见的，或可以通过本发明的实施而领会到。本发明的这些目的和优点可以通过权利要求书中特别指出的方式和结合形式来体会并得到。
为了达到上述目的并按照本发明的目的，正如本文中体现并详细描述的，本发明提供了一种含水辉石粘土如合成锂皂石粘土的、过敏牙齿用脱敏剂。
为进一步实现上述目的并按照本发明的目的，本发明进一步提供了治疗过敏牙齿的方法，即让含治疗量水辉石粘土如合成锂皂石粘土的脱敏制剂与牙齿接触。
优选实施方案的描述
现详细给出的本发明优选实施方案。
本发明包括治疗过敏牙齿的组合物，如洁牙剂(牙膏或牙凝胶)或其它适当的口腔用载体。此组合物含有水辉石粘土，其含量及配方足以使牙齿脱敏。优选的水辉石粘土包括合成锂皂石粘土，特别优选的是经处理的，所谓“合成”水辉石粘土如合成锂皂石D(LAPONITE D)和合成锂皂石DF(LAPONITE DF)，它们都由Southern ClayProducts，Inc.出售。这些粘土经处理后适于牙科用(作为清澈凝胶洁牙剂的增稠剂)，而LAPONITE DF经处理向粘土中加入了氟元素以防止由洁牙剂制剂中吸收氟离子。其它优选的合成锂皂石粘土，商品名LAPONITE，为Laporte Industries Inc.的产品。合成锂皂石粘土是含镁、锂、二氧化硅、氧、氢和钠的合成水辉石粘土。象其它粘土一样，合成锂皂石以干燥圆片堆积而成。每个圆片有两层结合有氧原子的二氧化硅四面体。在这两个二氧化硅之间，有一片镁和锂以5.3至0.7比例组成的阳离子。这些阳离子与结合氧的硅的内排及OH基团相协调。用锂离子(+1)将镁离子(+2)部分代替向二氧化硅表面传递了总的负电荷。作为中间片中心(Mg，Li)的不完全复合阳离子的存在给圆片边缘传递了正电荷。
在个体堆积的圆片之间为可交换阳离子如钠离子。当合成锂皂石粘土适当地分散于水中时，这些可交换阳离子通过渗透力将水吸入圆片之间。这种水的大量流入使圆片分离。在低电解质浓度下，当合成锂皂石粘土适当分散于水中时，阴离子二氧化硅表面及阴离子边缘可靠静电互相接触。这导致所谓的“板房结构”(card house structure)的形成。剪向力可以容易地破坏此板房结构。这种结构的形成和被剪向力的破坏意味着合成锂皂石粘土分散液具有显著的触变性，使它们成为增稠剂，特别是对于清澈凝胶洁牙剂。
但是，重要且出人意料的是，有利于合成锂皂石粘土分散液构成凝胶制剂的浓度和化学环境对脱敏能力未必有利。通过髓管阻断实验测量，分散有合成锂皂石粘土以防止或阻碍凝胶结构形成的组合物显示出极好的脱敏能力。这种组合物一般比具有理想凝胶结构的组合物使用较高量的粘土。此外，无机分散剂和有机聚合物分散剂提高了合成锂皂石粘土的脱敏能力。加入这种分散剂的、含合成锂皂石粘土的组合物具有极好的效果，并带有令人愉快的感官感觉特性，且与氟化物及大多数洁牙剂组份相容。
就其与氟化物共存于洁牙剂中的能力来说，氟化物处理的合成锂皂石粘土是优选的。检测含氟化物源和水辉石粘土或氟化物处理的合成锂皂石粘土的洁牙剂及混合物的氟化物生物利用度，含未处理的水辉石粘土的洁牙剂的氟化钠利用度下降，而氟化物处理的合成锂皂石粘土洁牙剂保持完全的氟化物生物利用度。
洁牙剂制剂优选为牙膏或凝胶的形式，其中含有约0.1％至约25％(重量)的粘土。更优选此粘土含量为约1％至约20％(重量)，并且最优选约2％至约15％。也可将此粘土掺入其它口腔护理剂如漱口水及洁牙剂制剂中。
粘土的流动降低性能可通过加入分散剂如盐、增稠剂及其它添加剂被惊人地改善。优选的盐包括钾盐、锶盐(特别优选的盐包括脱敏用盐，如硝酸钾、氯化钾、碳酸氢钾及氯化锶)及焦磷酸盐，特别是焦磷酸四钾和四钠及焦磷酸的酸式钾和钠盐。优选的增稠剂包括聚合物增稠剂，并特别优选纤维素增稠剂，包括离子修饰的纤维素聚合物如羧甲基纤维素钠(Aqualon的产品)及阳离子修饰的纤维素聚合物，称为CELQUAT(National Startch and Chemical Company的产品)。就其本身实验而言，用实施例中的技术测试CELQUAT聚合物引起不连贯的牙质流体流动的降低。相反，当对部分含合成锂皂石粘土的原形洁牙剂实验时，观察到连贯的较大流动降低。
虽然，发明人不希望生搬硬套任何理论，显然水辉石粘土，特别是合成锂皂石粘土，含有多个具正电荷边缘和负电荷扁平表面的个体无机圆片。似乎阳离子修饰的纤维素及其它正电荷体可以与粘土的阴离子表面作用，使粘土更好地分散，使其具有适于透过牙质髓管的粒度。同时，颗粒的电化学特性的改进，使粘土对髓管壁的静电粘附力提高。粘土化学方面在上述Mayes的文章及Pinnavaia等的美国专利4621070(1986年11月4日)中讨论得更详细。
使用粘土的漱口液可以是口腔用溶液或悬浮液的形式。漱口液可以含有常规矫味剂、着色剂及其它具有感官感觉或治疗作用的添加剂。
用水辉石粘土制备的洁牙剂一般以水为基质并含有湿润剂如甘油、山梨醇或其它糖醇、丙二醇或聚乙二醇。此洁牙剂可以是牙膏或牙凝胶。凝胶剂可以是碱金属羧甲基纤维素、羟乙基纤维素或羟甲基纤维素、合成生物聚合胶、viscarin、小角叉菜胶(iota carrageenan)、明胶、淀粉、葡萄糖、蔗糖、聚乙烯吡咯烷酮、聚乙烯醇、黄蓍胶、gumdaraya、羟丙基纤维素、甲基纤维素及藻酸钠、硅酸铝镁凝胶。优选与氟化物相容的试剂。
用于此洁牙剂中的其它试剂为抛光剂如沉淀二氧化硅、水合二氧化硅及其它已知磨擦抛光剂，氟化物，清洁剂、着色或增白剂如二氧化钛、芳香剂和矫味剂。其它治疗剂如牙石控制剂、抗菌剂如三氯生或洗必太。
本发明的洁牙剂可以通过将组份以任何常规方法混合制备，例如通过用水及凝胶剂制备凝胶，然后加入水溶性组份。最后，加入表面活性剂，并再加疏水性组份。然后将此混合物装于常规洁牙剂容器如管中，并通过常规方法如刷、包被、涂敷或其它直接或间接使用技术用于牙表面。
本发明的优点将在下列实施例中给出。
实施例
实验方法
用Pashley首先描述(J.Periodontology，Vol.55，No.9 p.522，1984年9月)的牙质敏感性体外模型检测水辉石粘土和多种组份在水中的分散液及含水辉石粘土的原形洁牙剂。美国专利5270031(Lim等，1993年12月14日)也描述了这种方法。
在此方法中，完整的、无龋或修补的臼齿被冶金锯垂直于牙齿的长轴方向切成厚约0.4至0.6mm的切片。含牙质而无釉质的切片留作实验。然后将这些切片用EDTA(乙二胺基四乙酸)溶液侵蚀除去涂层。将此片置于裂解室装置上，如J.Dent.Research，57：187(1978)所述。此特殊防漏室与含组织培养液的加压流体库相连。通过使用加压的氮气和二氧化碳气，此流体可以维持生理pH。为了进一步确保准确，用人唾液将此片润温至接近口腔内条件。包括玻璃毛细管的仪器放置于标尺或其它测量仪器上。将空气泡注入玻璃毛细管中。通过测量此气泡的位移来测量流体通过牙质片的时间。(已有报道流体准确地从正常人齿内的牙质髓管中流出。)
检测了牙质片中基准流体流动后，用尼龙刷将实验混合物或洁牙剂涂于外片表面。经一段确定时间的涂刷后，将实验物质清洗掉，并测量涂刷后的水传导力。以这种方式，可以测量不同实验物质阻塞牙质髓管中流体流动的能力，不论是单独的还是作为洁牙剂系统组份的。然后计算涂刷实验物质引起的流动降低的百分率。
实施例1-5
制备合成锂皂石粘土与水及其它特定组份的组合物并用上述方法测定其降低流动的能力。每种结合形式的组份见表1，其降低流动的能力也见表1。这些实施例表明水辉石粘土具有良好的降低牙质流体流动的能力，特别是当粘土与分散剂如聚合物分散剂或盐合用时更是这样。
表1
合成锂皂石的含水组合物的降低流动百分率
实施例     处理  涂刷后流体流动的降低
    1     5％LAPONITE D     55.3％
    2     5％LAPONITE DF，0.25％NaF     48.0％
    3     5％LAPONITE DF，5％KNO3     54.2％
    4     5％LAPONITE DF，5％KNO3，4％羧甲基纤维素，0.25％NaF     83.4％
    5     5％LAPONITE DF，5％KNO3，0.25％NaF，阳离子纤维素聚合物CELQUAT 240 SC(8％)     96.0％
实施例6-13
按照下列方式制备下列洁牙剂制剂。向装有真空系统的、适当的混合器(如实验室用whipmixer或工厂大批量用Koruma混合器)中，加入需要量的纯水。向混合器中加入关键组份如氟化钠(或MFP钠)、焦磷酸四钾、磷酸三钠、适当的钾盐或锶盐，然后加入糖精钠、二氧化硅及LAPONITE DF。将上述混合物混合约10-30分钟(真空下)，然后加入磨擦剂、预先混合的树胶(湿润剂和树胶)、矫味剂和清洁剂。最后真空混合20-30分钟除去产品中的空气。
实施例6
组份                     重量百分数
合成锂皂石DF              5.0
氟化钠                    0.24
山梨醇溶液                20.0
甘油                      20.0
二氧化硅                  1.0
无定型二氧化硅            10.0
羧甲基纤维素              1.5
聚羧乙烯制剂              0.1
糖精钠                    0.3
二氧化钛                  0.5
可可酰氨基丙基甜菜碱      5.0
无水磷酸三钠              1.0
矫味剂                    1.5
纯水                      适量至100.0
实施例7
组份                      重量百分数
合成锂皂石DF              8.0
氟化钠                    0.32
氯化钾                    4.0
水合二氧化硅              10.0
羟乙基纤维素                           1.5
糖精钠                                 0.3
十二烷基硫酸钠                         1.5
三氯生                                 0.3
山梨醇溶液                             40.0
矫味剂                                 1.3
纯水                                   适量加至100.0
实施例8
组份                                   重量百分数
合成锂皂石DF                           6.0
MFP钠                                  0.8
二氧化硅                               2.0
二水合磷酸二钙                         30.0
羧甲基纤维素                           1.0
糖精钠                                 0.25
二氧化钛                               0.5
可可酰氨基丙基甜菜碱                   7.0
可可甲基酸(cocomethyl acid)牛磺酸钠    0.75
无水磷酸三钠                           1.0
山梨醇溶液                             10.0
甘油                                   25.0
矫味剂                                 1.2
纯水                                   适量加至100.0
实施例9
组份                                   重量百分数
合成锂皂石DF                           7.5
MFP钠                                  0.8
二氧化硅                               1.0
碳酸钙                                 15.0
羧甲基纤维素                           1.0
聚羧乙烯制剂                 0.1
糖精钠                       0.3
二氧化钛                     0.5
十二烷基硫酸钠               1.5
焦磷酸二钠                   0.3
山梨醇溶液                   30.0
甘油                         10.0
矫味剂                       1.3
纯水                         适量加至100.0
实施例10
组份                         重量百分数
合成锂皂石DF                 5.0
氯化钾                       3.75
氟化钠                       0.24
二氧化硅                     1.5
无定型二氧化硅               10.0
羧甲基纤维素                 2.0
聚羧乙烯制剂                 0.1
糖精钠                       0.35
二氧化钛                     0.5
可可酰氨基丙基甜菜碱         6.0
可可甲基酸牛磺酸钠           0.5
焦磷酸四钾                   3.0
三氯生                       0.3
矫味剂                       1.3
山梨醇溶液                   40.0
纯水                         适量加至100.0
实施例11
组份                        重量百分数
合成锂皂石DF                 5.0
氟化钠                     0.243
焦磷酸四钾                 3.0
枸橼酸钾                   5.0
水合二氧化硅               12.0
羟乙基纤维素               1.4
糖精钠                     0.3
可可甲基酸牛磺酸钠         1.5
无水磷酸三钠               0.5
山梨醇溶液                 12.0
甘油                       12.0
矫味剂                     1.2
纯水                       适量加至100.0
实施例12
组份                       重量百分数
合成锂皂石DF               5.0
氟化钠                     0.243
焦磷酸四钾                 3.0
碳酸氢钾                   3.0
水合二氧化硅               12.0
羟乙基纤维素               1.4
糖精钠                     0.3
可可甲基酸牛磺酸钠         1.5
无水磷酸三钠               0.5
山梨醇溶液                 12.0
甘油                       12.0
矫味剂                     1.2
纯水                       适量加至100.0
实施例13
组份                       重量百分数
合成锂皂石DF               6.0
氯化锶六水合物             10.0
二氧化硅                   1.0
水合二氧化硅               12.0
糖精钠                     0.3
二氧化钛                   1.0
羧甲基纤维素               1.5
可可甲基酸牛磺酸钠         1.2
山梨醇溶液                 12.0
矫味剂                     12.0
甘油                       1.2
纯水                       适量加至100.0
对上述几种洁牙剂制剂的降低牙质流体流动的能力进行实验。实验结果见表2。
表2
            所选洁牙剂降低流动的百分数
实施例号           主要组份  流动降低率(％)
实施例6 合成锂皂石(5％)，NaF(0.24％)     79％
实施例7 合成锂皂石(8％)，NaF(0.32％)     82％
实施例10 合成锂皂石(5％)，NaF(0.24％)，焦磷酸四钾(3％)     87％
上述说明的目的在于举例说明本发明的一些实施方式，而不是限制本发明。对本领域技术人员来说，在不背离本发明的范围和精神的前提下，用本发明的仪器或按照本发明的方法作出不同的修饰和变化是显而易见的。

Claims (13)

1.一种治疗过敏牙齿的组合物，其中含有脱敏有效量的脱敏剂和载体，其特征在于所含脱敏剂是水辉石粘土。
2.权利要求1所述的组合物，其中所述粘土是合成锂皂石粘土。
3.权利要求2所述的组合物，其中所述粘土含有氟化物。
4.权利要求1所述的组合物，其中还含有分散剂。
5.权利要求4所述的组合物，其中所述分散剂是盐。
6.权利要求5所述的组合物，其中所述盐是碱金属盐。
7.权利要求4所述的组合物，其中所述盐选自焦磷酸、硝酸、氢卤酸、枸橼酸、碳酸、碳酸氢的碱金属盐，及锶盐及其混合物。
8.权利要求4所述的组合物，其中所述分散剂是纤维素化合物。
9.权利要求8所述的组合物，其中所述纤维素化合物是阳离子修饰的。
10.权利要求9所述的组合物，其中所述纤维素化合物含有阳离子修饰的纤维素。
11.权利要求10所述的组合物，其中还含有盐。
12.权利要求11所述的组合物，其中所述盐是碱金属盐。
13.权利要求12所述的组合物，其中所述盐选自焦磷酸、硝酸、氢卤酸、枸橼酸、碳酸、碳酸氢的碱金属盐，及锶盐及其混合物。
CN96194361A 1995-04-11 1996-04-10 牙齿脱敏用可分散微粒系统 Expired - Fee Related CN1102379C (zh)